• 한국재료학회지
• /
• 제12권1호
• /
• pp.48-53
• /
• 2002

$Al_2O_3-SiC$ and $Al_2O_3-SiC$-TiC composite powders were prepared by SHS process using $SiO_2,\;TiO_2$, Al and C as raw materials. Aluminum powder was used as reducing agent of $SiO_2,\;TiO_2$ and activated charcoal was used as carbon source. In the preparations of $Al_2O_3-SiC$, the effect of the molar ratio in raw materials, compaction pressure, preheating temperature and atmosphere were investigated. The most important variable affecting the synthesis of $Al_2O_3-SiC$ was the molar ratio of carbon. Unreactants remained in the product among all conditions without compaction. The optimum condition in this reaction was $SiO_2$: Al: C=3: 5: 5.5, 80MPa compaction pressure under Preheating of $400^{\circ}C$ with Ar atmosphere. However there remains cabon in the optimum condition. The effect of $TiO_2$ as additive was investigated in the preparations of $Al_2O_3-SiC$. As a result of $TiO_2$ addition, $Al_2O_3-SiC$-TiC composite powder was prepared. The $Al_2O_3$ powder showed an angular type with 8 to $15{\mu}m$, and the particle size of SiC powder were 5~$10{\mu}m$ and TiC powder were 2 to $5{\mu}m$.

• 한국세라믹학회지
• /
• 제33권10호
• /
• pp.1138-1146
• /
• 1996

Al2TiO5 powder was prepared by the sol-gel processing from th metal alkoxides ; aluminium sec-butoxide (Al(OC4H9)3 and tetraethyl orthotitanate (Ti(OC2H5)4) The particles of Al2TiO5 produced from alkoxides were measured to be below $1.5mutextrm{m}$ and mre than 90% weere below 1 ${\mu}{\textrm}{m}$ however those from commercial alumina and titania were over 0.5-7${\mu}{\textrm}{m}$ and only 60% were below 1${\mu}{\textrm}{m}$ and 90% were below 2.5${\mu}{\textrm}{m}$ Therefore Al2TiO5 powder produced from alkoxides had the narrower distributionin size than that produced from the commercial alumina and titania powders. The addition of mullite or Al2O3 powder to the prepared aluminum titanate inhibited the grain growth and this resulted in decreased and increase in density.

• 열처리공학회지
• /
• 제20권5호
• /
• pp.231-236
• /
• 2007

High velocity oxy-fuel (HVOF) spraying was used to coat Ti(Al,O)/$Al_2O_3$ powder onto the SS41 steel plate. Macrostructure of the coated specimen has been investigated by scanning electron micrograph (SEM). High temperature oxidation behavior of the coated specimen and SS41 steel have been studied. From the results of SEM observation, Ti(Al,O)/$Al_2O_3$ powder was coated well onto the substrate SS41 steel. Porosity onto the coated layer was only 0.38%. The oxidation results showed that Ti(Al,O)/$Al_2O_3$ powder coated SS41 steel have improved little oxidation resistance at $900^{\circ}C$ in air, but improved remarkably oxidation resistance at $800^{\circ}C $ in air compare to the substrate SS41 steel.

• 한국분말재료학회지
• /
• 제28권1호
• /
• pp.31-37
• /
• 2021

This study explores reducing the oxygen content of a commercial Ti-48Al-2Cr-2Nb powder to less than 400 ppm by deoxidation in the solid state (DOSS) using Ca vapor, and investigates the effect of Ca vapor on the surface chemical state. As the deoxidation temperature increases, the oxygen concentration of the Ti-48Al-2Cr-2Nb powder decreases, achieving a low value of 745 ppm at 1100℃. When the deoxidation time is increased to 2 h, the oxygen concentration decreases to 320ppm at 1100℃, and the oxygen reduction rate is approximately 78% compared to that of the raw material. The deoxidized Ti-48Al-2Cr-2nb powder maintains a spherical shape, but the surface shape changes slightly owing to the reaction of Ca and Al. The oxidation state of Ti and Al on the surface of the Ti-48Al-2Cr-2Nb powder corresponds to a mixture of TiO2 and Al2O3. As a result, the peaks of metallic Ti and Ti suboxide intensify as TiO2 and Al2O3 in the surface oxide layer are reduced by Ca vapor deposition.

