• The Korean Journal of Ceramics
• /
• 제6권3호
• /
• pp.245-249
• /
• 2000

Consolidation of amorphous powders is emerging as a route for synthesis of high strength composite materials. Diffusion processes necessary for consolidation are expected to be more rapid in amorphous state(SRO) than in the crystalline state(LRO). A new synthesis technique of exploiting polymeric ceramic precursors(polysilazane and polyborosilazane) is derived for Si$_3$N$_4$/SiC and boron-modified nanocomposites for extremely high temperature applications up to 200$0^{\circ}C$. The characterization methods include thermal analysis of DTA, and XRD, NMR, TEM, after pyrolysis, as a function of time and temperature.

• 한국결정성장학회지
• /
• 제9권2호
• /
• pp.260-265
• /
• 1999

$\alpha$-SiC에 ${\alpha}-Si_3N_4$ 를 10~30 vol%까지 10 vol% 간격으로 혼합하고 소결 조제로$Al_2O_3$와$Y_2O_3$를 각각 6wt% 로 첨가하여 $1,780^{\circ}C$에서 2시간동안 질소 분위기에서 상압소결하여 $Si_3N_4$ 복합체를 제조하였다. 상대 이론 밀도 및 꺽임 강도는 ${\alpha}-Si_3N_4$를 20 vol% 첨가하였을 때 92% 및 3,560 MPa로 가장 우수하였으며, 비마모량도 $2.68{\times}10^{-3}\;mm^2$ 으로 가장 작았다. 그리고, 파괴 인성$(K_{1c})$)은 ${\alpha}-Si_3N_4$를 30vol% 첨가하였을 때 $4.9\;MN/m^{3/2}$로 가장 좋았으나 이 경우 기공의 영향으로 내마모성은 저하된 것을 확인할 수 있었다.

• The Korean Journal of Ceramics
• /
• 제5권4호
• /
• pp.324-330
• /
• 1999

$Si_3N_4$-$TiB_2$ with 2 wt% $Al_2O_3$ and 4 wt% $Y_2O_3$ additives was hot pressed in a flowing $N_2$ environment with varying $TiB_2$ content from 10 to 50 vol%. Variations of mechanical (hardness, fracture toughness, and flexual strength), and tribological properties as a function of $TiB_2$ content were investigated. As the content of $TiB_2$ increased, relative density decreased due to the chemical reaction of $TiB_2$in $N_2$ environment. The reduction of density causes mechanical properties to be degraded with an increase of $TiB_2$ in $Si_3N_4$. Tribological properties were dependent of microstructure as well as mechanical properties, however, they were degraded strongly by the chemical reaction of $Si_3N_4$-$TiB_2$ during hot pressing in $N_2$ environment. SEM and TEM observations, and X-ray diffraction analysis that the chemical reaction products at the interface are TiCN, Si, and $SiO_2$. Also, the comparison of XRD patterns of the $Si_3N_4$-40 vol% $TiB_2$ composites hot pressed at $1,750^{\circ}C$ for 1 hour between in $N_2$ and in Ar gas was made. The XRD peaks of Si and $SiO_2$ were not found in Ar, but still a weak peak of TiCN was presented.

• 한국세라믹학회지
• /
• 제32권12호
• /
• pp.1417-1423
• /
• 1995

α/β sialon based composites containing silicon nitride whisker and silicon carbide platelet were fabricated by hot pressing. Effect of the reinforcing agents on the α to β phase transformation of the sialon as well as on the mechanical properties was investigated. Silicon nitride whisker and silicon carbide platelet promoted the phse transformation. TEM/EDS analysis revealed that the grain containing the whisker had 'core-rim' structure; core being high purity Si3N4 whisker and rim being β-sialon. Flexural strength of the composite decreased with the reinforcement addition which, on the other hand, improved fracture toughness of it. High temperature strength was measured at 1300℃ to be about 130 MPa lower than that measured at RT for the whisker reinforced composites.

