• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.7
• /
• pp.541-545
• /
• 1998

(PZT, PST, PT)/ YBCO structured have been grown on single crystal $LaAlO_3$ using in-situ Nb:YAG pulsed laser deposition technique. The optimum conditions of fabrication for high quality films have been established under various oxygen pressure. TBCO was used as a metallic electrode for polarizing ferroelectric thin fillms. Lattice mismatch of these materials were found to be with in 3%. As a result XRD patterns and rocking curves, (PZT, PST, PT)/ YBCO multiayered thin films on $LaAlO_3$ substrates showed preferred orientation to c-axis. For invastigation on electrical properties of ferroelectric thin films, remanent polaiztion $P_r$ and coercive field $E_c$ were measured for three samples. At each optimum condition, they showed the values of P_r=60 \mu C/cm^2 and E_c=240kV/ cm for PT, 30\mu C/cm^2 and 105kV/cm for PZT, 1.5\mu C/cm^2$ and 15kV/cm for PST. Frequency dependence of dielectric properties of ferroelectric thin fillms was also investigated. As a result, it showed the frequency dependence was relatively small in the range of 10Hz~10kHz.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.173-176
• /
• 2002

B $i_{3.3}$L $a_{0.7}$ $Ti_{3}$ $O_{12}$(BLT) 강유전체 박막을 Pt/Ti/ $SiO_2$/Si 기판위에 졸-겔법 (sol-gel method) 으로 스핀코팅하여 Metal-Ferroelectric-Metal(MFM) 구조의 커패시터를 형성하였다. BLT 박막의 결정성은 후속열처리 온도가 증가할수록 향상되었으며 $R_{근}$값은 as~coated된 BLT 박막의 경우 3.8$\AA$를 나타내었으나 열처리 온도를 $700^{\circ}C$로 증가한 경우 12.9$\AA$으로 거칠은 표면형상으로 변화되었다. $650^{\circ}C$로 열처리된 BLT 박막의 잔류분극 2Pr ($\pm$($P^{*}$ -$P^{ ^}$))값은 5V 인가전압에서 약 29.1 $\mu$C/$cm^2$을 나타내었다. 또한 $10^{10}$ 스위칭 cycles 가지 분극 스위칭을 반복한 후에도 뚜렷한 잔류분극의 변화를 발견할 수 없어서 우수한 피로특성을 나타내었다. 3V 전압에서 BLT 박막의 누설전류는 약 2.2$\times$$10^{-8}$ A/$cm^2$를 나타내었다.내었다.었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.2
• /
• pp.143-150
• /
• 2000

Ferroelectric SrxBi2+yTa2O9+$\alpha$ thin films with various compositions(x=0.7, 0.8, 1, y=0.3, 0.4) were prepared by sol-gel method. The film with moled ratio of 0.8:2.3:2.0 in Sr/Bi/Ta, which was deposited on Pt/SiO2/Si (100), showed better ferroelectric properties than other films. To investigate substrate effects, the same compositions were spin coated on Pt/Ti/SiO2/Si (100) substrates. At an applied voltage of 5V, the dielectric constant($\varepsilon$r), remanent polarization (2Pr) and coercive field (Ec) of the Sr0.8Bi2.3Ta2O9+$\alpha$ thin film prepared on Pt/Ti/SiO2/Si (100) were about 296, 24$\mu$C/$\textrm{cm}^2$ and Ec of 49kV/cm respectively. Both SBT films firred at 80$0^{\circ}C$ revealed no fatigue up to 1010 cycles. Retention characteristics of these capacitors showed no degradation up to 104 sec.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.13 no.4
• /
• pp.699-707
• /
• 2010

Electric-field-induced electron emission from the three kinds of $Pb(Zr_{0.56}Ti_{0.44})O_3$ ferroelectric cathodes with different electrode structure has been investigated. Regardless of the electrode structures, a threshold field of the each cathode was 2.5-2.6kV/mm, which is 3 times higher than the coercive field of $Pb(Zr_{0.56}Ti_{0.44})O_3$ material. Although the waveform of the electron currents was affected by the structure of the electrode, no significant difference for the emission properties such as the peak current and the pulse width was observed from the three kinds of the cathodes. However, the current density of the cathode was dependent on the electrode structure. From the simulation of electric field distribution, the surface flashover, and the injury region of the cathode surface, it was proved that the prime electrons were initiated at the electrode-ceramic-vacuum triple point by field emission and the emission currents were strongly enhanced by the surface plasma.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.743-746
• /
• 2000

Metal-ferroelectric-insulator-semiconductor(MFIS) devices using Pt/$LiNbO_3$/Si structure were successfully fabricated. The dielectric constant of the AIN film calculated from the capacitance in the accumulation region in the capacitance-voltage(C-V) curve was about 8.2. The gate leakage current density of MIS devices using a aluminum electrode showed the least value of 1$\times$$1O^{-8}$A/$cm^2$ order at the electric field of 500kV/cm. The dielectric constant of $LiNbO_3$film on AIN/Si structure was about 23 derived from 1MHz capacitance-voltage (C-V) measurement and the resistivity of the film at the field of 500kV/cm was about 5.6$\times$ $1O^{13}$ $\Omega$.cm.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.38 no.12
• /
• pp.8-13
• /
• 2001

