• Proceedings of the KIEE Conference
• /
• 2002.06a
• /
• pp.49-51
• /
• 2002

In this thesis, Josephson junction using high-Tc superconducting multi-layer thin film has been fabricated by on-axis RF magnetron sputtering method. And, the characterizations were performed by X-ray diffraction, SEM and the measuring system of critical current density. The physical properties of multi-layer superconducting thin films were also analyzed with the measured results. To fabricate the multi-layer superconducting thin films, the optimum partial pressure of Argon and Oxgen and the temperature of substrate were measured. Also, YBaCuO thin film was grown on MgO and $SrTiO_3$ substrates by rf-sputtering and LGO thin film of 30 A was epitaxially grown on the YBaCuO thin film as a josephson junction with the same condition. The schottky barrier at the contact surface between YBaCuO/LGO and YBaCuO/Au and the energy gap of 0.5 ${\sim}$ 0.6 mV in Nb were observed from the dI/dV-V of YBaCuO/LGO/Au/Nb and YBaCuO/Au/Nb.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.179-179
• /
• 2009

This is for the electrical characterization by IDC pattern using BST$(Ba_{0.5}Sr_{0.5}TiO_3)$ thin film. BST materials had been chosen for high frequency applications due to it's high permitivity and tunability. The BST thin films have been deposited on $Al_2O_3$ Substrates by Nd-YAG pulsed laser deposition with a 355nm wavelength at $700\;^{\circ}C$. The post deposition annealing at $750^{\circ}C$ in flowing $O_2$ atmosphere for 1 hours. The capacitance of IDC patterns have been measured from 1 to 10 GHz as a function of electric field ($\pm40$ KV/cm) at room temperature using inter-digital Au electrodes deposited on top of BST. The IDC patterns have three type of fingers number. For the 10 pairs finger was the best capacitance onto $Al_2O_3$ substrate. The capacitance was 0.9pF. Also Dielectric constant was been 351 at 100 mTorr and annealing temperature $750^{\circ}C$ for 1 hour. The loss tangent was been 0.00531.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.34-38
• /
• 2000

Recently, the ceramics of high permittivity are applied to DRAM and FRAM. In this study, (Ba, Sr)$TiO_3$ (BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/$SiO_2$/Si substrate at 4000 [rpm] for 10 seconds. Coated specimens were dried at $150[^{\circ}C]$ for 5 minutes. Coating process was repeated 3 times and then sintered at $750[^{\circ}C]$ for 30 minutes. Each specimen was analyzed structure and electrical characteristics by Fractal Process. Thickness of BST ceramics thin films are about $2000{\AA}$. Dielectric constant and loss of thin films was little decreased at 1[KHz] - 1[MHz]. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. The property of leakage current as the realation between the current and the voltage was that change of the leakage current was stable when the applied voltage was 0~3[V].

• KIEE International Transactions on Electrophysics and Applications
• /
• v.11C no.2
• /
• pp.18-22
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Sio$_2$/Si substrate at 4,000 [rpm] for 10 seconds. The structural characteristics of the surface were analyzed by fractal dimension. The thickness of BST ceramics thin films was about 260∼280 [nm]. The property of the leakage current was stable with 10-9∼10-11[A] when the applied voltage was 0∼3[V]. BST thin films ha low leakage current properties when fractal dimension was low and a coating area was high.

• Progress in Superconductivity
• /
• v.4 no.2
• /
• pp.109-113
• /
• 2003

We have developed a planar-type single layer second-order $high-T_{c}$ SQUID gradiometer, which can detect the $d^2$$B_{z/}$dxdy of the second-order field gradient. This SQUID gradiometer consists of four-way 'clover-leaf' pick-up loops and is coupled directly to a 4-junction dc SQUID in such a way that the coupling polarity of the two diagonal loops is opposite to that of the other two loops. The pickup loops are intrinsically balanced for both uniform field and the 1 st-order field gradient. The $YBa_2$$Cu_3$$O_{7}$ thin film was made by pulsed laser deposition method on $SrTiO_3$ single crystal substrate and patterned by photolithography with Ar ion milling technique. Response of this gradiometer was tested for both uniform field and the 2nd-order field gradient. Details of the design, fabrication, and results will be discussed.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.91-94
• /
• 1999

A new type of high-T$_c$ superconducting Josephson junctions has been prepared by Ar ion beam etching and electron beam lithography. YBa$_2Cu_3O_{7-x}$ (YBCO) films deposited on (001) SrTiO$_3$ single crystal substrate by pulsed laser deposition were patterned by Ar ion milling with photolithography. The narrow slit with a electroresist mask, about 1000 ${\AA}$ wide, was constructed over a 3 ${\sim}$ 5 ${\mu}$m bridge of a 1200-${\AA}$-thick YBCO film by electron beam lithography. The slit was then etched by the Ar ion beam to form a damaged 600-${\AA}$-thick YBCO. Thus prepared structure forms an S-N-S (YBCO - damaged YBCO - YBCO) type Josephson junctions. Those junctions exhibit RSI-like I-V characteristics at 77 K. The properties of the Josephson junctions such as I$_c$ R$_N$, and J$_c$ were characterized.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.111-115
• /
• 2003

