• Applied Chemistry for Engineering
• /
• v.31 no.1
• /
• pp.97-102
• /
• 2020

Recently, various degradation mechanisms of lithium secondary battery cathode materials have been revealed. As a result, many studies on overcoming the limitation of cathode materials and realizing new electrochemical properties by controlling the degradation mechanism have been reported. Li-rich layered oxide is one of the most promising cathode materials due to its high reversible capacity. However, the utilization of Li-rich layered oxide has been restricted, because it undergoes a unique atomic structure change during the cycle, in turn resulting in unwanted electrochemical degradations. To understand an atomic structure deterioration mechanism and suggest a research direction of Li-rich layered oxide, we deeply evaluated the atomic structure of 0.4Li₂MnO₃_0.6LiNi_1/3Co_1/3Mn_1/3O₂ Li-rich layered oxide during electrochemical cycles, by using an atomic-resolution analysis tool. During a charge process, Li-rich materials undergo a cation migration of transition metal ions from transition metal slab to lithium slab due to the structural instability from lithium vacancies. As a result, the partial structural degradation leads to discharge voltage drop, which is the biggest drawback of Li-rich materials.

• Journal of Powder Materials
• /
• v.21 no.2
• /
• pp.131-136
• /
• 2014

Cathode materials and their precursors are prepared with transition metal solutions recycled from the the waste lithium-ion batteries containing NCM (nickel-cobalt-manganese) cathodes by a $H_2$ and C-reduction process. The recycled transition metal sulfate solutions are used in a co-precipitation process in a CSTR reactor to obtain the transition metal hydroxide. The NCM cathode materials (Ni:Mn:Co=5:3:2) are prepared from the transition metal hydroxide by calcining with lithium carbonate. X-ray diffraction and scanning electron microscopy analyses show that the cathode material has a layered structure and particle size of about 10 ${\mu}m$. The cathode materials also exhibited a capacity of about 160 mAh/g with a retention rate of 93~96% after 100 cycles.

• Journal of the Korean Electrochemical Society
• /
• v.17 no.3
• /
• pp.149-155
• /
• 2014

In this study, a positive-electrode material in a lithium secondary battery $Li[Ni_{0.575}Co_{0.1}Mn_{0.325}]O_2$ was synthesized as precursor by co-precipitation. Cathode material was synthesized by adding iron. The synthesized cathode material was analyzed by scanning electron microscope and x-ray diffraction. The analysis of x-ray diffraction showed that the a-axis and c-axis is increased by doping iron. And $I_{(003)}/I_{(104)}$ is increased and $I_{(006)}+I_{(102)}/I_{(101)}$ is decreased. Through this result, it was confirmed that the structural stability is improved. And impedance measurements show that the charge transfer resistance ($R_{ct}$) is lowered by doping iron. Consequently, electrochemical properties are improved by doping iron. In particular, the cycle characteristics are improved at a high temperature condition (328 K). Structural stabilities are contributing to the cycle properties.

• Resources Recycling
• /
• v.30 no.6
• /
• pp.28-35
• /
• 2021

An experiment was conducted to separate or recover Co and Ni using Cyanex 301 from process by-products and waste resources containing Co and Ni. To separate and recover Co and Ni from simulated leaching solutions, 10 v/v% Cyanex 301 was used as an extractant in this study; Li was not extracted. At equilibrium pH 1.5 and a phase ratio (A/O) of 1.0, 0.44% of Mg and 11.57% of Mn were extracted, and more than 99% of Co and Ni were extracted. McCabe-Thiele diagram analysis confirmed that more than 99.9% of Co and Ni could be extracted simultaneously through two-stage extraction with an extraction phase ratio (A/O) of 2. It was possible to extract Mg and Mn simultaneously through the scrubbing process. In the scrubbing process, more than 99% of Mg and 87% of Mn were scrubbed using 0.05 M of H₂SO₄, and 99.9% of Mg and more than 80% of Mn were scrubbed using 0.05 M of HCl. In the stripping process, 93% of Co and 5% of Ni were stripped selectively by 3.0 M of H₂SO₄. However, when 8.0 M of HCl was used as a stripping solution, more than 99.9% of Co and more than 90% of Ni were stripped simultaneously.

• Applied Chemistry for Engineering
• /
• v.35 no.3
• /
• pp.182-191
• /
• 2024

Li(Ni_xCo_yMn_1-x-y)O₂ (NCM) is the intensively developed cathode material for expanding the electric vehicle market and developing lithium-ion batteries that meet higher capacity, longer life, and lower cost. High-nickel NCM increases the nickel content to 80% or more, securing price competitiveness by improving performance with high energy density and reducing the cost of cobalt. However, the high-nickel NCM materials have a residual lithium problem, leading to issues in battery performance degradation and stability. While various methods exist for removing residual lithium, such as washing, doping, and coating, this paper focuses on recent research trends in coatings aimed at enhancing NCM performance and stability by removing residual lithium.

