• 한국세라믹학회지
• /
• 제35권4호
• /
• pp.355-363
• /
• 1998

The oxygen flux of SDC ($Sm_2O_3\;doped\;CeO_2$) solid electrolyte membranes with electronic and oxygen ion-ic conductivities has been investigated as a basic research in order to develop the conversion process of na-tural gas to syngas using the ceramic membrane reactor. Tube type membranes(1 mm thickness) were fa-bricated by slip casting of SDC powders prepared by the oxalate coprecipitaion method. Dense oxygen per-meation membranes(0.1 mm thickness) could be synthesized via sintering at $1450^{\circ}C$ for 2h and their re-lative density was over 95% The oxygen flux through SDC membranes doped 20mol% $Sm_15$ was about $1.13{\times}10^{-5}\;mol/m_2{\cdot}sec$ at low temperature around $800^{\circ}C$. In addition the SDC membranes showed a good thermaal stability for a long period of service.

• Korean Chemical Engineering Research
• /
• 제54권1호
• /
• pp.127-134
• /
• 2016

A series of Ce-doped ZnO (Ce/ZnO) nanostructures were fabricated using the co-precipitation method, then a simply nontoxic hydrothermal approach was proposed for preparation of reduced graphene oxide (rGO)-Ce/ZnO composites. The synthesized composites were investigated by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FT-IR), photoluminescence spectroscopy (PL), electrochemical impedance spectroscopy (EIS), UV-vis diffuse reflectance spectroscopy (DRS) techniques and Raman pattern. The as-synthesized rGO-Ce/ZnO composites showed high photodecomposition efficiency in comparison with the rGO-ZnO, Ce/ZnO, pure ZnO under UV, visible-light and sunlight irradiation. The degradation of methylene blue (MB) (10 mg/L, 100ml) by 95.8% within 60 min by using rGO-2 (10 mg) under sunlight irradiation was observed. The repeated use of the rGO-2 was investigated, and the results showed almost no decay in the catalytic activity.

• 한국세라믹학회지
• /
• 제54권1호
• /
• pp.23-27
• /
• 2017

A series of $CeO_2-TiO_2$ composite samples with different Ce/Ti molar ratios were prepared by the paper template. Powder X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to confirm a face-centered cubic lattice of $CeO_2$ with Ce/Ti =8:2 or 9:1 and a two phase mixture of anatase titania and face-centered cubic ceria with Ce/Ti = 7 : 3. The field emission scanning electron microscopy (FESEM) results suggest that the products are micron braid structures consisting of fibers with diameters in a range of $1-6{\mu}m$ and lengths of several hundred micrometers. $N_2$ absorption-desorption testing shows that the composite at Ce/Ti molar fraction of 8 : 2 has the largest BET surface area (about $81m^2{\cdot}g^{-1}$). Compared to the pure $CeO_2$ sample, the composites show superior catalytic activity for $H_2$ reduction and CO oxidation. For the micron braid structure $CeO_2-TiO_2$ composite (Ce/Ti = 8 : 2), due to the high surface area and the solid solution with appropriate $Ti^{4+}$ incorporation, the CO conversion at about $280^{\circ}C$ was above 50% and at $400^{\circ}C$ was 100%.

• 한국재료학회지
• /
• 제21권11호
• /
• pp.604-610
• /
• 2011

The effect of $BaF_2$ flux in $Y_3Al_5O_{12}:Ce^{3+}$(YAG:Ce) formation was investigated. Phase transformation of $Y_3Al_5O_{12}$(YAG) was characterized by using XRD, SEM, and TEM-EDS, and it was revealed that the sequential formation of the $Y_4Al_2O_9$(YAM), $YAlO_3$(YAP) and $Y_3Al_5O_{12}$(YAG) in the temperature range of 1000-1500$^{\circ}C$. Single phase of YAG was revealed from 1300$^{\circ}C$. In order to find out the effect of $BaF_2$ flux, three modeling experiments between starting materials (1.5$Al_2O_3$-2.5$Y_2O_3$, $Y_2O_3$-$BaF_2$, and $Al_2O_3$-$BaF_2$) were done. These modeling experiments showed that the nucleation process occurs via the dissolution-precipitation mechanism, whereas the grain growth process is controlled via the liquid-phase diffusion route. YAG:Ce phosphor particles prepared using a proposed technique exhibit a spherical shape, high crystallinity, and an emission intensity. According to the experimental results conducted in this investigation, 5% of $BaF_2$ was the best concentration for physical, chemical and optical properties of $Y_3Al_5O_{12}:Ce^{3+}$(YAG:Ce) that is approximately 10-15% greater than that of commercial phosphor powder.

