• Journal of the Korean Electrochemical Society
• /
• v.2 no.2
• /
• pp.106-111
• /
• 1999

The effect of the MG on the electrochemical charge-discharge properties of $CaNi_5$ hydrogen storage alloys was investigated under Ar and $H_2$ atmosphere. $CaNi_5$ alloy was partially decomposed to CaO and Ni phase during the MG process. The decomposition of $CaNi_5$ alloy was enhanced by the MG process which leads to crash and reformation of oxide layer on the alloy surface. As the MG process time increased, initial discharge capacity of the electrode was reduced, but the decay rate of the capacity compared to $CaNi_5$ alloys was slower. It may be described that the degradation of $MG-CaNi_5$ electrode was caused by the reduction of the reversible hydrogen reaction sites and increasing polarization resistance of hydrogen adsorption resulted from phase decomposition and disorder during the MG process, and/or by hydroxide formation during the electrochemical charge-discharge cycles.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.20 no.6
• /
• pp.69-74
• /
• 2006

The effects of mechanical grinding(MG) treatment on the hydrogen storage of $Mg_2Ni$ alloy and $Mg_2Ni$ composite alloy($Mg_2Ni+graphite$) were investigated by pressure-composition-temperature(PCT) measurement, the micro-electrode technique of electrochemistry and etc, in which PCT was measured at high temperature(around $300[^{\circ}C]$) of gas phase and a carbon-filament micro-electrode for electrochemical evaluation was manipulated to make electrical contact with the particle in 1M KOH aqueous solution. It was found that the hydrogenation properties of $Mg_2Ni$ and graphite composite particle were greatly improved by the mechanical grinding treatment by which the $Mg_2Ni$ and graphite composite alloys could be changed into microstructure and nano-level particles. namely; the hydrogen dissociation pressure of PCT measurement was decreased from 0.55[MPa] to 0.42[MPa] and hydrogenation peaks by micro-electrode were also observed more clearly on the same sample.

• Korean Journal of Metals and Materials
• /
• v.48 no.3
• /
• pp.262-267
• /
• 2010

$LiNi_{1-x}Mg_xO_2$(x=0, 0.025, 0.05, 0.075, 0.1) samples were synthesized by the solid-state reaction method. The crystal structure was analyzed by X-ray powder diffraction and Rietveld refinement. $LiNi_{1-x}Mg_xO_2$samples give single phases of hexagonal layered structures with a space group of R-3m. The calculated cation-anion distances and angles from the Rietveld refinement were changed with Mg contents in $LiNi_{1-x}Mg_xO_2$. The thicknesses of $NiO_2$ slabs were increased and the distances between the $NiO_2$ slabs were decreased with the increase in Mg contents in the samples. The electrical conductivities of sintered $LiNi_{1-x}Mg_xO_2$ samples were around $10^{-2}$ S/cm at room temperature. The electrochemical performances of $LiNi_{1-x}Mg_xO_2$were evaluated by coin cell test. Compared to $LiNiO_2$, $LiNi_{0.95}Mg_{0.05}O_2$ exhibited improved high-rate capability and cyclability due to the well-ordered layered structure by doping of Mg ion.

• Transactions of the Korean hydrogen and new energy society
• /
• v.17 no.2
• /
• pp.174-180
• /
• 2006

The eutectic Mg-23.5%Ni alloy was casted by melting and solidification. The powders of Mg-23.5%Ni and (Mg-23.5%Ni)-10% iron oxide were prepared by mechanical grinding of casted Mg-Ni alloy and casted Mg-Ni alloy+oxide, respectively. As milling time increases, hydriding and dehydriding rates of Mg-Ni and Mg-Ni-oxide alloy powders increase. The additions of iron oxide to Mg-Ni alloy and Mg-Ni-oxide increase hydriding rates and slightly decrease dehydriding rates.

