• Korean Journal of Materials Research
• /
• v.20 no.4
• /
• pp.181-186
• /
• 2010

Since it was developed by Joseph Aspdin, cement has been a common construction materials up to the present time. However, there are trace constituents in cement clinker. One of the trace constituents included in cement clinker, chromium, has become prominent and highly noticed lately as a social issue both inside and outside of this country because it affects the human body negatively. The aim of the present study was to investigate the concentration of water-soluble hexavalent chromium in cement clinker by using industrial by-products. For that reason, raw materials were prepared to add different $SiO_2$, $Al_2O_3$, and $Fe_2O_3$ sources. After the raw materials such as the limestone, the sand and the clay, iron ore was pulverized and mixed, and the raw meal was burnt at about $1450^{\circ}C$ in a furnace with an oxidizing atmosphere. The part in the raw materials of the clinker was substituted with slag, sludge, etc. and this was used to manufacturing cement clinker. To investigate the water-soluble hexavalent chromium content in clinker, raw meal was prepared by changing the modulus, the type, and the content of clinker materials and tested concentrations of hexavalent chromium in the clinkers. To determine $Cr^{+6}$ formation of the clinker, tests were done with raw meals adding chromium by using different industrial by-products. Consequently because the chromium was to be included in the raw materials of the clinker, production of Portland cement clinker was included with the chromium. Also, the chromium was converted into hexavalent chromium in the burning process.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.145-152
• /
• 2002

Four commercial alumina powders having different particle size of $0.5{\mu}m,\;2.8{\mu}m,\;12{\mu}m,\;and\;45{\mu}m$ were presintered at 1120$^{\circ}C$ for 2h and then lanthanum aluminosilicate glass was infiltrated at 1100$^{\circ}C$ for 2h in the interval of 0.1h to investigate the penetration kinetic of the glass into the alumina preforms. The infiltration distance is parabolic with respect to time as described by the Washburn equation and the penetration rate constant, K, increases with raising the alumina particle size. The strength of glass-alumina composites increases as the alumina particle size reaches to 2.8${\mu}m$ due to the increase in packing, however, decreases with further increasing the alumina particle size. The fracture toughness of the composites rises with increasing the alumina particle size due to the crack bowing and the interaction between crack and alumina particles.

• Journal of Environmental Science International
• /
• v.9 no.3
• /
• pp.241-252
• /
• 2000

Twenty-two water samples(fifteen groundwater and seven geothermal water samples) were collected to elucidate chemical characteristics of the ground and geothermal waters in the Haeundae hot spring area and its vicinity. Major and honor elements were analyzed for ground and geothermal water samples. The concentrations of $K^+$, Na+$, $Ca^{2+}$, $SO_4^{2-}$, $Cl^-$, ^F^-$ and $SiO_2$ were higher in the geothermal water samples than the groundwater samples except $HCO_3^- and Mg^{2+}$ ions. Based on the contents of Fe, Zn, Cu, Al, Mn and Pb, some of the ground and geothermal water samples are contaminated by anthropogenic sources. The ground waters shown on the Piper diagram belong to $Ca-HCO_3$ type, while the geothermal waters Na-Cl type. The graphs of $Cl^-$ versus $Na^+$, $Ca^{2+}, Mg^{2+}, K^+, SO_4^{2-} and HCO_3^-$ indicate that the groundwater is related partly with mineral-water reaction and partly with anthropogenic contamination, while the geothermal water is related with saline water. On the phase stability diagram, groundwater and thermal water mostly fall in the field of stability of kaolinite. This indicates that the ground and geothermal waters proceed with forming kaolinite. Factor and correlation analyses were carried out to simplify the physicochemical data into grouping some factors and to find interaction between them. Based on the Na-K, Na-K-Ca and Na-K-Ca-Mg geothermometers and silica geothermometers, the geothermal reservoir is estimated to have equilibrium temperature between 125${$\mid$circ}C$ and 160${$\mid$circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.31 no.10
• /
• pp.1218-1230
• /
• 1994