• 한국결정성장학회지
• /
• 제27권6호
• /
• pp.309-312
• /
• 2017

세리아 분말은 Ce 이온의 산화, 환원 반응을 통한 산소저장능력(OSC)이 뛰어나 배기가스를 정화하는 자동차의 삼원촉매에 대표적인 재료로 사용된다. 그러나 일반적으로 세리아는 고온에서 열적 안정성이 떨어지기 때문에 금속이온을 도핑시켜 열적 안정성을 향상시켜 사용한다. 따라서 본 연구에서는 Zr 이온을 세리아 분말에 도핑시켰고, 도핑으로 인해 입자크기가 감소하면서 비 표면적 증가로 인해 그 특성은 더욱 향상되었다. 그리고 본 연구에서는 세리아 및 Zr 이온이 도핑된 세리아를 나노 크기로 합성하기 위해 수열반응법을 이용하여 합성하였다. 수열합성 조건은 pH = 11, 반응온도는 $200^{\circ}C$에서 6시간 동안 합성하였다. 수열합성법을 이용하여 합성된 세리아 및 Zr 도핑 $CeO_2$ 나노 분말의 평균 입자 크기는 약 20 nm 이하였다. 합성된 세리아 나노분말의 비표면적은 $52.03m^2/g$, Zr 이온이 도핑된 $CeO_2$ 분말의 비 표면적 $132.27m^2/g$이었다.

• 한국세라믹학회지
• /
• 제43권10호
• /
• pp.666-672
• /
• 2006

GDC20($Ce_{0.8}Gd_{0.2}O_{1.9}$) powder was synthesized by oxalate co-precipitation and milling and its thermal decomposition, phase formation, and sinterability were investigated. As-prepared precipitates were non-crystalline due to the milling process and completely decomposed at 400$^{\circ}C$ The powder calcined at 800$^{\circ}C$ for 2 h contained fine p]sty particles with an average size of 0.69 $\mu$m. Attrition milling of the calcined powder for 2 h had a little milling effect, resulting in a slight decrease in the particle size to 0.45 $\mu$m. The milled powder consisted of small spherical primary particles and some large particles, which had been agglomerated during calcination. Due to the excellent sinterability of the powder, sintering of the powder compacts for 4 h showed relative densities of 78.7% at 1000$^{\circ}C$ and 97.8% at 1300$^{\circ}C$, respectively. Densification was found to almost complete at temperature above 1200$^{\circ}C$ and a dense and homogeneous microstructure was obtained. A rapid grain growth occurred between 1200$^{\circ}C$ and 1300$^{\circ}C$. Grains in 0.1$\sim$0.5 $\mu$m sizes at 1200$^{\circ}C$ grew to 0.2$\sim$2 $\mu$m and their size distribution became broader at 1300$^{\circ}C$.

