• Journal of Adhesion and Interface
• /
• v.17 no.2
• /
• pp.67-71
• /
• 2016

In this study, low-viscosity polyurethane hot-melt were synthesized with polyether polyol / polyester polyol, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), 2-butanone oxime (MEKO) to improve the properties and peel strength. The properties of the synthesized low-viscosity polyurethane hot-melt was evaluated through FT-IR, viscosity meter and UTM. When the content of the reactive diluent increases and the NCO-blocked prepolymer decreases, the viscosity of low-viscosity polyurethane hot-melt adhesive was increased. When the ratio of OH-terminated oligomer, NCO-blocked prepolymer and content of reactive diluent is 1 : 0.5 : 0.5, low-viscosity polyurethane hot-melt showed 1.1 kgf/cm peel strength.

• Journal of Adhesion and Interface
• /
• v.22 no.1
• /
• pp.16-21
• /
• 2021

In the aircraft industry, anti- and de-icing are one of very important techniques for the safety. The anti-icing technique had not been studied while de-icing technique had been not only researched enough but applied to aircraft industry. In this work, surface roughness and energies of polyurethane (PU) topcoat were controlled with 3 different nanoparticles which was coated to PU topcoat. It was evaluated via static contact angle using distilled water. The adhesion property of 3 nanoparticles was evaluated directly using adhesion pull-off test. The color gamut of nanoparticle coated PU topcoat was also evaluated with 3 different nanoparticles. It was determined using RGB color degree variation between neat PU topcoat and coated nanoparticle. Finally, the optimized nanoparticle was determined to manufacture hydrophobic surface and to maintain color of neat PU topcoat for the aircraft.

• Journal of Adhesion and Interface
• /
• v.24 no.4
• /
• pp.113-119
• /
• 2023

Since it was reported that the unusual amino acid DOPA in synergy with lysine and histidine residues found in mussel adhesive proteins plays a pivotal role in mussel adhesion in underwater environments, there has been a burgeoning development of various catecholamines-based adhesives for biomedical applications. Among these, catechol-conjugated chitosan, containing catecholamine, featuring multiple catechol groups within its aminerich chitosan backbone, has found versatile utility in fields, such as tissue adhesion, wound dressing, tissue healing, hemostats, drug delivery systems, and tissue engineering scaffolds. Significantly, chitosan-catechol is a mussel-inspired material approved by both US Food and Drug Administration (FDA) and KR Ministry of Food and Drug Safety (MFDS) for its effectiveness in hemostasis. This review focuses on 1) general aspects of catechol-conjugated chitosan, highlighting catechol group integration into chitosan backbones, 2) examination of proposed mechanisms of hemostasis, and 3) exploration of diverse physical forms, including solution, hydrogels, patches, and thin films with practical applications inapplicable to hemostasis.

• Composites Research
• /
• v.30 no.4
• /
• pp.235-240
• /
• 2017

Animal glue, a water-soluble adhesive, has been used historically for high-performance traditional furniture despite the disadvantage of weakness against moisture. Many scientists studied the ways to improve water resistance of animal glue. Improvements on the interfacial, thermal, and water resistance properties of wood sandwich composites (WSC) was studied with carbon nanotube (CNT) wt% in animal glue. Real-time temperature of WSC was measured after WSC was heated with increasing CNT wt%. Lap shear test was performed to determine the interfacial properties of wood and animal glue with CNTs. Water resistance properties of animal glue were determined by lap shear test using specimens dipped in water and the results were compared with the dry case. Hydrophobicity of animal glue by static contact angle was correlated with the variation of lap shear test. Interfacial, thermal, and water resistance properties for animal glue were improved with properly added CNTs.

• Journal of Adhesion and Interface
• /
• v.23 no.4
• /
• pp.122-129
• /
• 2022

In this study, the hydrophilicity of the metal fiber is improved by introducing an oxygen-containing functional group to the fiber surface after treatment of the metal fiber using the oxygen plasma treatment time as an experimental variable. For the surface modification of metal fibers, changes in surface properties before and after plasma treatment were observed using SEM and x-ray photoelectron spectroscopy (XPS). In order to observe the effect of the plasma treatment time on the surface of the metal fiber, the change in contact angle of the metal fiber with respect to a polar solvent and a non-polar solvent was measured. After calculating the change in surface free energy using the measured contact angle, the contact angle and the surface free energy for metal fibers before and after oxygen plasma treatment were compared, and the correlation with the adhesion work was also considered. The microdroplet specimens were prepared to investigate the effect of surface changes of these metal fibers on the improvement of shear strength at the interface when combined with other materials and the interfacial shear strength was measured, and the correlation with the adhesion work was also identified. Therefore, the oxygen plasma treatment of the metal fiber results in an increase in the physical surface area on the fiber surface and a change in contact angle and surface energy according to the introduction of the oxygen-containing functional group on the surface. This surface hydrophilization resulted in improving the interfacial shear strength with the polymer resin.

