• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.65-76
• /
• 1995

Weldability of DS100 and HY type high strength-toughness steel plates, tentatively produced as domestic production, was investigated. DS100 and DS130A had nearly same hardenability in HAZ in spite of its difference in Ceq. Based upon the y-groove test results, cold cracking susceptibility of DS130 was superior to that of DS100 because of its lower hydrogen level in weld metal. Solidification cracking tested by the Trans-Varestraint test was occured in all of the weld metals, and its susceptibility was high in the row of DS100, DS130A and DS130B. However, no liquation cracking and ductility-dip cracking tested by the Longi-Varestraint test with 6.0% augmented strain were detected in base metal and reheated weld metal. Toughness in the GMA welding joint was satisfied with the relative Mill Spec, even though welded joint of DS100 had relatively low impact energy especially at the weld metal.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.22-22
• /
• 1998

304 는 BWR(boiling water reactor)의 reactor 구조용 재료로 사용되고 있고, 합금 600 은 PWR(pressurized water reator) 의 증기 발생기 세관으로 쓰이고 있으며 모두 약 $280{\;}^{\circ}C$ 이상 의 원자로 냉각수에 노출되어 있다. 원자로 냉각수 분위기에서 두 합금의 공통적인 특정은 입계응력부식균열(IGSCC)에 민감한것과 IGSCC가 예민화(sensitization)와 관련이 있는 것이 다. 두 합금에서 일어나는 IGSCC는 원자력발전소의 부식피해중 가장 빈도가 높고 발생시 방사능 누출로 인하여 원전의 신뢰성을 저하시키고, 가동중단으로 인한 경제적 손실을 초 래하여 지난 20 년 동안 가장 심도있게 연구된 주제다. 304 은 크롬 탄화물의 업계 석출로 언하여 예민화된경우 IGSCC 에 민감한 반면 600 은 예민화된 경우 뿐만 아니라 용체화처리된 상태에서도 IGSCC에 민감하다. 오히려 600은 용 체화처리 후 700 C에서 15~20시간 시효처리를 하여 크롬탄화물을 업계에 석출 시커었을 때 IGSCC 저항성이 향상된다. 두 합금의 IGSCC 특정 중 큰 차이는 304는 임계균열전위 ( (critical cracking potential) 이 존재하여 부식전위(corrosion potential) 가 엄계균열전위보다 낮 은 경우 IGSCC 가 일어나지 않지만 그 반대인 경우 IGSCC 에 민감하게된다. 반면에 600 은 뚜렷한 임계균열전위가 존재하지 않고 양극 분극(anodic polarization) 뿐만 아니라 음극분극 시에도 IGSCC 가 일어난다. 이련 이유로 600의 IGSCC 가구로 피막파괴-양극용해(film rupture-anodic dissolution)외에 수소취성(hydrogen embrittlement)기구도 제안되고 었다. 원전의 냉각수는 고 순도의 물이지만 수 처리 과정과 웅축기 배관의 누수로 인한 산소, $Cu^{2+},{\;}S_xO_6{\;}^{2-}(x=3~6)$ 등이 유입되어 오염되는데 이려한 오염물질들이 수 ppm정도 소량 포함된 경우 응 력부식민감도는 상당히 증가된다. 산성분위기 흑은 산소, $Cu^{2+}$, 등이 소량 포합된 산화성 분위기 그리고 sufur oxyanion 에 오염된 고온의 물에서 600 의 IGSCC 민감도는 예민화도가 증가할 수록 민감하여 304 의 IGSCC 와 매우 유사한 거동을 보인다. 본 강연에서는 304 와 600 의 고온 물에서 일어나는 IGSCC 민감도에 미치는 환경, 예민화처리, 합금원소의 영향을 고찰하고 이에 대한 최근의 연구 동향과 방식 방법을 다룬다.

• Journal of Welding and Joining
• /
• v.6 no.4
• /
• pp.16-26
• /
• 1988

The effect of carbon content on hot cracking of welded carbon steel was investigated Eight steel plates whose carbon content range from 0.02 to 0.23 percent were welded by autogeous gas tungsten are process. Constant strain was applied to the hot crack test specimen under the strain rate of 0.15 mm per second during welding. The hot cracking susceptibility ws high in the rnage of 0.02-0.05 and 0.12-0.23 percent carbon contents. The critical carbon content immune to hot cracking is in the range from 0.07 to 0.12 percent carbon. By electron probe microanalyser, amanganese segregation was not seen significantly in the whole carbon range. But segregation of silicon was higher in the region of low carbon contents. However, sulphur was segregated remarkably in the region betwen 0.18 and 0.23 percent carbon by peritectic reaction. Very smal lamount of dnedritic structure was observed in the region from 0.02 to 0.05 percent carbon by peritectic reaction. Very small amount of dendritic structure was observed in the region from 0.02 to 0.05 percent carbon but the predominant solidification structure was smooth by cellular growth. The higher the carbon content is, the more the columnar dendritic structure was observed.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.37-37
• /
• 2003

