• ETRI Journal
• /
• 제18권4호
• /
• pp.339-346
• /
• 1997

Good quality a-axis oriented thin films of $YBa_2Cu_3O_{7-x}$ may be grown by the use of a $PrBa_2Cu_3O_{7-x}$ (PBCO) layer as a template. Here we present a detailed study of the nucleation of the PBCO layer, explaining the orientations observed. It is determined that the wavy surface of a $LaSrGaO_4$ (LSGO) (100) substrate consists of the {101} planes by observing cross-sectional transmission electron microscopy images of the interface between the PBCO film and the substrate. The images and selected area diffraction patterns show that a mixed c-and b-axis oriented PBCO layer was initially grown on the substrate, followed by pure b-axis oriented PBCO growth. We explain that the c-axis oriented growth is the result of the growth of the PBCO (019) planes on the LSGO (101) planes. We conclude that the nucleation and growth of the PBCO films at the initial stages depends on the crystallographic plane of the substrate surfaces, however, as the film grows further, the kinetics of the deposition process favors b-axis oriented growth.

• 한국세라믹학회지
• /
• 제35권3호
• /
• pp.280-286
• /
• 1998

LaAlO3 Single crystals used as a substrate for thin film depositions of a high temperature oxide su-perconductor YB2Cu3O7 and applied to microwave frequencies were grown by the Traveling Solvent Flati-ing Zone (TSFZ) method and characterized. For the growth of LaAlO3 single crystals polycrystalline fe-edrods were prepared from powder mixture of La2O3 and Al2O3 with a mole ratio of 1:1 calcined at 110$0^{\circ}C$ for 3h and sintered at 140$0^{\circ}C$ for 4h The growth LaAlO3 crystals was 4-5mm in diameter 30mm in length and dark brown. The growth rate was 2-3mm/h and the rotation speeds were 10rpm for an upper ro-tation and 40 rpm for a lower rotation The growing crystals and the feedrods were counter-rotated. The orientation of the grown single crystals of LaAlO3 was identified to be [111] direction. Dielectric constants were measured to be 30-33 between 100 kHz and 1 MHz in the 30$0^{\circ}C$ to 45$0^{\circ}C$ temperature range and 102 in a range of 100 kHz at the phase transformation temperature of 522$^{\circ}C$ Dielectric losses were calculated to be 1.8$\times$10-4 at the room temperature and 5.7$\times$10-3 at the phase transformation temperature. Lattice con-stants of the grown crystlals were determined to be aR=5.3806 $\AA$ and $\alpha$=60.043$^{\circ}$ by the least square method.

• 자원환경지질
• /
• 제34권1호
• /
• pp.39-53
• /
• 2001

이 연구는 토현광산 수계의 환경오염에 관하여 지질, 광물 및 지구화학적으로 고찰한 것이다. 과안부근에 분포하는 토양과 퇴적물의 ${Al_2}{O_3}/{Na_2O}$와 ${K_2}O/{Na_2}O$의 비는 ${SiO_2}/{Al_2}{O_3}$에 대하여 부분적인 부의 상관관계를 갖는다. 또한 일부 미량 및 희토류 원소의 지구화학적 특성(V/Ni, Ni/Co, La/Ce, Th/Yb, Th/U, La/Th, ${La_N}/{Yb_N}$, Co/Th, La/Sc 및 Sc/Th)들은 비교적 좁은 범위를 보이며 균질한 조성을 갖는다. 이는 광산의 모암인 셰일의 근원암이 중성 또는 염기성 화성암에서 기원한 퇴적물이 우세하였던 것임을 지시하는 것이다. 토양과 퇴적물의 대표적인 광물종은 석영, 운모, 장석, 각섬석, 녹니석 및 점토광물 등이나, 함량비는 시료에 따라 다소 차이가 있다. 독성원소의 함량이 높은 토양과 퇴적물에서는 황철석, 유비철석, 섬아연석, 황동석, 방연석, 침철석 등의 중광물과 다양한 종류의 수산화물이 많이 산출된다. 기반암의 조성으로 표준화한 주원소의 부화지수는 퇴적물 = 1.0, 침전물 = 1.7, 밭 토양 =0.9, 논 토양 = 0.8이다. 이 광산 수계에서 검출된 중금속의 최대함량은 Ag = 186 ppm, As = 17,100 ppm, Bi = 127 ppm, Cd = 77 ppm, Cu = 12,299 ppm, Pb = 8,897 ppm, Sb = 1,350 ppm, W = 599 및 Zn = 12,250 ppm 이다. 이 독성원소들은 광폐석 야적장 주변의 퇴적물과 침전물에서 특히 높고, total FeO의 함량과 밀접한 관계가 있다. 기반암의 조성을 기준으로 이 독성원소(As, Bi, Cd, Cu, Pb, Sb, W, Zn)들의 부화지수를 구하면, 퇴적물 = 106.0, 침전물 = 279.6, 밭토양 = 3.5, 논 토양 = 1.6 이나, EPA의 기준치로 표준화된 부화지수는 각각 40.7, 121.4, 1.3 및 0.6 이다.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2002년도 High Temperature Superconductivity Vol.XII
• /
• pp.8-8
• /
• 2002

• Bulletin of the Korean Chemical Society
• /
• 제29권12호
• /
• pp.2325-2326
• /
• 2008

• 한국전기전자재료학회논문지
• /
• 제14권2호
• /
• pp.158-162
• /
• 2001

In this report, a new process for patterning of YBaCuO thin films, ICP(inductively coupled plasma) method, is described by comparing with existing wet etching method. Two 100㎛ wide and 2mm long YBaCuO striplines on LaAlO$_3$ substrates have been fabricated using two patterning techniques. And the properties were compared with the critical temperature and the SEM photography. Then, the critical temperatures of two samples were about 88 K, but the cross section of sample using ICP method was shaper than that using the wet etching method. ICP method can be used as a good etching technique process for patterning of YBaCuO superconductor.

