• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.346-349
• /
• 2002

Ferroelectric $Bi_{4-x}Nd_{x}Ti_{3}O_{12}(BNdT)$ thin films with the composition(x=0.75) were prepared on $Pt/Ti/SiO_{2}/Si(100)$ substrate by metal-organic deposition. The films were annealed by various temperatures from 550 to $650^{\circ}C$ and then the electrical and structural characteristics of BNdT films were investigated for the application of FRAM. Electrical properties such as dielectirc constant, 2Pr and capacitance were quite dependent on the thermal heat treatment. The measured 2Pr value on the BNdT capacitor annealed at $650^{\circ}C$ was $56{\mu}C/cm^{2}$ at an applied voltage of 5V. In fatigue characteristics value remained costant up to $8{\times}10^{10}$ read/write switching cycles at a frequency of 1Mhz regardless of annealing temperatures.

• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.10 no.6
• /
• pp.666-673
• /
• 1998

Solubilities (LiBr+$CaC1_2$) in water were measured at temperatures form 267.51 to 306.17K for $CaC1_2$ (LiBr+$CaC1_2$)=0.24 by mole. Experimental data were correlated with polynomial equations. Average absolute deviations between the measured and calculated values were 0.31% at concentration smaller than 60wt% and 0.41% at concentration larger than 60wt%, respectively. Vapor pressures were measured at temperatures from 296.75 to 436.75K and concentrations from 40 to 70wt%. Vapor pressure data were fitted to a Antoine-type equation and average absolute deviation was 2.98%. The P-T-X chart and H-T-X chart of $H_2O$/(LiBr+$CaC1_2$) system were constructed by using the correlation equations of solubility, vaper pressure, and heat capacity. The P-T-X chart indicates that $H_2O$/(LiBr+$CaC1_2$) system has potential as a possible working fluid for air-cooled absorption chillers.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.99-100
• /
• 2007

ZnO films on $Al_2O_3$ substrates were grown using a pulsed laser deposition method. Through photoluminescence (PL) and X-ray diffraction (XRD) measurements, the optimum growth conditions for the ZnO growth were established. The results of the XRD measurements indicate that ZnO films were strongly oriented to the c-axis of the hexagonal structure and epitaxially crystallized under constraints created by the substrate. The full width half maximum for a theta curve of the (0002) peak was $0.201^{\circ}$. Also, from the PL measurements, the grown ZnO films were observed to give free exciton behaviour, which indicates a high quality of the epilayer. The Hall mobility and carrier density of the ZnO films at 293 K were estimated to be $299\;cm^2/V\;s$ and $8.27\;{\times}\;10^{16}\;cm^{-3}$, respectively. The absorption spectra revealed that the temperature dependance of the optical band gap on the ZnO films was $E_g(T)\;=\;3.439\;eV\;-\;(5.30\;{\times}\;10^{-4}\;ev/K)T^2(367\;+\;T)$.

• Journal of Aquaculture
• /
• v.6 no.3
• /
• pp.147-157
• /
• 1993

The harpacticoid copepod, Tigriopus japonicus is one of the most important zooplankton as a live food for the production of marine fish fry. Thus, the salinity tolerance and the optimum culture environment of this copepod in terms of salinity, temperature and light were examined. The food values of 6 kinds of phytoplankters and 2 kinds of yeast were also investigated for mass culture of this copepod. The results are as follows: After 5 day culture in the experiment of salinity tolerance, the survival rates of the gravid female at $0\%\;and\;90%o\;were\;40\%\;and\;70\%$, respectively. However, at salinity ranging from $2\%o\;to\;80\%o$, high survival rates above $85\%$ were observed. It means T. japonicus is very euryhalinous species. Temperature was more important factor than salinity for the fecundity of T. japonicus. The optimum culture conditions of this species were $24^{\circ}C,\;24\%o$, and 3,000 lux with 24 L: 0D. Under these culture conditions, the average fecundity from a gravid female per spawning was 38 nauplii, and the interval time between spawnings were 2.05 days. Phaeodactylum tircornutum seemed to be the most suitable phytoplankton as a live food for T. japonicus, and the large chlorophyta, Tetraselmis suecica showed the lowest food value among 6 phytoplankters and 2 yeasts. The food value of w-yeast was better than that of baker's yeast, and it is similar to that of phytoplankton such as Amphora sp., Chlorella ellipsoidea and Nannochloris oculata. So, the w-yeast seems to be appropriate food source for mass culture of T. japonicus.

