• Journal of the Korean Ceramic Society
• /
• v.24 no.5
• /
• pp.447-452
• /
• 1987

${\alpha}$-Al2O3 powder was produced at 1000$^{\circ}C$ by the boehmite sol-gel process with seeding 2 wt% ${\alpha}$-Al2O3. The processes and mechanisms of fornation of ${\alpha}$-Al2O3 was investigated using DTA/TG, XRD, TR spectroscopy and thermodynamic analysis. The specific surface area of the obtained ${\alpha}$-Al2O3 was 16.3㎡/g.

• Journal of the Korean Ceramic Society
• /
• v.25 no.4
• /
• pp.373-379
• /
• 1988

$\alpha$-Al2O3-15m/o ZrO2 powder was prepared by a sol-gel method from boehmite and zirconium acetate. The transformation temperature of boehmite to $\alpha$-Al2O3 in the system Al2O3-ZrO2 was increased due to the coupled crystallization. On the other hand, the transformation temperature from boehmite to $\alpha$-Al2O3-15m/o ZrO2 could be prepared at 110$0^{\circ}C$ for 100min. The specific surface area of the product of $\alpha$-Al2O3-15m/o ZrO2 was 13.2$m^2$/g.

• Journal of the Korean Ceramic Society
• /
• v.32 no.4
• /
• pp.507-515
• /
• 1995

The monolithic dry gels of the Li2O-Al2O3-TiO2-SiO2 system were prepared by the sol-gel technique using metal alkoxides as starting materials to obtain monolithic glass-ceramics at low temperature without melting. Activation energy for the crystal growth of the gel with 6.05% TiO2, nucleating ageng, for the preparation of Li2O-Al2O3-TiO2-SiO2 system glass-ceramic was 101.14kcal/mol. As a result of the analysis of DTA & XRD, it was confirmed that the crytallization of Li2O-Al2O3-TiO2-SiO2 system glass-ceramic was the most efficient when 6.05% TiO2, nucleating agent, was added. $\beta$-eucryptite solid solution crystals and $\beta$-spodumene solid solution crystals were detected in the sample heat treated above 85$0^{\circ}C$. The sintered gel heat treated at 85$0^{\circ}C$ had the specific surface area of 185$m^2$/g, the pore volume of 0.19cc/g and the average pore radius of 20.8$\AA$. This shows that the sintered gel is also comparatively porous material. In temperature range of 25~85$0^{\circ}C$ thermal expansion coefficient of the specimen which was crystallized for 10hrs at 85$0^{\circ}C$ was 6.7$\times$10-7/$^{\circ}C$, which indicated that the crystallized specimen was turned out to be the glass-ceramic with low thermal expansion.

• Journal of the Korean Ceramic Society
• /
• v.24 no.5
• /
• pp.423-430
• /
• 1987

Characteristics of Al2O3-ZrO2 powders prepared by sol-gel process and their sintering behavior were investigated as a function of calcination temperature. The sol-gel processed powders were calcined at 800, 900, 1000, 1100, 1200$^{\circ}C$, and analyzed by X-ray diffraction technique. Pore size and distribution of green compact of the calcined powders were measured by mercury porosimeter. It is suggested that the optimal temperature of calcination for the sintering of Al2O3-ZrO2 powder prepared by sol-gel process is 1100$^{\circ}C$. In the Al2O3-17vol.% ZrO2 sintered specimen, which was sintered at 1600$^{\circ}C$ for 2hrs in air, 69vol.% tetragonal phse existed.

• Journal of the Korean Ceramic Society
• /
• v.52 no.1
• /
• pp.56-60
• /
• 2015

Discontinuous, polycrystalline $Al_2O_3$-dispersed TZP fibers were prepared by the centrifugal spinning of a colloidal $ZrO_2$ sol containing Y and Al nitrates and poly(vinyl alcohol). Factors affecting the rheological properties of the sols, such as sol concentrations, aging, and the amounts and types of additives, were investigated by measuring the shear viscosities. The flow characteristics of the sols were studied in relation to the spinnability by measuring the viscosity with respect to the shear rate. The spinnability was obtained through the addition of a polymer which increases the viscosity to a range of optimum viscosity values for spinning. Aging the sols containing the additives did not noticeably change the sol viscosities at room temperature up to 30 days. The flow behavior of the spinnable sols progressively changed from nearly Newtonian to pseudoplastic with an increase in the sol concentration.

• Journal of the Korean Ceramic Society
• /
• v.28 no.9
• /
• pp.705-711
• /
• 1991

Alumina precursor sol was obtained by the reaction of Al(OC4H9)3 and acetylacetone in the solvent followed by the partial hydrolysis. This sol was measured by viscosity and the effect of pH. The powders obtained from this sol were calcined at the various temperatures. The transition of crystals and crystal state were investigated at the various temperatures. The powders dried at 90$^{\circ}C$ showed amorphous and ${\gamma}$-Al2O3 at 900$^{\circ}C$, ${\alpha}$-Al2O3 mono-phase at 1050$^{\circ}C$ respectively. As a result of Al27-MASNMR analysis, amorphous and ${\alpha}$-Al2O3 powders showed 6-coordinated Al, ${\gamma}$-Al2O3 4-coordinated Al respectively.

