• 한국세라믹학회지
• /
• 제27권2호
• /
• pp.187-194
• /
• 1990

Effects of MnO2 addition ranged from 0.0wt% to 5.0wt% on the microstructure and dielectric and piezoelectric properties of the Pb(Zr0.52 Ti0.48)O3 Ceramics have been investigated. The solubility limit of MnO2 in Pb(Zr0.52 Ti0.48)O3 is about 0.5wt%, and MnO2 as a valence state of Mn3+ is substituted for (Zr, Ti) lattice site in PZT solid-solution. The addition of MnO2 up to 0.5wt% in Pb(Zr0.52 Ti0.48)O3 brings increase of density, but decreased of grain size and tetragonality. Dielectric constant slightly decreases, but both coupling factor(Kp) and mechanical quality factor(Qm) increase with the addition of MnO2. However, excess amount of MnO2 addition more than 0.75wt% results in rapid decrease of resistance. Dielectric constant and tan $\delta$ increase due to the second phase and inhomogeneous Mn distribution.

• 한국세라믹학회지
• /
• 제35권6호
• /
• pp.640-646
• /
• 1998

PbO-TiO2-B2O3-BaO계 유리에서 PbTiO3의 핵생성 및 결정화를 위한 최적조건의 확입을 위해 핵생성 속도 곡선을 도출하고자 열시차 분석법(DTA)을 응용하였다. PbTiO3의 함량비가 60mol%인 4성분계 유리 샘플은 용융액으로부터 자연 냉각시켜 제조되었으며, 핵생성을 위해 유리 샘플은 40$0^{\circ}C$와 50$0^{\circ}C$ 사이에서 열처리하였다. 이때 46$0^{\circ}C$에서 핵생성 속도가 최대값을 나타내었다. DTA의 결정화 피크 온도는 핵생성을 위한 열처리시간이 증가함에 따라 감소하였으며, DTA의 승온속도에 비례하여 증가하였다. 이러한 결과는 계에 생성된 핵의 밀도가 핵생성 처리온도와 시간의 증가에 따라 증가함을 보여주고 있다.

• 한국산학기술학회논문지
• /
• 제18권4호
• /
• pp.608-613
• /
• 2017

본 연구에서는 저품위인 35wt% 금합금에 대해 80.0wt% 이상의 Au를 얻기 위한 건식 정련 공정을 제안하였다. Au35wt%-Ag5wt%-Cu60wt%의 조성을 가진 금합금에 대해 PbO/(PbO+CaO)의 혼합비를 각각 0~1로 변화시키고 플럭스/금합금의 무게비는 1/2로 하여 $1200^{\circ}C$-5시간의 열처리를 진행하였다. 이때 공정 전, 후 시료의 조성 변화는 energy dispersive X-ray spectroscopy(EDS)로 확인하고, 공정이 완료된 후 분리된 플럭스 금속 원소 성분은 time of flight secondary ion mass spectromerty(ToF-SIMS)로 확인하였다. EDS분석 결과 플럭스의 비율이 1(PbO 단일)인 경우 Au의 함량이 35.0wt%에서 86.7wt%로 가장 크게 향상되었고, 다른 플럭스 조성의 경우도 84wt% 이상으로 정련이 가능하였다. 또한 2/3 혼합비의 플럭스에서 Ag가 플럭스부로 빠져나가는 손실이 가장 적었다. 플럭스부의 ToF-SIMS 분석 결과 플럭스의 비율이 1, 0 일 때 $Au^+$의 특성 피크의 강도가 각각 349, 37로 측정되었다. Au의 손실을 고려하였을 때 CaO 단일 플럭스의 사용이 더 유리할 수 있었으나, 이 정도의 신호강도는 무시할 수 있는 정도로 판단되었다. 따라서 혼합플럭스를 이용한 건식 열처리를 통해 효과적인 금의 정련이 가능하여 경제적인 습식제련의 전처리 공정으로 사용될 수 있음을 확인하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1988년도 춘계학술대회 논문집
• /
• pp.82-83
• /
• 1988

• 한국전기전자재료학회논문지
• /
• 제20권10호
• /
• pp.873-877
• /
• 2007

In order to apply a complex multilayer chip LC filter, this study has estimated the interfacial reaction and coupling properties of dielectric materials $Pb(Fe_{1/2}Nb_{1/2})O_3$ and Ni-Zn-Cu ferrite materials through low-temperature co-sintering (LTCS). PFN powders were fabricated using double calcinated at $700^{\circ}C$ and then $850^{\circ}C$. While the perovskite phase rate was found to be 91 %, after heat treatment at $900^{\circ}C$ for 6h, the perovskite phase rate and density exhibited a value of 100 % and 7.46$g/cm^3$, respectively. The PFN/Ni-Zn-Cu ferrite, PFN/CUO (or $Pb_2Fe_2O_5$) and ferrite/CuO (or $Pb_2Fe_2O_5$) were mechanically coupled through interfacial reactions after the specimen was co-sintered at $900^{\circ}C$ for 6 h. No intermediate layer exists for the mutual coupling reaction. This result indicates the possibility of low-temperature co-sintering without any interfacial reaction layer for a multilayer chip LC filter.

