• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제44회 동계 정기학술대회 초록집
• /
• pp.434-436
• /
• 2013

Ga-doped ZnO (GZO) was substitutes of the SnO2:F films on soda lime glass substrate in the photovoltaic devices such as CIGS, CdTe and DSSC due to good properties and low cost. However, it was reported that the electrical resistivity of GZO is unstable above $300^{\circ}C$ in air atmosphere. To improve thermal stability of GZO thin films at high temperature above $300^{\circ}C$ an $TiO_2$ thin film was deposited on the top of GZO thin films as a barrier layer by Pulsed Laser Deposition (PLD) method. $TiO_2$ thin films were deposited at various thicknesses from 25 nm to 100 nm. Subsequently, these films were annealed at temperature of $300^{\circ}C$, $400^{\circ}C$, $500^{\circ}C$ in air atmosphere for 20 min. The XRD measurement results showed all the films had a preferentially oriented ( 0 0 2 ) peak, and the intensity of ( 0 0 2 ) peak nearly did not change both GZO (300 nm) single layer and $TiO_2$ (50 nm)/GZO (300 nm) double layer. The resistivity of GZO (300 nm) single layer increased from $7.6{\times}10^{-4}{\Omega}m$ (RT) to $7.7{\times}10^{-2}{\Omega}m$ ($500^{\circ}C$). However, in the case of the $TiO_2$ (50 nm)/GZO (300 nm) double layer, resistivity showed small change from $7.9{\times}10^{-4}{\Omega}m$ (RT) to $5.2{\times}10^{-3}{\Omega}m$ ($500^{\circ}C$). Meanwhile, the average transmittance of all the films exceeded 80% in the visible spectrum, which suggests that these films will be suitable for photovoltaic devices.

• Transactions on Electrical and Electronic Materials
• /
• 제14권5호
• /
• pp.242-245
• /
• 2013

Sn-doped $In_2O_3$ (ITO) thin films were prepared by radio frequency magnetron sputtering without intentional substrate heating on bare glass and $TiO_2$-deposited glass substrates to investigate the effect of a $TiO_2$ buffer layer on the electrical and optical properties of ITO films. The thicknesses of $TiO_2$ and ITO films were kept constant at 5 and 100 nm, respectively. As-deposited ITO single layer films show an optical transmittance of 75.9%, while $ITO/TiO_2$ bi-layered films show a lower transmittance of 76.1%. However, as-deposited $ITO/TiO_2$ films show a lower resistivity ($9.87{\times}10^{-4}{\Omega}cm$) than that of ITO single layer films. In addition, the work function of the ITO film is affected by the $TiO_2$ buffer layer, with the $ITO/TiO_2$ films having a higher work-function (5.0 eV) than that of the ITO single layer films. The experimental results indicate that a 5-nm-thick $TiO_2$ buffer layer on the $ITO/TiO_2$ films results in better performance than conventional ITO single layer films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.571-574
• /
• 2000

In this study, Tin oxide thin film for secondary battery was deposited on Pt/Ti/Si(100). It was fabricated by r.f. reactive sputtering with Tin metal target. At constant power (130W), pressure (Base 5$\times$10$^{-6}$ Torr, working 5$\times$10$^{-3}$ Torr) and at room temperature, it was fabricated by Ar/O2 gas ratio. After deposition, we got AFM & SEM to investigated surface of thin films and had XRD to find crystalline of thin films. Charge/discharge characteristics were carried out in 1M LiPF$_{6}$ , EC:DMC = 1:1 liquid electrolyte using lithium metal at room temperature.

