• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.332-337
• /
• 2006

Monodisperse polymer particles were prepared via one-step seeded polymerization using PMMA seed particles and HDDA (or EGDMA) as crosslinking monomer. For the study, the effects of 1) the ratio of the absorbed monomer or monomer mixture to the seed polymer particles (swelling ratio), 2) the ratio of EGDMA in absorbed monomer mixture, 3) the dosage of initiator, and 4) electro less Ni plating on the variation of mechanical properties of monodisperse polymer particles, such as recovery rate, K-values, breaking strength and breaking displacement, were investigated by using MCT (micro compression test). It was observed that monomer swelling ratio influenced only breaking strength, but EGDMA ratio in monomer mixture, dosage of initiator and electroless Ni plating affected both K-values and breaking strength.

• Analytical Science and Technology
• /
• v.11 no.6
• /
• pp.452-459
• /
• 1998

Crosslinked chitin was prepared from epichlorohydrin and chitin which was isolated from waste marin source. The crosslinked chitosan were prepared by the deacetylation of the crosslinked chitin with a strong base. 2,2'-Iminodibenzoic acid-crosslinked chitosan was prepared by reacting 2,2'-Iminodibenzoic acid salt with crosslinked chitosan-Cl which was obtained by chlorination of crosslinked chitosan. The adsorptivity of Pb(II), Cu(II), Cd(II) was studied as a synthetic adsorbent. Experimental results for the adsorption and the recovery characteristics showed that the more pH increase, the more amount of adsorbed metal ion increase. Optimum adsorption time was 1 hr, and adsorption capacity was increased in order of $Cu^{2+}$<$Cd^{2+}$<$Pb^{2+}$, and recovery capacity was increased in order of $Cd^{2+}$<$Cu^{2+}$<$Pb^{2+}$.

• Membrane Journal
• /
• v.16 no.4
• /
• pp.241-251
• /
• 2006

In this study, crosslinked copolyimides with random (r-) and block (b-) structure were fabricated using N,N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid and pentanediol as crosslinkers. Linear r- and b-sulfonated copolyimides were also fabricated for comparison. Ion exchange capacities of r- and b-copolyimides were very similar to each other owing to their strong dependence of sulfonic acid content. The physical crosslinking via dimerization of carboxylic acid groups induced a reduced average interchain distance in b-copolyimide without crosslinkers. Consequently, its water uptake and methanol permeability were lower than those of r-sulfonated copolyimides. Simultaneously, the reduced interchain distance increased the content of fixed-charged ions per unit volume. The high fixed-charged ion density contributed to an enhancement of proton conductivity In the b-sulfonated copolyimide. Crosslinking caused the reduction of average interchain distance between polymer chains irrespective of types of crosslinker and polymer structure, leading to low methanol permeability. On the contrary, their proton conductivity was improved owing to formation of effective hydrophilic channels responsible for proton conduction. In particular, this trend was observed in r-copolyimide containing a fixed charged ion.

• Korean Chemical Engineering Research
• /
• v.49 no.2
• /
• pp.211-217
• /
• 2011

In this study, ion exchange membranes were prepared using high impact polystyrene(HIPS) with various crosslinking and sulfonation time. Degree of sulfonation(DS) of sulfonated HIPS(SHIPS) membrane was increased with sulfonation time and decreased with crosslinking time. The highest value of DS was 66%. Also, water uptake and ion exchange capacity(IEC) of SHIPS membrane were decreased with degree of crosslinking and increased with sulfonation time. Then their values were 35.2% and 1.55 meq/g, respectively. Electrical resistance and ion conductivity of the membranes were showed more excellent value with sulfonation time. The maximum value of electrical resistance and ion conductivity were $0.4\Omega{\cdot}cm^{2}$ and 0.1 S/cm, respectively. It is indicated that the SHIPS membrane has the higher performance compare with Nafion 117. Durability of SHIPS membranes in a organic solvent was increased with increasing crosslinking time. The surface roughness of HIPS membranes were confirmed with SEM that was become uneven surface with progressing sulfonation.

• Polymer(Korea)
• /
• v.33 no.3
• /
• pp.224-229
• /
• 2009

The dielectric properties of semi-IPN poly(phenylene oxide)(PPO) blend/$BaTiO_3$(BT) composites are investigated. The composites are fabricated via melt-mixing of crosslinker and peroxide in precursor PPO composite obtained by precipitating the suspension consisted of PPO, BT and toluene into methylethyl ketone, poor solvent of PPO. The permittivity of the precursor PPO composites shows higher value than that of integral-blended PPO composites by extruder and coincides with the theoretical value calculated by logarithmic rule of mixture. The blend of PPO and cross-linked triallyl isocyanurate is most effective for lowering the permittivity and loss tangent owing to the suppression of the orientation polarization of matrix. In contrast, 4,4'-(1,3-phenylene diisopropylidene) bisaniline, which has amine unit in its structure, increases the permittivity as well as loss tangent of the composite, but it has the ability to densify the matrix resin and the interfacial adhesion between the matrix and filler to improves flexural strength and modulus.

