• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.4
• /
• pp.110-115
• /
• 2017

This research was performed to investigate the mechanical performance of lightweight concrete including phase changing material(Low temperature PCM). Micro capsulised PCM consisted of wax type core and melamine based wall. Also, for PCM of one single kind, paraffin wax was inserted into Vermiculite and the surface was coated with melamine resin. Interfacial polymerization is based on the principle that macromolecule reaction takes place on the surfaces between 1-dodecanol(core material) and water (solvent) to form the wall material. Lightweight concrete has compressive strength of 10 MPa, tensile strength of 1.5 MPa, and oven dried density of 1.0kg/liter which included 10%, 20%, or 30% PCM by weight. To do so, this study fabricated light-weight foamed concrete ($1.0kg/m^3$) in pre-foaming method and mixed it with PCM micro capsule of 1-dodecanol and melamine to examine its physical properties.

• Analytical Science and Technology
• /
• v.15 no.5
• /
• pp.427-432
• /
• 2002

The combustion behavior of heavy oil and its emulsion with water was evaluated. The concentration of $SO_x$ in the combustion gas of emulsion oil was reduced to 57% with respect to that of the combustion gas from neat heavy oil. Also, the concentration of $NO_x$ in the combustion gas of emulsion oil was reduced to 67% with respect to that of the combustion gas of neat heavy oil. These reductions of $SO_x$ in the combustion gas of emulsion oil seems to be due to the reaction with salts included in surfactant of emulsion oil. Also, the combustion efficiency of emulsion oil is evaluated to be about 6% higher than that of neat heavy oil.

• Journal of Korean Society of Steel Construction
• /
• v.9 no.4 s.33
• /
• pp.515-521
• /
• 1997

The effects of heat treatment and fiber orientation on tensile strength and fatigue behavior were studied in a continuously reinforced. magnesium-based composite Following an earlier TEM investigation, specimens were thermally aged to modified the interfacial zone between the alumina fibers and the magnesium alloy matrix. From the tensile experimental results, the ultimate tensile strength of the aged specimens were lower than that of the as-fabricated due to weak fiber-matrix interfacial strength with chemical reaction during the thermal processing. The fatigue crack growth experiments were conducted with specimens having the fiber orientation normal to the crack growth direction (longitudinal) and also specimens with the fibers oriented parallel to the crack growth direction(transverse). A comparison of the fatigue crack growth behavior indicates that aged longitudinal specimens are more resistant to fatigue crack growth the as-fabricated longitudinal specimens. Conversely, as-fabricated transverse specimens are more resistant to fatigue crack growth than aged transverse specimens.

• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.335-340
• /
• 2000

We investigated the role of the capping layers in the formation of the cobalt silicide in Co/Si systems with TiN and Ti capping layers and without capping layers. The Co/Si interfacial reactions and the phase transformations by the rapid thermal annealing (RTA) processes were observed by sheet resistance measurements, XRD, SIMS and TEM analyses for the clean silicon substrate as well as for the chemically oxidized silicon substrate by $H_2SO_4$. We observed the retardation of the cobalt disilicide formation in the Co/Si system with Ti capping layers. In the case of Co/$SiO_2$/Si system, cobalt silicide was formed by the Co/Si reaction due to with the dissociation of the oxide layer by the Ti capping layers.

• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.346-352
• /
• 2000

We investigated the oxidation behavior of poly $Si_{1-x}Ge_x$ films (X=0.15, 0.42) at $700^{\circ}C$ in wet oxidation ambients and analyzed the oxide by XPS, RBS, and cross-sectional TEM. In the case of poly $Si_{0.85}Ge_{0.15}$ films, $SiO_2$ was formed on the poly $Si_{1-x}Ge_x$ films and Ge was rejected from growing oxide, subsequently leading to the increase of Ge content. In the case of poly $Si_{0.58}Ge_{0.42}$ films, we found that $SiO_2-GeO_2$ were formed on the poly $Si_{1-x}Ge_x$ films due to high Ge content. Finally, we proposed the oxidation model of poly $Si_{1-x}Ge_x$ films.

• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.373-378
• /
• 2000

There was a great difference in the formation kinetics of $TiO_2$ and $Bi_2O_3$ on silicon, but the growth of bismuth titanate (BIT) thin film was mainly limited by the formation of $TiO_2$. As a result, the BIT film was easy to be lack of bismuth. The pulse injection metalorganic chemical vapor deposition (MOCVD) process was introduced in order to overcome this problem by recovering the insufficient bismuth content in the film. By this pulse injection method, bismuth content was increased and also the uniform in-depth composition of the film was attained with a abrupt $Bi_4Ti_3O_{12}/Si$ interface. In addition, the crystallinity of $Bi_4Ti_3O_{12}$ thin film prepared by pulse injection process was greatly improved and the leakage current density was lowered by 1/2~1/3 of magnitude. Clockwise hysteresis of C-V was observed and the ferroelectric switching was confirmed for $Bi_4Ti_3O_{12}$ film deposited by pulse injection method.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.66-66
• /
• 2009

