The Effect of Negative electric field using charged PTFE membrane on Bone Healing of Rabbit Long Bone (Charged membrane에 의한 negative electric field가 토끼 장골의 골 치유에 미치는 영향)

  • Kwon, Yong-Su;Park, Jin-Woo;Lee, Jae-Mok;Suh, Jo-Young
    • Journal of Periodontal and Implant Science
    • /
    • v.34 no.3
    • /
    • pp.551-562
    • /
    • 2004
  • The purpose of this study was to evaluate the effects of negatively electric field on bone healing in rabbit segmental long bone defects using negatively charged PTFE membrane. Ten millimeter segmental defects in the rabbit radius were used as the experimental model. After membranes were then charge injected using a corona-charging apparatus, the left defects were covered with non charged PTFE membranes as control groups, whereas the right defect was covered with negatively charged PTFE membranes as test group. The animals were divided into 4 groups of 2 rabbits each, and sacrificed at 2, 4, 6, and 8 weeks. Histomorphometric analysis showed a more newly formed bone in negatively charged membrane at early healing period. At 2 weeks, the proportion of new bone formation to total defect area was 0.32% in control group, 1.10% in experimental group. At 4 weeks, the proportion of new bone formation to total defect area was 6.86% in control, and 13.75% in experimental. At 6 and 8 weeks, no obvious difference was found between the two groups but newly formed bone in test groups were slightly more than that in control groups. In conclusion, negatively charged membranes showed more newly bone tissue than noncharged membranes at an early healing period. Although the number of samples was small, this study showed that the combination of negatively electrical stimulation and P1FE membrane may be of value in long bone healing.

A Study on the Fundamental Properties of Mortar Mixed with Converter Slag and Ferronickel Slag (전로슬래그 및 페로니켈슬래그를 혼입한 모르타르의 기초물성 연구)

  • Kim, Ji-Seok;Park, Eon-Sang;Ann, Ki-Yong;Cho, Won-Jung
    • Journal of the Korean Recycled Construction Resources Institute
    • /
    • v.9 no.2
    • /
    • pp.152-160
    • /
    • 2021
  • Converter steel slag(BOF slag) is a vast amount of solid waste generated in the steelmaking process which has very low utilization rate in Korea. Due to the presence of free CaO which can derive bad volume stability in BOF slag, it usually land filled. For recycling BOF and identify its applicability as fine aggregate, this study investigates the fundamental characteristics of mortar with cement replaced ferronickel slag(FNS), which has the potential to be used as a binder. The results suggest that the mineral phases of BOF slag mainly include larnite(CaSiO4), mayenite(Ca12Al14O33) and wuestite(FeO) while olivine crystallines are shown in FNS. The results of flow and setting time reveals that the flowability and process of hardening increased when the amount of FNS and BOF slag incorporated was increased. The length change shows that the amount of change in the length of the mortar was almost constant regardless of mix proportion while compressive strength was reduced. Micro structure test results revealed that FNS or/and BOF slag mix took a long time to react in the cement matrix to form a complete hydration products. To achieve the efficient utilization of B OF slag as construction materials, proper replacement rate is necessary.

A Study on the Fundamental Properties of Concrete Using of the Oyster Shells (굴패각 콘크리트의 기본특성에 관한 연구)

  • Koo, Hae-Shik;Jun, Hak-Su;An, Yong-Deok
    • Journal of the Korea institute for structural maintenance and inspection
    • /
    • v.9 no.3
    • /
    • pp.169-177
    • /
    • 2005
  • This study is to analyze the application of the oyster shells as a substitute fine aggregate of concrete. For this purpose, the fundamental experiments of the composed materials and the variations of the main factors on it were considered and then the variations of workability and strength properties of the specimens with each case were also studied. The experimental results on the properties as construction material showed that the use of oyster shells in concrete would not cause abnormal chemical reactions or lead to the formation of any new objects, the workability and strengths decreased with increase in proportion of oyster shells. The compressive strength of concrete with oyster shells is developed as much as that of normal concrete and the grain size of oyster shells is superior on 3.0~5.0mm and the percentage of substitution of them to fine aggregate about 30% from the properties of concrete with them. The relationship equation between compressive strength and tensile strength is ( ).

