• Korean Journal of Materials Research
• /
• v.8 no.7
• /
• pp.621-627
• /
• 1998

The formation of Co-silicide between Co/Zr bilayer on the amorphous and crystalline Si substrates has been investigated. The films of Zr(50$\AA$) and Co(l50$\AA$) were deposited with e-beam evaporation system and were heattreated with the rapid thermal annealing system at the temperatures between 50$0^{\circ}C$ and 80$0^{\circ}C$ with 10$0^{\circ}C$ increments for 30 seconds. The phase identification of Co-silicide was carried out by XRD and the chemical analysis was examined by AES and RBS. The interface morphologies of Co/Zr bilayer films were investigated by cross sectional TEM and HRTEM. $CoSi_2$ was formed epitaxially on the crystalline Si substrate above $700^{\circ}C$ while polycrystalline $CoSi_2$ was grown on the amorphous Si substrate. The formation temperature of Co-silicide on the amorphous Si substrate was about 100 C lower than that on the crystalline Si. The COzSi phase was not identified on the both Si substrates. The formation temperature of first phase of Co-silicide on ColZr bilayer was higher than that on Co mono layer. CoSizlayer formed on the amorphous Si substrate exhibits better uniformity compared to the CoSiz formed on the crystalline substrate. The sheet resistance of CoSiz layer on crystalline Si was lower than that on the amorphous Si at high temperatures.tures.

• Bulletin of the Korean Chemical Society
• /
• v.29 no.1
• /
• pp.94-98
• /
• 2008

A fundamental study was developed concerning the novel solvent extraction of the tetravalent metal ions; zirconium(IV), hafnium(IV) and thorium(IV). Their extraction behavior in toluene was investigated with a recently synthesized naphthol-derivative Schiff base, 1-({[4-(4-{[(E)-1-(2-hydroxy-1-naphthyl)methyliden]amino}phenoxy) phenyl]imino}methyl)-2-naphthol (HAPMN). The spectrophotometrical examination of the complex formation between HAPMN and the Zr(IV), Hf(IV) and Th(IV) ions in acetonitrile revealed the formation of stable 1:1 complexes in the solution. After the thorium extraction in toluene, it was found that [Th(OH)3HA] was the respective deriving substance. While, in the case of zirconium and hafnium extraction, the extracted adduct was found to be [M4(OH)8(H2O)16Cl62HA]. The stoichiometric coefficients of these extracted species were determined by the slope analysis method. The extraction reaction followed a cation exchange mechanism.

• 한국신재생에너지학회:학술대회논문집
• /
• 2006.11a
• /
• pp.463-466
• /
• 2006

직접 알콜 연료전지는 액체인 알콜을 직접 연료전지에 공급하여 연소시킴으로써 높은 효율을 갖는 휴대용전원으로 주목받는 장치이다. 직접 알콜 연료전지에 담지체로 사용되는 탄소 소재는 넓은 표면적과 우수한 전기전도도를 가지고 있다는 장점 있으나 금속 촉매와의 상호작용이 약하여 촉매 활성에 영향을 주지 못한다. 산화물을 담지체로 사용할 경우 이러한 금속-담지체 간의 상호작용으로 인한 촉매활성 증가 및 입자성장 억제의 효과를 기대할 수 있다. 본 연구에서는, 안티몬 도핑된 주석산화물 (Sb-doped SnO2 : ATO nanoparticle)을 직접 메탄올 연료전지용 담지체어 적용하였으며 합성 과정은 다음과 같다. SnC14 5H2O SbC13, NaOH, HCl 수용액 혼합물을 삼구 플라스크에 넣고 $100^{\circ}C$ 온도에서 환류(reflux) 시킨 후 세척 및 건조하여 Air 분위기에서 열처리하였다. 합성된 산화물 수용액에 폴리올 방법으로 합성된 백금 콜로이드를 담지하였으며, 세척과 건조를 통하여 산화물에 담지된 백금 촉매를 촉매를 합성하였다. 촉매의 구조분석을 위해 XRD, TEM을 사용하였으며, 전극촉매로서의 활성을 평가하기 위해 cyclic voltammetry을 평가하였다. 본 연구에서는 백금의 담지량에 따른 Costripping voltammetry특성과 메탄올 및 에탄올 산화 반응 특성에 대하여, 탄소를 담지체로 사용한 Pt/C 촉매와 비교 평가하였다. 알콜 산화반응 평가결과, 주석산화물에 담지한 촉매가 탄소를 담지체로 사용한 촉매보다 우수한 활성을 나타내었으며 활성증가는 메탄올에 비해 에탄올 산화 반응의 경우 크게 증가하였다. 막과 비교해 보았다. $ZrO_2$ 입자는 전도성이며 동시에 친수성을 나타내기 때문에 상용 막에 비하여 함수율 및 수소이온 전도도가 우수하게 나타났다. 복합막의 이러한 물성은 $100^{\circ}C$이상의 고온에서 전해질 막 내의 물 관리를 용이하게 한다. 단위 전지 운전 온도 $130^{\circ}C$, 상대습도 37%의 운전 조건에서도 상당히 우수한 전지 성능을 보임에 따라 고온/저가습 조건에서 상용 Nafion 112 막보다 우수한 막 특성을 나타냄을 확인하였다.소/배후방사능비는 각각 $2.18{\pm}0.03,\;2.56{\pm}0.11,\;3.08{\pm}0.18,\;3.77{\pm}0.17,\;4.70{\pm}0.45$ 그리고 $5.59{\pm}0.40$이었고, $^{67}Ga$-citrate의 경우 2시간, 24시간, 48시간에 $3.06{\pm}0.84,\;4.12{\pm}0.54\;4.55{\pm}0.74 $이었다. 결론 : Transferrin에 $^{99m}Tc$을 이용한 방사성표지가 성공적으로 이루어졌고, $^{99m}Tc$-transferrin의 표지효율은 8시간까지 95% 이상의 안정된 방사성표지효율을 보였다. $^{99m}Tc$-transferrin을 이용한 감염영상을 성공적으로 얻을 수 있었으며, $^{67}Ga$-citrate 영상과 비교하여 더 빠른 시간 안에 우수한 영상을 얻을 수 있었다. 그러므로 $^{99m}Tc$<

