• Electrical & Electronic Materials
• /
• v.8 no.3
• /
• pp.272-277
• /
• 1995

We report the properties of optically pumped stimulated emission at room temperature (RT) from column-III nitride semiconductors of GaN, AlGaN/GaN double heterostructure (DH) and AlGaN/GaInN DH which prepared on a sapphire substrate using an AIN buffer-layer by the nietalorganic vapor phase epitaxy (MOVPE) method. The peak wavelength of the stimulated emission at RT from AIGaN/GaN DH is 369nm and the threshold of excitation pumping power density (P$\_$th/) is about 84kW/cm$\^$2/, and they from AlGaN/GaInN DH are 402nm and 130kW/cm$\^$2/ at the pumping power density of 200kW/cm$\^$2/, respectively. The P$\_$th/ of AIGaN/GaN and AlGaN/GaInN DHs are lower than the single layers of GaN and GaInN due to optical confinement within the active layers of GaN and GaInN, respectively.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.24 no.2
• /
• pp.321-324
• /
• 2020

In this work, we developed a selective etching process for GaN that is a key process in p-GaN/AlGaN/GaN enhancement-mode (E-mode) power switching field-effect transistor (FET) fabrication. In order to achieve a high current density of p-GaN/AlGaN/GaN E-mode FET, the p-GaN layer beside the gate region must be selectively etched whereas the underneath AlGaN layer should be maintained. A selective etching process was implemented by oxidizing the surface of the AlGaN layer and the GaN layer by adding O2 gas to Cl2/N2 gas which is generally used for GaN etching. A selective etching process was optimized using Cl2/N2/O2 gas mixture and a high selectivity of 53:1 (= GaN/AlGaN) was achieved.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.105-105
• /
• 2003

InGaN/GaN MQW 구조는 청색 및 녹색 범위의 밴드 갭을 가지는 반도체로 최근 LED 및 LD 제조 등에 이용되고 있다. InGaN/GaN MQW은 InGaN와 GaN의 최적 성장온도의 중간온도에서 실행된다. InGaN와 GaN는 최적 성장온도의 차이가 크므로 중간온도에서 성장 시에 많은 결함이 생긴다. 성장온도가 높으면 InN가 분해되고 낮을 경우에는 질소의 결핍이 일어난다. 최적성장온도의 선택이 매우 중요한 문제로 주목되었다. Si 도핑으로 중간온도 성장 시에 형성되는 결함을 감소시키고 광학적 특성을 향상시킨다고 보고되었다. 그러나, Si 도핑효과에 대한 구체적이고 체계적인 연구는 부족한 실정이다. MQWs 구조의 GaN 장벽층에 미치는 성장온도와 Si 도핑 효과를 이해하기 위해서는 고온에서 성잠시킨 GaN박막(HT-GaN) 위에 중간온도에서 성장된 GaN 에피층(IT-GaN)의 구조에 관한 연구가 선행되어야한다. 본 연구에서는 HT-GaN 위에 성장된 GaN 에피층에 미치는 성장 온도와 Si 도핑 효과에 관해 연구하였다.

• Journal of the Korean Vacuum Society
• /
• v.17 no.4
• /
• pp.359-364
• /
• 2008

We have investigated optical and structural properties of $Al_{0.3}Ga_{0.7}N$/GaN and $Al_{0.3}Ga_{0.7}N/GaN/Al_{0.15}Ga_{0.85}N/GaN$ heterostructures (HSs) grown by metal-organic chemical vapor deposition, by means of Hall measurement, high-resolution X-ray diffraction, and temperature- and excitation power-dependent photoluminescence (PL) spectroscopy. A strong GaN band edge emission and its longitudinal optical phonon replicas were observed for all the samples. At 10 K, a 2DEG-related PL peak located at ${\sim}\;3.445\;eV$ was observed for $Al_{0.3}Ga_{0.7}N$/GaN HS, while two 2DEG peaks at ${\sim}\;3.42$ and ${\sim}\;3.445\;eV$ were observed for $Al_{0.3}Ga_{0.7}N/GaN/Al_{0.15}Ga_{0.85}N/GaN$ HS due to the additional $Al_{0.15}Ga_{0.85}N$ layers. Moreover, the emission intensity of the 2DEG peak was higher in $Al_{0.3}Ga_{0.7}N/GaN/Al_{0.15}Ga_{0.85}N/GaN$ HS than in $Al_{0.3}Ga_{0.7}N$/GaN HS probably due to an effective confinement of the photo-excited holes by the additional $Al_{0.15}Ga_{0.85}N$ layers. The 2DEG-related emission intensity decreased with increasing temperature and disappeared at temperatures above 150 K. To investigate the origin of the new 2DEG peaks, the energy-band structure for multiple AlGaN/GaN HSs were simulated and compared with the experimental data. As a result, the observed high- and low-energy peaks of 2DEG can be attributed to the spatially-separated 2DEG emissions formed at different AlGaN/GaN heterointerfaces.