In manufacturing process of porous glass-ceramics by the filler method, the sintering behaviour of crystallizable glass powder mixed with various salts was studied and also the effects of precipitated crystal phases on the properties of porous glass-ceramics were investigated. Fine-grained crystallizable glass powder was homogeneously mixed with various slat having grain size 100~200 ${\mu}{\textrm}{m}$ and sintered for densification. After washing out the inorganic salt with distilled water, the porous sintered body was heat treated additionly for crystallization. The MgO-Al2O3-SiO2 base glass was used as crystallizable glass powder and the water soluble salts such as K2SO4 and MgSO4 were used as filler. When K2SO4 was used, leucite crystal phase was formed as a result of the ion exchange and porous glass-ceramics which exhibit high temperature resistance and high thermal expansion coefficient of 17$\times$10-6/$^{\circ}C$ could be obtained. On the contrary, when MgSO4 was used, only slight ion exchange is observed and $\mu$-cordierite and $\alpha$-cordierite crystal phases were formed and porous glass-ceramics which exhibit low thermal expansion coefficient schedule were determined with the results of DTA curves, thermal shrinkage curves and XRD patterns analysis. From DTA curves and thermal shrinkage curves, it was found that the sintering densification have been completed at the temperature range of exothermic peak for crystallization. The pore size distributions and pore diameters were measured by mercury porosimeter. The pore diameter of porous glass-ceramics was 10~15 ${\mu}{\textrm}{m}$ when 100~200${\mu}{\textrm}{m}$ grain size of K2SO4 was used and it was 25~30 ${\mu}{\textrm}{m}$ when the same grain size of MgSO4 was used. The porous glass-ceramics K2SO4 used shows bimodal pore size distribution and its porous skeleton structure was ascertained by SEM observation.

• Journal of the Mineralogical Society of Korea
• /
• v.32 no.2
• /
• pp.87-102
• /
• 2019

Pallancata Ag mine is located at the Ayacucho region 520 km southeast of Lima. The geology of mine area consists of mainly Cenozoic volcanic-intrusive rocks, which are composed of tuff, andesitic lava, andesitic tuff, pyroclastic flow, volcano clasts, rhyolite and quartz monzonite. This mine have about 100 quartz veins in tuff filling regional faults orienting NW, NE and EW directions. The Ag grades in quartz veins are from 40 to 1,000 g/t. Quartz veins vary from 0.1 m to 25 m in thickness and extend to about 3,000 m in strike length. Quartz veins show following textures including zonation, cavity, massive, breccia, crustiform, colloform and comb textures. Wallrock alteration features including silicification, sericitization, pyritization, chloritization and argillitization are obvious. The quartz veins contain calcite, chalcedony, adularia, fluorite, rutile, zircon, apatite, Fe oxide, REE mineral, Cr oxide, Al-Si-O mineral, pyrite, sphalerite, chalcopyrite, galena, electrum, proustite-pyrargyrite, pearceite-polybasite and acanthite. The temperature and sulfur fugacity ($f_{s2}$) of the Ag mineralization estimated from the mineral assemblages and mineral compositions are ranging from 118 to $222^{\circ}C$ and from $10^{-20.8}$ to $10^{-13.2}atm$, respectively. The relatively low temperature and sulfur-oxygen fugacities in the hydrothermal fluids during the Ag mineralization in Pallancata might be due to cooling and/or boiling of Ag-bearing fluids by mixing of meteoric water in the relatively shallow hydrothermal environment. The hydrothermal condition may be corresponding to an intermediate sulfidation epithermal mineralization.

