• 한국전기전자재료학회논문지
• /
• 제11권1호
• /
• pp.62-66
• /
• 1998

M$\ddot{o}$ssbauer spectra of ferrimagnetic $Fe_2SE_8$ prepared with $^{57}Fe$ enriched iron have been taken at 298 K and below 78K, and Fe\ulcornerSe\ulcorner has been studied by X-ray diffraction. The crystal structure is found to be a "3c" hexagonal superstructure of the NiAs structure. Three sets of six-line hyperfine patterns were obtained and assigned to three magnetically nonequivalent sites of a superstructure of the crystal. The iron ions at all three sites are found to be in a highly covalent ferrous state. It is shown that the results obtained at the low temperature region are well consistent with Okazaki's "3c" superstructure model.uperstructure model.

• 한국자기학회지
• /
• 제19권3호
• /
• pp.106-112
• /
• 2009

상온에서 준강자성을 띠는 $Ni_{1-x}Mg_xFe_2O_4$ ferrite 내에 존재하는 금속양이온 Ni을 Mg로 대치시킬 때 나타나는 결정학적 구조의 변화와 자기적 성질 변화, 그리고 양이온의 분포를 X-선 회절무늬와 $M{\ddot{o}}ssbauer$ spectrum을 측정하고 분석하여 연구하였다. $NiFe_2O_4$ ferrite의 $M{\ddot{o}}ssbauer$ spectrum 공명흡수면적비(oct/tet)는 1.007로서 거의 완전한 inverse spinel 구조를 형성하나 Mg의 함량인 x가 증가함에 따라 Mg 이온이 tetrahedral site를 점유하게 되어 면적비(oct/tet)가 점차 증가하여 $MgFe_2O_4$의 경우 1.449로서 불완전한 inverse spinel 구조를 형성한다. 시료들의 isomer shift 값으로부터 $Ni_{1-x}Mg_xFe_2O_4$ ferrite계 내에 존재하는 Fe는 $Fe^{3+}$ 상태임을 알 수 있다. 비자성 이온인 Mg의 함량이 증가함에 따라 최인접 금속 양이온에 의해 발생되는 A-B exchange interaction이 발생할 확률이 작아져서 magnetic hyperfine field가 감소하며 Yafet-Kittel 자기구조를 나타낸다.

• 비파괴검사학회지
• /
• 제20권3호
• /
• pp.183-190
• /
• 2000

본 연구에서는 고속 중성자가 조사된 원자로 용기 재료의 자기적 성질 변화를 $M{\ddot{o}}ssbauer$ 분광법을 이용하여 측정하였으며, X-선 회절실험을 이용하여 중성자 조사재료의 결정성 변화를 평가하였다. 시편은 크기가 $23mm{\times}18mm{\times}70{\mu}m$로 제작되었으며, 343K에서 $10^{12}n/cm^2{\sim}10^{18}n/cm^2$의 범위에서 중성자 조사를 하였다. X-선 회절실험 결과로부터, $10^{16}n/cm^2$의 중성자가 조사된 시료에서부터 결정성이 변화가 시작되고, $10^{17}n/cm^2$ 이상의 중성자가 조사된 시료에서 결정성이 심각하게 손상되는 것이 관찰되었다. 또한 $M{\ddot{o}}ssbauer$ 분광실험으로부터 중성자 조사량이 $10^{16}n/cm^2$ 이하인 시료에서는 자기적성질의 변화가 관찰되지 않았으나, $10^{17}n/cm^2$ 이상의 중성자가 조사된 시료에서 자기완화 현상이 일어나는 것이 관찰되었다. 따라서 두 실험 모두 비파괴적 실험방법에 따른 중성자 조사취화 평가로 활용이 가능한 것으로 평가되었다.

