• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 추계학술대회 논문집
• /
• pp.121-124
• /
• 1999

The (Ba,Sr)TiO$_3$[BST] thin film were fabricated on the Pt/Ti/SiO$_2$/Si substrate by RF sputtering technique. The structural properties of the BST thin films were investigated with deposition time and substrate temperature by XRD. In the case of the BST thin films which has the deposition thin of 20 min, second phases and BST (111) peaks were increased with increasing the temperature of substrate. The capacitance of the BST thin film (deposition time of 20 min.) was decreased with the substrate temperature and was 1500pF with applied voltage of 1V.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.649-652
• /
• 1999

The (Ba, Sr)TiO$_3$(BST) thin films were fabricated on Pt/Ti/SiO$_2$/Si substrate by RF sputtering technique. The structural properties of the BST thin films were investigated with substrate temperature by XRD, SEM, EDS and AES depth profils. Increasing the substrate temperature, barium multi titanate phases were decreased. The BST thin film had a structure of perovskite type, and had peaks of (100), (200) at the substrate temperature of 50$0^{\circ}C$. When the BST thin films were deposited at the substrate temperature of 50$0^{\circ}C$, the composition ratio of Ba/sr was 52/48.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.73-76
• /
• 2001

We deposited epitaxial $Ba_{0.6}Sr_{0.4}TiO_{3}(BST)$ films having thickness of 400 nm on MgO(001) substrates, where a 10 nm thick $Ba_{1-x}Sr_{x}TiO_{3}$ (x = 0.1 - 0.7) interlayer was inserted between BST and MgO to manipulate the stress of the BST films. Since the main difference of those epitaxial BST films was the lattice constant of the interlayers, we were very successful in controlling the stress of the BST films. BST films under small tensile stress showed larger dielectric constant than that without stress as well as those under compressive stress. Stress relaxation was investigated using epitaxial BST films with various thicknesses grown on different interlayers. For BST films grown on $Ba_{0.7}Sr_{0.3}TiO_{3}$ interlayers, the critical thickness was about 600 nm. On the other hand, the critical thickness of single-layer BST film was less than 100 nm.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 추계학술대회 논문집
• /
• pp.37-40
• /
• 1998

(Ba.Sr)TiO$_3$(BST) ceramics were fabricated with different Ba/Sr ratios and the str dielectric properties of the BST bulk ceramics were investigated. As the Ba/sr ratios dielectric constant decreased. (Ba$_{0.7}$Sr$_{0.3}$)TiO$_3$ (BST(70/30)) showed a maximum dielec value of $\varepsilon$$_{r}$=8.856, this showed that the decrease of Ba/Sr ratios had made BST thin dielectrics. Targets were fabricated and made into film by PLD process and the thin film by PLD process have good stoichiometry with the targets.rgets.

• Transactions on Electrical and Electronic Materials
• /
• 제1권4호
• /
• pp.30-39
• /
• 2000

The variation of electrical properties of (Ba, Sr)TiO$_3$[BST] thin films deposited of RuO$_2$electrode with (Ba+Sr)/Tr ration was investigated. BST thin films with various (Ba+Sr)/Tr ration were deposited on RuO$_2$/Si substrates using in-situ RF magnetron sputtering. It was found that the electrical properties of BST films depends on the composition in the film. The dielectric constant of the BST films is about 190 at the (Ba+Sr)/Tr ration of 1.0, 1,025 and does not change markedly. But , the dielectric constant degraded to 145 as the (Ba+Sr)/Tr ratio increase to 1.0. In particular, the leakage current mechanism of the films shows the strong dependence on the (Ba+Sr)/Tr ration in the films. At the ration (Ba+Sr)/Tr=1,025, the Al/BST/RuO$_2$ capacitor show the most asymmetric behavior in the leakage current density, vs, electric field plot. It is considered that the leakage current of the (Ba+Sr)/Tr=1,025 thin films is controlled by the battier-Iimited process, i,e, Schottky emission.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 추계학술대회 논문집
• /
• pp.243-246
• /
• 1998