Cerium oxide ($CeO_2$) thin film has been proposed as a buffer layer between the ferroelectric thin film and the Si substrate in Metal-Ferroelectric-Insulator-Silicon (MFIS) structures for ferroelectric random access memory (FRAM) applications. In this study, $CeO_2$ thin films were etched with $Cl_2$/Ar gas mixture in an inductively coupled plasma (ICP). Etch properties were measured for different gas mixing ratio of $Cl_2$($Cl_2$+Ar) while the other process conditions were fixed at RF power (600 W), dc bias voltage (-200 V), and chamber pressure (15 mTorr). The highest etch rate of $CeO_2$ thin film was 230 ${\AA}$/min and the selectivity of $CeO_2$ to $YMnO_3$ was 1.83 at $Cl_2$($Cl_2$+Ar gas mixing ratio of 0.2. The surface reaction of the etched $CeO_2$ thin films was investigated using x-ray photoelectron spectroscopy (XPS) analysis. There is a Ce-Cl bonding by chemical reaction between Ce and Cl. The results of secondary ion mass spectrometer (SIMS) analysis were compared with the results of XPS analysis and the Ce-Cl bonding was monitored at 176.15 (a.m.u). These results confirm that Ce atoms of $CeO_2$ thin films react with chlorine and a compound such as CeCl remains on the surface of etched $CeO_2$ thin films. These products can be removed by Ar ion bombardment.

• Journal of the Korean Vacuum Society
• /
• v.9 no.2
• /
• pp.136-143
• /
• 2000

$SrBi_2Ta_2O_9;(SBT)$ films were deposited on p-type Si(100) at room temperature by rf magnetron sputtering method to confirm the possibility of application of $Pt/SBT/Pt/Ti/SiO_2/Si$ structure (MFM) for destructive read out ferroelectric RAM (random access memory). Their structural characteristics with the various annealing times and Ar/$O_2$ gas flow ratios in sputtering were observed by XRD (X-ray diffractometer) and the surface morphologies were observed by FE-SEM (field emission scanning electron microscopy), and their electrical properties were observed by P-V (polarization-voltage measurement) and I-V (current-voltage measurement). The Ar/$O_2$ gas flow ratios of sputtering gas were changed from 1 : 4 to 4 : 1 and SBT thin films were deposited at room temperature. The films show (105), (110) peaks of SBT by XRD measurement. SBT thin films deposited at room temperature were crystallized by furnace annealing at 80$0^{\circ}C$ in oxygen atmosphere during either one hour or two hours. Among their electrical properties, P-V curves showed shaped hysteresis curves, but the SBT thin films showed the asymmetric ferroelectric properties in P-V curves. When Ar/$O_2$ gas flow ratios are 1 : 1, 2: 1, the leakage current density values of SBT thin films are good, those values of 3 V, 5 V, and 7 V are respectively $3.11\times10^{-8} \textrm{A/cm}^2$, $5\times10^{-8}\textrm{A/cm}^2$, $7\times10^{-8}\textrm{A/cm}^2$.After two hours of annealing time, their electrical properties and crystallization are improved.

• Journal of the Institute of Electronics and Information Engineers
• /
• v.50 no.7
• /
• pp.102-108
• /
• 2013

In manufacturing of solution-processed organic electronic devices, a spin coating method is frequently used, but which has a big problem. Solvent in a solution has a decisive effect such as physical and chemical damage for successive solution-based film deposition. Such a severe damage by solvent restricts for fabricating building blocks of multi-layered films from solutions. In this work, it will be shown that a proper combination of well-known solvents gives a chance to fabricate multi-layered film, also this new method was applied to make organic field effect transistor. Two types of bottom gate, bottom contact transistors were fabricated, one of which is fabricated by conventional single spin coating method, the other fabricated by double spin coating method. Compared with the electrical characteristics in a single spin coated transistor, the leakage current between source and gate electrode was decreased, ON state current was increased, and the extracted saturation mobility was multiplied more than 2.7 time for double spin coated transistors. It is suggested that the multiple coated gate dielectric structure is more desirable for high performance organic ferroelectric field effect transistors.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.37 no.6
• /
• pp.24-33
• /
• 2000