200nm 정도의 두께를 가진 SBT 박막이 liquid delivery MOCVD 공정에 의해 (111) oriented Pt/Ti/$SiO_2$/Si 기판 위에 증착되었다 이 실험에서는 $Sr(TMHD)_2$tetraglyme, $Bi(ph)_3$ 그리고 $Ta(O^iPr)_4$(TMHD)를 출발 물질로 사용하였다. Sr 출발 물질의 열적 안정화를 위해서 adduct로 tetraglyme를 사용하여 실험하였고 유기 용매로는 n-butyl acetate를 사용하였다 Substrate temperature와 reactor pressure는 각각 $570^{\circ}C$와 5Torr로 유지시켰다. 또한 vaporizer의 용도는 $190-200^{\circ}C$, 그리고 delivery line 의 온도는 vaporizer 보다 높게 유지 $(220-230^{\circ}C)$하여 출발 용액을 분당 0.1ml로 50분간 주입하였다. 수송가스로 Ar, 산화제로 $O_2$ 가스를 사용하였다. 제조한 SBT 박막은 $750^{\circ}C$에서 열처리한 후 인가전압 3V와 5V에서 $2P_r$값이 각각 6.47, $8.98{\mu}C/cm^2$이었으며, $2E_c$값은 인가전압 3V와 5V에서 각각 2.05, 2.31V이었다 그리고 $800^{\circ}C$에서는$750^{\circ}C$에서 열처리한 SBT 박막보다 다소 우수한 이력특성을 나타내어 $2P_r$ 값은 인가전압 3V와 5V에서 각각 7.59, $10.18{\mu}C/cm^2$ 이었으며, $2E_c$값은 인가 전압 3V와 5V에서 각각 2.00, 2.21V 이었다.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.1
• /
• pp.10-13
• /
• 2005

$Sr_{0.6}Ba_{0.4}Nb_{2}O_{6}$, hereafter SBN60, thin films of 300 nm thickness were deposited using ion beam sputtering technique, in which sintered ceramic target of the same composition was utilized and the $Ar:O_{2}$ gas ratio was controlled during deposition onto $Pt(100)/TiO_{2}/SiO_{2}/Si$ substrate. Crystallization and orientation behavior as well as electrical properties of the films were examined after annealing treatment at $650{\sim}800{\cric}C$. It was found that the film orientation was dependent upon $Ar:O_{2}$ratio, in which strong (00l) orientation was developed when the gas ratio was about 1:4 at $4.3{\times}10^{-4}$ torr. Typical remanent polarization (2Pr), the coercive field (Ec) and the dielectric constant of Pt/SBN60/Pt thin film capacitor were approximately $10{\mu}C/cm^{2}$, 60 kV/cm, and 615, respectively.

• Korean Journal of Materials Research
• /
• v.9 no.1
• /
• pp.86-91
• /
• 1999

We have fabricated high-$\textrm{T}_c$ superconducting $\textrm{YBa}_{2}\textrm{Cu}_{3}\textrm{O}_{7-x}$(YBCO) grain boundary junctions at a step-edge on (001) $\textrm{SrTiO}_3$(STO) substrates. A diamond-like carbon (DLC) film grown by plasma enhanced chemical vapor deposition were used as an ion milling mask to make steps on the STO (100) single crystal and was removed by an oxygen reactive ion etch process. The c-axis oriented YBCO and TO thin films were deposited epitaxially on the STO substrate with a step-edge by pulsed laser deposition. The grain boundary junctions were formed at the top and the bottom of the step. The junctions worked at temperatures above 77 K, and had I\ulcornerR\ulcorner products of 7.5mV at 16K and 0.3 mV at 77K, respectively. The I-V characteristics of these junctions showed the shape of the two noisy resistively shunted junction model.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.28-28
• /
• 2010

This study realized low-temperature crystallization process of the $Ba_{0.6}Sr_{0.4}TiO_3$ (BST) thin films without thermal damage of substrate using excimer laser annealing (ELA) and structural and electrical characteristics were investigated. The amorphous BST thin films were prepared on Pt/Ti/$SiO_2$/Si substrate by sol-gel method at $250^{\circ}C$. The ELA was carried out using KrF excimer laser which provided excitation wavelength of 248 nm. The beam homogenizing system was used in order to homogenize beam shape of Gaussian fit. The XRD and SEM were used to analyze structural characteristics and the microwave capacitance, dielectric loss and tunability of the BST films were measured by a symmetrical stripline resonator method with shorted end. Consequently, the crystallinity of BST thin films were improved after ELA process and RF tunable capacitor was demonstrated at low temperature below $300^{\circ}C$.