• Economic and Environmental Geology
• /
• v.46 no.2
• /
• pp.179-198
• /
• 2013

The Boziguoer A-type granitoids in Baicheng County, Xinjiang, belong to the northern margin of the Tarim platform as well as the neighboring EW-oriented alkaline intrusive rocks. The rocks comprise an aegirine or arfvedsonite quartz alkali feldspar syenite, an aegirine or arfvedsonite alkali feldspar granite, and a biotite alkali feldspar syenite. The major rock-forming minerals are albite, K-feldspar, quartz, arfvedsonite, aegirine, and siderophyllite. The accessory minerals are mainly zircon, pyrochlore, thorite, fluorite, monazite, bastnaesite, xenotime, and astrophyllite. The chemical composition of the alkaline granitoids show that $SiO_2$ varies from 64.55% to 72.29% with a mean value of 67.32%, $Na_2O+K_2O$ is high (9.85~11.87%) with a mean of 11.14%, $K_2O$ is 2.39%~5.47% (mean = 4.73%), the $K_2O/Na_2O$ ratios are 0.31~0.96, $Al_2O_3$ ranges from 12.58% to 15.44%, and total $FeO^T$ is between 2.35% and 5.65%. CaO, MgO, MnO, and $TiO_2$ are low. The REE content is high and the total ${\sum}REE$ is $(263{\sim}1219){\times}10^{-6}$ (mean = $776{\times}10^{-6}$), showing LREE enrichment HREE depletion with strong negative Eu anomalies. In addition, the chondrite-normalized REE patterns of the alkaline granitoids belong to the "seagull" pattern of the right-type. The Zr content is $(113{\sim}1246){\times}10^{-6}$ (mean = $594{\times}10^{-6}$), Zr+Nb+Ce+Y is between $(478{\sim}2203){\times}10^{-6}$ with a mean of $1362{\times}10^{-6}$. Furthermore, the alkaline granitoids have high HFSE (Ga, Nb, Ta, Zr, and Hf) content and low LILE (Ba, K, and Sr) content. The Nb/Ta ratio varies from 7.23 to 32.59 (mean = 16.59) and the Zr/Hf ratio is 16.69~58.04 (mean = 36.80). The zircons are depleted in LREE and enriched in HREE. The chondrite-normalized REE patterns of the zircons are of the "seagull" pattern of the left-inclined type with strong negative Eu anomaly and without a Ce anomaly. The Boziguoer A-type granitoids share similar features with A1-type granites. The average temperature of the granitic magma was estimated at $832{\sim}839^{\circ}C$. The Boziguoer A-type granitoids show crust-mantle mixing and may have formed in an anorogenic intraplate tectonic setting under high-temperature, anhydrous, and low oxygen fugacity conditions.

• Korean Journal of Mineralogy and Petrology
• /
• v.35 no.3
• /
• pp.345-353
• /
• 2022

This study aimed to fundamentally understand changes of cell parameters of cation-exchanged mordenites using high resolution X-ray powder diffraction for studies that immobilization of various heavy metal cation using synthesis mordenite (Na_6.6Al_6.6Si_41.4O₉₆·20.4H₂O, Na-MOR). As a results of measurement by Thermogravimetric analysis (TGA), it was confirmed that 19.4, 20.4 water molecules per unit cell were present in monovalent-cation substituted MOR (Cs-MOR, Na-MOR), and 21, 23.1, 23.2 water molecules per unit cell were present in divalent-cation substituted MOR (Pb-MOR, Sr-MOR, Cd-MOR). The space group of all the samples were identified as Cmcm belonging to the orthorhombic crystal system. Compared to Na-MOR, starting material, relative peak intensity of (110) and (200) is significantly changed after cation substitution whereas peak position is almost similar. Also, (220) peak that was not found in Na-MOR was clearly observed in Pb-, Cd- and Sr-exchanged MOR. Thus, it was estimated that changes of atomic distribution usually occurred on ab-plane while changes of cell parameters were little. Detailed changes in the cell parameters of cation-exchanged mordenites were derived from whole profile fitting method using the GSAS suite program. Changes in the axial lengths and unit cell volume of cation substitution showed different relationship depending on ionic radius and charge number. In case of monovalent-cation substituted MOR, the length of a-axis increases whereas the length of b- and c-axis decrease by absorbed cation radius. In the case of divalent-cation exchanged MOR, the length of a-axis usually decreases while the length of b- and c-axis increases by cation radius. It was confirmed that unit cell volume of monovalent and divalent cation substituted MORs had an independent tendency by cation radius.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.66-66
• /
• 2008

