• Journal of the Korean Ceramic Society
• /
• v.35 no.3
• /
• pp.280-286
• /
• 1998

LaAlO3 Single crystals used as a substrate for thin film depositions of a high temperature oxide su-perconductor YB2Cu3O7 and applied to microwave frequencies were grown by the Traveling Solvent Flati-ing Zone (TSFZ) method and characterized. For the growth of LaAlO3 single crystals polycrystalline fe-edrods were prepared from powder mixture of La2O3 and Al2O3 with a mole ratio of 1:1 calcined at 110$0^{\circ}C$ for 3h and sintered at 140$0^{\circ}C$ for 4h The growth LaAlO3 crystals was 4-5mm in diameter 30mm in length and dark brown. The growth rate was 2-3mm/h and the rotation speeds were 10rpm for an upper ro-tation and 40 rpm for a lower rotation The growing crystals and the feedrods were counter-rotated. The orientation of the grown single crystals of LaAlO3 was identified to be [111] direction. Dielectric constants were measured to be 30-33 between 100 kHz and 1 MHz in the 30$0^{\circ}C$ to 45$0^{\circ}C$ temperature range and 102 in a range of 100 kHz at the phase transformation temperature of 522$^{\circ}C$ Dielectric losses were calculated to be 1.8$\times$10-4 at the room temperature and 5.7$\times$10-3 at the phase transformation temperature. Lattice con-stants of the grown crystlals were determined to be aR=5.3806 $\AA$ and $\alpha$=60.043$^{\circ}$ by the least square method.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2003.06a
• /
• pp.220-221
• /
• 2003

Equiatomic FePt and CoPt alloy thin films have received considerable attention as possible magnetic and magneto-optic recording because of their high magnetic anisotropy energy and high coercivity. The high coercivity in these thin films is due to the presence of finely dispersed ordered FePt phase mixed with disordered FePt phase. However, a high temperature treatment, either substrate heating during deposition or post annealing, is needed to obtain the ordered L1$\_$0/ phase with high value of magneto crystalline anisotropy. Recent microstructural studies on these films suggest that the average grain size ranges from 10-50 nm and the grains are magnetically coupled between each other. On the other hand, the ultrahigh-density magnetic recording media with low media noise imposes the need of a material, which consists of magnetically isolated grains with size below 10 nm. The magnetic grain isolation can be controlled by the amount of additional non-magnetic element in the system which determines the interparticle separation and therefore the interparticle interactions. Recently, much research work has been done on various non-magnetic matrices. Preliminary studies showed that the samples prepared in B$_2$O$_3$ and Carbon matrices have shown strong perpendicular anisotropy and fine grain size down to 4nm, which suggest these nanocomposite films are very promising and may lead to the realization of a magnetic medium capable of recording densities beyond 1 Tb/in$^2$. So, in this work, the effect of Carbon doping on the magnetic properties of FePt nanoparticles were investigated.

• Journal of the Korean Magnetics Society
• /
• v.11 no.4
• /
• pp.168-172
• /
• 2001

Co-Zn ferrite thin films grown on thermally oxidized silicon wafers were fabricated by a sol-gel method. Magnetic and structural properties of Co-Zn thin films were investigated by using x-ray diffractometer (XRD), atomic force microscopy (AFM), auger electron spectroscopy (AES) and a vibrating sample magnetometer (VSM). Co-Zn ferrite thin films annealed at 400 $^{\circ}C$ presented have only a single phase spinel structure without any preferred crystallite orientation. Their surface roughness of Co-Zn ferrite thin films was shown as less than 3 nm and the grain size was about 40 nm for annealing temperatures over 600 $^{\circ}C$. A moderate saturation magnetization of Co-Zn ferrite thin films for recording media was obtained in this study and there is no significant difference of their magnetic property with those external fields of parallel and perpendicular to planes of the films. The maximum value of the coercivity was obtained as 1,900 Oe for Co-Zn ferrite thin film annealed at 600 $^{\circ}C$.