• 한국자기학회지
• /
• 제15권2호
• /
• pp.125-129
• /
• 2005

$A1_2O_3$ 기판을 하지층으로 하는 Ba-ferrite 박막을 pulsed laser deposition system으로 제조하여 결정학적 및 자기적 성질을 SEM, $M\ddot{o}ssbauer$ 분광법 및 VSM을 사용하여 연구하였다. Ba-ferrite박막은 $A1_2O_3$ 기판위에 PLD를 이용하여 기판온도 $400^{\circ}C$, 산소압력 0.1 Torr로 증착 하였고 증착 시간을 달리하여 두께 조절하였다. Ba-ferrite 박막은 5분 증착한 시료에서만 판상으로 결정이 형성되었음을 볼 수 있고 그보다 두꺼운 시료의 경우에는 침상모양과 판상모양이 임의의 방향으로 혼재되었음을 확인하였다. $M\ddot{o}ssbauer$ssbauer 분광법으로부터 측정된 Ba-ferrite결정 내 Fe 원자의 스핀 방향은 두께가 얇을수록 판상의 결정이 많이 존재하여 기판에 수직으로 정렬하려는 경향을 보이고 있다. VSM으로 측정한 자기이력곡선은 판상과 침상의 상이한 2가지 형태가 공존하는 것으로 나타났다.

• Journal of Magnetics
• /
• 제7권2호
• /
• pp.40-44
• /
• 2002

Crystallographic and magnetic properties of ;$LaFe_{1-x}Ga_xO_3$($\chi$= 0, 0.1, 0.3, 0.5, and 0.7) were studied using XRD and Mossbauer spectroscopy. The crystal structures were found to be orthorhombic and the lattice parameters $\alpha$, b, and c were found to decrease with increasing Ga substitution. M$\ddot{o}$ssbauer spectra were obtained at various absorber temperatures ranging from 20 K to 750 K. The M$\ddot{o}$ssbauer spectra were all sextets below $T_N$ and were all singlets above $T_N$. Asymmetric broadening of the M$\ddot{o}$ssbauer spectral lines at 20 K was explained by the multitude of possible environments for an iron nucleus. As the temperature increases to $T_N$, a systematic line broadening in M$\ddot{o}$ssbauer spectra was observed and interpreted to originate from different temperature dependencies of the magnetic hyperfine fields at various iron sites.

• Journal of Magnetics
• /
• 제17권2호
• /
• pp.83-85
• /
• 2012

Magnetic particles in a novel, wound-healing ointment were studied using M$\ddot{o}$ssbauer spectroscopy and VSM to estimate the stability of the properties of the magnetic particles. The isomer shifts of $Fe_3O_4(A)$ were found to be 0.49-0.56 mm/s relative to iron metal, this indicates that the iron ions in $Fe_3O_4(A)$ are $Fe^{3+}$. On the other hand, the isomer shifts of $Fe_3O_4(B)$ were found to be 0.91-1.13 mm/s relative to iron metal, this shows that the ion state of $Fe_3O_4(B)$ is a mixed state of $Fe^{2+}$ and $Fe^{3+}$. It is noted that this composition, as well as that of the initial pure component in the form of a highly dispersed fraction (${\sim}10\;{\AA}$), differs from the stoichiometric one. It was found that the area ratio of the M$\ddot{o}$ssbauer subspectra of $Fe_3O_4(A)$ / $Fe_3O_4(B)$ taken at 87 and 181 K linearly increased in comparison to the initial pure magnetic particles, but the rate of increase of the area ratio at 181 K was about two times that at 87 K. From the magnetic hyperfine field, despite their small size, the particles exhibit no superparamagnetism.

• Journal of the Korean Physical Society
• /
• 제73권11호
• /
• pp.1708-1711
• /
• 2018

The polycrystalline sample of $Ba_2Co_{1.5}Mg_{0.5}Fe_{11.88}Ga_{0.12}O_{22}$ Y-type hexaferrite, doped with Ga-cation, was prepared by using the solid-state reaction method. The crystalline structure of sample was investigated by x-ray diffractometer (XRD), and the magnetic properties of sample were measured by vibrating sample magnetometer (VSM), and $M{\ddot{o}}ssbauer$ spectrometer. The crystal structure of prepared sample was determined to be rhombohedral with space group R-3m. From the temperature dependence of the magnetization curves under 100 Oe between 4.2 and 740 K, two temperature-dependent magnetic transitions occurred in the $Ba_2Co_{1.5}Mg_{0.5}Fe_{11.88}Ga_{0.12}O_{22}$ sample. $M{\ddot{o}}ssbauer$ spectra of the sample were analyzed at various temperatures ranging from 4.2 to 620 K, and the $Ba_2Co_{1.5}Mg_{0.5}Fe_{11.88}Ga_{0.12}O_{22}$ sample showed abrupt changes in $H_{hf}$ and $E_Q$ at 200 K, indicating the spin transition effect. We have also determined the magnetic transition temperature $T_C$, in addition to the temperature dependent magnetization and ZVC measurements.