• Journal of Adhesion and Interface
• /
• v.14 no.4
• /
• pp.167-174
• /
• 2013

In this study, Ultraviolet (UV) curable urethane acrylates for ink binder was prepared by reaction of IPDI, polyether polyol and HEA. The UV curing behavior of compositions with HEA/PETA ratio on UV irradiation time was investigated by FT-IR spectrophotometer, probe tack tester and Photo-DSC. Conversion % and gel content were increased with increasing UV irradiation time, but probe tack was decreased. Storage modulus, tensile strength and decomposition temperature were increased as PETA content increased. In case of HEA/PETA ratio was 30/70, adhesion property of UV-cured composition on PMMA sheet was excellent.

• Journal of Adhesion and Interface
• /
• v.23 no.2
• /
• pp.33-38
• /
• 2022

In this study, we report on the synthesis and properties of eco-friendly waterborne polyurethane (WPU) according to bio-polyol contents. It was successfully synthesized by the different polyester polyol (DT-1040) and castor oil based polyol (COP) ratios. The glass transition temperature (Tg) of the synthesized bio polyol based waterborne polyurethane was around -70 ℃ and -30 ℃, and it was confirmed that the Tg range was widened as the COP content increased. In addition, as the COP content increased, the tensile strength decreased, and optimum adhesive strength showed when DT-1040:COP ratio was 7:3.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.2
• /
• pp.67-74
• /
• 2008

This paper provides the test results of bonding behavior of the interface between concrete substrate and carbon fiber in the rehabilitation method applying carbon fiber with epoxy based resin adhesive. The difference in each components was gradually increased subjected to the repetition of temperature variation, regardless of the strength of the substrate concrete, while the ultrasonic interface between each component occurred. An increase in difference of the temperature resulted in a decrease in bond strength of each component. Associated failure mode was shown to be interfacial failure and substrate concrete failure. No remarkable changes were found in the deformation and ultrasonic velocity of each component until the four cycles of the dry and moisture test. Hence, the moisture condition may not affect the bonding behavior of each component. After the repetition of dry and moisture test, corresponding bond strength was reduced to 40% of that before test. For the effect of freeze and thaw test, the cycle of freeze and thaw within 4 cycles resulted in debonding of each component.

• Journal of Adhesion and Interface
• /
• v.4 no.1
• /
• pp.1-8
• /
• 2003

In this work, the effect of PMR-15 content on the variation of surface free energy of the DGEBA/PMR-15 blend system was investigated in terms of contact angles and mechanical interfacial tests. Based on FT-IR result of the blend system. C=O (1,772, $1,778cm^{-1}$) and C-N ($1,372cm^{-1}$) peaks appeared with imidization of PMR-15 and -OH ($3,500cm^{-1}$) peak showed broadly at 10 phr of PMR-15 by ring-opening of epoxy. Contact angle measurements were performed by using deionized water and diiodomethane as testing liquids. As a result, the surface free energy of the blends gave a maximum value at 10 phr of PMR-15, due to the significant increasing of specific component. The mechanical interfacial properties measured from the critical stress intensity factor ($K_{IC}$) and the critical strain energy release rate ($G_{IC}$) showed a similar behavior with the results of surface energetics. This behavior was probably attributed to The improving of the interfacial adhesion between intermolecules, resulting from increasing the hydrogen bondings of the blends.

• Composites Research
• /
• v.22 no.6
• /
• pp.45-51
• /
• 2009

The marginal integrity at the composite resin-tooth interface has been analyzed in real time through acoustic emission (AE) monitoring during the polymerization shrinkage of composite resin subjected to the light exposure. It was found that AE signals were generated by the polymerization shrinkage. Most AE hit events showed a blast type signal having the principal frequency band of 100-200kHz. Bad bonding states were indicated by many hit events in the initial curing period of 1 minute with high contraction rate. The quantity of hit events for the human molar dentin specimen was much less than that for the steel ring specimen but more than that for the PMMA ring specimen. The better the bonding state, the less the AE hit events. The AE characteristics were related with the tensile crack propagation occurring in the adhesive region between the composite resin and the ring substrate as well as the compressive behavior of the ring substrate, which could be used for a nondestructive characterization of the marginal disintegrative fracture of the dental restoration.