• Journal of the Korean Magnetics Society
• /
• v.5 no.1
• /
• pp.42-47
• /
• 1995

FeN thin films for inductive recording heads were sputter deposited using RF diode sputtering mehtod from a pure iron target onto 7059 glass substrates, and their magnetic properties were measured. The magnetic properties were greatly affected by film thickness, gas pressure, sputter power and flow ratio of $N_{2}$ to Ar. Single layer FeN films with their thickness varied from $1,000\;{\AA}$ to $6,000\;{\AA}$ were doposited. 800 W sputter power, 3 mT gas pressure, $N_{2}$ to Ar flow ratio of 6.6 : 100 were the sputtering conditions. Up to 7 layers of FeN films having total thickness of $6,000\;{\AA}$ were deposited using $SiO_{2}$ of $30\;{\AA}$ thickness as intermediate layers and their coercivity and saturation magnetization were measured. The sputtering conditions were the same as those in the single layer films. Easy axis coercivity of the single layer FeN films gradually decreased as their thickness was increased, but for the films with their thicknesses above $3,000\;{\AA}$, the coercivity changed very little. As the number of the FeN layers were increased, the coercivity decreased We estimated the grain size of FeN films from the FWHM (Full Width at Half Maximum) of X-ray diffraction peaks. The grain size steadily decreased from about $200\;{\AA}$ to $120\;{\AA}$ as the number of layers were increased. Minimum hard axis coercivity of 0.4 Oe was obtained when the number of layers was four. Maximum relative permeability was 2,900 when the number of layers was three. The cut off frequeocy of the multilayer films were above 100 MHz.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.08a
• /
• pp.285-293
• /
• 2004

Oxidation behavior of 304 and 430 stainless steel were studied using thin film X-ray analysis and glow discharge spectrum analysis (here-after GDS). The oxidation layer of 304 stainless steel was composed of $Cr_2O_3\;and\;FeCrO_4$ and its thickness was about $1.5{\mu}m$ after $1\~5$ minutes of annealing at $1120^{\circ}C$ open air. However, the oxidation layer of 430 stainless steels was mainly composed of $Cr_2O_3$ and its typical thickness was 0.5um after $1\~5$ minutes of annealing at $1000^{\circ}C$ open air. Electro-chemical analysis revealed that the descaling of oxidation layer could be activated by Fe, Cr dissolution from the matrix behind the oxidation layer at the current density of $5\~10ASD$ and by Fe, Cr-oxide dissolution from the oxidation layer at the current density over than 10ASD. Electrolytic stripping of 430 and 304 revealed the intial incubation period of descaling by oxygen evolving at low current density range such as $5\~10ASD$. However the dissolution of oxide layer was occurred when applying the anodic current of $10\~20ASD$ on 430 and 304 stainless steels. It was suggested that the electrolytic pickling of high Cr bearing stainless steel such as 430 and 304 seemed to be the more effective in the high current density range such as $10\~20ASD$ than the low current density range such as $5\~10ASD$.

• Journal of Surface Science and Engineering
• /
• v.27 no.3
• /
• pp.158-165
• /
• 1994

Cu-Cr alloy thin film requires good quality of etching be used for TAB technology. The etched cross sec-tion was clean enough when the etching was performed in 0.1M $FeCl_3$ solution at $50^{\circ}C$. The etching rate was increased with the amount of $KMnO_4$. For enhanced profile of cross section and rate, the spray etchning was found to be superior compared to the immersion etching. A series of experiments were performed to improve the uniformity of the current distribution in electrodeposition onto the substrate with lithographic patterns. Copper was electrodeposited from quiescent-solution, paddle-agitated-solution, and air-bubbled-solution to in-vestigate the effect of the fluid flow. The thickness profile of the specimen measured by profilmetry has the non uniformity at feature scale in quiescent-solution, because of the longitudinal vortex roll caused by the natural convection. However, uniform thickness profile was achieved in paddle-agitated or air bubbled solu-tion.

