• Corrosion Science and Technology
• /
• 제18권6호
• /
• pp.285-291
• /
• 2019

In this study, the corrosion characteristics of T22 and T92 steel were investigated in 6O₂ + 16CO₂ + 2SO₂ gas environment at 650 ℃. Corrosion characteristics were characterized by weight gain, oxide layer thickness, scanning electron microscope, optical microscope, energy dispersive X-ray spectroscopy, and X-ray diffraction. T22 and T92 steel tended to stagnate oxide layer growth over time. Oxidation kinetics were analyzed using the data of oxide layer thickness, and a regression model was presented. The regression model was significantly acceptable. The corrosion rate between the two steels through the regression model showed significant difference. The T92 steel was approximately twice as large as the time exponent and showed very good corrosion resistance compared to the T22 steel. In both steels, the oxide layer mainly formed a Fe-rich oxide layer composed of hematite (Fe₂O₃), magnetite (Fe₃O₄), and spinel (FeCr₂O₄). Sulfide segregation occurred in the oxide layer due to SO₂ gas. However, the locations of segregation for the T22 and T92 steel were different.

• 한국표면공학회지
• /
• 제54권2호
• /
• pp.43-52
• /
• 2021

The Ni-based superalloy, Inconel 740, was corroded between 800 and 1100℃ for up to 100 hr in air and Ar-0.2%SO₂ gas in order to study its corrosion behavior in air and sulfur/oxygen environment. It displayed relatively good corrosion resistance in both environment, because its corrosion was primarily dominated by not sulfidation but oxidation especially in Ar-0.2%SO₂ gas. Such was attributed to the thermodynamic stability of oxides of alloying elements when compared to corresponding sulfides. The scales consisted primarily of Cr₂O₃, together with some NiAl₂O₄, MnCr₂O₄, NiCrMnO₄, and rutile-TiO₂. Sulfur from SO₂ gas made scales prone to spallation, and thicker. It also widened the internal corrosion zone when compared to air. The corrosion resistance of IN740 was mainly indebted to the formation of protective Cr₂O₃-rich oxides, and suppression of the sulfide formation.

• 한국표면공학회지
• /
• 제40권5호
• /
• pp.219-224
• /
• 2007

The corrosion characteristics of Fe-18Cr-10Ni steels were studied between $600^{\circ}C$ and $1000^{\circ}C$ in Ar+(0.2, 1)%$SG_2$ gas for up to 300 hr in order to employ Fe-18Cr-10Ni steels in the coal-fired power plants. The corrosion resistance of Fe-18Cr-10Ni steels was good due mainly to the high amount of Cr, which formed $Cr_2O_3$ from the initial corrosion stage. Fe in the steels corroded to mainly $Fe_2O_3$ and $Fe_3O_4$. Ni was not susceptible to corrosion under the current corrosion condition. Relatively thin, single-layered scales formed.

• 한국세라믹학회지
• /
• 제28권8호
• /
• pp.625-625
• /
• 1991

2wt% Al2O3와 10wt% Al2O3를 첨가하여 2000℃와 2050℃에서 가압소결된 SiC를 37 mol% NaCl과 63 mol% Na2SO4 Salt에 의해 60분까지 hot corrosion을 시켰다. 부식은 SiC표면에 형성된 SiO2층이 Na2O 이온에 의한 basic dissolution에 이해 일어남이 관찰되었고 10wt%의 Al2O3가 함유된 시편은 입계에 Al2O3를 함유한 입계상의 존재로 2wt% Al2O3가 함유된 시편보다 낮은 corrosion rate를 나타냈다. SiC와 산화물층 사이에서 gas bubble의 형성이 관찰되었고 이 gas bubble이 산화물층을 심하게 파괴하기 전까지 corrosion rate은 linear하게 변했다. 부식 양상은 개기공과 입계에서 pitting corrosion에 의해 시작되었다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2007년도 춘계학술발표회 초록집
• /
• pp.114-115
• /
• 2007

The corrosion characteristics of Cr steels were investigated to protect Cr steels from the SO2-gas corrosion in the coal-fired power plant. The samples tested were low alloy ferritic steel (ASTM T22, 23), martensitic steel (ASTM T91, 92, 122), and austenitic stainless steel (ASTM 347HFG). The corrosion tests were performed between 600oC and 1000oC in Ar + (0.2, 1)%SO2 gas for 100 hr. Chromium was quite beneficial to corrosion resistance, while iron was not. The corrosion resistance increased in the order of T22, T23, T91, T92, T122, and 347HFG.

