A Bi$_4$Ti$_3$O$_{12}$ (BIT) thin film is prepared by sol-gel method using acetate precursors and evaluated whether it could be applied to NVFRAM. The drying and the annealing temperature are 40$0^{\circ}C$ and $650^{\circ}C$, respectively and they are determined from the DT-TG analysis. The BIT thin film deposited on Pt/Ta/SiO$_2$/Si substrate shows orthorhombic perovskite phase. The grain size and the surface roughness are about 100 nm and 70.2$\AA$, respectively. The dielectric constant and the loss tangent at 10 KHz are 176 and 0.038, respectively, and the leakage current density at 100㎸/cm is 4.71$mutextrm{A}$/$\textrm{cm}^2$. In the results of hysteresis loops measured at $\pm$250㎸/cm, the remanent polarization (Pr) and the coercive field (Ec) are 5.92$mutextrm{A}$/$\textrm{cm}^2$ and 86.3㎸/cm, respectively. After applying 10$^{9}$ square pulses of $\pm$5V, the remanent polarization of the BIT thin film decreases as much as about 33% from 5.92 $\mu$C/$\textrm{cm}^2$ of initial state to 3.95 $\mu$C/$\textrm{cm}^2$.

• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.558-567
• /
• 2001

본 연구에서는 알콕사이드를 전구물질로 하는 졸겔공정을 이용하여 Bi 과잉 12 mol%의 조성인 B $i_4$ $Ti_3$ $O_{12}$ 박막과 B $i_4$ $Ti_{3-x}$T $a_{x}$ $O_{12}$(x=0.1, 0.2, 0.3) 박막을 제조하였다. XPS 분석에 따르면 Ta 치환 x=0.2에서 Bi 4f의 photoemission 곡선이 낮은 결합에너지로 이동하였고 피크 강도가 감소하는 현상이 관측되었다. 이는 x=0.1과 0.2 사이에서 Bi-O 결합이 길어져 인장상태 하에 있었음을 나타내었다. B $i_4$ $Ti_3$ $O_{12}$(BIT) 박막의 유전상수와 유전손실은 100 kHz에서 340, 0.05이었고, B $i_4$ $Ti_{3-x}$T $a_{x}$ $O_{12}$ 박막에서 이들 값은 x=0.1에서 가장 높았으며, 각각 480, 0.13이었다. B $i_4$ $Ti_3$ $O_{12}$ 박막의 잔류분극과 항전계는 1.24$\mu$C/$ extrm{cm}^2$, 31.4 kV/cm 이었으나, Ta 치환 x=0.2에서 이들 값은 각각 19.7$\mu$C/$\textrm{cm}^2$, 49.5 kV/cm 에 이르렀다. 또한, B $i_4$ $Ti_3$ $O_{12}$ 박막의 누설전류 밀도는 ~$10^{-6}$ A/$\textrm{cm}^2$ 정도이었으며, Ta 치환은 누설전류를 감소시켜 Ta 치환 x=0.2 이상에서 BIT 박막에 비해 한 차수 정도 낮아졌다. Ta 치환에 따른 B $i_4$ $Ti_3$ $O_{12}$ 전기 물성에서 변화는 Bi-O 결합에서 관측된 인장상태로의 전이와 연관성이 있었으며, 덧붙여 치환에서 생성된 전자에 의한 정공보상이 이에 영향을 끼쳤다. 정공보상이 이에 영향을 끼쳤다.끼쳤다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1994.02a
• /
• pp.41-42
• /
• 1994

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.05a
• /
• pp.88-88
• /
• 1994

• The Korean Journal of Ceramics
• /
• v.3 no.4
• /
• pp.263-268
• /
• 1997

RuO$_3$ thin films were deposited on Si(100) substrate at low temperatures by hot-wall metalorganic chemical vapor deposition. Bis(cyclopentadienyl) ruthenium, Ru$(C_5H_5)_2$, was used as the precursor RuO$_2$single phase was obtained at a low deposition temperature of 25$0^{\circ}C$ and the crystallinity of RuO$_2$thin films improved with increasing deposition temperature. RuO$_2$thin films grow perpendicularly to the substrate and show the columnar structure. The grain size of RuO$_2$films drastically increases with increasing the deposition temperature. The resistivity of the 180 nm-thick RuO$_2$thin films deposited at 27$0^{\circ}C$ was 136 $\mu$$\Omega$-cm and increased with decreasing film thickness. SrBi$_2Ta_2O_4$ thin films deposited by rf magnetron sputtering on the RuO$_2$bottom electrodes showed a fatigue-free characteristics up to ~10$^10$ cycles under 5 V bipolar square pulses and the remanent polarization, 2 P$_r$ and the coercive field, 2 E, were 5.2$\mu$C/$\textrm{cm}^2$ and 76.0 kV/cm, respectively, for an applied voltage of 5 V The leakage current density was about 7.0$\times$10$^{-6}$ A/$\textrm{cm}^2$ at 150 kV/cm.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.202-208
• /
• 1997