Effects of Ulmus davidiana Planch(Ulmaceae) herbal acupuncture solution on the proliferation of human bone cells (유근피 약침액이 인체의 골세포 증식에 미치는 영향)

  • Lee, Eon-do;Kim, Kap-sung
    • Journal of Acupuncture Research
    • /
    • v.21 no.4
    • /
    • pp.237-249
    • /
    • 2004
  • 유근피는 혈액청정작용과 혈액순환에 영향을 주는 성분으로서 골 손상의 처방전으로 자주 사용된다. 현재까지 유근피가 골재형성에 미치는 영향은 약리학적으로 불확실하였다. 이에 저자들은 본 연구에서 유근피를 약침액으로 제조하여 유근피 약침액이 골세포에 미치는 영향을 in vitro에서 연구하였다. 방법으로 인체의 골아전구세포osteoprecursor cells (OPC-1)를 각각의 다른 유근피 농도를 함유한 매체내에서 부화시키고 그에 따른 세포증식을 연구하였으며, 유근피 약침액의 농도가 $100{\mu}g/ml$ 미만이었을 때 OPC-1의 증식량은 증가되었다. 그러나 농도가 $180{\mu}g/ml$을 초과하였을 때는 약물의 독성에 의해서 OPC-1의 증식량이 확연히 억제되었다. 대부분의 처치에서 세포들이 cyclooxygenase-2 (Cox 2) 단백질에 대해서 매우 명백한 발현을 보여줬다. 배양과정 중에 유근피 약침액 농도 최소치인 $1.0{\mu}g/ml$에서 최대치인 $500{\mu}g/ml$까지 경미하게 강화된 띠를 나타내었다. 이와 같은 실험의 결과로 볼 때 유근피 약침액은 골세포의 증식활동, alkaline phosphatse(ALP) 활동 및 total protein 분비의 증가와 골세포내에서의 농도의존적 약침액 투여량에 따른 OPC-1의 독특한 type I collagen 합성에 직접적인 억제작용을 주는 것을 관찰할 수 있으므로 추후 이와 유사한 실험을 통한 보다 발전적인 연구가 이루어져야 한다고 사료되었다.

  • PDF

Analysis of Pore Characteristics on the Porous Body-Porosity Index of Ic and Is in Light Weight Aggregate (다공체 소지의 기공 특성 분석-경량골재에서의 기공지수 Ic와 Is에 대하여)

  • 권영진;이기강
    • Journal of the Korean Ceramic Society
    • /
    • v.41 no.2
    • /
    • pp.176-181
    • /
    • 2004
  • EAF (Electric Arc Furnace) dust is classified as special wastes containing heavy metal contaminants may cause to damage an environment such as underground water contamination if they were not treated properly. For reutilizing the EAF dust, the porous body was made from EAF dust/clay composition system, and analyzed pore characteristics. It was found that a light-aggregate body was made up two different microstructures. One was non-black and dense microstructure which located near surface, and the other was black and porous microstructure (black coring) which located inner part. For systematizing the relationship of the black-coring area and the bloating degree, we defined the Ic(core index) and Is(shell index). It was found that the optimal bloating conditions of artificial light-weight aggregate were more than 0.5 of Ic and 0.4 of Is.

