• Electrical & Electronic Materials
• /
• v.10 no.10
• /
• pp.1041-1047
• /
• 1997

In this paper the dielectric properties of (0.8-x)Pb(Mb$_{1}$3//Nb/2/3)O$_3$/BaTiO$_3$-CaZrO$_3$(x=0.1, 0.15, 0.2, 0.25) ceramics were investigated. Specimens were prepared by the conventional mixed oxide method and sintering temperature and time were 1000~115$0^{\circ}C$ 2hr, respectively. The structural and dielectric properties with variation of sintering temperature and composition were investigated. All the specimens sintered at 115$0^{\circ}C$ for 2hr showed the highest value of 1043. With increasing the contents of CZ and frequency dielectric constant was decreased and which was decreased with increasing temperature from 3$0^{\circ}C$ to 15$0^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.41 no.1
• /
• pp.9-12
• /
• 2004

The effect of x wt% CuO-y wt% $V_2O_5$ content on the microwave properties of $(Pb_{0.45}Ca_{0.55})[(Fe_{0.5}Nb_{0.5})_{0.9}Sn_{0.1}]O_3$ (PCFNS) ceramics was investigated. In order to decrease the sintering temperature and use as a Low Temperature co-firing Ceramics (LTCC), CuO-$V_2O_5$ are added in the PCFNS. The bulk density, dielectric constant (${\varepsilon}_r$) and quality factor(Q${\cdot}f_0$) increased with increase in CuO content within a limited value. The microwave properties were degraded with increases in $V_2O_5$ content. The temperature coefficient of the resonant frequency (${\tau}_f$) of PCFNS was shifted to positive value abruptly with increasing the $V_2O_5$ content, while the ${\tau}_f$ was slightly shifted to positive value with increasing the CuO content. The optimized microwave properties, ${\varepsilon}_r$ = 88, Q${\cdot}f_0$ = 6100 (GHz), and ${\tau}_f$ = 18 ppm/$^{\circ}C$, were obtained in $(Pb_{0.45}Ca_{0.55})[(Fe_{0.5}Nb_{0.5})_{0.9}Sn_{0.1}]O_3$ with 0.2wt% CuO 0.05 wt% $V_2O_5$ and sintered at $1000^{\circ}C$ for 3 h. The relationship between the microstructure and microwave dielectric properties of ceramics was studied by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM)

• Journal of the Korean Ceramic Society
• /
• v.40 no.4
• /
• pp.323-327
• /
• 2003

Microwave dielectric properties of (P $b_{0.4}$C $a_{0.6}$)[($Fe_{\frac{1}{2}}$N $b_{\frac{1}{2}}$)$_{1-x}$ (M $g_{1}$ 3/N $b_{2}$ 3/)x] $O_3$ (PCFMN) ceramics were investigated as a function of (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$ content (0.1$\leq$x$\leq$0.8). A single perovskite phase with the cubic structure was obtained through the given composition range. The unit cell volume was increased with (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$, due to the larger average ionic size of (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$ than that of ($Fe_{\frac{1}{2}}$N $b_{\frac{1}{2}}$)$^{4+}$ for B-site ion. Dielectric constant (K) and Temperature Coefficient of Resonant Frequency(TCF) of PCFMN ceramics were dependent on (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$ content due to the decrease of ionic polarizability and B-site bond valence, respectively. Qf value was decreased with (M $g_{1}$ 3/N $b_{2}$ 3/)$^{4+}$ content due to the decrease of grain size. Typically, K of 73.56, Qf of 5,074 GHz and TCF of -6.45 ppm/$^{\circ}C$ were obtained for the specimens with x=0.4 sintered at 125$0^{\circ}C$ for 3 h.125$0^{\circ}C$ for 3 h.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.178-180
• /
• 2005

In this study, in order to develop multilayer low temperature sintering piezoelectric transformer, $Pb_{0.97}Sr_{0.03}[(Mn_{1/3}Nb_{2/3})x(Zr_{0.48}Ti_{0.52})_{1-x}O_3]+$ 0.25wt% $CeO_2$+0.3 wt% $Nb_2O_5$ system ceramics were fabricated using $Li_2CO_3-CaCO_3$ and CuO as sintering aids and their piezoelectric and dielectric characteristics were investigated with the amount of PMN substitution. With increasing PMN substitution, electromechanical coupling factor kp and dielectric constant were increased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.563-566
• /
• 2000

