This study is to assess the differences between concrete having only one of fine aggregates such as crushed fine aggregates, sea sand and blast furnace slag in it and concrete having mixture of two kinds of those fine aggregates in it in order to find out how to deal with the lack of some aggregates. The findings are as follows. In terms of slump, the concrete containing sea sand and blast furnace slag has very low slump values while the concrete having the mixture of crushed fine aggregate and the other fine aggregates showed better workability. In terms of compressive strength, the concrete containing the mixture of two kinds of aggregates showed higher compressive strength. Accordingly, it is likely that the concrete containing the mixture of crushed fine aggregate, sea sand and blast furnace slag is better than the concrete with only one kind of fine aggregates in terms of the usability.

• 한국건설순환자원학회논문집
• /
• 제6권4호
• /
• pp.112-118
• /
• 2012

철강 산업에서는 고로 슬래그, 전기로 슬래그, 전로 슬래그 등 많은 부산물이 발생한다. 그 중 제강 슬래그는 일반 골재와 달리 높은 CaO와 낮은 $SiO_2$가 존재하며, 이를 시멘트와 콘크리트에 적용하게 되면 일부 알칼리 반응을 발생시키는 원인이 된다. 한편, 국내외적으로 제강 슬래그 중 전기로 산화슬래그의 콘크리트 구조용 골재로 사용하는 기준이 제정되어 사용을 장려하고 있지만, 슬래그에 대한 체적 안정성은 해결하지 못하였다. 최근에 이런 문제점을 해결하기 위하여 제강 슬래그의 고속의 공기로 냉각하는 방법이 국내에서 개발되었으며, 이를 적용할 경우 슬래그의 체적 붕괴를 야기시키는 유리 석회의 함유량을 최소화시키고 철 산화물에 대한 안정성을 갖는 것으로 보고되고 있다. 이에 본 연구에서는 철강 산업에서 발생되는 제강슬래그의 고속의 공기로 냉각한 급냉 전기로 산화슬래그의 콘크리트용 골재로서 활용하기 위한 기초 연구이다. 이를 위해 급냉 전기로 산화슬래그 잔골재의 품질 특성을 검토하였으며, 골재의 입도별에 따른 모르타르 특성을 검토하였다. 실험 결과 급냉 전기로 산화슬래그 잔골재의 특성은 아토마이저 공정에 의한 특성을 반영하고 있으며, 기존 콘크리트용 골재 입도 분포 범위에 비해 작은 입도 분포 범위를 가지는 것으로 나타났다.

• 한국건축시공학회지
• /
• 제15권6호
• /
• pp.553-559
• /
• 2015

본 연구는 순환골재의 재활용 방안 및 시멘트를 대체할 수 있는 결합재에 대한 연구가 필요한 실정으로 고로슬래그, 플라이애시, 열병합플라이애시 등을 시멘트 대체재로 활용하여 무시멘트 모르타르를 제조하고자 하였다. 기초 실험에서는 결합재의 비율 및 알칼리 자극제의 선정을 위한 실험을 실시하였으며, 실험결과 결합재는 플라이애시 20%, 열병합플라이애시 40%를 치환한 경우 가장 높은 강도 값을 나타내었으며 알칼리 자극제로 NaOH 2.5%, $Ca(OH)_2$ 7.5%를 혼합하여 사용할 경우 가장 높은 강도 값을 나타내었다. 따라서 본 실험에서는 기초 실험에서 얻어진 최적 배합을 토대로 순환 잔골재의 치환율에 따른 무시멘트 모르타르의 특성을 검토하여 열병합플라이애시와 순환 잔골재를 사용한 모르타르의 공학적 특성을 분석하고자 하였다. 실험결과, 순환 잔골재의 적정 치환율은 75%인 것으로 나타났다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 춘계 학술논문 발표대회
• /
• pp.99-100
• /
• 2012

This study tried to present the appropriate replacement ratio of the recycled sand through the properties of the ternary system inorganic composite mortar according to replacement ratio change of the recycled sand about the natural sand through test verification. The flowing and compressive strength was degraded as the replacement ratio of the experimental result recycled sand increased. The appropriate replacement ratio of the recycled sand according to it was shown up less than 15%.