• 한국세라믹학회지
• /
• 제34권5호
• /
• pp.461-466
• /
• 1997

Dielectric and piezoelectric properties of (Pb1-1.5xLnx)(Ti0.98Mn0.02)O3 ceramics with x=0~0.2 have been investigated. Pb(Ti0.98Mn0.02)O3 showed poor sinterability and cracking on cooling, but the substitution of Nd3+ ions into Pb2+ sites resulted in dense microstructures without cracking through reducing crystallographic anisotropy. The Nd3+ substitution, however, deteriorated the temperature stability of the piezoelectric properties because of lowering the Curie point. Electromechanical anisotropy(Kt/Kp) indicated a maximum value of 10 when x=0.1. This result might be attributed to the counteracting effects that with increasing x, the lattice anisotropy decreases while the poling becomes easier due to the increase in O2- vacancy concentration. Thickness-shear mode resonators with (Pb0.85Nd0.1)(Ti0.98Mn0.02)O3 composition showed good resonant characteristics around 4.5 MHz.

• Bulletin of the Korean Chemical Society
• /
• 제32권2호
• /
• pp.463-466
• /
• 2011

In this work, we investigate anodization of Pb in ethylene glycol containing small amount of $NH_4F$, demonstrating that ${\beta}-PbF_2$ particles with octahedral morphology can be prepared by adjusting the applied potential and anodizing time. FE-SEM images and XRD measurements of anodic nanostructures as a function of anodizing time clearly show that PbO is first formed on Pb. Subsequently, a local dissolution of PbO leads to formation of skeleton structure of PbO, releasing $Pb^{2+}$ ions in the electrolyte. The lead ions can be precipitated on the walls or intersection of the skeleton walls when the concentration of lead ions is saturated. The method described in this article shows the feasibility of formation of metal fluoride crystal by anodization of metal in a fluoride containing solution.

• 한국전기전자재료학회논문지
• /
• 제19권5호
• /
• pp.417-421
• /
• 2006

In this study, in order to develop low temperature sintering piezoelectric ceramics for LTCC (Low-Temperature Cofired Ceramic) multilayer piezoelectric actuator, PMW-PMN-PZT ceramics using $0.2wt%\; Li_2CO_3$ and $0.25wt%\;CaCO_3$ as sintering aids were investigated according to the varation of PMW substution. Composition ceramics could be sintered at $900^{\circ}C$ by adding sintering aids. As the amount of PMW substitution increased, the crystal structure of PMW-PMN-PZT ceramics moved from tetragonal phase to rhombohedral phase gradually, and MPB(Morphotrophic Phase Boundary) region appeared at 2 mol% PMW substitution. At the sintering temperature of $900^{\circ}C$, the density, electromechanical coupling factor(kp), mechanical quality factor(Qm), dielectric constant(${\epsilon}r$), piezoelectric constant(d33) and Curie temperature(Tc) of 2 mol% PMW substituted PMW-PMN-PZT ceramics showed the optimal values of $7.88g/cm^3$, 0.58, 1002, 1264, 352 pC/N and $336^{\circ}C$, respectively, for LTCC multilayer piezoelectric actuator application.

• 한국세라믹학회지
• /
• 제29권1호
• /
• pp.60-64
• /
• 1992

In the ceramics of PFN-PFW system modified with MnO2 dielectric properties and the relation of its microstructure have been investigated. The amount of MnO2 variations was 0, 0.05, 0.1, 0.15, 0.2, 0.25 and 0.3 mol%, respectively. In the result of the microstructure and electrical properties, the solid solution range of MnO2 was 0.15 mol%.

• 한국결정학회지
• /
• 제8권2호
• /
• pp.97-104
• /
• 1997

수열합성법에 의한 Pb(TixZr1-x)O3분말 합성에 대하여 연구하였다. 합성원료로는 Lead-acetate trihydrate와 Titanium isoproprxide, Zirconium propoxide를 isopropanol로 희석시킨후 가수분해 시켜 얻은 Ti/Zr 젤을 사용하였고, 광화제로서 KOH(0.5m, 1m, 2m)를 사용하였으며 140℃, 150℃, 160℃의 반응온도에서 합성하였다. 합성된 Pb(TixZr1-x)O3분말은 입방체의 형태를 띄고 있었으며 응집된 형태로 나타났다. 1m과 2m의 KOH에서는 PZT 합성이 잘 이루어졌으며 1m의 경우 8시간, 2m의 경우 1시간 이상의 반응이 필요하였고 0.5m KOH에선 5일의 반응시간에도 순수한 PZT분말만이 합성되지 않았다. 낮은 반응온도와 짧은 반응시간의 실험조건에선 합성된 분말이 대부분 PZT분말이었으나 미반응 Ti/Zr 젤이 상당량 존재하였다. 합성된 PZT분말의 크기는 KOH농의 증가에 따라 증가하였다. 중간생성물로서 PbO고용체가 생성되었으며 이는 Ti고용량이 10% 정도의 큰것과 3%정도의 작은 것으로 크게 나눌 수 있었다.