• Nuclear Engineering and Technology
• /
• v.53 no.8
• /
• pp.2582-2590
• /
• 2021

The high-energy milling is one of the most extended techniques to produce Oxide dispersion strengthened (ODS) powder steels for nuclear applications. The consequences of the high energy mill process on the final powders can be measured by means of deformation level, size, morphology and alloying degree. In this work, an ODS ferritic steel, Fe-14Cr-5Al-3W-0.4Ti-0.25Y₂O₃-0.6Zr, was fabricated using two different mechanical alloying (MA) conditions (M_std and M_act) and subsequently consolidated by Spark Plasma Sintering (SPS). Milling conditions were set to evidence the effectivity of milling by changing the revolutions per minute (rpm) and dwell milling time. Differences on the particle size distribution as well as on the stored plastic deformation were observed, determining the consolidation ability of the material and the achieved microstructure. Since recrystallization depends on the plastic deformation degree, the composition of each particle and the promoted oxide dispersion, a dual grain size distribution was attained after SPS consolidation. M_act showed the highest areas of ultrafine regions when the material is consolidated at 1100 ℃. Microhardness and small punch tests were used to evaluate the material under room temperature and up to 500 ℃. The produced materials have attained remarkable mechanical properties under high temperature conditions.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2004.02a
• /
• pp.73-82
• /
• 2004

This paper studies the leaching behaviors of pyrochlore-rich synroc incorporated 46.8wt% simulated actinides waste under the five simulated geological disposal media, which included the bentonite, granite, granite ＋ ferroferric oxide, granite ＋ cement, bentonite ＋ ferroferric oxide, respectively. The mass loss rates reached to equilibrium after 182 day and was 10-7 g/$\textrm{mm}^2{\cdot}d$. That suggests the mass loss rate of pyrochlore-rich synroc, loaded 46.8wt% actinides waste, was very low. The surfaces of the leached specimens were analyzed by XRD, SEM/EDS. The experimental results show that the pyrochlore-rich synroc samples in the systems, which contained bentonite and cement, have two new phases formed on the leached specimens surface at $90^{\circ}C$ for 728d; The bentonite and cement can retard the elements leaching; $Fe_3O_4$ can speed the elements leaching; Expect for Ti ion depleted on the sample surface, other ion, such as U, Zr, AI, Ca, were in equable states and Ba ion was enriched during test time, which indicated the simulated disposal media have good ability to retard the leaching behavior of the pyrochlore-rich synroc.