• 한국초전도학회:학술대회논문집
• /
• v.14
• /
• pp.7-7
• /
• 2004

• Advances in nano research
• /
• v.15 no.1
• /
• pp.1-13
• /
• 2023

Ti₃C₂T_x MXene, a 2D material, is known to exhibit unique characteristics that are strongly dependent on surface termination groups. Here, we developed a novel annealing approach with Ca as a reducing agent to simultaneously remove F and O groups from the surface of multilayered MXene powder. Unlike H₂ annealing that removes F effectively but has difficulty in removing O, annealing with Ca effectively removed both O and F. X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray spectroscopy revealed that the proposed approach effectively removed F and O from the MXene powder. The results of O/N analyses showed that the O concentration decreased by 57.5% (from 2.66 to 1.13 wt%). In addition, XPS fitting showed that the volume fraction of metal oxides (TiO₂ and Al₂O₃) decreased, while surface termination groups (-O and -OH) were enhanced, which could increase the hydrophilic and adsorption properties of the MXene. These findings suggest that when F and O are removed from the MXene powder, the interlayer spacing of its lattice structure increases. The proposed treatment also resulted in an increase in the specific surface area (from 5.17 to 10.98 m²/g), with an increase in oxidation resistance temperature in air from ~436 to ~667 ℃. The benefits of this novel technology were verified by demonstrating the significantly improved cyclic charge-discharge characteristics of a lithium-ion battery with a Ca-treated MXene electrode.

• The Korean Journal of Ceramics
• /
• v.4 no.3
• /
• pp.204-206
• /
• 1998

The Gibbs free energy of formation of $BaThO_3$ from elemental oxides has been measured at temperatures between 853 and 903 K using a $CaF_2$ solid electrolyte galvanic cell. The galvanic cell consisted of Pt, $O_2, CaO+CaF_2 \parallel CaF_2 \parallelBaThO_3+ThO_2+BaF_2, O_2$, Pt EMF gave the standard Gibbs free energy for the reaction $CaF_2+BaThO_3=CaO+BaF_2+ThO_3$ as $\DeltaG^o$,/TEX>=124111.031-117.597 T(J/mol).

• Korean Chemical Engineering Research
• /
• v.55 no.2
• /
• pp.156-162
• /
• 2017

CuO(x)/0.3Al-0.7Ce catalysts with different CuO loadings (x = 2~20 wt%) were prepared by impregnation method and investigated the effects of CuO loadings on the low temperature CO oxidation. Of the used catalysts, the CuO(10)/0.3Al-0.7Ce catalyst showed the highest catalytic performance in the absence or presence of water vapor. In the presence of water vapor, the catalytic performance was drastically decreased, with a temperature of 50% CO conversion ($T_{50%}$) shifted to higher temperature by $50^{\circ}C$ compared to the those in dry conditions because of the competitive adsorption of water vapor on the active sites. The copper metal surface area calculated from $N_2O$-titration analysis and the oxygen capacity from CO-pulse experiments were increased with the CuO loadings and showed a maximum at 10 wt%CuO/0.3Al-0.7Ce catalyst. These trends are in good agreement with the tendency of $T_{50%}$ of the catalysts. From these characteristic aspects, it could be deduced that the catalytic performance was closely related to the oxygen capacity and the copper metallic surface area.

• Korean Journal of Materials Research
• /
• v.23 no.9
• /
• pp.531-536
• /
• 2013

This paper investigates the effect of prolonged high temperature exposure on concentric laminated $Al_2O_3-ZrO_2$ composites. An ultrafine scale microstructure with a cellular 7 layer concentric lamination with unidirectional alignment was fabricated by a multi-pass extrusion method. Each laminate in the microstructure was $2-3{\mu}m$ thick. An alternate lamina was composed of 75%$Al_2O_3$-(25%m-$ZrO_2$) and t-$ZrO_2$ ceramics. The composite was sintered at $1500^{\circ}C$ and subjected to $1450^{\circ}C$ temperature for 24 hours to 72 hours. We investigated the effect of long time high temperature exposure on the generation of residual stress and grain growth and their effect on the overall stability of the composites. The residual stress development and its subsequent effect on the microstructure with the edge cracking behavior mechanism were investigated. The residual stress in the concentric laminated microstructure causes extensive micro cracks in the t-$ZrO_2$ layer, despite the very thin laminate thickness. The material properties like Vickers hardness and fracture toughness were measured and evaluated along with the microstructure of the composites with prolonged high temperature exposure.

• Proceedings of the PSK Conference
• /
• 2002.10a
• /
• pp.368.2-368.2
• /
• 2002

Fruits of Hovenia dulcis T. (Rhamnaceae) was called ′jiguja ′ in oriental medicine which has been used for diuresis, remove of hangover and leaves has been used for detoxified the alcohol. From the MeOH Extraction. five compounds were isolated by column chromatography and elucidated as quercetin quercetin-3-O-rhamnose. quercetin-3-O-gal(6"1") rha, quercetin-3-O-glc(6"${\rightarrow}$1")glc, and kaemferol through specroscopic methods. (omitted)