• 전기학회논문지
• /
• 제60권3호
• /
• pp.584-587
• /
• 2011

In this work, the $TiO_2$ and $SnO_2$ thin films as blocking layers were coated directly onto the metal-mesh electrode surface to prevent unnecessary inflow of back-transfer electrons from the electrolyte ($I^-/I_3^-$) to the metal-mesh electrode. The DSCs were fabricated with working electrode of SUS mesh coated with blocking $TiO_2$ and $SnO_2$ layers, dye-attached mesoporous $TiO_2$ film, gel electrolyte and counter electrode of Pt-deposited F:$SnO_2$. From the experimental result, it was ascertained that the efficiency of metal electrode coated with $TiO_2$ by Dip-coating was superior to that of metal electrode coated with $SnO_2$ by Dip-coating and screen printing with the results of experiments. The photo-current conversion efficiency of the cell obtained from optimum fabrication condition was 3% ($V_{oc}$=0.61V, $J_{sc}$=11.64 mA/$cm^2$, ff=0.64) under AM1.5, 100 mW/$cm^2$ illumination.

• 한국전기전자재료학회논문지
• /
• 제23권4호
• /
• pp.311-316
• /
• 2010

$Zr_{0.7}Sn_{0.3}TiO_4$ (ZST) thin films were fabricated by metal-organic decomposition, and their dielectric properties were investigated in order to evaluate their potential use in passive capacitors for rf and analog/mixed signal integrated circuits. The ZST thin film annealed at the temperature of $800^{\circ}C$ showed a dielectric constant of 27.3 and a dielectric loss of 0.011. The capacitor using the ZST film had quadratic and linear voltage coefficient of capacitance (VCC) of -65 ppm/$V^2$ and -35 ppm/V at 100 kHz, respectively. It also exhibited a good temperature coefficient of capacitance (TCC) value of -32 ppm/$^{\circ}C$ at 100 kHz.

• 한국전기전자재료학회논문지
• /
• 제27권1호
• /
• pp.18-21
• /
• 2014

Because the Pb-based piezoelectric materials showed problems such as an environmental pollution. lead-free $O_3$ materials were studied in the present study. The $O_3$ thin films were deposited at $640^{\circ}C$ on $Pt/Ti/SiO_2$ substrate by pulsed laser deposition (PLD) and were annealed for 5 min at $750^{\circ}C$ using rapid thermal annealing (RTA) in nitrogen atmosphere. Samples annealed at $750^{\circ}C$ showed a smooth morphology and an improvement of the dielectric and leakage properties, as compared with as-grown samples. However, electrical properties of the $O_3$ thin films obtained in the present study should be improved for piezoelectric applications.

• 센서학회지
• /
• 제9권3호
• /
• pp.242-247
• /
• 2000

10 mole%의 과잉 PbO가 첨가된 타겟을 이용하여 $(La_{0.5}Sr_{0.5})CoO_3(LSCO)/Pt/Ti/SiO_2/Si$ 위에 RF 마그네트론 스퍼터링 방법을 이용하여 $Pb_{0.99}[(Zr_{0.6}Sn_{0.4})_{0.9}Ti_{0.1}]_{0.98}Nb_{0.02}O_3(PNZST)$ 박막을 증착시켰다. $500^{\circ}C$의 기판온도, 80W의 RF power에서 증착된 박막은 급속열처리(RTA)후에 페로브스카이트 상으로 결정화되었다. $650^{\circ}C$, 공기중에서 10초 동안 열처리된 박막이 가장 우수한 결정성과 전기적 특성을 나타내었다. 이러한 박막으로 제작된 PNZST 커패시터는 약 $20\;{\mu}C/cm^2$ 정도의 잔류분극과 약 50 kV/cm 정도의 항전계를 나타내었다. 또한, $2.2{\times}10^9$의 스위칭 후에도 잔류분극의 감소는 10% 미만이었다.

