• Proceedings of the KIEE Conference
• /
• 1989.07a
• /
• pp.329-332
• /
• 1989

Lead titanate thin films were deposited on titanium substrates by a chemical vapour deposition(CVD) process involving the application of vapour mixtures of Pb, ethyl titanate( Ti($C_2H_5O_4$)), and oxygen. The lead titanate having a stoichiometric composition has a dc conductivity of $3.2{\times}10^{-12}{\Omega}^{-1}{\cdot}cm^{-1}$ at room temperature. The nonsaturating loops observed in present investigation may be attributed to the $TiO_2$ and TiO layers between the conductive substrate and the $PbTiO_3$ ferroelectric film. The ferroelectric properties of the stoichiometric $PbTiO_3$ film included a remanent polarization of 14.1 ${\mu}C/cm^2$ and a coercive field of 20.16 kV/cm.

• Electrical & Electronic Materials
• /
• v.5 no.1
• /
• pp.14-27
• /
• 1992

핫프레스법으로 제작된 0.05Pb(M $n_{1}$3/N $b_{2}$3/) $O_{3}$+ 0.95Pb(Z $r_{0.47}$ $Ti_{0.53}$) $O_{3}$ 세라믹스에 있어서 C $r_{2}$ $O_{3}$의 첨가량이 그 시편의 구조적특성, 유전특성, 압전특성, 온도안정성 및 포아손비에 미치는 영향이 조사되었다. C $r_{2}$ $O_{3}$의 첨가량의 범위가 0.3~0/75[wt%]인 시편만이 포아손비가 1/3이상으로 주파수저하형 에너지포획소자의 기판으로 사용될 수 있으며 이 중에서 C $r_{2}$ $O_{3}$의 첨가량이 0.5[wt%]인 시편이 보다 우수한 압전특성과 안정된 주파수 온도특성을 갖고 있다. 있다.

• Journal of the Korean Ceramic Society
• /
• v.30 no.7
• /
• pp.543-548
• /
• 1993

Stability and formation of Pb(Mg1/3Nb2/3)O3 (PMN) phase synthesized in Li2SO4-Na2SO4 molten salts have been investigated. And powder characteristics of PMN have been studied with a variation of processing parameters such as temperature, time, amount of the salts, and excess PbO. More ratio of Li2SO4 to Na2SO4 influences the percentage of perovskite phase due to the difference of the eutectic point of the salts, but does not influence the powder characteristics. The shape of PMN particles shows faceted morphology with bimodal distribution consisting with large and submicron parts. Particle size of PMN increased greatly with increasing soaking time or amount of salts rather than temperature. The addition of excess PbO resulted in round PMN crystallites without submicron particles. These results are discussed by XRD, SEM and thermal analyses.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.839-846
• /
• 1996

Epitaxial (La, Sr)$CoO_3/Pb(Zr,\;Ti)O_3/(La,\;Sr)CoO_3$by pulsed laser deposition for ferroelectric field effect transistor. Epitaxial $LaCoO_3/Pb(Zr,\;Ti)O_3/(La,\;Sr)CoO_3$ heterostructures exhibited 70$\mu C/cm^2$ and 17 $\mu C/cm^2$at a positively and negatively poled states, respectively. On the other hand, epitaxial (La, Sr)$CoO_3/Pb(Zr,\;Ti)O_3/LaCoO_3$heterostructures show the remnant polarization states opposite to the $LaCoO_3/Pb(Zr,\;Ti)O_3/(La,\;Sr)CoO_3$ heterostructures. This indicates that the interface between (La, Sr)$CoO_3$ (LSCO) and $Pb(Zr, Ti)O_3(PZT)$ layers affects the asymmetric polarization remanence through electrochemical nature. The resistivity of $LaCoO_3$ (LCO) layer was found to be dependent on an ambient oxygen, primarily the ambient oxygen pressure during deposition. The resistivity of the LCO layer varied in the range of 0.1-100 $\Omega$cm. It is suggested that, with an appropriate resistivity of the LCO layer, the LCO/PZT/LSCO heterostructure can be used as the ferroelectric field effect transistor.

• Electrical & Electronic Materials
• /
• v.3 no.3
• /
• pp.233-241
• /
• 1990

본 연구에서는 xPb(Zn$_{1}$3/Nb$_{2}$3/)O$_{3}$-yBa(Zn$_{1}$3/Nb$_{2}$3/)O$_{3}$-zPbTiO(0.50.leq.x.leq.0.60, 0.10.leq.y.leq.0.20, 0.20.leq.z.leq.0.40)세라믹을 1050.deg.C에서 2시간동안 유지시켜 일반소성법으로 제작하였다. 시편 제작시 조성은 조성변태 상경계부근을 선택하였으며 Ba(Zn$_{1}$3/ Nb$_{2}$3/)O$_{3}$ 고용량에 따른 purochlore상의 억제 및 그 영향을 조사하고 구조적, 유전적 및 압전적 특성을 측정하였다. X-선 회절분석 및 미세구조의 관찰 결과, Ba(Zn$_{1}$3/Nb$_{2}$3/)O$_{3}$의 고용량에 따라 pyrochlore상 및 미반응 물질등은 억제되어 0.20mol 고용된 시편에서는 균질한 perovskite상이 형성되었다. Ba(Zn$_{1}$3/Nb$_{2}$3/)O$_{3}$의 고용량이 증가함에 따라 유전상수는 증가하여 0.50PZN-0.20BZN-0.30PT시편의 경우 6880.9의 높은 값을 나타내었으며 정전용량의 온도계수는 감소하여 0.383[%/.deg.C]의 양호한 값을 나타내었다. 큐리온도는 PbTiO$_{3}$의 고용량이 0.20mol에서 0.40mol로 증가함에 따라 30.deg.C에서 170.deg.C로 증가하였다. 전기기계 결합계수 (K$_{p}$), 기계적 품질계수(Qm) 및 압전전하 계수 (d$_{33}$)는 조성변태 상경계 부근의 조성에서 크게 나타났으며 0.60PZN-0.15BZN-0.25PT 시편의 경우 각각 58.5%, 120.5, 150x$10^{-12}$[C/N]의 값을 나타내었다.다.다.