• Journal of Magnetics
• /
• 제21권3호
• /
• pp.303-307
• /
• 2016

$Y_{3-x}R_xFe_5O_{12}$ (R = La, Nd, and Gd) powder were fabricated using a sol-gel pyrolysis method. Their magnetic properties and crystalline structures were investigated using x-ray diffraction (XRD), a vibrating sample magnetometer (VSM), and $M{\ddot{o}}ssbauer$ Spectrometer. The $M{\ddot{o}}ssbauer$ spectra for the powders were taken at various temperatures ranging from 12 K to Curie temperature (Tc). The isomer shifts indicated that the valence states of Fe ions for the 16(a) and 24(d) sites have a ferric character. The saturation magnetization (Ms) increases from 32 to 34 (emu/g) for the YIG, and Nd-YIG, respectively. However, Ms decreases to 27 (emu/g) at Gd-YIG.

• 한국자기학회지
• /
• 제20권3호
• /
• pp.114-119
• /
• 2010

울릉도의 해안지역에서 채취한 화산암 시료에 대하여 X-선 회절분석 실험, X-선 형광 분광 분석 및 M$\ddot{o}$ssbauer 분광 분석으로 물리적 특성을 조사하여 화산암의 화학적 조성과 시료 내에 존재하는 Fe의 원자가 상태와 자기적 성질을 연구하였다. X-선 형광분광 분석의 결과로부터 울릉도 해안지역의 화산암은 지역에 따라 적철석인 hematite($\alpha-Fe_2O_3$)를 포함한 총 철 화합물의 양이 10.6 w%에서 14.5 w%인 전형적인 염기성암인 것을 알 수 있었다. M$\ddot{o}$ssbauer 분광 분석 결과로부터 울릉도 해안지역의 모든 시료에서 hematite에 의한 6중선의 공명 흡수선과 다양한 clay mineral에 포함된 $Fe^{3+}$에 의한 2중선의 공명흡수선이 나타나고 있으며, pyroxene($(Ca,Fe,Mg)_2(SiO_4)_2$)과 ilmenite($FeTiO_3$) 그리고 olivine($(Mg,Fe)_2SiO_4$) 들에 포함되어 있는 $Fe^{2+}$에 의한 2중선의 공명흡수선들도 나타나고 있음을 알 수 있었다. 또한 모든 시료들에서 철 화합물들이 주로 $Fe^{3+}$의 산화철 형태로 존재하므로 울릉도 해안지역의 염기성 화산암들은 육상형성 화산암임을 알 수 있다.

• Journal of Magnetics
• /
• 제20권3호
• /
• pp.246-251
• /
• 2015

This study was aimed to study the effect of Zn content on the hyperfine parameters and the structural variation of $Ni_{1-x}Zn_xFe_2O_4$ for x = 0, 0.2, 0.4, 0.6, and 0.8. To achieve this, a sol-gel route was used for the preparation of samples and the obtained ferrites were investigated by X-ray diffraction, scanning electron microscopy, and $M{\ddot{o}}ssbauer$ spectroscopy. The formation of spinel phase without any impurity peak was identified by X-ray diffraction of all the samples. Moreover, the estimated crystallite size by X-ray line broadening indicates a decrease with increasing Zn content. This result was in agreement with the scanning electron microscopy result, indicating the reduction in grain growth with further zinc substitution. The room-temperature $M{\ddot{o}}ssbauer$ spectra show that the hyperfine fields at both the A and B sites decreased with increasing Zn content; however, the rate of reduction is not the same for different sites. Moreover, the best fit parameter showed that the quadrupole splitting values of B site increased from the pure nickel ferrite to the sample with x = 0.8.