• 대한전자공학회논문지SD
• /
• 제38권7호
• /
• pp.473-478
• /
• 2001

강유전 물질인 Pb/sub 0.99/［(Zr/sub 0/6Sn/sub 0.4/)/0.9/Ti/sub 0.1/］0.98/Nb/sub 0.02/O₃(PNZST) 박막을 10 mole%의 과잉 PbO가 첨가된 타겟을 이용하여 La/sub 0.5/Sr/sub 0.5/CoO₃(LSCO)/Pt/Ti/SiO₂/Si 기판상에 RF 마그네트론 스퍼터링 방법으로 증착하였다. 증착된 박막에 대하여 온도와 시간을 다양하게 변화시키면서 급속 열처리(rapid thermal annealing) 한 후, 그 결정성과 전기적 특성을 조사하였다. 80 W의 RF 전력, 500 ℃의 기판온도에서 증착한 후, 급속 열처리된 박막이 페로브스카이트상으로 결정화되었으며, 650 ℃, 공기중에서 10초동안 급속 열처리된 박막이 가장 우수한 결정성을 나타내었다. 이러한 박막으로 제작된 PNZST 커패시터는 약 20 μC/㎠정도의 잔류 분극과 약 50 kV/cm 정도의 항전계를 나타내었으며, 2.2×10/sup 9/의 스위칭 후에도 잔류분극의 감소는 10 %미만이었다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제44회 동계 정기학술대회 초록집
• /
• pp.543-543
• /
• 2013

Thin-film transistors (TFTs) based on oxide semiconductors have been regarded as promising alternatives for conventional amorphous and polycrystalline silicon TFTs. Oxide TFTs have several advantages, such as low temperature processing, transparency and high field-effect mobility. Lots of oxide semiconductors for example ZnO, SnO2, In2O3, InZnO, ZnSnO, and InGaZnO etc. have been researched. Particularly, zinc-tin oxide (ZTO) is suitable for channel layer of oxide TFTs having a high mobility that Sn in ZTO can improve the carrier transport by overlapping orbital. However, some issues related to the ZTO TFT electrical performance still remain to be resolved, such as obtaining good electrical contact between source/drain (S/D) electrodes and active channel layer. In this study, the bottom-gate type ZTO TFTs with staggered structure were prepared. Thin films of ZTO (40 nm thick) were deposited by DC magnetron sputtering and performed at room temperature in an Ar atmosphere with an oxygen partial pressure of 10%. After annealing the thin films of ZTO at $400^{\circ}C$ or an hour, Cu, Mo, ITO and Ti electrodes were used for the S/D electrodes. Cu, Mo, ITO and Ti (200 nm thick) were also deposited by DC magnetron sputtering at room temperature. The channel layer and S/D electrodes were defined using a lift-off process which resulted in a fixed width W of 100 ${\mu}m$ and channel length L varied from 10 to 50 ${\mu}m$. The TFT source/drain series resistance, the intrinsic mobility (${\mu}i$), and intrinsic threshold voltage (Vi) were extracted by transmission line method (TLM) using a series of TFTs with different channel lengths. And the performances of ZTO TFTs were measured by using HP 4145B semiconductor analyzer. The results showed that the Cu S/D electrodes had a high intrinsic field effect mobility and a low effective contact resistance compared to other electrodes such as Mo, ITO and Ti.

• 한국재료학회지
• /
• 제33권6호
• /
• pp.229-235
• /
• 2023

An all-perovskite oxide heterostructure composed of SrSnO₃/Nb-doped SrTiO₃ was fabricated using the pulsed laser deposition method. In-plane and out-of-plane structural characterization of the fabricated films were analyzed by x-ray diffraction with θ-2θ scans and φ scans. X-ray photoelectron spectroscopy measurement was performed to check the film's composition. The electrical transport characteristic of the heterostructure was determined by applying a pulsed dc bias across the interface. Unusual transport properties of the interface between the SrSnO₃ and Nb-doped SrTiO₃ were investigated at temperatures from 100 to 300 K. A diodelike rectifying behavior was observed in the temperature-dependent current-voltage (IV) measurements. The forward current showed the typical IV characteristics of p-n junctions or Schottky diodes, and were perfectly fitted using the thermionic emission model. Two regions with different transport mechanism were detected, and the boundary curve was expressed by ln I = -1.28V - 13. Under reverse bias, however, the temperature- dependent IV curves revealed an unusual increase in the reverse-bias current with decreasing temperature, indicating tunneling effects at the interface. The Poole-Frenkel emission was used to explain this electrical transport mechanism under the reverse voltages.