• Journal of the Korean institute of surface engineering
• /
• v.48 no.5
• /
• pp.227-232
• /
• 2015

Corrosion characteristic of the duplex Al-Mg-Si alloys with low, commercial and high solute contents were studied using an anodic polarization test in 1M NaCl solution at room temperature. Polarization range condition of the experiment were form .0.3V to .1.3V with a 0.2 mV scanning speed. The exchange current density means corrosion rate of the low solute alloy was low as about $16.29{\mu}A/cm^2$, and that of the high solute alloy was high as $84.92{\mu}A/cm^2$. The difference was mainly attributed to the inter-granular precipitates $Mg_2Si$ and Si which could make a galvanic corrosion on the aluminum base. The amount of precipitates was greater in high solute alloy at mainly in grain boundary. While, the extruded alloys had better corrosion resistance than the cast alloy because the silicon precipitates become coarse during the extrusion process.

• Journal of the Korean Ceramic Society
• /
• v.17 no.1
• /
• pp.20-26
• /
• 1980

The crystallization behaviors of slag-based glass in $CaO-MgO-Al_2O_3-SiO_2(-Na_2O)$ system have been studied. The mother glass containing 16.50 CaO, 7.50MgO, 19.70Al2O3, 50.80SiO3 and 2.09wt% $Na_2O$ was prepared by using Korean domestic raw materials such as granulated slag, serpentine, sea sand and etc. The glass-ceramics composed of major crystalline phase diopside was produced by the heat treatment in a temperature range from 850$^{\circ}$ to 9$25^{\circ}C$ for 0-6hr. The composition and morphology of diopside phase formed in the system were examined by X-ray diffraction analysis and electron microscopy. The kinetic measurements such as J.M. A plot and Arrhenius plot indicated that the process of nucleation of the initially formed diopside phase could be described from the view point of instantaneous nucleation. It was also demonstrated that the linear crystal growth of diopside phase was proceeded by short range diffusion of $Mg^{2+}$ and $Ca^{2+}$ ion. The microstructures of the resulting glass-ceramics were consisted of leafroidal shaped crystalline aggregations.

• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.241-248
• /
• 1997

RuO2 thin films were deposited on SiO2(1000$\AA$)/Si and MgO(100) single crystal substrates at low tem-peratures by hot-wall metalorganic chemical vapor deposition(MOCVD), and effects of deposition paramet-ers on the properties of the thin films were investigated. RuO2 single phase was obtained at lower de-position temperature of 25$0^{\circ}C$. RuO2 thin films deposited onto SiO2(1000$\AA$)/Si substrates showed a random orientation, and RuO2 films onto MgO(100) single crystals showed the (hk0) orientation. The crystallinity and resistivity of RuO2 thin films increased and decreased with increasing deposition temperature, respec-tively. The resistivity of RuO2 thin films decreased with decreasing the flow rate. The resistivity of the 2600$\AA$-thick RuO2 thin films deposited with O2 flow rate of 50 sccm at 35$0^{\circ}C$ was 52.7$\mu$$\Omega$-cm, and they could be applicable to bottom electrodes of high dielectric materals.

• Journal of Power System Engineering
• /
• v.18 no.6
• /
• pp.29-33
• /
• 2014

The electrochemical characteristics of Al-Si casting alloys (Al-10%Si, Al-9%Si, Al-7%Si) in 3.5% NaCl solution at room temperature was studied using potentiodynamic techniques. The electrochemical values of corrosion potential($E_c$), corrosion current density($I_c$) and corrosion rate(mpy) were examined. The Al-Si alloys had several compounds such as $Mg_2Si$, ${\pi}$-$Al_8Si_6Mg_2Fe$ and $Al_2CuMg$ which could affect corrosion resistance significantly. The potentiodynamic polarization curve exhibited typical active behavior in anodic polarization curve. The major corrosion mechansim for the Al-Si alloys were pitting and grain boundary corrosion. As increasing Si and Cu contents, their corrosion resistance was decreased.

• Korean Journal of Metals and Materials
• /
• v.47 no.6
• /
• pp.383-390
• /
• 2009

The effects that processing atmospheres and alloy composition have on the wetting characteristics of Al-Mg alloys on the $SiO_{2}$ substrate were investigated by measuring the wetting angles. It was observed that the wetting behavior of the Al-Mg alloys on the $SiO_{2}$ substrate vary depending on the Mg content of the alloys and atmospheres. The results showed that the contact angle decreases with increasing Mg content, angle is generally larger in the $N_{2}$ atmosphere than in the Ar atmosphere. We discussed the validity of the results obtained from the wetting test on the basis of recent theories and the results observed from the actual penetration tests.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.05a
• /
• pp.34-34
• /
• 2002

• Korean Journal of Materials Research
• /
• v.30 no.3
• /
• pp.111-116
• /
• 2020

