The efects of mechanical aloying conditions and the type of reducing agent on the solid state reductionof haematite $Fe_2O_3$ have been investigated at room temperature. Aluminium titanium zinc and copper were used as reducing agent. Nanocomposites of metal-oxide in which oxide particles with nano size were dispersed in Fe matrix were obtained by mechanical alloying of $Fe_2O_3$ with aluminium and titanium respectively However the reduction of $Fe_2O_3$ by coppe was not occurred Composite materials of iron with $Al_2O_3$ and $TiO_2$ were obtained from the system of $Fe_2O_3-Al$ and $Fe_2O_3-Ti$ after ball milling for 20 hrs and 30 hrs respectively. And the system of $Fe_2O_3-Zn$ resulted in the formationof FeO with ZnO after ball milling of 120 hrs. The final grain sizes of iron estimated by X-ray diffraction line-width measurement were in the ranges of 24~33 nm.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.552-555
• /
• 1995

The magnetic properties of Mg-Mn ferrites were investigated in the composition range of $Mg_{a}Mn_{b}Fe_{c}O_{4\pm\delta}$ (a+b+c=3) with the addition of $Al_{2}O_{3}$. In $MgO-MnO-Fe_{2}O_{3}$ ternary system, the spinel single phase existed within the composition range of MgO-50 mol%, MnO-70 mol% and $Fe_{2}O_{3}-60\;mol%$. The saturation magnetic flux density increased with the increase of $Fe_{2}O_{3}$ content and showed the maximum at the stoichiometric composition of $(Mg,Mn)Fe_{2}O_{4}$. In $Mg_{x}Mn_{1-x}Fe_{2}O_{4}(x=0.2~0.8)$ system, the saturation magnetic flux density showed the maximum at $Mg_{0.2}Mn_{0.8}Fe_{2}O_{4}$. The addition of $Al_{2}O_{3}$ resulted in the decrease of saturation magnetic flux density but increased the electrical resistivity.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.1
• /
• pp.64-67
• /
• 2013

$Fe_3O_4$(magnetite) having half metallic property attracts great attention material with high curie temperature in spintronics. $Fe_3O_4$ thin films and nanowires were grown onto c-$Al_2O_3$(0001) at various substrate temperatures. $Fe_3O_4$ films deposited from 300 to $600^{\circ}C$ are influenced by thermal stress induced from mismatch of thermal expansion coefficient between $Fe_3O_4$ and $Al_2O_3$ (0001) substrate. The $Fe_3O_4$ nanowires grown at $640^{\circ}C$ showed a diameter of 130 nm and a length of $2-10{\mu}m$. The nanowire arrays fabricated by pulsed laser deposition technique have high coercivity($H_c$) of 608 Oe and Squareness($M_r/M_s$) of 0.68 in perpendicular direction.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.11a
• /
• pp.186-186
• /
• 1999

• Journal of the Korean institute of surface engineering
• /
• v.52 no.5
• /
• pp.246-250
• /
• 2019

Nano-multilayered $Cr_{25.2}Al_{19.5}Si_{4.7}N_{50.5}$ films were deposited on the steel substrate by cathodic arc plasma deposition. They were corroded at $900^{\circ}C$ in $Ar/1%SO_2$ gas in order to study their corrosion behavior in sulfidizing/oxidizing environments. Despite the presence of sulfur in the gaseous environment, the corrosion was governed by oxidation, leading to formation of protective oxides such as $Cr_2O_3$ and ${\alpha}-Al_2O_3$, where Si was dissolved. Iron diffused outward from the substrate to the film surface, and oxidized to $Fe_2O_3$ and $Fe_3O_4$. The films were corrosion-resistant up to 150 h owing to the formation of thin ($Cr_2O_3$ and/or ${\alpha}-Al_2O_3$)-rich oxide layers. However, they failed when corroded at $900^{\circ}C$ for 300 h, resulting in the formation of layered oxide scales due to not only outward diffusion of Cr, Al, Si, Fe and N, but also inward movement of sulfur and oxygen.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.5
• /
• pp.365-372
• /
• 2000

Pure $Fe_3$Al alloys with three different compositions of Fe-21.8%Al, Fe-24.1%Al and Fe-27.2%Al were prepared by vacuum induction melting followed by homogenization and hot forging. The long-time oxidation behavior of the prepared alloys was studied at 1073, 1273 and 1473k in air. The oxidation resistance greatly increased with an increase in Al contents. Thin and uniform oxide scales were always formed on Fe-27.2%Al, while thick and fragile oxide scales were formed on Fe-(21.8, 24.1%)Al. Internal oxidation was observed in Fe-(21.8, 24.1%)Al, when oxidized above 1273K. The major oxidation product of all the oxidized alloys was always $\alpha$-$Al_2$$O_3$.