• Journal of Korean Ophthalmic Optics Society
• /
• v.5 no.2
• /
• pp.167-173
• /
• 2000

Four glasses of $B_2O_3-Bi_2O_3-PbO-SiO_2$ (BBPS) system were prepared by melting the appropriate amounts of reagent grade oxides of $B_2O_3$, $Bi_2O_3$, PbO, and $SiO_2$ in an open crucible. The differential thermal analysis showed crystallization temperature decreased with increasing $Bi_2O_3$ or PbO content in the sample. The structures of glasses system were studied using scanning electron microscopy and Fourier transform-Infra red (FT-IR) spectroscopy. The UV cut-off and refractive index were found to be sensitive to the $Pb^{+2}$ and $Bi^{+3}$ content in the glasses. The behavior of the IR spectra of the glasses in the BP series was consistent with a role of $Bi_2O_3$ as a network former. In the BP series of glasses, the result of IR spectrum indicated that PbO behaved as a network former.

• Electrical & Electronic Materials
• /
• v.6 no.3
• /
• pp.207-213
• /
• 1993

Pb(Z $r_{0.54}$, $Ti_{0.46}$) $O_{3}$에 B $i_{2}$ $O_{3}$를 0.0wt%까지 첨가하여 미세구조, 유전, 압전, 성질에 미치는 영향을 고찰하였다. B $i_{2}$ $O_{3}$의 고용범위는 약 0.5~0.7wt%정도 이었고 B $i_{2}$ $O_{3}$ 첨가량이 증가함에 따라서 결정립의 크기가 감소하였다. B $i_{2}$ $O_{3}$첨가량이 증가함에 따라 고용한계까지는 $d_{33}$ , tan .delta., .xi.$_{r}$(분극후)값이 증가하였으며 Qm값과 밀도는 감소하였다. $K_{p}$ 값은 B $i^{3+}$ 가 P $b^{2+}$를 치환하므로 형성되는 Pb공공의 형성에 의해 자발분극이 증가됨에 따라 증가하였다.다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.1
• /
• pp.35-39
• /
• 2006

In this study, in order to develop the multilayer piezoelectric actuator and ultrasonic resonator, PMN-PNN-PZT ceramics were fabricated by sintering with $Li_2CO_3-Na_2CO_3$ as sintering aids at $950^{\circ}C$ and their piezoelectric and dielectric characteristics were investigated as a function of PNN substitution. With increasing PNN substitution, dielectric constant(${\epsilon}_r$), electromechanical coupling factor(kp), and piezoelectric d constant($d_{33}$) were increased to $12 mol\%$ PNN substitution and then showed a tendency to decrease rapidly With increasing PNN substitution, crystal structure changed from tetragonal to rhombohedral at $12 mol\%$ PNN substitution and then secondary phase was appeared and its intensity was increased. At the $12 mol\%$ PNN substituted PMN-PZT composition ceramic sintered at $950^{\circ}C$, density, kp, $d_{33}$ and Qm showed the optimum value of $7.79 g/cm^3$, 0.599, 419 pC/N, and 894, respectively for multilayer piezoelectric actuator application.

• Applied Science and Convergence Technology
• /
• v.25 no.4
• /
• pp.77-80
• /
• 2016

The $PbSc_{1/2}Nb_{1/2}O_3$ ceramics at a relatively low temperature of $1300^{\circ}C$ was successful synthesized. Solid state reaction of two-step process is not necessary. The dielectric constant, dielectric loss and admittance of ceramic samples were determined. The pyroelectric characteristics are in good agreement with the dielectric properties. Ferroelectric properties of well-formed the $PbSc_{1/2}Nb_{1/2}O_3$ ceramics are in agreement with broad distribution of relaxation phenomenon. Relatively strong frequency dependent of dielectric constant is observed at about $110^{\circ}C$. The distinct thermal hysteresis was observed in the measurement of the dielectric constant and dielectric loss. The critical exponents of during cooling and heating measurements in the $PbSc_{1/2}Nb_{1/2}O_3$ ceramics were 1.14 and 1.59 at 1 kHz, respectively.

• Journal of the Korean Ceramic Society
• /
• v.21 no.4
• /
• pp.313-322
• /
• 1984

Phase relationships of the pseudobinary systems in melanotekite-plumboferrite and melanotekite-magnetoplumbite in $PbO-Fe_2O_3-SiO_3$ system were obtained. Dielectric electric and magnetic properties were measured in the chosen pseudo-ternary system.