탄소-탄소 복합체는 가벼우면서 고온에서도 강도의 저하가 적은 특성을 가지고 있어 터빈 블레이드 소재, 우주왕복선의 내열타일 등 광범위 한 고온재료로 응용이 이루어지고 있거나 기대되는 소재이다. 그러나 고온 산화분위기에서 쉽게 산화되는 단점이 있어 이러 한 산화특성을 향상시키는 방법으로 SiC, Si$_3$N$_4$ 등 내산화 저항성이 우수한 재료를 탄소-탄소 복합체 위에 코팅하는 연구가 행해지고 있다. 하지만 이들 코팅층과 탄소-탄소 복합체간의 열팽창계수 차이에 의한 열응력 발생으로 코팅층에 균열이 발생한다. 따라서 탄소-탄소 복합체와 코팅층간의 열응력을 최소화하여 균열 발생을 억제하기 위해 기능경사재료 (Functionally Graded Material, FGM)를 중간층으로 도입하는 방법이 최근 활발히 연구되고 있다. FGM 중간충의 형성방법 중 화학기상증착법 (CVD)은 증착물의 조성이나 미세구조 조절이 용이한 방법으로 알려져 있어 최근 CVD법에 의한 FGM층의 형성에 많은 연구가 진행되고 있지만, 지금까지 CVD법을 이용한C/SiC FGM 중간충의 형성 연구결과에서는 모든 조성비의 C/SiC층의 증착과 치밀한 구조를 지닌 증착층을 얻기가 어려워 체계적인 연구의 진행이 어려웠다.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.3
• /
• pp.260-267
• /
• 2021

The purpose of this study was to experimentally investigate the effects of curing methods on the compressive strength and tensile behavior of alkali-activated slag-based fiber-reinforced composite with a water-to-binder ratio of 15%. Three kinds of mixtures according to the curing conditions were prepared and compressive strength and tension tests were performed. Test results showed that the compressive strength and the first cracking strength of composites decreased when high temperature curing and air curing were adopted, while tensile strain capacity of composites increased. It was also observed that crack spacing and crack width of composites decreased by applying high temperature and air curing.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.1
• /
• pp.27-35
• /
• 2015

The material properties of crack growth models at an elevated temperature were derived from the results of numerous crack growth tests for Mod.9Cr-1Mo (ASME Grade 91) steel specimens under fatigue loading and creep loading at an elevated temperature. These crack growth models were needed for defect assessment under creep-fatigue loading. The mathematical crack growth rate models for fatigue crack growth (FCG) and creep crack growth (CCG) were determined based on the test results, and the models were compared with those of the French design code RCC-MRx to investigate the conservatism of the code. The French design code RCC-MRx provides an FCG model and a CCG model for Grade 91 steel in Section III Tome 6. It was shown that the FCG model of RCC-MRx is conservative, while the CCG model is non-conservative compared with the present test data. Thus, it was shown that further validation of the property was required. Mechanical strength tests and creep tests were also conducted, and the test results were compared with those of RCC-MRx.

• Proceedings of the KWS Conference
• /
• 1997.10a
• /
• pp.22-24
• /
• 1997

• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.168-170
• /
• 2004

터빈로터는 발전설비 중에서 가장 핵심 부분이며 동시에 심한 고온 응력을 받는 부분이다. 터빈로터 재료로는 Ni-Cr-Mo-V강과 CrMoV 강등이 사용된다. CrMoV 강은 발전 설비로 장시간 사용 중 열적피로나 크립손상, 고온 부식 등의 문제가 단독 혹은 복합적으로 발생하여 재료에 손상을 입히게 되고 결국에는 설비의 수명을 단축 시키곤 한다. (중략)

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.6
• /
• pp.1193-1202
• /
• 1989

본 논문에서는 발전소의 소재로 많이 쓰이고 있는 304 스테인리스강(앞으로는 304SS로 표기함)과 316스테인리스강(앞으로는 316SS로 표기함)의 크립 균열 발생 거동 을 각각 600.deg. C와 625.deg. C에서 조사한다. 이 온도는 발전소의 반응기(reactor)에 사용 되는 304SS와 316SS이 받는 온도이다. 즉 304SS와 316SS의 크립 균열 발생을 지배 하는 파괴 매개변수가 무엇인지가 크립 파괴 실험을 통하여 조사된다. 실험 결과는 이미 제안되어 있는 크립 균열 발생 모델에서 예측된 결과와 비교된다. 특히 304SS 와 316SS은 고온에서의 연성도가 변형률 속도에 따라 변하는 것으로 알려져 있다. 본 연구에서는 '변형률 속도에 따른 재료의 연성도의 변화에 근거한 균열 발생 모델' 을 제안하고, 그 모델에서 예측된 크립 발생 거동을 실험 결과와 비교한다.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.10a
• /
• pp.147-153
• /
• 2000

The fatigue crack propagation behavior of the SA516/70 steel which is used for pressure vessels was examined experimentally at room temperature, $150^{\circ}C$, $250^{\circ}C$ and $370^{\circ}C$ with stress ratio of R=0.1 and 0.3. The fatigue crack propagation rate da/dN related with the stress intensity factor range $\Omega\textrm{K}$ was influenced by the stress ratio within the stable growth of fatigue crack(Region II) with an increase in $\Omega\textrm{K}$. The resistance to the fatigue crack growth at high temperature is higher in comparison with that at room temperature, and the resistance attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and high temperatures are mainly explained by the crack closure and oxide-induced by high temperature.