• The Korean Journal of Ceramics
• /
• v.1 no.2
• /
• pp.91-95
• /
• 1995

Polycrystalline bismuth- and aluminum- substituted dysporsium and yttrium iron garnet (Bi2R3-xAlyFe5-yO12, R=Dy or Y, $0\leqx\leq3, \; 0\leqy\leq3$) films have been prepared by pyrolysis. The crystallization temperatures, the solubility limit of bismuth ions into the garnet phase, and magnetic and magneto-optic properties of the films have been investigated as a function of bismuth and aluminum concentration. It was found that the crystallization temperatures as a function of bismuth and aluminum concentration. It was found that the crystallization temperatures of these films rapidly decreased as bismuth concentration. It was found that the crystallization temperatures of these films rapidly decreased as bismuth concentration (x) increased up to x=1.5 and then remained temperatures of these films rapidly decreased as bismuth concentration (x) increased up to x=1.5 and then remained unchanged at x>1.5, whereas, showed no changes as aluminum concentration (y) increased up to y=1.0 and then gradually increased at y>1.0. The solubility limit of bismuth ions was x=1.8 when y=0 but increased to x=2.3 when y=1.0. It was demonstrated that the magnetic and magneto-optic properties of the dysprosium iron garnet films could be tailored by bismuth and aluminum substitution suitable for magneto-optic recording as follows. The saturation magnetization and coercivity data obtained for the films indicated that the film composition at which the magnetic compensation temperature became room temperature was y=1.2 when x=1.0. Near this composition the coercivity and the squareness of the magnetic hysteresis loop of the films were several kOe and unit, respectively. The Curie temperatures of the films increased with the increase of x but decreaed with the increase of y, and was 150-$250^{\circ}C$ when x=1.0 and y=0.6-1.4. The Faraday rotation at 633 nm of the films increased as x increased but decreased as y increased, and was 1 deg/$\mu\textrm{m}$ when x=1.0 and y=1.0. Based on the data obtained, the appropriate film composition for magneto-optic recording was estimated as near x=1.0 and y=1.0 or $BiDy_2AlFe_4O_{12}$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.277-277
• /
• 2007

$(Bi,La)_4Ti_3O_{12}$ (BLT) 물질은 결정 방향에 따른 강한 이방성의 강유전 특성을 나타낸다. 따라서 BLT 박막을 이용하여 FeRAM 소자 등을 제작하기 위해서는 결정의 방향성을 세심하게 제어하는 것이 매우 중요하다. 현재까지 연구된 BLT 박막의 방향성 조절 결과를 보면, BLT 박막을 스핀 코팅 법 (spin coating method)으로 중착하고, 핵생성 열처리 단계를 조절하여 무작위 방향성 (random orientation)을 갖는 박막을 제조하는 방법이 일반적이었다. 그런데 이러한 스핀 코팅법에서의 핵생성 단계의 제어는 공정 조건 확보가 너무 어려운 단점이 있다. 이러한 어려움을 극복할 수 있는 대안은 스퍼터링 증착법 (sputtering deposition method), PLD법 (pulsed laser deposition method) 등과 같은 PVD (physical vapor deposition) 법의 증착방법을 적용하는 것이다. PVD 법으로 증착하는 경우에는 이미 박막 내에 무수한 결정핵이 존재하기 때문에 핵생성 단계가 필요 없게 된다. PVD 증착법의 적용을 위해서는 타겟 (target)의 제조 및 평가 실험이 선행되어야 한다. 그런데 벌크 BLT 재료의 소결공정 조건과 전기적 특성에 관한 연구 결과는 거의 발표 되지 않고 있다. 본 실험에서는 $Bi_2O_3$, $TiO_2$ and $La_2O_3$ 분말을 이용하여 최적의 조성을 구하기 위하여 Bi양을 변화시키며 타겟을 제조 하였다. 혼합된 분말을 하소 후 pallet 형태로 성형하여 소결을 실시하였다. 시편을 1mm 두께로 연마하고, 표면에 silver 전극을 인쇄하여 전기적 특성을 측정하였다. Bi양이 3.28몰 첨가된 조성에서 최대의 잔류분극 (2Pr) 값을 얻었고, 이때의 값은 약 $18{\mu}C/cm^2$ 정도였다. 최적화된 조성 ($Bi_{3.28}La_{0.75}Ti_3O_{12}$)으로 BLT 타겟을 제조하여 PLD법으로 박막을 제조하였다. 박막 제조 시 압력은 $1{\times}10^{-1}\;{\sim}\;1{\times}10^{-4}\;Torr$ 범위에서 변화시켰다. $1{\times}10^{-1}\;Torr$ 압력을 제외하고는 모든 압력에서 BLT 박막이 증착되었다. 중착된 박막을 $650\;{\sim}\;800^{\circ}C$에서 30분간 열처리를 실시하고 전기적 특성을 평가한 결과, $1{\times}10^{-2}\;Torr$에서 증착한 박막에서 양호한 P-V (polarization-voltage) 이력곡선을 얻을 수 있었고, 이때의 잔류분극 (2Pr) 값은 약 $6\;{\mu}C/cm^2$ 이었다. 주사전자현미경 (SEM)을 이용하여 BLT 박막 표면의 미세구조도 관찰하였는데, 스핀코팅 법으로 증착한 경우에 관찰되었던 조대화된 입자들은 관찰되지 않았고, 상당히 양호한 입자 크기 균일도를 나타내었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.66-66
• /
• 2008