• Polymer(Korea)
• /
• v.35 no.4
• /
• pp.342-349
• /
• 2011

The effect of the amount of vinyltriethoxysilane (VTEOS) in precipitated silica filled silicone rubbers was extensively investigated in terms of the change of mechanical properties, heat resistance, oil resistance, compression set, resilience, and curing characteristics. As the content of VTEOS increased from 0 to 2.0 phr, the hardness of the silicone rubber increased, however, tensile strength, elongation at break, and tear strength decreased. From heat resistance test, the change of mechanical properties was pronounced for silicone rubber treated with more VTOES. The best heat resistance was achieved at 2.0 phr VTOES. In addition, oil resistance was proportionally improved with VTEOS content. From oil resistance test. it was found that the decrease in hardness and maximum elongation was reduced for VTEOS-added systems. Finally, resilience, compression set, degree of cure and crosslink density were significantly enhanced with the amount of VTEOS.

• Journal of the Korean Applied Science and Technology
• /
• v.36 no.1
• /
• pp.305-311
• /
• 2019

The acrylic copolymer was designed and prepared for soft lens with high content. The copolymers were prepared using 2-hydroxyethyl methacrylate(HEMA) as a monomer and ethylene glycol dimethacrylate(EGDMA), glycerol dimethacrylate(GD), or glycerol 1,3-diglycerolate diacrylate (GDD) as a cross linking agent. The water content for high water content lens was 46%, which was higher compared to general purpose of 36%. The contact angle decreased from 38.6 to 34.4, which appears hydrophilic surface. The tensile strength decreased from 0.1 Mpato 0.08, then again to 0.05 as hydrophilic properties of cross linking agents increased. No phase separation was observed in the cross section of lens using scanning electron microscope. The real-time infrared technique was used in photo-polymerization. The initial polymerization rate increased from 0.6 to 0.9, depending on crosslinking agent.

• Membrane Journal
• /
• v.13 no.3
• /
• pp.191-199
• /
• 2003

Cation exchange polymer electrolyte membrane for the application of direct methanol fuel cell (DMFC) was studied. Poly(vinyl alcohol)(PVA) well known as a methanol barrier in pervaporation separation was used fur the base materials and poly(acrylic acid)(PAA) was used for the crosslinking agent with various concentration. Methanol permeability, ion conductivity, ion exchange capacity, water contents and fixed ion concentration of the membranes were investigated to evaluate the performance of the fuel cell electrolyte membrane. Methanol permeability and ion conductivity of the membranes were decreased with increasing PAA content and were increased over 15% of PAA content. These phenomena would be explained with the introduction of hydrophilic crosslinking agent. The membranes with 15% content of PAA showed methanol permeability of $6.49{\times}10^{-8}/cm^2/s,\; 2.85{\times}10^{-7}CM^2/s$ at $25^{\circ}C,\; 50^{\circ}C$ of operating temperatures, respectively. ion conductivities of the membrane were $2.66{\times}10^{-3}\;S/cm,$ $9.16{\times}10^{-3}\;S/cm$ at $25^{\circ}C,\; 50^{\circ}C$ of operating temperatures, respectively. ion exchange capacity, water content and fixed ion concentration of the membrane were revealed 1.32 meq/g membrane,0.25 g $H_2$O/g membrane and 5.25 meq/g $H_2O$, respectively.

• Polymer(Korea)
• /
• v.35 no.1
• /
• pp.30-34
• /
• 2011

In this study, the effects of the electron beam irradiation on the thermal behavior and the abrasion properties of the glass fiber reinforced nylon 12 was investigated. The electron beam irradiation was carried out over a range of irradiation dose from 100 to 600 kGy with additive crosslinking agents such as triallyl cyanurate (TAC), triallyl isocyanurate (TAIC) and trimethylolpropane trimethacrylate (TMPTMA) for enhancing the crosslinking effects. The gel contents were increased dramatically above 200 kGy. It was verified that the degree of crosslinking depends on the radiation dose. The decreases of the melting temperature and the area of endothermic peak were observed as increasing the absorbed dose in the results of DSC analysis. The enhanced thermal stability was confirmed by the increases of decomposition temperature by electron beam irradiation. Furthermore, the negative deviations of the abrasion loss and the abrasion coefficients confirmed the improvement of the abrasion properties of irradiated nylon 12, as evidenced by SEM observation on the abrasion surfaces. The addition of the crosslinking agents to nylon 12 during effectively improved the thermal behavior and the abrasion properties of nylon 12 by the electron beam irradiation.

• Journal of the Korean Electrochemical Society
• /
• v.17 no.1
• /
• pp.65-70
• /
• 2014

In this study, crosslinked poly(POEM-co-AMPSLi-co-GMA)s were prepared by epoxy coupling of GMA after radical copolymerization of AMPS, POEM and GMA followed by acid-base titration reaction between sulfonic acid of AMPS and $Li_2CO_3$. It was observed that the crystalline melting temperature of POEM was effected by mol% of components and shifted to lower value by lithiation of AMPS group. The ionic conductivity of crosslinked polymer electrolyte was decreased by addition of GMA but maintained over $1.0{\times}10^{-6}S\;cm^{-1}$ until 16 mol%. Particularly, the self-doped polymer electrolyte with 2 mol% of GMA showed its ionic conductivity as high as $4.08{\times}10^{-6}S\;cm^{-1}$ at room temperature and electrochemical stability up to 6 V. In addition, 0.11 MPa of modulus and 270% of elongation were obtained from the free standing film of crosslinked polymer electrolyte.