• Journal of the Korean institute of surface engineering
• /
• v.53 no.6
• /
• pp.351-359
• /
• 2020

Formation behavior and properties of PEO (Plasma Electrolytic Oxidation) film on AA2024 were investigated under application of pulsed current as a function of Na3PO4 concentration in 0.05 M Na2SiO3 solution by analyzing voltage-time behavior, in-situ observation of arc generation, observation of surface morphology and measurements of thickness and surface roughness. Arc generation voltage decreased with increasing Na3PO4 concentration. Color difference of PEO films between edge and inner part disappeared by addition of Na3PO4. It was also observed that size of nodules on PEO film decreased with increasing Na3PO4 concentration. Thickness of PEO films formed on AA2024 increased with increasing Na3PO4 concentration. Whereas, surface roughness of PEO films decreased with increasing Na3PO4 concentration up to 0.05 M of Na3PO4 which is attributed to the deceased size of nodules on the PEO films. However, the surface roughness increased with increasing Na3PO4 concentration more than 0.07 M of Na3PO4 which seems to be due to the formation of non-uniform PEO films with smooth surface and large size pores formed by orange-colored big arcs. The experimental results suggest that added sodium phosphate less than 0.2 M in an alkaline silicate solution can contribute to the formation of relatively thick and uniform thickness of PEO films under arc generation voltage lower than 300 V.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.5
• /
• pp.265-274
• /
• 2019

Formation behavior of PEO (Plasma Electrolytic Oxidation) films on AZ31 Mg alloy was investigated under application of 310 Hz AC as a function of $Na_3PO_4$ concentration from 0.02 M to 0.2 M. Film formation voltage and in-situ observation of arcs generated on the specimen surface were recorded with time, and surface morphologies of the PEO films were investigated using optical microscopy, confocal scanning laser microscopy and scanning electron microscopy. PEO film formation voltage decreased linearly with increasing $Na_3PO_4$ concentration which is attributed to the increase of solution pH. PEO films were grown uniformly over the entire surface in $Na_3PO_4$ solutions between 0.05 M and 0.1 M. However, non-uniform PEO films with white spots were formed in $Na_3PO_4$ solutions containing more than 0.1 M. Thickness and roughness of PEO films on AZ31 Mg alloy increased linearly with increasing $Na_3PO_4$ concentration and their increasing rates appeared to be much higher under 1 M than above 1 M. The experimental results suggest that phosphate ions can contribute to the formation of PEO films but higher $Na_3PO_4$ concentration more than 1 M results in local damages of PEO films due to repeated generation of white arcs at the same surface site of AZ31 Mg alloy.

• Journal of the Korean Society of Radiology
• /
• v.13 no.4
• /
• pp.645-652
• /
• 2019

Phosphor with phosphorus doped with rare earth ions was investigated by searching Sr and Eu phosphors suitable for substitution of Eu ions with similar ionic radius to polyphosphate host. The $NaSr(PO_3)_3$ phosphor was synthesized by the solid state method and the $NaSr(PO_3)_3:Eu^{2+}$ phosphor was prepared by the carbon thermal reduction method. Both of the phosphors were identified by X - ray diffraction. The excitation and emission spectra of $NaSr(PO_3)_3:Eu^{3+}$ increased fluorescence intensity and intensity quenching with increasing $Eu^{3+}$ concentration. The higher the $Eu^{3+}$ concentration in the emission spectrum, the higher the local symmetry of $Eu^{3+}$ environment. The mechanism of concentration quenching, in which fluorescence decreases due to the energy transfer between $Eu^{2+}$ ions with the closest critical distance between $Eu^{2+}$ ions with increasing $Eu^{2+}$ ion concentration, was confirmed in the emission spectrum of $NaSr(PO_3)_3:Eu^{2+}$ concentration. It is possible to change the fluorescent region through the post-processing of single rare earth ion added phosphors, and it is possible to change the fluorescence by applying the energy transfer and concentration quenching mechanism according to the local symmetry of $Eu^{3+}$ will be used for high phosphor development.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.1
• /
• pp.46-53
• /
• 2016