• Transactions on Electrical and Electronic Materials
• /
• v.18 no.6
• /
• pp.334-337
• /
• 2017

In this paper, to develop the ceramics with high $d_{33}$ and high $Q_m$ for ultrasonic transducer applications, $0.10Pb(Ni_{1/3}Nb_{2/3})O_3-0.07Pb(Mn_{1/3}Nb_{2/3})O_3-0.83Pb(Zr_{0.5}Ti_{0.5})_{0.83}O_3$ (PNN-PMN-PZT) ceramics were sintered at $940^{\circ}C$ using $CuO-Li_2CO_3-Bi_2O_3$ (CLBO) as a sintering aid by a traditional solid-state technique. The influence of zinc oxide additive on the physical properties of the prepared ceramics were systematically investigated. The R-T (rhombohedral-tetragonal) phase coexistence was found in the ceramics without zinc oxide additive and with increasing amounts of ZnO additive, the specimens showed a tetragonal phase. The formation of a liquid phase between ZnO and $Bi_2O_3$ contributed significantly to the grain growth of specimens. For the 0.1 wt% ZnO ceramics, the optimal physical properties of $d_{33}=370pC/N$, ${\varepsilon}_r=1,344$, $k_p=0.621$, and $Q_m=1,523$ were obtained.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1337-1338
• /
• 2007

In this study, in order to develop low temperature sintering ceramics for multilayer piezoelectric actuator, 0.07Pb$(Mn_{1/3}Nb_{2/3})O_{3}-xPb(Ni_{1/3}Nb_{2/3})O_{3}-(0.93-x)Pb(Zr,Ti)O_{3}$ ceramics system were fabricated using $Li_{2}CO_{3}-Bi_{2}O_{3}$-CuO sintering aids and the specimens were sintered at $930^{\circ}C$. Thereafter their piezoelectric and dielectric characteristics were investigated with the amount of PNN substitution. At 9[mol%] PNN substitution, electromechanical coupling factor (kp), mechanical quality factor (Qm) and piezoelectric constant ($d_{33}$) showed the optimum value of 0.60, 1323 and 387pC/N, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.05a
• /
• pp.113-116
• /
• 2006

자발착화 연소반응법 (Glycine Nitrate Process)을 응용한 초음파분무열분해장치를 이용하여 이차전지의 양극재료인 Ni치환형 $LiMn_2O-4$ 분말을 합성하였고, 각각의 하소온도에 따른 분말의 특성을 평가하였다. 전구용액은 산화제로 $Mn(NO_3)_2{\cdot}6H_20$EX>, $LiNO_3$, $Ni(NO_3)_2{\cdot}6H_20$를 사용하였고, 자발착화 에너지를 공급하기 위한 연료로는 glycine를 사용하였다. 분말의 결정상을 확인하기 위해 X-선 회절 시험을 시행하였으며, 각각의 조성별로 ICP측정결과 여러 조성들($LiNi_xNm_{2-x}O_4\;0{\leq}x{\leq]0.5$) 중 $LiNi_{0.3}Nm_{1.7}O_4$의 분말이 비교적 우수한 특성을 나타내었지만, 전기화학적 특성 평가 결과 이론용량값에 미치지 못하는 용량값을 나타내었다. 이것은 분말 합성 시 미량의 미 반응된 유기물들이 분말 표면에 피복되어 전기적 성질을 변화시키고 있기 때문임을 확인하였다. 이러한 특성을 개선하고자 추가적으로 하소 공정을 실시하여 전지의 성능를 평가 하였다. 분말의 미세구조와 형태, 크기, 전기 화학적 특성을 관찰하여 하소 전 후의 분말을 비교하였다.

• Resources Recycling
• /
• v.28 no.6
• /
• pp.79-86
• /
• 2019

Recently, the use of lithium ion battery(LIB) has increased. As a result, the price of lithium and the amount spent lithium on ion battery has increased. For this reason, research on recycling lithium in waste LIBs has been conducted1). In this study, the effect of roasting for the selective lithium leaching from the spent LIBs is studied. Chemical transformation is required for selective lithium leaching in NCM LiNi_xCo_yMn_zO₂) of the spent LIBs. The carbon in the waste EV cell powder reacts with the oxygen of the oxide at high temperature. After roasting at 550 ~ 850 ℃ in the Air/N₂ atmosphere, the chemical transformation is analysed by XRD. The heat treated powders are leached at a ratio of 1:10 in D.I water for ICP analysis. As a result of XRD analysis, Li₂CO₃ peak is observed at 700 ℃. After the heat treatment at 850 ℃, a peak of Li₂O was confirmed because Li₂CO₃ is decomposed into Li₂O and CO₂ over 723 ℃. The produced Li₂O reacted with Al at high temperature to form LiAlO₂, which does not leach in D.I water, leading to a decrease in lithium leaching ratio. As a result of lithium leaching in water after heat treatment, lithium leaching ratio was the highest after heat treatment at 700 ℃. After the solid-liquid separation, over 45 % of lithium leaching was confirmed by ICP analysis. After evaporation of the leached solution, peak of Li₂CO₃ was detected by XRD.

• Journal of Electrochemical Science and Technology
• /
• v.7 no.2
• /
• pp.179-184
• /
• 2016

The interface between the surface of a cathode material and the electrolyte gives rise to surface reactions such as solid electrolyte interface (SEI) and chemical side reactions. These reactions lead to increased surface resistance and charge transfer resistance. It is consequently necessary to improve the electrochemical characteristics by suppressing these reactions. In order to suppress unnecessary surface reactions, we coated cathode material using polypropylene (PP). The PP coating layer effectively reduced the SEI film that is generated after a 4.3 V initial charging process. By mitigating the formation of the SEI film, the PP-coated Li[(Ni_0.6Co_0.1Mn_0.3)_0.36(Ni_0.80Co_0.15Al0.05)_0.64)]O₂(NCS) electrode provided enhanced transport of Li⁺ ions due to reduced SEI resistance (R_SEI) and charge transfer resistance (R_ct). The initial charge and discharge efficiency of the PP-coated NCS electrode was 96.2 % at a current density of 17 mA/g in a voltage range of 3.0 ~ 4.3 V, whereas the efficiency of the NCS electrode was only 94.7 %. The presence of the protective PP layer on the cathode improved the thermal stability by reducing the generated heat, and this was confirmed via DSC analysis by an increased exothermic peak.