• Korean Journal of Metals and Materials
• /
• v.50 no.12
• /
• pp.949-953
• /
• 2012

$MgH_2$ was employed as a starting material instead of Mg in this work. A sample with a composition of 94 wt% $MgH_2-6$ wt% Ni (called $MgH_2-6Ni$) was prepared by reactive mechanical grinding. The hydriding and dehydriding properties were then examined. An $MgH_2-Ni$ hydrogen storage alloy that does not require an activation process was developed. The alloy was prepared in a planetary ball mill by grinding for 4 h at a ball disc revolution speed of 250 rpm under a hydrogen pressure of about 12 bar. The sample absorbed 3.74 wt% H for 5 min, 4.07 wt% H for 10 min, and 4.41 wt% H for 60 min at 573 K under 12 bar $H_2$, and desorbed 0.93 wt% H for 10 min, 1.99 wt% H for 30 min, and 3.16 wt% H for 60 min at 573 K under 1.0 bar $H_2$. $MgH_2-6Ni$ after reactive mechanical grinding contained ${\beta}-MgH_2$ (a room temperature form of $MgH_2$), Ni, ${\gamma}-MgH_2$ (a high pressure form of $MgH_2$), and a very small amount of MgO. Reactive mechanical grinding of Mg with Ni is considered to facilitate nucleation, and to reduce the particle size of Mg. $Mg_2Ni$ formed during reactive mechanical grinding also increases the hydriding and dehydriding rates of the sample.

• Korean Journal of Metals and Materials
• /
• v.49 no.12
• /
• pp.989-994
• /
• 2011

Samples with compositions of 80 wt% Mg-14 wt% Ni-6 wt% $Fe_2O_3$ (named $Mg-Ni-Fe_2O_3$), and 78 wt% Mg-14 wt% Ni-6 wt% $Fe_2O_3-2$ wt% CNT (named $Mg-Ni-Fe_2O_3-CNT$ ) were prepared by reactive mechanical grinding. Hydriding and dehydriding properties and effects of CNT addition on the hydriding and dehydriding rates of $Mg-Ni-Fe_2O_3$ were then investigated. Activation of the $Mg-14Ni-6Fe_2O_3$ sample was completed after three hydriding (under 12 bar $H_2$)-dehydriding (under 1.0 bar $H_2$) cycles at 573 K. The addition of CNT to the $Mg-14Ni-6Fe_2O_3$ sample made the activation process unnecessary, with a small decrease in the hydrogen-storage capacity.

• Transactions of the Korean hydrogen and new energy society
• /
• v.9 no.4
• /
• pp.151-160
• /
• 1998

The variation of the hydrogen-storage properties of Mg contained in the mechanically-allyed mixture with the weight percentage of nickel in the sample is investigated. The weight percentage of nickel transformed into the Mg2Ni phase, on the basis of the nickel weight, is highest in the Mg-10 wt.%Ni sample. For the first hydriding cycle, the effect of mechanical alloying on the hydriding rate of Mg is highest in the Mg-25 wt.%Ni sample. After activation, the effects of mechanical alloying and hydriding-dehydriding cycling on the hydriding rate of Mg are highest in the Mg-10 wt.%Ni sample. After sufficient hydriding-dehydriding cycling, the effects on the hydrogen-storage capacity of Mg are highest in the Mg-10 wt.%Ni sample. The effects on the hydriding and dehydriding rates of Mg are highest in the Mg-25wt.%Ni sample. Mg-25wt.%Ni, followed by Mg-10 wt.%Ni, is the optimum composition which has the best effects on the hydrogen-storage properties of Mg contained in the sample. The mechanical alloying and the hydriding-dehydriding cycling produce many defects, which can act as active nucleation sites, and increase the specific surface area, shortening the diffusion distance of hydrogen.