The structure of plasma electrolytic oxidation (PEO) coatings was investigated as a function of NaOH concentration in 0.06 M $Na_2SiO_3$ + 0.06 M $Na_3PO_4$ solution by using SEM and epoxy replica method. The PEO film was formed on AZ31 Mg alloy by the application of anodic pulse current with 0.2 ms width and its formation behavior was studied by voltage-time curves during the formation of PEO films. It was found that the addition of NaOH into $PO_4{^{3-}}$ and $SiO_3{^{2-}}$ containing aqueous solution causes a decrease in the PEO film formation voltage, suggesting that dielectric breakdown of the PEO becomes easier with increasing $OH^-$ ion concentration in the solution. With increasing $OH^-$ ion concentration, thickness of the PEO film increased and surface roughness decreased. The size of pores formed in the PEO layer became smaller and the number of cracks in the PEO layer increased with increasing $OH^-$ ion concentration. Based on the experimental results obtained in the work, it is suggested that $OH^-$ ions in the solution can contribute not only to the dielectric breakdown but also to the formation of PEO films in the presence of $PO_4{^{3-}}$ and $SiO_3{^{2-}}$ ions in the solution.

• Microbiology and Biotechnology Letters
• /
• v.5 no.3
• /
• pp.153-158
• /
• 1977

These experiments were conducted to investigate the condition of the production and the heat resistance of the acid protease by Rhizopus japonicus S-62. The results obtained were as follows: 1) The optimum concentrations of sucrose, yeast, ammonium chloride and sodium phosphate monobasic added to the wheat bran medium in the acid protease production were 0.5％, 2.0％, 0.4％, and 0.4％, respectively. 2) KH$_2$PO$_4$ and NaH$_2$PO$_4$ were the most effective as the heat resistant agents. 3) When the enzyme solutions added with KH$_2$PO$_4$ and NaH$_2$PO$_4$ to the concentration of 2％ were heated for 10 min, at 50$^{\circ}C$, their residual activities were 100％, respectively. 4) The heat resistant effects of KH$_2$PO$_4$ and NaH$_2$PO$_4$ were not observed almost above 55$^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.16 no.10
• /
• pp.624-628
• /
• 2006

In this study, divalent europium-activated $NaCaPO_4$ green phosphor powders were prepared by the chemical synthetic method followed by heat treatment in reduced atmosphere, and the crystal structures, morphologies and photoluminescent properties of the powders were investigated by x-ray powder diffraction, scanning electron microscope and spectrometer for the first time. The effects of Ca/P and Na/Ca mole ratios on the final products were also investigated. The influences of input amount change of europium as the activator on the light emission intensity were studied, and the resulting concentration quenching phenomenon was observed. The optimized synthesis conditions obtained in this study were Ca/P mole ratio 1.2, Na/Ca mole ratio 3.0 and 4 mole%Eu. The peak wavelength was 505 nm for all the samples. The result of excitation spectrum measurement indicated that the excitation efficiency was high for the long-wavelength UV region. It was thus concluded that the samples prepared in this study can be successfully applied for the light-emitting devices such as LED excited with long-wavelength UV light sources.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.95-95
• /
• 2012

In this study, the effect of $PO{_4}^{3-}$ ions on formation of PEO(Plasma Electrolytic Oxidation) films was investigated in aqueous solution. A minimum concentration of $PO{_4}^{3-}$ ions was necessary for the formation of PEO film on pure Mg and arcing voltage of pure Mg decreased with increasing $PO{_4}^{3-}$ ion concentration. Immersion test to evaluate the corrosion resistance of PEO-treated pure Mg and Mg alloys were conducted in 0.5M NaCl solution.