• 한국세라믹학회지
• /
• 제28권9호
• /
• pp.667-674
• /
• 1991

In this study, Kaolin was carbonized at 1300~175$0^{\circ}C$ and its constituent mineral change was investigated. Carbonized kaolin at 1$650^{\circ}C$ was mixed with metallic silicon, formed and nitrified at 135$0^{\circ}C$ in N2-NH3 atmosphere. Properties of this product such as porosity, bulk density, MOR, nitrization rate and oxidation resistence were measured, and its mineralogical changes were investigated by XRD. The results were as follows; 1) $\beta$-SiC was initially synthesized at 150$0^{\circ}C$, and its amount was continuously increased with reaction temperature to 1$700^{\circ}C$. 2) At 1$600^{\circ}C$, mullite was rapidly decomposed and the amounts of $\beta$-SiC and $\alpha$-Al2O3 were increased simultaneously. 3) By adding alkali to kaolin, the decomposition temperature of mullite was dropped approximately 10$0^{\circ}C$, but the amount of $\alpha$-SiC was increased. 4) The highest values of their nitrization rate and MOR were obtained at the specimen of 35 wt% metallic silicon in nitrization reaction. 5) It seems that increment of $\alpha$-Si3N4 and $\alpha$-Al2O3 phase during nitrization was due to the decomposition of Al4SiC4 existed in carbonized kaolin. 6) Si3N4 bonded SiC-Al2O3 composite were fabricated from kaolin at relatively low temperature (135$0^{\circ}C$).

• 한국주조공학회지
• /
• 제21권6호
• /
• pp.359-365
• /
• 2001

The superplastic behavior of whisker reinforced aluminum alloy matrix composites fabricated by squeeze casting as one of high pressure routes was investigated. The preforms of ${\alpha}-Si_3N_4$ and ${\beta}-SiC$ whiskers without any binder as a reinforcement were used. The matrix materials were 2024 and 7075 aluminum alloys. For the purpose of optimum superplastic condition, respectively, the whiskers volume fraction, extrusion temperature, tensile test temperature and initial strain rate were changed. Fracture surface of tested specimens were observed by SEM. By the results, it became possible to produce superplastic composites by applying only a hot extrusion process to composites obtained by the squeeze casting. The superplastic composites developed are ${\alpha}-Si_3N_4w/7075$, ${\alpha}-Si_3N_4w/2024$ and ${\beta}-SiCw/2024$ systems at high strain rate.

• 한국재료학회지
• /
• 제19권12호
• /
• pp.637-643
• /
• 2009

In this study, we analyzed the effect of silicon oxynitride matrix on the optical properties of Au nanoparticles dispersed on composite film and explored the effectiveness of the silicon in fine tuning the refractive index of the composite film for applications in optical waveguide devices. The atomic fraction of nitrogen in $SiO_xN_y$ films was controlled by varying the relative flow ratio of nitrogen gas in reactive sputtering and was evaluated optically using an effective medium theory with Bruggeman geometry consisting of a random mixture between $SiO_2$ and $Si_3N_4$. The Au nanoparticles were embedded in the $SiO_xN_y$ matrix by employing the alternating deposition technique and clearly showed an absorption peak due to the excitation of surface plasmon. With increasing nitrogen atomic fraction in the matrix, the surface plasmon resonance wavelength shifted to a longer wavelength (a red-shift) with an enhanced resonance absorption. These characteristics were interpreted using the Maxwell-Garnett effective medium theory. The formation of a guided mode in a slab waveguide consisting of 3 $\mu$m thick Au:$SiO_xN_y$ nanocomposite film was confirmed at the telecommunication wavelength of 1550 nm by prism coupler method and compared with the case of using $SiO_2$ matrix. The use of $SiO_xN_y$ matrix provides an effective way of controlling the mode confinement while maintaining or even enhancing the surface plasmon resonance properties.