• Clean Technology
• /
• v.21 no.1
• /
• pp.39-44
• /
• 2015

This study investigated the effects of six metal oxide nanoparticles (NPs: CuO, NiO, TiO₂, Fe₂O₃, Co₃O₄, ZnO) on seed germination and germination index (G.I) for five types of seeds: Brassica napus L., Malva verticillata L., Brassica olercea L., Brassica campestris L., Daucus carota L. NPs of CuO, ZnO, NiO show significant toxicity impacts on seed activities [CuO (6-27 mg/L), ZnO (16-86 mg/L), NiO (48-112 mg/L)], while no significant effects were observed at > 1000 mg/L of TiO₂, Fe₂O₃, Co₃O₄. Tested five types of seed showed different sensitivities on seed germination and root activity, especially on NPs of CuO, ZnO, NiO. Malva verticillata L. seed was highly sensitive to toxic metal oxide NPs and showed following EC₅₀s : CuO 5.5 mg/L, ZnO 16.4 mg/L, NiO 53.4 mg/L. Mostly following order of toxicity was observed, CuO > ZnO > NiO > Fe₂O₃ ≈ Co₃O₄ ≈ TiO₂, where slightly different toxicity order was observed for carrot, showing CuO > NiO ≈ ZnO > Fe₂O₃ ≈ Co₃O₄ ≈ TiO₂.

• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.3
• /
• pp.238-245
• /
• 2017

Mg-Ni nanoparticles were synthesized by a physical vapor condensation method (DC arc-discharge) in a mixture of argon and hydrogen atmosphere, using compressed mixture of micro powders as the raw materials. The crystal phases, morphology, and microstructures of nanoparticles were analyzed by means of X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). It was found that the intermetallic compounds of $Mg_2Ni$ and $Mg_2Ni$ formed with existence of phases of Mg, Ni, and MgO in Mg-Ni nanoparticles. After one cycle of hydrogen absorption/desorption process (activation treatment), Mg-Ni nanoparticles exhibited excellent hydrogen absorption properties. $Mg_2Ni$ phase became the main phase by aphase transformation during the hydrogen treatments. The phenomenon of refinement of grain size in the nanoparticle was also observed after the hydrogen absorption/desorption processes, which was attributed to the effect of volume expansion/shrinkage and subsequent break of nanoparticles. Maximum hydrogen absorption contents are 1.75, 2.21 and 2.77 wt.% at 523, 573 and 623 K, respectively.

• Journal of the Korean Ceramic Society
• /
• v.13 no.2
• /
• pp.24-30
• /
• 1976

To observe the influence of tetrahedral and octahedral preference of cations of Ni2+, Ti4+ upon the formation and the color development of the MgO-SnO2 spinel containing Ni2+ and Ti4+ ions, the gradual substitution of Ni2+ ions for Mg2+ ions and of Ti4+ ions for Sn4+ ions of the spinel in NiO-MgO-SnO2-TiO2 system was carried out. On samples prepared by calcining the oxide and basic carbonate mixtures at 130$0^{\circ}C$ for 1.5 hour, the X-ray analysis, measurement of reflectance and the test of their stability as a glaze pigment were also carried out. On samples prepared by calcining the oxide and basic carbonate mixtures at 130$0^{\circ}C$ for 1.5 hour, the X-ray analysis, measurement of reflectance and the test of their stabiality as a glaze pigment were also carried out. The results are summarized as follows. 1) As increasing the amounts of Ni2+ ions in the xNiO.(2-x)MgO.SnO2 system, spinel was not formed easily, and the mixed-spinel was formed in NiO.MgO.SnO2 of x=1 but the spinels was not formed completely in the range of x>1.5 2) The spinels was not more formed in NiO-MgO-TiO2 system than NiO-MgO-SnO2 system. Therefore, Ti4+ ions have strong octahedral preference than Sn4+ ions. The color changed the yellow region little. The mixed-spinel or non-spinel was formed easily NiO.TiO2, MgO.TiO2 of illmenite type as the gradual substitution of Ti4+ ions for Sn4+ ions. 3) The results of glaze test. The color changed from white through graish brown to brown as the gradual substitution of Ni2+ ions for Mg2+ ions in calcium-zinc glaze and calcium glaze, and from white through light yellowish beige to dull beige in tile glaze. Also, the color did not change generally as the gradual substitution of Ti4+ ions for Sn4+ ions in NiO-MgO-SnO2-TiO2 system.