• Bulletin of the Korean Chemical Society
• /
• 제20권3호
• /
• pp.281-284
• /
• 1999

Two La1.82Ca1.18Cu2O6+δ (2126) compounds exhibited different properties depending upon how they were synthesized. The compound prepared under high oxygen pressure showed superconductivity. But the compound prepared under low oxygen pressure did not exhibit superconductivity, and showed a metal-insulator transition. Our study on these compounds shows that a small amount of additional oxygen intercalated into the superconducting phase plays an important role for superconductivity. The Fermi surface of non-superconducting 2126 compound possesses nesting phenomena, which is the reason for the M-1 transition. On the other hand, the superconducting 2126 compound does not show Fermi surface nesting. This is because the additional oxygen removes some electrons from Cu d-orbitals, thereby bradking the Fermi surface nesting.

• 대한환경공학회지
• /
• 제22권12호
• /
• pp.2255-2261
• /
• 2000

본 연구에서는 질소산화물 저감기술의 하나인 선태적 촉매 환원법(SCR)을 이용하여 실제 디젤엔진에서의 $NO_x$저감에 관한 실험을 수행하였다. 특히 선택적 촉매 환원법 중에서 금속산화물(metal oxide)과, 페롭스카이트(perovskite)형의 환원촉매를 사용하였으며 ${\gamma}-Al_2O_3$ 담체에 여러 가지 주촉매, 조촉매를 사용하여 배기가스 온도 범위 내에서 높은 $NO_x$제거효율을 가지고 있는 $LaCuMnO_x$을 선택하였다. $NO_x$ 제거를 위한 실험은 실제 디젤엔진에서 배출되는 배기가스를 이용하였으며 공간속도 $3,300h^{-1}$인 상태에서 촉매 반응기 통과전후의 $NO_x$의 변화량을 측정하였다. 그 결과 페롭스카이트 형태의 촉매가 활성화 온도범위가 우수함을 알 수 있었고 $LaCuMnO_x$의 경우에는 촉매 온도범위 $150{\sim}450^{\circ}C$하에서 $NO_x$의 제거효율이 전반적으로 우수하였다.

• 대한화학회지
• /
• 제59권6호
• /
• pp.493-498
• /
• 2015

The reductive amination of cyclohexanone with ammonia over Cu-Cr-a/γ-Al₂O₃ was investigated. It was found that a proper solvent with high solubility of ammonia and 4Å molecular sieves for the elimination of generated water contributed to the formation of cyclohexylamine in the premixing process. In addition, the addition of ammonia in the fixedbed reactor could obviously improve the conversion of cyclohexanone to cyclohexylamine. Finally, reaction conditions including reaction temperature, hydrogen pressure and charging rate of the premix were optimized. Under the optimized conditions, cyclohexylamine was obtained in 83.06% yield.

• 한국세라믹학회지
• /
• 제36권2호
• /
• pp.203-209
• /
• 1999

Si 기판위에 Ba2YCu3O7-$\delta$ 고온초전도체를 응용하기 위해 요구되는 buffer층으로 유망한 재료인 LaAlO3 단일상 분말을 고상반응법과 자발착한 연소반응법으로 제조하였다. 제조된 LaAlO3 분말의 입자형태와 결정상태는 scanning electron microscope (SEM)과 X-ray diffractometer (XRD)를 이용하여 분석하였다. 분말의 비표면적과 소결특성은 각각 Brunauer-Emmett-Teller(BET) 방법과 dilatometer를 측정하였다. 고상반응법으로 LaAlO3 분말을 제조할 때에는 하소온도를 150$0^{\circ}C$까지 높게 하여도 단일상을 얻는 것이 어려웠으나 자발착한 연소반응법에 의한 분말제조는 $650^{\circ}C$의 저온에서 하소하여도 쉽게 얻을 수 있었다. Dilatometer 측정을 통하여 분석해 보면, 고상반응법에 의한 분말보다 자발착한 연소반응법에 의한 분말로 제조된 소결체가 고상반응법에 의한 소결체에 비해 1.4배나 큰 소멸밀도(98.87%)를 가졌다. 이렇게 소결밀도에서 큰 차이가 나는 것은 자발착한 연소방법에 의한 분말의 평균 입자크기가 nano crystal size이고 비표면적 값(56.54 $m^2$/g)이 매우 크기 때문이다. 두가지 방법으로 제조된 분말을 이용, LaAlO3 layer를 스크린 프린팅과 소결법으로 Si 기판상에 제조하였으며 자발착한 연소합성법으로 제조된 분말은 110$0^{\circ}C$에서 우수한 소결특성을 나타내었다.