Switching behaviour of the ferroelectric thin film and device characteristics of the MFSFET(Metal-Ferroelectric-Semiconductor FET) are simulated with taking into account the accumulation of oxygen vacancies near interface between the ferroelectric thin film and the bottom electrode caused by the progress of fatigue. In our switching model, relative switched charge is 0.74 nC before fatigue, but after the progress of fatigue it reduces to 0.15 nC with the generation of oxygen vacancies. It indicates that the generation of oxygen vacancies strongly suppresses polarization reversal. $C-V_G\;and\;I_D-V_G$ curves in our MFSFET device model exhibit the memory window of 2 V and show the accumulation, the depletion and the inversion regions in capacitance characteristic clearly. The difference of saturation drain current of the device before fatigue in shown by the dual threshold voltages in $I_D-V_G$ curve as 6nA/$cm^2$ and decreases as much as 50% after fatigue. Decrease of the difference of saturation drain currents by fatigue implies that the accumulation of oxygen vacancies with the fatigue should be avoided in the device application. Our simulation model is expected to play an important role in estimation of the behavior of MFSFET device with various ferroelectric thin films.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.84-84
• /
• 1999

최근 큰 잔류분극을 가진 강유전체 Pb(Zr, Ti)O3 박막을 이용한 비휘발성 기억소자의 연구가 활발히 진행되고 있다. 그러나 Pb(Zr, Ti)O3 박막을 비휘발성 기억소자로 응용하는 경우 분극피로(polarization fatigue), imprint, 누설전류 등의 문제점이 나타나는 것으로 알려져 있다. 특히 분극반전 횟수가 증가할수록 잔류분극이 감소하는 분극피로 현상은 비휘발성 기억소자의 응용에 있어서 치명적인 장애가 되므로 기억소자의 실용화를 위해서는 분극피로 현상의 개선이 무엇보다 중요하다. 본 연구에서는 Pb(Zr, Ti)O3 강유전체 박막의 분극피로 현상을 규명하고 개선하기 위해서 다음과 같은 세가 실험적 방법으로 접근하였다. 먼저 Pt와 금속산화물인 LaNiO3을 이용하여 상·하부 전극을 달리하여 제조한 축전기에 대해서 분극피로 특성을 관찰하고 이로부터 분극피로 현상에 대한 전극의 효과를 조사하였다. 여기서 금속산화물인 LaNiO3 박막과 Pt 박막은 r.f. 스퍼트 법으로 증가하였으며 Pb(Zr, Ti)O3 박막은 LaNiO3/Si(100)/와 Pt/Ti/SiO2/i(100) 기판위에 졸겔법으로 제조하였다. 다음으로 분극피로된 박막의 상부전극에 극성이 다른 직류전압을 인가해주었을 때 나타나는 분극회복 현상을 광범위하게 관찰하였으며, 특히 직류전압의 극성에 따라 비대칭적인 분극회복 특성을 보였다. 마지막으로 이와 같은 직류전압에 대한 비대칭적인 분극회복현상에 착안하여 양과 음의 방향으로 바이어스된 스윗칭 펄스를 인가하여 분극피로 특성을 조사한 결과 비대칭적인 분극피로 현상을 관찰할 수 있었다. 이와 같은 Pv(Zr, Ti)O3 박막의 분극피로와 회복의 비대칭적인 현상은 분극피로 현상의 기구를 밝히는 중요한 근거가 되었으며, 본 연구에서는 하부 계면에서의 산소빈자리의 역할로 분극피로 현상을 모형화하였다.식각하기 시작하였으며, 19.5J/cm2에서 유리기판의 rudraus(격벽 두께 130$\mu\textrm{m}$)까지 식각하였다. 대한 정보(RDF)는 명확하게 얻을 수 있었다.nospec과 SEM으로 관찰하였다. 또한 Ge 함량 변화에 따른 morphology 관찰과 변화 관찰을 위하여 AFM, SEM, XRD를 이용하였으며, 이온주입후 열처리 온도에 따른 활성화 정도의 관찰을 위하여 4-point probe와 Hall measurement를 이용하였다. 증착된 다결정 SiGe의 두게를 nanospec과 SEM으로 분석한 결과 Gem이 함량이 적을 때는 높은 온도에서의 증착이 더 빠른 증착속도를 나타내었지만, Ge의 함량이 30% 되었을 때는 온도에 관계없이 일정한 것으로 나타났다. XRD 분석을 한 결과 Peak의 위치가 순수한 Si과 순수한 Ge 사이에 존재하는 것으로 나타났으며, ge 함량이 많아짐에 따라 순수한 Ge쪽으로 옮겨가는 경향을 보였다. SEM, ASFM으로 증착한 다결정 SiGe의 morphology 관찰결과 Ge 함량이 높은 박막의 입계가 다결정 Si의 입계에 비해 훨씬 큰 것으로 나타났으며 근 값도 증가하는 것으로 나타났다. 포유동물 세포에 유전자 발현벡터로써 사용할 수 있음으로 post-genomics시대에 다양한 종류의 단백질 기능연구에 맡은 도움이 되리라 기대한다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(nano)화하여 나노 입자를 제조, 기존의 기능성 안료에 대한 비용 절감 효과등을 유도 할 수 있다. 역시 기술적인 측면에서도 특수소재 개발에 있어 최적의 나노 입자 제어기술 개발 및 나노입자를 기능성 소재로 사용하여 새로운 제품의 제조와 고압 기상 분사기술의 최적화에