• Journal of the Korean Vacuum Society
• /
• v.2 no.4
• /
• pp.416-423
• /
• 1993

Hydrogen depth profiling was performed by H(19F, $\alpha$${\gamma}$) nuclear resonance reactin . A cesium sputtering ion sorce and 1.7MV Tandem Van de Graaff accelerator was used for the production of 6.5MeV 19F ion. The ${\gamma}$ rays produced by the reaction were measure dby 3" $\times$3" and 6" $\times$8" Nal detectors . A test measurement was done for hydrogen contaminatin layer of a bare silicon wafer, Si3N4(H) and Zr(O)a-Si/Si for the purpose of verifying the applicability , detection limit and the reliability of the method.ility of the method.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.3
• /
• pp.186-189
• /
• 2003

The role of excess Pb about the crystallization behavior and electrical properties in b(Zr$\sub$0.52/Ti$\sub$0.48/)O3(PZT) thin films has not been precisely defined. In this work, the effect of excess Pb content on the ferroelectric properties of these films was investigated. To analyze the effect, PZT films containing various amounts of excess Pb were Prepared. PZT thin films were deposited on the Pt/Ti bottom electrode by rf magnetron sputtering method and then they were crystallized by rapid thermal annealing (RTA). The experiment showed that all PZT films indicated perovskite polycrystalline structure with preferred orientation (111) and no pyrochlore phase was observed. As higher excess Pb was included, the films showed that value of leakage current shift from 2.03${\times}$10$\^$-6/ to 6.63 ${\times}$ 10$\^$-8/A/cm$^2$ at 100kV/cm, and value of remanent polarization shift from 8.587 ${\mu}$C /cm$^2$ to 4.256 ${\mu}$C/ cm$^2$. Electrical properties of PZT thin film affected by Pb excess content of target were explained to be caused of defect among space charges and defect grain boundaries.

• Transactions of the Korean hydrogen and new energy society
• /
• v.26 no.6
• /
• pp.516-523
• /
• 2015

Nickel based oxygen transfer materials supported on two different YSZs were tested to evaluate their performance in methane chemical-looping reforming. The oxygen transfer materials of YSZs were selected with different amount of the doped yittrium in the $ZrO_2$ structure. The yittrium of 8 mol% stabilized the zirconia oxide to a cubic structure compare to the 3 mol% doping, which is known to be a good for oxygen transfer. Various nickel amounts (16wt.%, 32wt.%, 48wt.%) were loaded on the selected supports. The nickel amount of 32% shows the optimized catalyst structure with good physical properties and reducibility from the XRD, BET and H2-TPR analysis, especially when the support of 8YSZ was used. From the methane chemical-looping reforming, hydrogen was produced by methane decomposition catalyzed by Ni on both YSZs. Comparing two YSZ supports of 3YSZ and 8YSZ during the cycling tests, the catalyst with 8YSZ (Ni 32%) exhibits not only the higher methane conversion and hydrogen production but also a faster reaction rate reaching to the stable point.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.55 no.9
• /
• pp.429-433
• /
• 2006

PZT(80/0) powder was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The coating and drying procedure was repeated 4 times. And then the PZT(20/80) precusor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5mol/L and the number of coating was varied from 0 to 6. The porosity decreased and the grain size increased with increasing the number of coatings. The thickness of the PZT-6(6: number of coatings) films was about $60{\mu}m$. The relative dielectric constant increased and the dielectric loss decreased with increasing the number of PZT(20/80) sol coatings. The relative dielectric constant and dielectric loss of the PZT-6 thick film were 275 and 3.5%, respectively. The remanent polarization, coercive field and breakdown strength of the PZT-6 film were $19.8{\mu}C/cm^2$, 13.7kV/cm and 130kV/cm, respectively.

• Journal of the Korean Ceramic Society
• /
• v.45 no.11
• /
• pp.681-687
• /
• 2008

The sintering and electrical properties of the hydrothermal PSZT powders obtained by substituting 4, 6 and 8mol% Sr for Pb in PZT lattice structure were investigated. The lattice constant and particle size decreased in proportion to a quantity of Sr. The sintering properties of PSZT powders showed $7.754g/cm^3$ of sintered density and $4{\mu}m$ of grain size at sintering temperature of $1250^{\circ}C$. Curie temperature lowered gradually from $363.6^{\circ}C\;to\;319.2^{\circ}C$ and relative dielectric constants increased rapidly by a quantity of Sr. In comparison to PZT, moreover, the quality factor of PSZT was increased more than three times with increase of Sr mole ratio, and piezoelectric constant $(d_{31}\;and\;g_{31})$ was decreased. It was found that dielectric loss of PSZT was decreased by 0.574% which was half of PZT.