Two different casting speeds of 60 and 80mm/min are adopted to determine the effect of casting speed on the microstructure and mechanical properties of Al-Mg-Si/Al hybrid material prepared by duo-casting. The obtained hybrid material has a uniform and straight macro-interface between the pure Al side and the Al-Mg-Si alloy side at both casting speeds. When the casting speed is increased to 80mm/min, the size of primary α phases in Al-Mg-Si alloy decreases, without change of shape. Although the Al-Mg-Si alloy produced at higher casting speed of 80mm/min shows much higher ultimate tensile strength (UTS) and 0.2 % proof stress and lower elongation, along with higher bending strength compared to the case of the 60mm/min in casting speed, the tensile properties and bending strength of the hybrid material, which are similar to those of pure Al, are the same regardless of the increase of casting speed. Despite the different casting speeds, deformation and fracturing in hybrid materials are observed only on the pure Al side. This indicates that the macro-interface is well-bonded, allowing it to endure tensile and bending deformation in all hybrid materials.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.2
• /
• pp.62-71
• /
• 2019

Al1050 and Al7075 alloy specimens were exposed to atmospheric conditions for 24 months and analyzed by Transmission Electron Microscopy to characterize their corrosion behavior and oxide film characteristics, especially focusing on intergranular corrosion or oxidation. In general, the intergranular oxygen penetration depth of Al1050 was deeper than Al7075. Since O and Si signals were overlapped at the oxidized grain boundaries of Al1050 and Mg is not included in Al1050, it is concluded that Si segregated along the grain boundaries directly impacts on the intergranular corrosion of Al1050. Cr-Si or Mg-Si intermetallic particles were not observed along the grain boundaries of Al7050, but Mg-Si particle was barely observed in the matrix. 10-nm size Mg-Zn particles were also found all over the matrix. Mg was mainly observed along the oxidized grain boundary of Al7075, but Si was not detected due to the Mg-Si particle formation in the matrix and relatively low concentration of Si in Al7075. Therefore, it is thought that Mg plays an important role in the intergranular corrosion of Al7075 under atmospheric corrosion conditions.

• Journal of Korea Foundry Society
• /
• v.17 no.6
• /
• pp.560-568
• /
• 1997

The dissolution behavior of secondary solidification phases in squeeze cast Al-3.9wt%Cu-1.5wt%Si-1.0wt%Mg has been studied using a combination of optical microscope, image analyzer, scanning electron microscope(SEM), energy dispersive spectrometer(EDS), X-ray diffractometer(XRD) and differential thermal analyzer (DTA). Special emphasis was placed on the investigation of the effects of the nonequilibrium heat treatment on the dissolution of the second solidification phases. Ascast microstructure consisted of primary solidification product of ${\alpha}-Al$ and secondary solidification products of $Al_2Cu$, $Mg_2Si$ and $Al_2CuMg$. Equilibrium and non-equilibrium solution treatments were carried out at the temperatures of $495^{\circ}C$, $502^{\circ}C$ and $515^{\circ}C$ for 3 to 5 hours. The amount of the dissolved secondary phases increased with increasing solution treatment temperature, for example, area fractions of $Al_2Cu$, $Mg_2Si$ and $Al_2CuMg$ were approximately 0%, 1.6% and 4.2% after solution treatment at $495^{\circ}C$ for 5hours, and were approximately 0%, 0.36% and 2% after solution treatment at $515^{\circ}C$ for 5hours. The best combination of tensile properties was obtained when the as-cast alloy was solution treated at $515^{\circ}C$ for 3hours followed by aging at $180^{\circ}C$ for 10 hours. Detailed DTA and TEM study showed that the strengthening behavior during aging was due to enhanced precipitation of the platelet type fine ${\theta}'$ phase.

• Journal of Technologic Dentistry
• /
• v.21 no.1
• /
• pp.5-14
• /
• 1999

Glass ceramics for dental crown prosthesis were prepared by crystallization of CaO-MgO-SiO2-$P_2O_5-TiO_2$ glasses. Their crystallization behaviors have been investigated as a function of heattreatment temperature, holding time and chemical composition in relation to mechinical properties. Crystallization peak temperatures were determined by differential thermal analysis(DTA). Crystalline phases and mircostructures of heat-treated sample were determined by the means of powder X-ray diffraction(XRD) and scanning electron microscopy(SEM). The final crystalline phase assemblages and the microstructures of the samples were found to be dependent on glass compositions, heattreatment temperature, and holding time. 1st crystallization peak temperature(TP), affected strongly by apatite, was found to be increased or decreased. From the experiment, the following results were obtained : 1. The crystallization peak temperature($T_P$) formed by apatite increased until adding up to 9wt% $TiO_2$ to base glass composition, then decreased above that. 2. Apatite($Ca_{10}P_6O_{25}$), whitlockite(${\beta}-3CaO-P_2O_5$), $\beta$-wollastonite($CaSiO_3$), magnesium tianate($MaTiO_3$) and diopside(CaO-MgO-$2SiO_2$) crystal phase were precipitated in MgO-CaO-$SiO_2-TiO_2-P_2O_5$ glass system containing 9wt% and 11wt% of $TiO_2$ 3. Vickers hardness of samples increased with increasing heat-treatment temperature and Vickers hardness of S415T9 samples heat-treated at 1075 was approxi-mately 813Kg $mm^{-2}$ as maximum value. 4. Vickers hardness of samples increased due to precipitation of apatite, whitlockite, $\beta$-wollastonite, magnesium titanate, and diopside crystal phases within glass matrix.