• The Korean Journal of Physiology
• /
• v.16 no.1
• /
• pp.69-76
• /
• 1982

The effect of parathyroid hormone on calcium and phosphate metabolism have been widely investigated, however less attention has been paid to the effect on urinary excretion. This study was performed for the purpose determining urinary excretion of Na, K, Ca, and $Po_4$, of 18 thyroparathyroidectomized (TPTX) rabbits, which were TPTX previously 7 to 10 days compared with the same normal ones. After TPTX 0.2 mg/day of synthyroid was donated to the rabbits. The concentration of electrolytes in the serum and urine was determined by the following method; Na and K were determined by means of flame photometry, Ca was by EDTA titration $method^{19)}$, and $Po_4$ by Fiske and Subba-Raw $method^{20)}$. The results as follows. The concentrations of electrolytes in the serum were 1) In the normal control rabbits (N = 25) (data, $Mean{\pm}S.E.$) $Na\;131.72{\pm}1.33\;mEq/L$, $K\;3.59{\pm}0.28\;mEq/L$, $Ca\;12.58{\pm}0.29\;mg%$, $Po_4\;4.50{\pm}\;0.45mg%$. 2) In the TPTX rabbits(N= 18) $Na\;140.6l{\pm}2.56\;mEq/L$, $K\;3.38{\pm}0.36\;mEq/L$, $Ca\;l2.18{\pm}0.45\;mg%$, $Po_4\;3.92{\pm}\;0.35\;mg%$. There was no significant change between the normal and TPTX rabbits. The concentration of elelctrolytes in the urine were variously changed. 3) In the normal rabbits. $Na\;8.40{\pm}1.09\;mEq/L$, $K\;81.59{\pm}10.19\;mEq/L$, $Ca\;16.02{\pm}3.12\;mg%$, $Po_4\;13.16{\pm}2.89mg%$. 4) In the TPTX rabbits, $Na\;14.57{\pm}3.39\;mEq/L$ slight ncreased, $K\;116.06{\pm}12.77\;mEq/L$ significant increased (P<0.05), $Ca\;18.90{\pm}5.44\;mg%$ no significant increased, $Po_4\;43.38{\pm}8.67\;mg%$ significant increased (p<0.01). The effect of TPTX was assumed that it affected upon increasing tubular secretion of $K^+$ and inhibition of the tubular reabsorption of $Po_4$.

• Korean Journal of Materials Research
• /
• v.21 no.11
• /
• pp.587-591
• /
• 2011

The effect of the precipitator (NaOH, $NH_4OH$) and the amount of the precipitator (150, 200, 250, 300 ml) on the formation of $Fe_3(PO_4)_2$, which is the precursor used for cathode material $LiFePO_4$ in Li-ion rechargeable batteries was investigated by the co-precipitation method. A pure precursor of olivine $LiFePO_4$ was successfully prepared with coprecipitation from an aqueous solution containing trivalent iron ions. The acid solution was prepared by mixing 150 ml $FeSO_4$(1M) and 100 ml $H_3PO_4$(1M). The concentration of the NaOH and $NH_4OH$ solution was 1 M. The reaction temperature (25$^{\circ}C$) and reaction time (30 min) were fixed. Nitrogen gas (500 ml/min) was flowed during the reaction to prevent oxidation of $Fe^{2+}$. Single phase $Fe_3(PO_4)_2$ was formed when 150, 200, 250 and 300 ml NaOH solutions were added and 150, 200 ml $NH_4OH$ solutions were added. However, $Fe_3(PO_4)_2$ and $NH_4FePO_4$ were formed when 250 and 300 ml $NH_4OH$ was added. The morphology of the $Fe_3(PO_4)_2$ changed according to the pH. Plate-like lenticular shaped $Fe_3(PO_4)_2$ formed in the acidic solution below pH 5 and plate-like rhombus shaped $Fe_3(PO_4)_2$ formed around pH 9. For the $NH_4OH$, the pH value after 30 min reaction was higher with the same amount of additions of NaOH and $NH_4OH$. It is believed that the formation mechanism of $Fe_3(PO_4)_2$ is quite different between NaOH and $NH_4OH$. Further investigation on this mechanism is needed. The prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and the pH value was measured by pH-Meter.

• Korean Journal of Environmental Agriculture
• /
• v.15 no.3
• /
• pp.348-354
• /
• 1996

This study was carried out to investigate factors influencing on the groundwater quality at controlled horticulture in Honam area in 1995. The deeper groundwater sampling, the lower concentrations of $NH_4-N$ and $NO_3-N$ were observed. There was no difference in concentrations of $SO_4\;^{2-}$ and $Na^+$ in the groundwater below 15m. Contents of $NH_4-N$, $NO_3-N$ and $PO_4\;^{3-}$ in groundwater were the highest at rice transplanting season(the late May) and that of $SO_4\;^{2-}$, $Na^+$ and $Cl^-$ were the highest at dry season(the mid-February). Continuous cultivation of horticultural crops showed higher concentration of $NH_4-N$, $NO_3-N$, $PO_4\;^{3-}$, $Na^+$ and $Cl^-$ in groundwater than rotational culture with rice. The longer cultivation years with horticultural crops, the higher concentrations of $NO_3-N$, $PO_4\;^{3-}$, $SO_4\;^{2-}$ and $Cl^-$ were shown, and constitutional ratio of $NO_3-N$ among the anions increased gradually. Nitrate-N level, exceeded 20mg/l, the critical level for agricultural usage, frequently at Yongjinmyeon Wanju and Janglockdong Kwangju, and $PO_4\;^{3-}$ levels were higher at Seogtandong Iksan than the other places.