• Journal of the Korean Ceramic Society
• /
• v.32 no.1
• /
• pp.63-70
• /
• 1995

A crack-free ceramic composite membrane with micropores has been synthesized by the pressurized sol-gel coating technique using the mixed Al2O3-SiO2 sols. The mixed sols were prepared by mixing nanoparticulate SiO2 and boehmite sols. These sols were more stable at lower pH, but very unstable when their copositions were in the range of 50~75mol% of SiO2 at the same pH. The mixed Al2O3-SiO2 membrane prepared from the mixed sol (0.2mol/$\ell$ of solid content and pH=2) containing 40mol% of SiO2 had the mean pore radius of 0.80nm and the specific surface area of 280$m^2$/g. The nitrogen permeability through the coated Al2O3-SiO2 layer was 42$\times$107mol/$m^2$.s.Pa. It was found that the thermal stability of aluminosilicate membranes, even through similar to that of SiO2 membranes, was much improved in comparison with ${\gamma}$-alumina membranes.

• Journal of the Korean Ceramic Society
• /
• v.29 no.9
• /
• pp.719-728
• /
• 1992

ZrO2/Al2O3-Mullite composites were prepared by infiltration of the silica sol to the porous ZrO2/Al2O3 bodies. The porous ZrO2/Al2O3 bodies for infiltration were fabricated using ZrO2 (20wt%)/Al2O3 composite powders synthesized by the emulsion-hot kerosene drying method. The preparation of silica sols was conducted by the hydrolysis-peptization of an alcoholic TEOS solution. When ZrO2/Al2O3-Mullite and ZrO2/Al2O3 composites were sintered at 1$650^{\circ}C$ for 4 hrs, both of them showed an excellent sinterability. As the amount of mullite added in the composites increased, the ratio of the tetragonal phase of zirconia to the monoclinic phase at the room temperature became higher. It was known that values of the fracture toughness of the ZrO2/Al2O3-Mullite composites were about 5.48 MPa.m1/2 much larger than that of the ZrO2/Al2O3 system.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.191-191
• /
• 2003

가시광선영역에서 높은 광학적 투명도를 갖는 n-type 반도체인 ZnO 박막은 넓은 범위에서 응용되고 있다. 현재 ZnO 박막의 특성 향상을 위하여 여러 원소(Al, Ga)의 도핑을 시도하고 있다. 특히 Al-doped ZnO 박막은 sol-gel dip coating에 의해서도 높은 전기전도도와 투과율로 활발히 연구되고 있다 본 논문에서는 여러 도핑농도를 갖는 Al-doped ZnO 박막이 sol-gel dip coating법에 의해 준비되었다. Al-doped ZnO 박막은 zinc acetate [Zn($CH_3$COO$_2$)ㆍ2$H_2O$] powder 와 여러 도핑농도를 갖는 aluminum nitrate (Al(NO$_3$)$_3$ㆍ9$H_2O$) powder를 알코올에 용해하여 $H_2O$, Ethylene glycol, Ethylene diamine 등을 첨가하여 제조하였다 XRD와 SEM (Scanning electron microscope)이 막의 상형성 분석을 위해 이용되었으며, 가시광선 영역 투과율(UV/VIS spectrophotometer)과 표면전기저항(four point probe)이 주요 특성으로 분석되었다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.2
• /
• pp.59-65
• /
• 2006

Al-doped and F-doped ZnO (ZnO : Al & ZnO : F) thin films were coated onto glass substrate by sol-gel method. These films showed c-axis orientation in common, but different I(002)/[I(002) + I(101)] and FWHM (full width at half-maximum). In particular, the grain size of the ZnO : Al films decreased with the increase in the Al-doping concentration, while for the ZnO : F films the grain siae increased up to F 3 at% and then decreased. For the electrical properties, Hall effect measurement was used. The resistivity of the ZnO : Al films and the ZnO : F films were, respectively, $2.9{\times}10^{-2}{\Omega}cm$ at Al 1 at% and $3.3{\times}10^{-1}{\Omega}cm$ at F 3 at%. Moreover compared with ZnO:Al films, ZnO:F films have lower carrier concentration (ZnO : Al $4.8{\times}10^{18}cm^{-3}$, ZnO : F $3.9{\times}10^{16}cm^{-3}$) and higher mobility (ZnO : Al $45cm^2/Vs$, ZnO : F $495cm^2/Vs$). For average optical transmittances, ZnO : Al thin films have $86{\sim}90%$ and ZnO : F films have $77{\sim}85%$ comparatively low.