The Expression of Type I Collagen in Periodontal Tissue during the Experimental Movement of Rat Incisors (백서의 실험적 치아 이동시 교원질 발현에 관한 면역조직화학적 연구)

  • Kim, Sang-Cheol;Jeon, In-Seop
    • The korean journal of orthodontics
    • /
    • v.26 no.4
    • /
    • pp.455-467
    • /
    • 1996
  • This study was designed to evaluate the expression of type I collagen in periodontal tissue during the experimental movement of rat incisors. Twenty-one Sprague-Dawley rats were divided into a control group(3 rats), and experimental groups(18 rats) where a force(75g) from helical springs across the maxillary incisors was applied. Experimental groups were sacrificed at 12 hours, 1, 4, 7, 14 and 28 days after force application, respectively. And tissue slides of control and experimental groups were studied histologically and immunohistochemically by LSAB(Labelled streptavidine Biotin) immunohistochemical staining for type I collagen. The results were as follows: 1. Until 28-day after force application, periodontal fibers were strectched on the tension side, and compressed in pressure side, and the arrangement of periodontal fibers was not recovered by that time. 2. The degree of type I collagen expression in control group was rare in the oral epithelium, predentin, pulp and periodontal ligament, but was mildly positive in osteoblasts, acellular cementum, cementoblasts, intermaxillary suture. 3. At acellular cementum of experimental group, the expression of type I collagen was moderate in 1-day and severe in 7-day, which was maintained until 28-day. 4. Type I collagen was observed in the newly formed fibrous connective tissue and osteoblasts at intermaxillary suture, moderately in 1-day, and severely in 14-day. 5. The tension side of periodontal ligament showed a more positive expression of type I collagen than the pressure side in 4-day. The degree was highest in 7-day and was not differentiated between sides in 14-day. 6. In the side wall of bone matrix on which osteoblasts were attached, type I collagen was expressed severely, especially in 7-day. From the above findings, we could suggest that bone remodeling in tooth movement be intimately related to the cell differentiation and the resulting formation of type I collagen.

  • PDF

The Effect of Recombinant Human Bone Morphogenetic Protein-2/Macroporous Biphasic Calcium Phosphate Block system on Bone Formation in Rat Calvarial Defects (백서 두개골 결손부에서 bone morphogenetic protein-2의 전달체로서 macroporous biphasic calcium phosphate-block의 골재생효과)

  • Lee, Young-Jun;Jung, Sung-Won;Chae, Gyung-Joon;Cho, Kyoo-Sung;Kim, Chang-Sung
    • Journal of Periodontal and Implant Science
    • /
    • v.37 no.sup2
    • /
    • pp.397-407
    • /
    • 2007
  • 골형성 유도 단백질(bone morphogenetic protein, BMP)은 성장이나, 골형성과정에서 중용한 역할을 한다고 입증되었고 그것의 운반체에 대한 연구가 이뤄져 왔다. 하지만 수직압이 존재하는 곳에서 골증대술에 적용할 수 있을 만큼 강한 공간유지능력이 있는 운반체에 대한 연구는 그리 많지 않았다. Macroporous biphasic calcium phosphate block (MBCP block)은 공간유지능력이 뛰어나며 강한 수직압을 견딜수 있는 골대체물질이다. 이 연구의 목적은 MBCP block을 골형성유도 단백질(rhBMP-2)의 운반체로 사용하여 백서 두개골 결손부에 적용하였을 때, 골 형성 효과를 평가하는 것이다. 36마리의 웅성백서에서 8mm 지름을 갖는 임계크기의 두 개부 결손을 형성하였다. 20마리씩 2개의 군으로 나누어 MBCP block만 이식한 군, MBCP block을 운반체로 사용하여 농도 0.025mg/ml rhBMP-2를 이식한 군으로 나누어 술 후 2주와 8주에 치유결과를 조직학적, 조직계측학적으로 비교 관찰 하였다. 조직계측학적 관찰 결과, rhBMP-2/MBCP block 군에서 MBCP block군에서 보다 2, 8주 모두 골밀도(bone density)가 유의성있게 증가하였다 (P<0.01). 각 군에서도 8주째가 2주째보다 골밀도가 유의성있게 증가하였다(P<0.01). 총조직 형성량 (augmented area)에서는 변화가 없었다. 이 연구 결과, 백서 두개골 결손부에서 MBCP block은 rhBMP의 운반체로 사용하였을 때 신생골 형성에 유의한 효과가 있을뿐 아니라 공간유지능력이 우수해서 수직압이 존재하는 골증대술(bone augmentation)시 rhBMP의 운반체로 가능성이 있다고 사료된다.