• 한국분말재료학회지
• /
• 제11권3호
• /
• pp.247-252
• /
• 2004

Recently, it has been found that mechanical alloying (MA) facilitates the nanocomposites formation of metal-metal oxide systems through solid-state reduction during ball milling. In this work, we studied the MA effect of Fe$_{3}$O$_{4}$-M (M = Al, Ti) systems, where pure metals are used as reducing agents. It is found that composite powders in which $Al_{2}$O$_{3}$ and TiO$_{2}$ are dispersed in $\alpha$-Fe matrix with nano-sized grains are obtained by mechanical alloying of Fe$_{3}$O$_{4}$ with Al and Ti for 25 and 75 hours, respectively. It is suggested that the large negative heat associated with the chemical reduction of magnetite by aluminum is responsible for the shorter MA time for composite powder formation in Fe$_{3}$O$_{4}$-Al system. X-ray diffraction results show that the reduction of magnetite by Al and Ti if a relatively simple reaction, involving one intermediate phase of FeAl$_{2}$O$_{4}$ or Fe$_{3}$Ti$_{3}$O$_{10}$. The average grain size of $\alpha$-Fe in Fe-TiO$_{2}$ composite powders is in the range of 30 nm. From magnetic measurement, we can also obtain indirect information about the details of the solid-state reduction process during MA.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.49-50
• /
• 2006

[ $Ti(Al,\;O)-Al_2O_3$ ] composite powders were produced by high energy mechanical milling of a mixture of Al and $TiO_2$ powders followed by a combustion reaction. The powders were subsequently thermally sprayed on H13 steel substrates. Microstructural examination was conducted on the composite powders and thermally sprayed coatings, using X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The performance of the coatings was evaluated in terms of micro-hardness and thermal fatigue. The thermally sprayed coatings performed very well in the preliminary thermal fatigue tests and showed no wetting tendency to molten aluminum.

• 청정기술
• /
• 제24권4호
• /
• pp.280-286
• /
• 2018

본 연구에서는 금속산화물 2종, $TiO_2$ 분말과 $Al_2O_3$ 분말을 이용하여 건식 조건에서의 기상 VOCs 흡착 성능을 평가하였으며, BET분석과 암모니아 in-situ FT-IR 분석을 통해 비표면적, 표면 산점을 분석하고 성능과의 상관성을 평가하였다. 그 결과 $TiO_2$ 분말, $Al_2O_3$ 분말은 각각 $317.6m^2\;g^{-1}$, $64m^2\;g^{-1}$의 비표면적을 갖으며, $TiO_2$ 분말의 경우 표면에 다수의 산점이 관찰되었다. 두 금속 산화물 분말을 이용하여 기상 VOCs 흡착 성능을 평가한 결과, 비표면적이 크고 다수의 산점을 보유한 $TiO_2$ 분말이 비교적 우수한 흡착 성능을 나타내었다. 특히 비표면적이 흡착성능에 직접적인 영향을 미치는 것으로 판단되며, 산점에 의한 영향에 대해서는 추가적인 연구가 요구된다. 우수한 흡착 성능을 나타낸 $TiO_2$를 기반으로 honeycomb, hollow fiber, disc의 성형체로 제조 한 결과, 분말보다 흡착 성능은 낮았으나 적용성 측면에서 유리하며 제조공정의 특성상 우수한 열적 내구성을 갖는 polymeric disc 흡착제의 경우, 수회의 고온 탈착공정 후에도 흡착 성능을 안정적으로 유지함을 확인하였다.

• The Korean Journal of Ceramics
• /
• 제1권3호
• /
• pp.137-142
• /
• 1995

Monodispersed $Al_2O_3-TiO_2$ Powder was prepared by metal-alkoxide hydrolsis. A homogeneous nucleation/growth occurred in the solutions containing ethanol, butanol and acetonitrile, and resulted in spherical, submicrometer-sized powder. The titania and the alumina crystals were formed at $800^{\circ}C$ and $1000^{\circ}C$, respectively. These crystala were subsequently reacted each other beyond $1320^{\circ}C$ and formed $Al_2TiO_5$. The relative densities of sintered bodies prepared with as-received powder were examined at the temperature range of 1300-$1500^{\circ}C$ and they were about 79% at $1300^{\circ}C$. The formation of aluminum titanata decreased the relative density at the temperature range of 1300-$1450^{\circ}C$, and at above $1450^{\circ}C$, the relative density started to increase again. It was observed that $\alpha-Al_2O_3$-doped aluminum titanate was more stable than pure aluminum titante at $1200^{\circ}C$.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2001년도 추계 학술발표강연 및 논문개요집
• /
• pp.133-133
• /
• 2001

• 한국세라믹학회지
• /
• 제33권10호
• /
• pp.1147-1155
• /
• 1996