• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.56-59
• /
• 2000

In this study, Ferroelectric $Pb(Zr_x,Ti_{1-x})O_3$(x=0.53) thin films were fabricated by the spin-coating on the Pt/Ti/$SiO_2$/Si substrate using the PZT metal alkoxide solutions with various excess Pb contents. Etching of PZT film was performed using planar inductively coupled Ar(20)$/Cl_2/BCl_3$ plasma. The etch rate of PZT film was 2450 ${\AA}/min$ at Ar(20)$/BCl_3$(80) gas mixing ratio and substrate temperature of $80^{\circ}C$. The leakage current densities of before etching and after etching PZT thin film were $6.25\times10^{-8}A/cm^2$, $8.74\times10^{-7}A/cm^2$ with electric field of 0.07MV/em, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.869-873
• /
• 2004

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient, piezoelectric, and a photo refractive properties. In this study, SBN60(x=0.6) thin film was manufactured by ion beam sputtering technique. Using the prepared SBN60 target in $Ar/O_2$ atmosphere as-deposited SBN60 thin film on Pt(100)/$TiO_2/SiO_2/Si$ substrate crystallization and orientation behavior as well as electric properties of SBN60 thin film were examined. SBN60 deposition up to $3000{\AA}$ in thickness, SBN60 thin film was heat-treated at $650^{\circ}C{\sim}800^{\circ}C$. The orientation was shown primarily along (001) plane from XRD pattern where working pressure was $4.3{\times}10^{-4}$ torr. The deposited layer was uniform, preferred orientatin and crystallization behavior resulted in the change of $O_2$ ratio was observed. In electric propertie of Pt/SBN60/Pt thin film capacitor remnant polarization (2Pr) value was $10{\mu}C/cm^2$, the coercive filed (Ec) 50 kV/cm, and the dielectric constant 615, respectively.

• Electrical & Electronic Materials
• /
• v.9 no.7
• /
• pp.668-673
• /
• 1996

In this paper, (P $b_{1-x}$ L $a_{x}$)(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ (X=0-13[at%]) thin film were prepared by the Sol-Gel method, Multiple PLZT thin films were spin-coated on the Pt/Ti/ $SiO_{2}$Si substrate. The electrical properties of the films were investigated for varying the annealing temperature. In the PLZT(11/52/48) specimens, the dielectric ocnstant of 1236 and the polarization reversal time of 460[nm] were obtained and the breakdown of the film did not occur up to 1*10$^{10}$ cycles at the voltage of 7[V] by the bipolar acceleration. The remanent polarization and coercive field decreased with increasing the content of La in the range of 0-13[at%] and thin film of the PLZT(11/52/48) showed the value of 2.56[.mu.C/c $m^{2}$] and 21.1[kV/cm], respectively.ly.y.

• Korean Journal of Materials Research
• /
• v.14 no.10
• /
• pp.701-706
• /
• 2004

Bismuth layered structure ferroelectric thin films, La-substituted $Bi_{4}Ti_{3}O_{12}$ ($Bi_{1-x}La_{x}Ti_{3}O_{12}$, x=0.75, BLT) were prepared on the $Pt(111)/Ti/SiO_2/Si(100)$ substrates by a sol-gel spin coating process. The thin films were annealed in various conditions, i.e., oxygen, nitrogen and vacuum atmospheres for various annealing time. We investigated the annealing condition effects on the grain orientation and ferroelectric properties. The measured XRD patterns revealed that the BLT thin films showed only $Bi_{4}Ti_{3}O_{12}$-type phase with random orientation. $La^{3+}$ ion substitution for $Bi^{3+}$ ion in perovskite layers of $Bi_{4}Ti_{3}O_{12}$ decreased the degree of c-axis orientation and increased the remanent polarization ($2P_{r}$). The remanent polarization ($2P_{r}$) and the coercive field ($2E_{c}$) of the BLT thin film annealed at $650^{\circ}C$ for 5 min in oxygen atmosphere were $87{\mu}C/cm^2$ and 182 kV/cm, respectively, at an applied electric field of 240 kV/cm. For all of the BLT thin films annealed in various conditions, the fatigue resistance was shown. The improvement of ferroelectric properties with La substitution in $Bi_{4}Ti_{3}O_{12}$ could be attributed to the changes in space charge densities and grain orientation in the thin film.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.3
• /
• pp.229-233
• /
• 2019

Pure $BiFeO_3$ (BFO) and (Eu, V) co-doped $Bi_{0.9}Eu_{0.1}Fe_{0.975}V_{0.025}O_{3+{\delta}}$ (BEFVO) thin films were deposited on $Pt(111)/Ti/SiO_2/Si(100)$ substrates by chemical solution deposition. The effects of co-doping were observed by X-ray diffraction, Raman spectroscopy, and scanning electron microscopy (SEM). The electrical properties of the BEFVO thin film were improved as compared to those of the pure BFO thin film. The remnant polarization ($2P_r$) of the BEFVO thin film was approximately $26{\mu}C/cm^2$ at a maximum electric field of 1,190 kV/cm with a frequency of 1 kHz. The leakage current density of the co-doped BEFVO thin film ($4.81{\times}10^{-5}A/cm^2$ at 100 kV/cm) was two orders of magnitude lower than of that of the pure BFO thin film.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.9
• /
• pp.1588-1590
• /
• 2007