Pulp and periodontal tissue changes following rapid tooth retraction by periodontal distraction in young adult dogs (유성견에서 periodontal distraction에 의한 급속 치아견인 시 치수 및 치주조직의 변화에 관한 연구)

  • Lee, Jong-Jin;Hong, Hyun-Sil;Chae, Jong-Moon;Jo, Jin-Hyung;Kim, Sang-Cheol
    • The korean journal of orthodontics
    • /
    • v.37 no.5
    • /
    • pp.351-363
    • /
    • 2007
  • The aim of this study was to evaluate pulp and periodontal changes following rapid tooth retraction by periodontal distraction after bone undermining surgery in young adult dogs. Methods: Alter extraction of second premolars, the interseptal bone mesial to the upper 3rd premolar was undermined. After activating the distraction appliance at 0.5 mm/day for six days, the dogs were sacrificed at 0, 1, 3, 5, 7, and 9 weeks during the consolidation period. Tissue changes of periodontium and pulp were evaluated radiologically, histologically, and immunohistochemically. Results: Digital subtraction radiography showed active bone formation in the stretched periodontal ligament from 0 - 4 weeks. Resorption of the alveolar bone, appearance of osteoclasts, and infiltration of inflammatory cells were observed just after the activation period at the pressure side, and distinctive bone formation was seen in the tension side of the periodontal ligament from 1 week. New bone formation was active at 1 - 3 weeks. The expression of calcitonin gene-related peptide in the experimental group was increased at the alveolar bone and pulp, and periodontal ligament at the pressure side from 0 - 1 week, and it decreased after 5 weeks to become similar to that of the control group. Conclusions: The results showed that rapid tooth movement using periodontal distraction can be new form of orthodontic tooth movement for accelerating normal bone formation.

Tissue Engineered Bone Formation Using Porous Chitosan and Chitosan/Tricalcium Phosphate Matrices (Chitosan 및 Chitosan/Tricalcium Phosphate 다공성 기질을 이용한 조직공학적 골형성에 관한 연구)