Bi-layered SrBi2Ta2O9(SBT) films were deposited on Pt/Ti/SiO2/Si sibstrates by rf magnetron sputt-ering at room temperature and then were annealed at 75$0^{\circ}C$, 80$0^{\circ}C$ and 85$0^{\circ}C$ for 1 hour in oxygen at-mosphere. The film composition of SrBi2Ta2O9 was obtained after depositing at room temperature and annealing at 80$0^{\circ}C$. Excess 20mole% Bi2O3 and 30 mole% SrCO3 were added to the target to compensate for the lack of Bi and Sr in SBT film. 200 nm thick SBT film exhibited and dense microstructure, adielectric constant of 210, and a dissipation factor of 0.05 at 1 MHz frequency. The films exhibited Curie temperature of 32$0^{\circ}C$ and a dielectric constant of 314 at that temperature under 100 kHz frequency. The remanent polarization(2Pr) and the coercive field(2Ec) of the SBT films were 9.1 $\mu$C/$\textrm{cm}^2$ and 85 kV/cm at an applied voltage of 3V, resspectively and the SBT film showed a fatigue-free characteristics up to 1010 cy-cles under 5V bipolar pulse. The leakage current density of the SBT film was about 7$\times$10-7A/$\textrm{cm}^2$ at 150 kV/cm. Fatigue-free SBT films prepared by rf magnetron sputtering can be suitable for application to non-volatile memory device.

• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.360-366
• /
• 2000

$Sr_xBi_{2.4}Ta_2O_9$ (SBT) thin films of 150 nm thickness were prepared using LSMCD (Liquid Source Misted Chemical Deposition) process with variation of the Sr/Ta mole ratio of 0.35~0.65, and their crystalline phase, microstructure, ferroelectric properties and leakage current characteristics were investigated. Ferroelectric characteristics of the LSMCD-derived SBT films were optimized at the Sr/Ta moleratio of 0.425. The remanent polarization (2Pr) and coercive field (Ec) of the SBT film with the Sr/Ta mole ratio of 0.425 were measured as 15.01 $\mu$C/$ \textrm{cm}^2$ and 41 kV/cm at an applied voltage of $\pm$5 V respectively. LSMCD-derived SBT films with the Sr/Ta mole ratio of 0.35~0.5 exhibited leakage current densities lower than $10^{-5} A/\textrm{cm}^2$ at an applied field of 100 kV/cm, and excellent fatigue-free characteristics of the remanent polarization decrement less than 1% after $10^{10}$ switching cycles at$\pm$5 V.

• Korean Journal of Materials Research
• /
• v.10 no.8
• /
• pp.575-580
• /
• 2000

Diamond thin films were deposited on $Si_3N_4$, SiC, TiC and $Al_2O_3$, substrates by the CVD method using Ta(TaC)Filament, and the appearance of the diamond films and their adhesion properties were examined by SEM, optical microscopy, indentation test and compression topple test. Diamond films were deposited at lower $CH_4$ concentration than 5%$CH_4$ for all kinds of the substrate material, but graphitic(amorphous)carbon was observed at 10%$CH_4$. The diamond film of about $12\mu\textrm{m}$ thickness on WC substrate partly peeled off, but the film on $Si_3N_4$ substrate held good adhesion. The indentation test showed that roughly ground surface was very effective for adhesion of diamond films to substrate. The topple test revealed that film thickness was an important factor governing the adhesion of the diamond film.

• Korean Journal of Optics and Photonics
• /
• v.11 no.3
• /
• pp.147-151
• /
• 2000

We deposited the ion assisted ${Ta_2}{O_5}$ films and conventional thermal evaporated ${Ta_2}{O_5}$ films by using electron beam gun, and measured the optical properties and mechanical properties of the fabricated films according to the evaporation conditions. In the case of the TazOs films by oxygen ion assisted deposition with the anode voltage of 120 V, and current density of $50~500\muA/cm^2$, the refractive index exhibited 2.15 which was higher than the conventionally deposited film index 1.94 and the tensile stress exhibited $5.0\times10^8 dyne/cm^2$ which was lower than $7.0\times10^8 dyne/cm^2$. This properties coincided with the optical and mechanical properties of the films deposited at the elevated substrate temperature of $230^{\circ}C$. In the case of the argon ion assisted films the tensile stress was decreased but the absorption existed at the short wavelength in the visible spectral region. And all the fabricated films were found to be amorphous by the X-ray diffraction analysis. lysis.