Most of the properties of ITO films depend on their substrate nature, deposition techniques and ITO film composition. For the display panel application, it is normally deposited on the glass substrate which has high strain point (>575 degree) and must be deposited at a temperature higher than $250^{\circ}C$ and then annealed at a temperature higher than $300^{\circ}C$ in order to high optical transmittance in the visible region, low reactivity and chemical duration. But the high strain point glass (HSPG) used as FPDs is blocking popularization of large sizes FPDs because it is more expensive than a soda lime glass (SLG). If the SLG could be used as substrate for FPDs, then diffusion of Na ion from the substrate occurs into the ITO films during annealing or heat treatment on manufacturing process and it affects the properties. Therefore proper care should be followed to minimize Na ion diffusion. In this study, we investigate the electrical, optical and structural properties of ITO films deposited on the SLG and the Asahi glass(PD200) substrate by rf magnetron sputtering using a ceramic target ($In_2O_3:SnO_2$, 90:10wt.%). These films were annealed in $N_2$ and air atmosphere at $400^{\circ}C$ for 20min, 1hr, and 2hrs. ITO films deposited on the SLG show a high electrical resistivity and structural defect as compared with those deposited on the PD200 due to the Na ion from the SLG on diffuse to the ITO film by annealing. However these properties can be improved by introducing a barrier layer of $SiO_2$ or $Al_2O_3$ between ITO film and the SLG substrate. The characteristics of films were examined by the 4-point probe, FE-SEM, UV-VIS spectrometer, and X-ray diffraction. SIMS analysis confirmed that barrier layer inhibited Na ion diffusion from the SLG.

• Journal of Korean Society for Atmospheric Environment
• /
• v.24 no.5
• /
• pp.594-603
• /
• 2008

A single particle analytical technique, named low-Z particle electron probe X-ray microanalysis, was applied to characterize four samples collected at an underground shopping area connected to Dongdeamun subway station, in January and May 2006. Based on the analysis of their chemical compositions of the samples, many distinctive particle types are identified and the major chemical species are observed to be soil-derived particles, iron-containing particles. sulfates. nitrates, and carbonaceous particles. which are encountered both in coarse and fine fractions. Carbonaceous particles exist in carbon-rich and organic. Soil derived particles such as aluminosilicates, AlSi/C, $CaCO_3\;and\;SiO_2$ are more frequently encountered in spring samples than winter samples. Nitrate- and sulfate-con taming particles are more frequently encountered in winter samples, and those nitrate- and sulfate-containing particles mostly exist in the chemical forms of $Ca(CO_3,\;NO_3),\;Ca(NO_3,\;SO_4),\;(Na,\;Mg)NO_3\;and\;(Mg,\;Na)(NO_3,\;SO_4)$. Fe-containing particles which came from nearby subway platform are in the range of about 10% relative abundances for all the samples. It is observed that nitrate- and sulfate-containing particles and carbonaceous particles are much more frequently encountered in indoor aerosol samples than in outdoor aerosols, implying that $NO_x,\;SO_x$, and VOCs at the underground shopping area were more partitioned into aerosol phase.

• Journal of Microbiology and Biotechnology
• /
• v.22 no.9
• /
• pp.1288-1295
• /
• 2012

Exposure to bioaerosols causes various adverse health effects including infectious and respiratory diseases, and hypersensitivity. Controlling exposure to bioaerosols is important for disease control and prevention. In this study, we evaluated the efficacies of various functional filters coated with antimicrobial chemicals in deactivating representative microorganisms on filters or as bioaerosols. Tested functional filters were coated with different chemicals that included (i) Ginkgo and sumac, (ii) Ag-apatite and guanidine phosphate, (iii) $SiO_2$, ZnO, and $Al_2O_3$, and (iv) zeolite. To evaluate the filters, we used a model ventilation system (1) to evaluate the removal efficiency of bacteria (Escherichia coli and Legionella pneumophila), bacterial spores (Bacillus subtilis spore), and viruses (MS2 bacteriophage) on various functional filters, and (2) to characterize the removal efficiency of these bioaerosols. All experiments were performed at a constant temperature of $25^{\circ}C$ and humidity of 50%. Most bacteria (excluding B. subtilis) rapidly decreased on the functional filter. Therefore, we confirmed that functional filters have antimicrobial effects. Additionally, we evaluated the removal efficiency of various bioaerosols by these filters. We used a six-jet collision nebulizer to generate microbial aerosols and introduced it into the environmental chamber. We then measured the removal efficiency of functional filters with and without a medium-efficiency filter. Most bioaerosol concentrations did not significantly decrease by the functional filter only but decreased by a combination of functional and medium-efficiency filter. In conclusion, functional filters could facilitate biological removal of various bioaerosols, but physical removal of these by functional was minimal. Proper use of chemical-coated filter materials could reduce exposure to these agents.