  • Lee, Yong-Moo;Choi, Sang-Mook;Park, Yoon-Jeong;Lee, Seung-Jin;Ku, Young;Chung, Chong-Pyoung
    • Journal of Periodontal and Implant Science
    • /
    • v.28 no.4
    • /
    • pp.577-604
    • /
    • 1998
  • chitosan은 골치유증진 및 골세포의 분화를 촉진하는 것으로 알려진 천연의 생분해성 고분자이다. 이연구에서는 chitosan 및 chitosan/tricalcium phosphate(TCP) 다공성 기질을 제조하여 골이식재 및 조직공학적 골형성을 위한 3차원적 세포배양 지지체로서의 가능성을 평가하고자 하였다. chitosan 용액 및 TCP가 포함된 chitosan 용액을 동결건조함으로써 소공의 크기가 $100-200{\mu}m$인 스폰지형태의 chitosan 및 chitosan/TCP 다공성 기질을 제작하였다. 골이식재로서의 효과를 평가하기 위하여 백서의 두개골 결손부에 제작된 chiosan 및 chitosan/TCP 다공성 기질을 각각 이식하고 2주 및 4주 후에 동물을 희생하여 조직학적으로 치유양상을 관찰하였다. 조직공학적 골형성을 위한 세포배양 지지체로서의 가능성을 평가하기 위하여 백서 태자의 두개골에서 분리된 골아세포를 chitosan 및 chitosan/TCP 다공성 기질에 각각 접종하고 56일간 배양하면서 각 기간 별로 세포수, 염기성 인산효소 활성, 축적된 calcium의 양을 측정하였고 배양된 세포-기질 혼합체를 광학현미경 및 주사전자현 미경하에서 조직학적 관찰을 시행하였다. 백서 두개골결손부에 이식된 chitosan 및 chiosan/TCP 다공성 기질은 별다른 이물반응 없이 자연 분해되면서 신생골조직 내에 매립되었으며 이식하지 않은 대조군에 비해 유의하게 높은 신생골형성 효과를 나타내어 우수한 골전도성이 있음이 확인되었다. 신생골형성 양상이나 형성된 양에 있어서 두 가지 기질간의 유의한 차이는 없었다. 골아세포-기질 혼합체의 배양결과, 접종후 배양 28일 경과 시까지 골아세포수는 지속적으로 증가하다가 이후에는 5 8일까지 성장정도가 둔화되었다. 염기성 인산효소의 활성 및 calcium 축적량은 접종후 배양시간경과에 따라 56일까지 지속적으로 증가하였다. 세포수 및 염기성 인산효소의 활성에서 두 기질간의 유의한 차이는 없었고, calcium 축적량에 있어서는 chitosan/TCP 기질에서 유의하게 높았고 증가속도도 컸다. 배양된 골아세포가 접종된 다공성 기질의 조직학적 관찰결과, 골아세포는 다공성 기질에 잘 부착하여 중층의 형태로 성장하면서 광화된 골기질을 형성함이 관찰되었다. 배양 14일부터 작은 골편형태의 골형성이 기질 표면에 부착되어 관찰되었고, 배양기간이 길어짐에 따라 성장하여 배양 56일째에는 상당한 양의 광화된 골질이 형성됨이 관찰되었다. 배양 56일 경과후의 광화된 골질의 양은 chitosan/TCP 기질에서 더 많았다. 이 연구의 결과, chitosan 및 chitosan/TCP 다공성 기질이 골이식재로서 뿐만 아니라, 조직공학적 골형성에 적용되는 골아세포의 배양을 위한 3차원구조의 세포지지체로 이용되어 골재생술식에 유용한 생체재료로 활용될 수 있음이 확인되었다.

  • PDF

Manufacture and Applications of Cellular Glass for Recycling Waste Glass (폐유리 재활용을 위한 발포유리의 제조 및 활용 기술)

  • Jeon, Bae-Ho;Kim, Jung-Gon
    • Proceedings of the Korean Society of Disaster Information Conference
    • /
    • 2017.11a
    • /
    • pp.241-242
    • /
    • 2017
  • 본 논문에서는 폐유리를 재활용하는 발포유리에 대한 기술 및 활용방법에 대한 고찰을 통해 국내에서 적용 가능한 폐유리 재활용기술에 대하여 검토하였다. 폐유리를 재활용한 발포유리는 폐유리를 분쇄한 유리 미분에 규산나트륨, 탄산칼슘, 그라파이트 등의 발포제를 첨가하여 형틀에 넣고 가열을 하면, 유리분말은 소결(sinter)상태가 되는 약 $800^{\circ}C$ 정도가 되면 녹기 시작하고, 발포제는 분해되어 $O_2$와의 반응에서 발생하는 $CO_2$ 가스에 의한 기포가 발생하여 발포유리가 형성되는 제조 방식이다. 이러한 발포유리 방식으로 제작된 판재 및 배관 형태의 불연재료는 건설 및 LGN선박용으로 널리 활용되고 있고, 인공경량 골재의 형태는 건설용 채움재 및 빗물 저류용, 정화용으로 활용되고 있다. 이러한 활용 방식은 국내에서도 충분히 적용 가능한 방식이며, 국내에서의 적용을 통해 폐기물 및 환경부하 저감 효과를 높일 수 있다.

  • PDF