• 한국건설순환자원학회논문집
• /
• 제5권3호
• /
• pp.70-77
• /
• 2010

본 연구는 순환잔골재에 고로슬래그 미분말 만을 사용한 무 시멘트 모르터의 모르터 배합비, 플로우치, W/B 등 배합요인 변화가 품질특성에 미치는 영향에 대하여 분석하였다. 그 결과를 요약하면 다음과 같다. 먼저, 굳지 않은 모르터의 특성으로, 플로우치가 증가할수록 단위수량의 증가에 기인하여 W/B는 커지는 것으로 나타났고, 공기량은 W/B의 증가와 반대로 공기포의 소실이 용이해짐에 따라 감소하는 경향을 보였다. 경화 모르터의 경우, 압축강도는 전체 재령에서 플로우치가 증가할수록 높게 선정된 W/B로 인해 반비례적으로 저하하는 것으로 나타났고, B/W의 증가에 따라서는 비례적으로 증가하게 나타났는데, 재령이 경과할수록 BS의 잠재수경성 반응에 의해 압축강도의 증가폭은 더욱 향상되었다. B/W의 증가에 따른 재령 28일 휨강도는 거의 증가 없이 유사한 강도값을 나타내었는데, 압축강도에 대한 휨강도의 비는 대체적으로 1/2 ~ 1/3의 범위 내에 분포되어, 일반적인 콘크리트의 범위보다 높게 형성되었다.

• 한국건설순환자원학회논문집
• /
• 제1권2호
• /
• pp.107-113
• /
• 2013

연구에서는 문제시 되는 순환자원의 종류를 상호 보완적으로 활용하여 문제를 해결하고자하는 연구이다. 즉, 고로슬래그 미분말(BS)의 잠재 수경성반응을 순환 잔 굵은 골재의 알칼리로 반응시키고, 부족분의 알칼리를 보통포틀랜드 시멘트(OPC)로 해결하면서 소석회 처리된 소각장애시(WA)의 치환율을 실험변수로하여 최적치를 구하고자 실험하였다. 실험결과 WA 치환율이 증가할수록 유동성과 공기량은 약간 저하하고, 염화물량은 증가하여 불리하였지만 압축 및 인장강도가 1% 에서 최대 값을 나타내어 폐기물 유효처리 관점까지도 고려하면 WA 1% 혼합이 최적인 것으로 분석되었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 춘계 학술논문 발표대회
• /
• pp.242-243
• /
• 2014

In this study, industrial by-products including blast furnace slag, incineration ash and waste gypsum were used with recycled fine aggregates to manufacture the zero-cement mortar. The replacement ratio of anhydrite gypsum was fixed as 0, 10%, 20% the replacement ratio fo WA1 was fixed as 0.5% and 1.0%, respectively. It could be identified that when the replacement of gypsum was 20% and WA1 of 1.0%, the strength could be in the range of normal strength.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 춘계 학술논문 발표대회
• /
• pp.210-211
• /
• 2014

Nowadays, as to reduce the emission volume of CO₂, blast furnace slag has been widely used to replacement of cement. Techniques about using industrial by-products has been extensively studied. For the previous study, blast furnace slag has been used with recycled fine aggregates. In thess study, considering about the different properties of blast furnace slag, as the change of blaine and chemical performances of blast furnace slag, the results of flowability and compressive strength has been analysed.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 추계 학술논문 발표대회
• /
• pp.154-155
• /
• 2014

The object of this research is showing the effect of additional hydration of BS with OPC and less amount of gypsum in WA for the binder of BS with RFA mortar on strength development. The test performed was using factors of 0, 10, 30, and 50 % of OPC replacement for effect on strength development with additional stimulation.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2002년도 학술.기술논문발표회
• /
• pp.29-36
• /
• 2002

High fluid concrete unlike OPC concrete is made with various material, and the phase of fresh concrete is considerably different. In order to understand fluidity phase and mix properties of high fluid concrete, concrete is required to access as suspension structure which consists of aggregate and paste. The focus of this paper is to analyze the test results and quantify the effect of mix proportions of molar and fineness modulus of ,and on the properties of fresh mortar. The effect of water-binder ratio, sand-binder ration, content; of ggbs (by mass of total cementitious materials), and various contents of water reducing agent on the yield stress and plastic viscosity of the mix is studied. Based on the experimental results, the following conclusion; can be drawn: (1) The mixing time needed (or high fluid mortar was approximately two times more than that of ordinary portland mortar. (2) The fluidity phase of mortar could be explained by yield stress of mix and the fluidity of mortar. (3) As the content of ggbs increased, yield stress of mortar was decreased and plastic viscosity of it was increased. (4) For the high fluid mortar, it was appeared that sand-binder ratio should be below 1.5.