The effect of CuO and CuO-B $i_2$ $O_3$ additives on microwave dielectric properties of (P $b_{0.45}$C $a_{0.55}$)[F $e_{0.5}$N $b_{0.5}$)$_{0.9}$S $n_{0.1}$] $O_3$were investigated to decrease the sintering temperature for usage of Low Temperature Co-firing Ceramics (LTCC). The (P $b_{0.45}$C $a_{0.55}$)[F $e_{0.5}$N $b_{0.5}$)$_{0.9}$S $n_{0.1}$] $O_3$ceramics was sintered at 11$65^{\circ}C$. In order to decrease the sintering temperature, CuO and Cuo-B $i_2$ $O_3$ were added in the (Pb,Ca)[(Fe,Nb)Sn] $O_3$ with CuO-B $i_2$ $O_3$. For the addition of 0.4 wt.% CuO, the sintered density and the dielectric constant of the ceramics were revealed the maximum values of the 6.06g/c $m^2$ and 83 respectively and temperature coefficient of resonance frequency ($\tau$$_{f}$) shifted to the positive value. As increasing B $i_2$ $O_3$to the (Pb,Ca)[(Fe,Nb)Sn] $O_3$ with CuO-B $i_2$ $O_3$with 0.2 wt.% CuO, the sintered density, the $\varepsilon$$_{r}$ and the Q was decreased, and $\tau$$_{f}$ was minimized at 0.2 wt.% CuO, and 0.2 wt.% B $i_2$ $O_3$. For this composition, dielectric properties were $\varepsilon$$_{r}$ of 81, Q. $f_{0}$ of 4400 GHz, and $\tau$$_{f}$ of 5 ppm/$^{\circ}C$ at sintering temperature of 100$0^{\circ}C$. the relationship between the microstructure and properties of ceramics was studied by X-ray diffraction(XRD), scanning electron microscopy(SEM).copy(SEM).oscopy(SEM).copy(SEM).EM).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.2
• /
• pp.90-94
• /
• 2016

In this work, [$Pb(Mg_{1/2}W_{1/2})_{0.03}(Ni_{1/3}Nb_{2/3})_x(Zr_{0.5}Ti_{0.5})_{0.97-x}O_3-BiFeO_3$] (x=0.02 to 0.12) composition ceramics were fabricated by the conventional soild state reaction method and their microstructure and piezoelectric properties were investigated according to PNN substitution. The addition of small amount of $BiFeO_3$, $Li_2CO_3$, and $CaCO_3$ were used in order to decrease the sintering temperature of the ceramics. The XRD (x-ray diffraction patterns) of all ceramics exhibited a perovskite structure. The sinterability of PMW-PNN-PZT-BF ceramics was remarkably improved using liquid phase sintering of $CaCO_3$, $Li_2CO_3$. However, it was identified from of the X-ray diffraction patterns that the secondary phase formed in grain boundaries decreased the piezoelectric properties. According to the substitution of PNN, the crystal structure of ceramics is transformed gradually from a tetragonal to rhombohedral phase. The x=0.10 mol PNN-substituted PMW-PNN-PZT-BF ceramics sintered at $920^{\circ}C$ showed the optimum values of piezoelectric constant($d_{33}$), piezoelectric figure of merit($d_{33{\cdot}}g_{33}$), planar piezoelectric coupling coefficient($k_p$) and density : $d_{33}=566$ [pC/N], $g_{33}=29.28[10^{-3}mV/N]$, $d_{33{\cdot}}g_{33}=16.57[pm^2/N]$, $k_p=0.61$, density=7.82 [$g/cm^3$], suitable for duplex ultrasonic sensor application.

• Journal of the Korean Ceramic Society
• /
• v.38 no.7
• /
• pp.597-601
• /
• 2001

The effect of CuO, $B_2$ $O_3$, $V_2$ $O_{5}$ and CuO-B $i_2$ $O_3$additives on microwave dielectric properties of (P $b_{0.45}$C $a_{0.55}$) [(F $e_{0.5}$N $b_{0.5}$)$_{0.9}$S $n_{0.1}$] $O_3$(PCFNS) were investigated. The PCFNS ceramics were sintered at 11$65^{\circ}C$. To decrease the sintering temperature for using as a low-temperature co-firing ceramics (LTCC), CuO, $B_2$ $O_3$, $V_2$ $O_{5}$ and CuO-B $i_2$ $O_3$were added to the PCFNS. As the content of CuO increased, the sintered density and dielectric constant increased and the temperature coefficient of resonance frequency ($\tau$$_{f}$) shifted to the positive value. When the CuO-B $i_2$ $O_3$were added, dielectric properties were $\varepsilon$$_{r}$ of 83, Q. $f_{0}$ of 6085 GHz, and $\tau$$_{f}$ of 8ppm/$^{\circ}C$ at a sintering temperature of 100$0^{\circ}C$. The relationship between the microstructure and properties of ceramics was studied by X-ray diffraction and scanning electron microscopy.icroscopy.y.icroscopy.y.