(Ba, Sr)TiO$_3$[BST] thin films were fabricated on Pt/SiO$_2$/Si substrate by RF sputtering technique. The structural, dielectric and electrical properties of BST thin films were investigated with Ar/O$_2$ ratio. Dielectric constant and dielectric loss of the BST thin film were about 1020 and 2.0[%], respectively. (at RF power 80W, post annealing temperature $650^{\circ}C$, deposition pressure of 5mTorr and Ar/O$_2$=80/20). For the BST(Ar/O$_2$=80/20) thin film with Polarization switching cycles of 10$^{10}$ , remanent polarization and coercive field were 0.084[$\mu$C/cm$^2$], 1.954[kV/cm], respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.73-76
• /
• 2001

We deposited epitaxial $Ba_{0.6}$S $r_{0.4}$Ti $O_3$(BST) films having thickness of 400 nm on MgO(001) substrates, where a 10 nm thick $Ba_{1-x}$S $r_{x}$Ti $O_3$(x=0.1-0.7) interlayer was inserted between BST and MgO to manipulate the stress of the BST films. Since the main difference of those epitaxial BST films was the lattice constant of the interlayers, we were very successful in controlling the stress of the BST films. BST films under small tensile stress showed larger dielectric constant than that without stress as well as those under compressive stress. Stress relaxation was investigated using epitaxial BST films with various thicknesses grown on different interlayers. For BST films grown on $Ba_{0.7}$S $r_{0.3}$Ti $O_3$ interlayers, the critical thickness was about 600 nm. On the other hand, the critical thickness of single-layer BST film was less than 100 nm.00 nm.m.m.m.

• 한국세라믹학회지
• /
• 제36권4호
• /
• pp.403-409
• /
• 1999

RF 마그네트론 스퍼터링방법으로 Pt/Ti/NON/Si 기판 위에 $Ba_{0.66}$$Sr_{0.38}$$TiO_{3}$(BST) 박막을 증착한 다음 유전 및 초전특성을 살펴보았다. BST 박막을 증착할 때 기판온도를 300~-$600^{\circ}C$로 변화시킨 결과 기판온도가 증가할수록 박막의 결정성과 입도가 증가하여 유전율과 초전계수가 증가하였다. 한편 하부전극인 Pt의 증착조건이 BST 박막의 몰성에 미치는 영향도 살펴보았다. Pt의 증착온도와 Pt의 미세구조와 결정성뿐만 아니라 상부에 형성된 BST 박막의 배향성에도 큰 영향을 미쳤으며, 그 결과 BST의 초전특성에도 큰 영향을 미쳤다. BST 박막과 Pt 하부전극의 증착조건을 적정화함으로써 본 연구에엇는 상온에서 초전계수가 240 $nCcm^{-2}K^{-1}$인 BST 박막을 얻었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 춘계학술대회 논문집 반도체 재료 센서 박막재료 전자세라믹스
• /
• pp.18-21
• /
• 2004

An alkoxide-based sol-gel method was used to fabricate $Ba_{0.6}Sr_{0.4}TiO_3$ thin films doped by Bi from 5 to 20 mol% on a $Pt/Ti/SiO_2/Si$ substrate. The structural and dielectric properties of BST thin films were investigated as a function of Bi dopant concentration. The dielectric properties of the Bi doped BST films were strongly dependent on the Bi contents. The dielectric constant and dielectric loss of the films decreased with increasing Bi content. However, the leakage current density of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin film showed the lowest value of $5.13{\times}10^{-7}\;A/cm^2$ at 5 V. The figure of merit (FOM) reached a maximum value of 32.42 at a 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin films. The dielectric constant, loss factor, and tunability of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin films were 333, 0.0095, and 31.1%, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 센서 박막재료 반도체재료 기술교육
• /
• pp.103-106
• /
• 2002

The applicability of models based on fractal morphology to characterize $(Ba\;Sr)TiO_{3}$ thin film surfaces was investigated. The fractal morphology of coated barium strontium titan oxide thin film surfaces was described using fractal dimension from scanning electro microscopy image. The $(Ba\;Sr)TiO_{3}$ coating were deposited on silicon wafers using $(Ba\;Sr)TiO_{3}$ solution and spin coater. BST solution was composited by mol ratio, and then spin-coated from 3 times to 5 times coating on $Pt/SiO_{2}/Si$ substrate. Qualitative thin film analysis was performed with scanning electro microscopy (SEM), and surfaces parameters such as average grain diameter, roughness exponent and fractal dimension were determined.