Most of the properties of ITO films depend on their substrate nature, deposition techniques and ITO film composition. For the display panel application, it is normally deposited on the glass substrate which has high strain point (>575 degree) and must be deposited at a temperature higher than $250^{\circ}C$ and then annealed at a temperature higher than $300^{\circ}C$ in order to high optical transmittance in the visible region, low reactivity and chemical duration. But the high strain point glass (HSPG) used as FPDs is blocking popularization of large sizes FPDs because it is more expensive than a soda lime glass (SLG). If the SLG could be used as substrate for FPDs, then diffusion of Na ion from the substrate occurs into the ITO films during annealing or heat treatment on manufacturing process and it affects the properties. Therefore proper care should be followed to minimize Na ion diffusion. In this study, we investigate the electrical, optical and structural properties of ITO films deposited on the SLG and the Asahi glass(PD200) substrate by rf magnetron sputtering using a ceramic target ($In_2O_3:SnO_2$, 90:10wt.%). These films were annealed in $N_2$ and air atmosphere at $400^{\circ}C$ for 20min, 1hr, and 2hrs. ITO films deposited on the SLG show a high electrical resistivity and structural defect as compared with those deposited on the PD200 due to the Na ion from the SLG on diffuse to the ITO film by annealing. However these properties can be improved by introducing a barrier layer of $SiO_2$ or $Al_2O_3$ between ITO film and the SLG substrate. The characteristics of films were examined by the 4-point probe, FE-SEM, UV-VIS spectrometer, and X-ray diffraction. SIMS analysis confirmed that barrier layer inhibited Na ion diffusion from the SLG.

• Journal of Electrochemical Science and Technology
• /
• v.14 no.1
• /
• pp.85-95
• /
• 2023

In recent years, solid-state Li metal batteries (SSLBs) have attracted significant attention as the next-generation batteries with high energy and power densities. However, uncontrolled dendrite growth and the resulting pulverization of Li during repeated plating/stripping processes must be addressed for practical applications. Herein, we report a plastic-crystal-based polymer/ceramic composite solid electrolyte (PCCE) to resolve these issues. To fabricate the one-side ceramic-incorporated PCCE (CI-PCCE) film, a mixed precursor solution comprising plastic-crystal-based polymer (succinonitrile, SN) with garnet-structured ceramic (Li₇La₃Zr₂O₁₂, LLZO) particles was infused into a thin cellulose membrane, which was used as a mechanical framework, and subsequently solidified by using UV-irradiation. The CI-PCCE exhibited good flexibility and a high room-temperature ionic conductivity of over 10^-3 S cm^-1. The Li symmetric cell assembled with CI-PCCE provided enhanced durability against Li dendrite penetration through the solid electrolyte (SE) layer than those with LLZO-free PCCEs and exhibited long-term cycling stability (over 200 h) for Li plating/stripping. The enhanced Li⁺ transference number and lower interfacial resistance of CI-PCCE indicate that the ceramic-polymer composite layer in contact with the Li anode enabled the uniform distribution of Li⁺ flux at the interface between the Li metal and CI-PCCE, thereby promoting uniform Li plating/stripping. Consequently, the Li//LiFePO₄ (LFP) full cell constructed with CI-PCCE demonstrated superior rate capability (~120 mAh g^-1 at 2 C) and stable cycle performance (80% after 100 cycles) than those with ceramic-free PCCE.