Various alloy system, such as Cu-Sn-Ti, Cu-Ag-Ti, and Ni-B-Cr-based alloy are used for the brazing of diamond grits. However, the problem of the adhesion strength between the diamond grits and the brazed alloy is presented. The adhesion strength between the diamond grits and the melting filler alloy is predicted by the contact angle, thereby, instead of diamond grit, the study on the wettability between the graphite and the brazing alloy has been indirectly executed. In this study, Cu-13Sn-12Ti filler alloy was manufactured, and the contact angles, the shear strengths and the interfacial area between the graphites(diamond grits) and braze matrix were investigated. The contact angle was decreased on increasing holding time and temperature. The results of shear strength of the graphite joints brazed filler alloys were observed that the joints applied Cu-13Sn-12Ti alloy at brazing temperature 940 $^{\circ}C$ was very sound condition indicating the shear tensile value of 23.8 MPa because of existing the widest carbide(TiC) reaction layers. The micrograph of wettability of the diamond grit brazed filler alloys were observed that the brazement applied Cu-13Sn-12Ti alloy at brazing temperature $990^{\circ}C$ was very sound condition because of existing a few TiC grains in the vicinity of the TiC layers.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.80-80
• /
• 2009

패키징 구조의 발전이 점차 중요한 문제로 대두되어, 칩의 집적 기술의 발전에 따라 실장기술에서도 고속화, 소형화, 미세피치화, 고정밀화, 고밀도화가 요구되고있다. 최근 선진국을 중심으로 전자 전기기기 및 부품의 실장기술에서도 환경 친화적인 기술을 요구함에 따라, 저에너지 공정 및 무연 실장 기술에 대한 연구가 활발하게 진행되고 있다. 기존의 SOP(Small Out-line Package), QFP(Quad Flat Package) 등은 소형화, 다핀화, 고속화, 실장성에 한계가 있기 때문에, SMT(Surface Mount Technology) 형식으로 된 BGA(Ball Grid Array)가 휴대형 전화를 비롯한 기타 전자 부품 실장에 널리 사용되고 있다. BGA ball shear 법은 BGA 모듈의 생산 및 취급 중에 발생할지도 모르는 기판에 수평으로 작용하는 기계적인 전단력에 BGA solder ball이 견딜 수 있는 정도를 측정하기 위해 사용되는 시험법이다. 전단 시험에 의한 전단 강도의 측정 외에 전기전도도 측정, 파면 관찰, 이동거리(displacement), 유한요소 해석법 등을 병행하여 시험법의 신뢰성 향상에 대한 연구가 이루어지고 있다. 본 실험에서는 지름이 $500{\mu}m$인 Sn-3.5Ag 솔더볼을 이용하여 세라믹 기판을 접합하여 BGA 패키지를 완성하였다. 상부 기판에 솔더볼을 정렬시켜 리플로우 방법으로 접합 한 후 솔더볼이 접합된 상부 기판과 하부 기판을 접합 하여 시편을 제작하였다. 접합된 시편들은 $150^{\circ}C$에서 0~800시간 열처리를 실시하였고, 열처리를 하면서 각각 $3{\times}10^2A/cm^2,\;5{\times}10^3A/cm^2$의 전류를 인가하였다. 시편들을 전단 시험기를 이용하여 솔더볼의 기계적 특성 평가를 하였으며, 계면 반응을 관찰하였다.

• Journal of the Korean Society for Heat Treatment
• /
• v.16 no.5
• /
• pp.260-266
• /
• 2003

In order to study the interfacial reaction between Nb thin sheet and Fe-C-(Si) alloy with different Chemical compositions, they were cast-bonded. The growth of carbide layer formed at the interface after isothermal heat treatment at 1173K, 1223K, 1273K and 1323K for various times was investigated. The carbide formed at the interface was NbC and the thickness of NbC layer was increased linearly in proportional to the heat treating time. Therefore, It was found that the growth of NbC layer was controlled by the interfacial reaction. The growth rate constant of NbC layer was slightly increased with increase of carbon content when the silicon content is similar in the cast irons. However, as silicon content increases with no great difference in carbon content, the growth of NbC layer was greatly retarded. The calculated activation energy for the growth of NbC layer was varied in the range of 447.4~549.3 kJ/moI with the compositions of cast irons.

• Applied Chemistry for Engineering
• /
• v.20 no.5
• /
• pp.557-560
• /
• 2009

In this study, a new wet etching method and the solution for thinning the glass with the thickness below $100{\mu}m$ were investigated. For the preparation of etching solution with low hydrofluoric acid, it was effective to use $NH_4F$ or $NH_4HF_2$ as a main ingredient with the addition of sulfuric acid or nitric acid. Influence of the composition of mixed acid solution and the temperature on the etching rate was investigated. The addition of anionic surfactant provides the function to prevent the adhesion of sludge generated by the etching reaction. A new wet etching pilot device equipped with streaming generation parts was used to test etching of commercial non-alkali glass and soda lime glass. The non-alkali glass with the thickness of 640 ${\mu}m$ and soda lime glass with the thickness of $500{\mu}m$ were etched to $45{\mu}m$ and $100{\mu}m$, respectively, by using the pilot device. After the etching by pilot device, the roughness degree of the glass surface was maintained at $0.01{\sim}0.02{\mu}m$.