• 한국표면공학회지
• /
• 제38권3호
• /
• pp.100-105
• /
• 2005

Cr-Si-C-N coatings were deposited on steel substrate (SKD 11) by a hybrid system of arc ion plating (AIP) and sputtering techniques. From XRD, XPS, and HRTEM analyses, it was found that Cr-Si-C-N had a fine composite microstructure comprising nano-sized crystallites of Cr(C, N) well distributed in the amorphous phase of $Si_3N_4/SiC$ mixture. Microhardness of Cr(C, N) coatings and Cr-Si-N coatings were reported about $\~22 GPa$ and $\~35 GPa$, respectively. As the Si was incorporated into Cr(C, N) coatings, The Cr-Si-C-N coatings having a Si content of $9.2 at.\%$ showed the maximum hardness value. As increased beyond Si content of $9.2 at.\%$, the interaction between nanocrystallites and amorphous phase was gone, the hardness was reduced as dependent on amorphous phase of $Si_3N_4/SiC$. In addition, the average coefficient of Cr-Si-C-N coatings largely decreased compared with Cr(C, N) coatings.

• 한국표면공학회지
• /
• 제54권5호
• /
• pp.230-237
• /
• 2021

In this study, the influence of silicon contents on the microstructure, mechanical and tribological properties of Ti-Al-Si-N coatings were systematically investigated for application of cutting tools. The composition of the Ti-Al-Si-N coatings were controlled by different combinations of TiAl₂ and Ti₄Si composite target powers using an arc ion plating technique in a reactive gas mixture of high purity Ar and N₂ during depositions. Ti-Al-Si-N films were nanocomposite consisting of nanosized (Ti,Al,Si)N crystallites embedded in an amorphous Si₃N₄/SiO₂ matrix. The instrumental analyses revealed that the synthesized Ti-Al-Si-N film with Si content of 5.63 at.% was a nanocomposites consisting of nano-sized crystallites (5-7 nm in dia.) and a three dimensional thin layer of amorphous Si₃N₄ phase. The hardness of the Ti-Al-Si-N coatings also exhibited the maximum hardness value of about 47 GPa at a silicon content of ~5.63 at.% due to the microstructural change to a nanocomposite as well as the solid-solution hardening. The coating has a low friction coefficient of 0.55 at room temperature against an Inconel alloy ball. These excellent mechanical and tribological properties of the Ti-Al-Si-N coatings could help to improve the performance of machining and cutting tool applications.

• 한국재료학회지
• /
• 제11권7호
• /
• pp.585-589
• /
• 2001

많은 연구결과들은 국부적 용융체의 존재가 고온인장 변형 시 발생하는 내부공극의 발달을 억제할 수 있음을 보고하고 있다. 그러나 이러한 국부적 용융체가 존재한다고 해서 반드시 고변형속도 초소성 현상이 관찰될 수 있는 것은 아니다. 금속기지와 보강재간의 계면에 국부적 용융체의 양이 너무 많이 존재하면 두상간의 결합력이 떨어져 금속기지상으로부터 보강재가 분리되는 현상이 야기될 수 있기 때문이다. 그러므로, $Si_3$$N_{4p}$ 2124 Al 복합재의 초소성 유동 특성을 이해하기 위해 변형온도에 따른 미세구조 변화와 계면특성을 조사하였다. 본 연구를 룽해 $Si_3$$N_{4p}$ 2124 Al 복합재에서 Al-기지와 $Si_3$$N_{4p}$ 강화상간의 계면상의 국부적 용융이 시작되는 온도부근에서는 큰 초소성 특성이 얻어지지만, 국부적 용융이 시작되는 온도를 지난 인장온도범위에서는 오히려 초소성 특성이 현저하게 저하되는 현상이 관찰되었다. 위의 실험결과는 $Si_3$$N_{4p}$ 2124 Al복합재의 고변형속도 초소성 거동에 기여하는 최적의 액상량이 존재한다는 것을 의미한다.