• 한국분말재료학회지
• /
• 제26권1호
• /
• pp.49-57
• /
• 2019

Layered $LiNi_{0.83}Co_{0.11}Mn_{0.06}O_2$ cathode materials single- and dual-doped by the rare-earth elements Ce and Nd are successfully fabricated by using a coprecipitation-assisted solid-phase method. For comparison purposes, non-doping pristine $LiNi_{0.83}Co_{0.11}Mn_{0.06}O_2$ cathode material is also prepared using the same method. The crystal structure, morphology, and electrochemical performances are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) mapping, and electrochemical techniques. The XRD data demonstrates that all prepared samples maintain a typical ${\alpha}-NaFeO_2$-layered structure with the R-3m space group, and that the doped samples with Ce and/or Nd have lower cation mixing than that of pristine samples without doping. The results of SEM and EDS show that doped elements are uniformly distributed in all samples. The electrochemical performances of all doped samples are better than those of pristine samples without doping. In addition, the Ce/Nd dual-doped cathode material shows the best cycling performance and the least capacity loss. At a 10 C-rate, the electrodes of Ce/Nd dual-doped cathode material exhibit good capacity retention of 72.7, 58.5, and 45.2% after 100, 200, and 300 cycles, respectively, compared to those of pristine samples without doping (24.4, 11.1, and 8.0%).

• 한국응용과학기술학회지
• /
• 제22권2호
• /
• pp.175-181
• /
• 2005

The spherical particles of $CeO_2/SiO_2$ composite powder with narrow-size distribution and pure phase particles were synthesized by ultrasonic spray pyrolysis method from aqueous cerium sulfate solution. The resulting composite powder was characterized by X-ray diffraction, scanning electron microscopy, transmittance electron microscopy, in-vitro sun protect factor, and BET surface area analysis. The concentration of cerium sulfate was tested to vary the particle size from $3.40{\times}10^{-3}$ to $1.02{\times}10^{-2}mol/cm^3$ to study concentration effect of starting material. The average particle size from the $3.40{\times}10^{-3}mol/cm^3$ concentration was found to be slightly smaller than that from the $1.02{\times}10^{-2}mol/cm^3$ concentration, because of the relation between the droplet size and the concentration of the starting material solution.

• Korean Chemical Engineering Research
• /
• 제45권6호
• /
• pp.663-668
• /
• 2007

$Ni/CeO_2-ZrO_2$ 촉매를 이용하여 수소 제조를 위한 메탄의 자열개질반응 특성을 조사하였다. 메탄의 자열개질반응에서 촉매의 활성과 안정성을 향상시키기 위해 알루미나가 코팅된 금속 모노리스를 사용하였으며, 금속모노리스 촉매체는 높은 반응온도에서 분말형태의 촉매에 비해 높은 메탄 전환율을 나타내었다. 자열개질반응에 있어서 $H_2O/CH_4/O_2$의 비는 전환율에 영향을 미치는 중요한 변수임을 알 수 있었다. $H_2O/CH_4$ 비가 증가함에 따라 수소 수율은 증가되고, 또한 $O_2/CH_4$ 비가 증가함에 따라 메탄 전환율은 증가하지만 수소 수율은 감소하였다. $Ni/CeO_2-ZrO_2$ 촉매에 0.5 wt%의 귀금속 촉매인 Ru 첨가로 인해 낮은 반응온도에서 촉매 활성이 향상되었다.

• 한국재료학회지
• /
• 제22권10호
• /
• pp.526-530
• /
• 2012

Silica-based ceramic-matrix composites have shown promise as advanced materials for many applications such as chemical catalysts, ceramics, pharmaceuticals, and electronics. $SiO_2$-CuO-$CeO_2$ multi-component powders and their thin film, using an oxalic acid template as a chelating agent, have larger surface areas and more uniform pore size distribution than those of inorganic acid catalysts. $SiO_2$-CuO-$CeO_2$ composite powders were synthesized using tetraethylorthosilicate, copper (II) nitrate hemi (pentahydrate), and cerium (III) nitrate hexahydrate with oxalic acid as template or pore-forming agent. The process of thermal evolution, the phase composition, and the surface morphology of these powders were monitored by thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffractometry (XRD), field-emission scanning electron microscopy (FE-SEM), and energy dispersive X-ray spectrometry (EDXS). The mesoporous property of the powders was observed by Brunner-Emmett-Teller surface (BET) analysis. The improved surface area of this powder template with oxalic acid was $371.4m^2/g$. This multi-component thin film on stainless-steel was prepared by sol-gel dip coating with no cracks.