• Corrosion Science and Technology
• /
• 제22권5호
• /
• pp.351-358
• /
• 2023

Although many thermal power plants use heat recovery systems, high exhaust gas temperatures are maintained due to corrosion at dew points and ash deposits caused by condensate formation. The dew point of exhaust gas is primarily determined by the concentration of SO₃ and steam, and various experiments and calculation equations have been employed to estimate it. However, these methods are known to be less suitable for exhaust gases with low SO₃ concentrations. Therefore, in this study, since the temperature of the exhaust gas is expected to decrease due to the low-load operation of the coal-fired power plant, sulfuric acid condensation and low-temperature corrosion are anticipated. We aimed to conduct a quantitative evaluation to propose ways to prevent damage by limiting operating conditions and improving facilities. The experimental results showed that the corrosion rate increased linearly with rising temperatures at a certain sulfuric acid concentration. Furthermore, variations in sulfuric acid concentrations generated during the current power plant operation process did not significantly affect the dew point, and the dew point of sulfuric acid under these conditions was observed to be between 120 - 130 ℃.

• 한국표면공학회지
• /
• 제43권1호
• /
• pp.36-40
• /
• 2010

The SiO vapor that was generated from a mixture of Si and $SiO_2$ was reacted at $1350^{\circ}C$ for 2 h under vacuum with carbon nanofibers to produce SiC nanofibers having an average diameter of 100~200 nm. In order to understand the gas corrosion behavior, SiC nanofibers were exposed to air up to $1000^{\circ}C$. SiC oxidized to amorphous $SiO_2$, but its oxidation resistance was inferior unlike bulk SiC, because of high surface area of nanofibers. When SiC nanofibers were exposed to Ar-1% $SO_2$ atmosphere, SiC oxidized to amorphous $SiO_2$, without forming $SiS_2$, owing to the thermodynamic stability of $SiO_2$.

• 한국표면공학회지
• /
• 제50권2호
• /
• pp.85-90
• /
• 2017

The carbon steel formed the thick, somewhat porous, loosely adherent iron oxide scale when oxidized at $500-800^{\circ}C$ for 15 h in air. It formed the thicker, more porous, nonadherent scale consisting of FeS plus iron oxides in $Ar/1%SO_2$-mixed gas. It formed the much thicker, more porous, nonadherent scale consisting of FeS plus iron oxides in Ar/0.1% $H_2S$-mixed gas. However, the aluminized carbon steel formed the thin, protective $Al_2O_3$ surface scale even in $Ar/1%SO_2$-, and $Ar/0.1%H_2S$-mixed gas. Aluminizing drastically improved the corrosion resistance in (O, S, H)-containing gas.

• 한국표면공학회지
• /
• 제55권6호
• /
• pp.433-440
• /
• 2022

Environmental pollution caused by power plant exhaust gas is highlighted and eco-friendly regulations are being strengthened. However, due to the abundant reserves and low prices of coal, still the most used for power generation in the world. Therefore, flexible operation of coal-fired power plants to reduce emissions has become an inevitable option. However, lowering the output increases the possibility of acid dew point corrosion as the exhaust gas temperature decreases. The dew point corrosion occurs when condensable gases such as SO₃, HCl, NO₂ and H₂O cools below the saturation temperature. SO₃ is already well known to cause severe low- temperature corrosion in coal-fired power plants. Therefore, this study aims to prevent damage that may occur during operation by analyzing the dew point and corrosion resistance with exhaust gas temperature and sulfuric acid concentration of the power plant economizer tube.

• 한국표면공학회지
• /
• 제51권3호
• /
• pp.149-156
• /
• 2018

The corrosion and strength degradation characteristics of 1.25Cr-0.5Mo steels were studied under $650^{\circ}C$ in $76%N_2+6%O_2+16%CO_2+2%SO_2$ gas condition up to 500 hrs. Corroded specimens were characterized by weight gain, scanning electron microscope(SEM), energy dispersive X-ray spectroscopy(EDS), and X-ray diffraction(XRD). The tensile test was conducted to evaluate the mechanical strength and fracture mode with corrosion at high temperature. As the results of the experiments, thick Fe-rich oxide layers over $200{\mu}m$ were formed on the surface within 500 hrs. The thick oxide layers are formed with reduction of the cross-sectional area of the specimens. Thus, the strength tended to decrease with reduction of the cross-sectional area.