• Korean Journal of Materials Research
• /
• v.28 no.7
• /
• pp.371-375
• /
• 2018

The manganese-, nickel-, and aluminum-doped cobalt ferrite powders, $Mn_{0.2}Co_{0.8}Fe_2O_4$, $Ni_{0.2}Co_{0.8}Fe_2O_4$, and $Al_{0.2}CoFe_{1.8}O_4$, are fabricated by the sol-gel method, and the crystallographic and magnetic properties of the powders are studied in comparison with those of $CoFe_2O_4$. All the ferrite powders are nano-sized and have a single spinel structure with the lattice constant increasing in $Mn_{0.2}Co_{0.8}Fe_2O_4$ but decreasing in $Ni_{0.2}Co_{0.8}Fe_2O_4$ and $Al_{0.2}CoFe_{1.8}O_4$. All the $M{\ddot{o}}ssbauer$ spectra are fitted as a superposition of two Zeeman sextets due to the tetrahedral and octahedral sites of the $Fe^{3+}$ ions. The values of the magnetic hyperfine fields of $Ni_{0.2}Co_{0.8}Fe_2O_4$ are somewhat increased in the A and B sites, while those of $Mn_{0.2}Co_{0.8}Fe_2O_4$ and $Al_{0.2}CoFe_{1.8}O_4$ are decreased. The variation of $M{\ddot{o}}ssbauer$ parameters is explained using the cation distribution equation, superexchange interaction and particle size. The hysteresis curves of the ferrite powders reveal a typical soft ferrite pattern. The variation in the values of saturation magnetization and coercivity are explained in terms of the site distributions, particle sizes and the spin magnetic moments of the doped ions.

• Bulletin of the Korean Chemical Society
• /
• v.27 no.6
• /
• pp.853-856
• /
• 2006

Dion-Jacobson phases $CsCa_2Nb_2FeO_9$ and $CsCa_2Nb_2AlO_9$ were reinvestigated by the Rietveld analysis of powder X-ray diffraction (XRD) method, scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS). These nominal compounds, previously known as the oxygen-deficient layered perovskites with the sequences of $NbO_6-MO_4-NbO_6$ in tripled slab, in fact, were mixed phases of n = 3 Dion-Jacobson phases and impurities such as $Ca_2NbFeO_6$ and $Ca_3Al_2O_6$. The difference of morphology and chemical in-homogeneity between Dion-Jacobson phases and impurities could be clearly identified by scanning electron microscopy with energy-dispersive X-ray spectroscopy. The chemical composition of $CsCa_2Nb_2FeO_9$ was calculated into $Cs_{0.59}Ca_{2.64}Nb_{2.92}Fe_{0.81}$ in small agglomerate crystals and $Cs_{0.95}Ca_{1.97}Nb_{3.08}Fe_{0.15}$ in long plate-like crystals.

• Journal of the Korean Ceramic Society
• /
• v.46 no.4
• /
• pp.350-356
• /
• 2009

Perovskite codoped with chromium and iron have been studied. Samples with $YAl_{0.96}(Cr_{0.04-x}Fe_x)O_3$(x=0.01, 0.02, 0.03, 0.04) were prepared by solid state reaction at $1450^{\circ}C$ for 6 h and were characterized by XRD, FT-IR, Raman spectroscopy, SEM and UV-vis spectrophotometer. The color of the synthesized pigments were from red to dark brown(in bulk). Up to 0.02 mole $Fe_2O_3$ for substituting $Cr_2O_3$ development of color in lime-glaze gives good red color but as increasing amount of $Fe_2O_3$ and decreasing $Cr_2O_3$ proportionally produce from brownish red to brown. Increasing $Fe_2O_3$ amount lead to weaken crystal field relatively due to have smaller ionic radius than $Cr_2O_3$ ionic one. The UV-vis peaks were shifted to lower wavelength.

• Journal of the Mineralogical Society of Korea
• /
• v.8 no.1
• /
• pp.29-36
• /
• 1995

연옥은 구성광물의 조직, 결합양상 및 화학조성 등에 의해 일반적인 투각섬석과 구분되며, 색, 경도 및 인성 등에 의해 등급과 가치가 달라진다. 본 연구에서는 춘천산 연옥을 대상으로 연옥의 물리적 특성(조직, 경도 및 인성) 등의 연구가 수행되었다. 춘천산 연옥은 구성광물인 투각섬석의 조직, 입도 및 공생광물(불순물)의 특성에 따라 세 가지 유형(유형 I, 유형 II, 유형 III)으로 구분된다. 유형 I은 치밀한 극미립의 초미정질(<5$\mu\textrm{m}$) 투감섬석의 치밀한 집합체로서 구성되며, 유형 II와 유형 III은 미정질(10~30$\mu\textrm{m}$) 및 세립 (>50$\mu\textrm{m}$)의 투각섬석 집합체로서 투휘석, 활석, 녹니석 및 사문석 등이 미량으로 함유된다.연옥을 구성하는 세 유형의 투각섬석의 화학조성은 Fe, Al 성분이 유형 III에서 가장 높은 함량(1.07~1.88wt.% FeO, 1.3~2.59wt.% Al2O3)을 나타내며, 유형 II(0.22~0.37wt.% FeO, 0.66~0.77wt.% Al2O3), 유형 I (0.20~0.24wt.% FeO, 0.05~0.12wt.% Al2O3)의 순으로 감소함을 보이고, SiO2 성분은 유형 I (59.13~59.67 wt.%), 유형 II(58.02~59.40wt.%), 유형 III (57.34~58.63 wt.%)순으로 함량이 낮아짐을 알 수 있다.연옥의 미경도(VHN=311~659)와 파괴인성치(2.38$\times$105~5.62$\times$105 dyne.cm-3/2)는 유형 I, 유형 II, 유형 III의 순으로 낮아진다. 이러한 결과는 조직 및 집합구조의 특성과 밀접한 관계를 갖고 있음을 반영한다.