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.34D no.2
• /
• pp.27-37
• /
• 1997

Photoluminescent and cathodoluminescent charcteristics of inorganic luminescent materials were investigated ot develop possible phosphors for thin film electroluminescent (TFEL) device applications. Mg, Zn, and Photoluminescent and cathodoluminescent charcteristics of inorganic luminescent materials were investigated ot develop possible phosphors for thin film electroluminescent (TFEL) device applications. Mg, Zn, and $Si_3N_4$ powders were used to synthesize $(Mg_xZn_{1-x})SiN_2$ host materials. $Tb_4O_7$ and $Eu_2O_3$ powdrs were added as luminescent centers. Very sharp emission spectra of $Tb^{3+}$ ions were observed from $Mg._5Zn._5SiN_2:Tb$ sampels sintered at $1400^{\circ}C$ for an hour and the maximum intensity of emission spectra occured at wavelength of 550nm (green light). Synthetic conditions of $(Mg_xZn_{1-x})SiN_2:Eu$ phosphors were optimized for the hghest luminescence. The Eu concentrations were varied from 0.2% to 1.6%. Before firing, the powders were mixed using ballmills, methanol, acetone, or D.I. water. The Mg/Zn ratio also were varied from x=0.3 to x=0.7. The maximum PL intensity was obtained from a sample with 1.2% Eu concentration and the powder was mixed with methanol and dried before firing. The maximum intensity of the emission spectra occurred t the wavelength of 470nm(blue light). TFEL devices fabricated by using sputter deposition of $(Mg._3Zn._7)SiN_2:Eu$ phosphor layer showed yellowish white emission at the phosphor field of 2MV/cm.

• Journal of the Korean Electrochemical Society
• /
• v.9 no.1
• /
• pp.34-39
• /
• 2006

Electrochemical properties of Cu foil current collector with a $Li_{0.5}La_{0.5}TiO_3$ Cu a Si thin film deposited by r.f sputtering as an anode for Li free battery were evaluated. The Cu foil current collectors were lied in and out of plasma during sputtering process. The X-ray diffraction results indicated that the as-deposited Si and $Li_{0.5}La_{0.5}TiO_3$ thin films in and out of plasma did not show any crystalline difference. The $Li_{0.5}La_{0.5}TiO_3$ film in plasma and Si film out of plasma showed better cyclability since crystalline $Li_{0.5}La_{0.5}TiO_3$ has much higher ionic conductivity and crystalline Si film is much sensitive far volume change during charge-discharge process. These results suggested that the deposition of amorphous Si on Cu foil current collector is much better for fabrication of Li free battery and it can be useful for the unique battery with a cycling number constraint of below 10.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.1092-1095
• /
• 2004

The $ZnGa_2O_4$ phosphor target is synthesized through solid-state reactions as calcine and sintering temperature in order to deposit $ZnGa_2O_4$ phosphor thin film by rf magnetron sputtering system. The $ZnGa_2O_4$ phosphor thin film is deposited on $Pt/Ti/SiO_2/Si$ substrate and prepared $ZnGa_2O_4$ Phosphor thin film is annealed by rapid thermal processor(RTP) at $750^{\circ}C$, 10 sec. The x-ray diffraction patterns of $ZnGa_2O_4$ phosphor target and thin film show the position of (311) main peak. The cathodolumincsccnce(CL) succtrums of $ZnGa_2O_4$ phosphor target show main peak of 360nm and broad bandwidth of about 180nm.

• Journal of the Korean Chemical Society
• /
• v.50 no.3
• /
• pp.243-246
• /
• 2006

The LiCoO2 thin films were prepared on the Pt/Ti/SiO2/Si substrate by spin coating using citrate sol. The citrate sol was spin-coated on substrate and dried at 380oC for 15 min. to evaporate the solvents and remove the organic materials. The as-deposited films were annealed at 750oC for 10 min. in air for crystallization. The X-ray diffraction patterns for the film have been indexed hexagonal system with space group R3m. The active area of LiCoO2 films for electrochemical test was about 11cm2. A Li foil and 1M LiClO4 in propylene carbonate(PC) and ethylene carbonate(EC) (1:1)were used as an anode and an electrolyte, respectively. The galvanostatic charge-discharge test was carried out at constant current density ranging from 5 A/cm2 in the voltage window between 4.2 and 3.0 V. The first discharge capacity of the film is 0.35Ah/cm2-m. The cycling behavior of the LiCoO2 film is also reported.