• Journal of the Optical Society of Korea
• /
• v.17 no.1
• /
• pp.16-21
• /
• 2013

In this paper, we report the effect of GaN/graded-composition AlGaInN/GaN quantum barriers in active regions on the electrical and optical properties of GaN-based vertical light emitting diodes (VLEDs). By modifying the aluminum composition profile within the AlGaInN quantum barrier, we have achieved improvements in the output power and the internal quantum efficiency (IQE) as compared to VLEDs using conventional GaN barriers. The forward voltages at 350 mA were calculated to be 3.5 and 4.0 V for VLEDs with GaN/graded-composition AlGaInN/GaN barriers and GaN barriers, respectively. The light-output power and IQE of VLEDs with GaN/graded-composition AlGaInN/GaN barriers were also increased by 4.3% and 9.51%, respectively, as compared to those with GaN barriers.

• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.3
• /
• pp.1-5
• /
• 2018

In this study, the effects of indium (In) doping in InGaN/GaN multi quantum well (MQW) on photoelectrochemical (PEC) properties were investigated. Each quantum well (QW) layer with controlled In content were grown on sapphire substrate. Before growth of MQW, GaN growth consisted of various stages in the following order: buffer GaN growth, undoped GaN growth, and Si-doped n-type GaN growth. Absorbance of InGaN/GaN MQW having different In composition was higher than that of the InGaN/GaN MQW having a constant In composition. It indicates that InGaN layer having different In composition absorbs light having a broad spectrum energy. These results are in agreement with those in photoluminescence (PL). After evaluation of PEC properties, it demonstrated that InGaN/GaN MQW having different In composition was improved InGaN/GaN MQW having constant In composition in PEC water splitting ability.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.6 no.2
• /
• pp.90-94
• /
• 2006

We report on the growth and characterization of InGaN/GaN MQWs on two different types of sapphire substrates and GaN substrates. The InGaN/GaN MQWs are grown by using metalorganic chemical vapor deposition. Our analysis of the satellite peaks in the HRXRD patterns shows, GaN substrates InGaN/GaN MQW compared to sapphire substrates InGaN/GaN MQW, more compressive strain on GaN substrates than on sapphire substrates. However, results of optical investigation of InGaN/GaN MQWs grown on GaN substrates and on sapphire substrates, which have lower Stokes-like shift of PL to GaN substrates compared to sapphire substrates, are shown to the potential fluctuation and the quantum-confined Stark effect induced by the built-in internal field due to spontaneous and straininduced piezoelectric polarizations. The InGaN/GaN MQWs are shown to quantify the Stokes-like shift as a function of x.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.11a
• /
• pp.50-53
• /
• 1994

In this study. we report the properties of optically pumped stimulated emission at room temperature (RT) from column-III nitride semiconductors of GaN, GaInN, AlGaN/GaN double hetero-structure (DH) and AlGaN/GaInN DH which grown by low pressure metal-organic vapor phase epitaxy on sapphire substrate using an AIN buffer-layer. The peak wavelength of the stimulated emission at RT from AlGaN/GaN DH is 370nm and the threshold of excitation pumping power density (P$\_$th/) is about 89㎾/$\textrm{cm}^2$, and they from AlGaN/GaInN DH are 403nm and 130㎾/$\textrm{cm}^2$, respectively. The P$\_$th/ of AlGaN/GaN and AlGaN/GaInN DHs are lower than the bulk materials due to optical confinement within the active layers of GaN and GaInN. The optical gain and the polarization of stimulated emission characteristics are presented in this article.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.13 no.6
• /
• pp.617-621
• /
• 2013

This study examined the effect of electron-beam (E-beam) irradiation on the electrical properties of n-GaN, AlGaN and AlGN/GaN structures on sapphire substrates. E-beam irradiation resulted in a significant decrease in the gate leakage current of the n-GaN, AlGaN and HEMT structure from $4.0{\times}10^{-4}A$, $6.5{\times}10^{-5}A$, $2.7{\times}10^{-8}A$ to $7.7{\times}10^{-5}A$, $7.7{\times}10^{-6}A$, $4.7{\times}10^{-9}A$, respectively, at a drain voltage of -10V. Furthermore, we also investigated the effect of E-beam irradiation on the AlGaN surface in AlGaN/GaN heterostructure high electron mobility transistors(HEMTs). The results showed that the maximum drain current density of the AlGaN/GaN HEMTs with E-beam irradiation was greatly improved, when compared to that of the AlGaN/GaN HEMTs without E-beam irradiation. These results strongly suggest that E-beam irradiation is a promising method to reduce leakage current of AlGaN/GaN HEMTs on sapphire through the neutralization the trap.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.37 no.12
• /
• pp.11-17
• /
• 2000

We investigated the growth of InGaN/GaN multiple quantum wells (MQWs) structures which emit blue light. The samples were grown in a low pressure metalorganic chemical vapor deposition system. We examined InGaN/GaN MQWs by varying growth temperatures and thicknesses of InGaN well and GaN barrier layers in MQWs. Especially, the thickness of GaN barrier in InGaN/GaN MQWs was found to severely affect the interfacial abruptness between InGaN well and GaN barrier layers. The higher order satellite peaks in the high resolution x-ray diffraction spectra and the high resolution cross sectional transmission electron microscope image of MQW structrues revealed that the interface between InGaN and GaN layers was very abrupt. Room-temperature photoluminescence spectra also showed a blue emission from InGaN/GaN MQWs at the wavelength of 463.5nm with a narrow full width at half maximum of 72.6meV.