• Journal of the Korean institute of surface engineering
• /
• v.50 no.1
• /
• pp.35-41
• /
• 2017

$TiO_2$, $Al_2O_3$, and $TiO_2-Al_2O_3$ nanolaminated films were grown by atomic layer deposition (ALD) on the 316L stainless steel (SS316L) substrates at a temperature of $150^{\circ}C$. The growth kinetics of $ALD-TiO_2$ and $Al_2O_3$ thin films were systematically investigated in order to precisely control the thickness of each layers in the $TiO_2-Al_2O_3$ nanolaminated films using a high-resolution transmission electron microscopy. And, the exact deposition rates of $ALD-TiO_2$ on $Al_2O_3$ surface and $ALD-Al_2O_3$ on $TiO_2$ surface were revealed to be 0.0284 nm/cycle and 0.11 nm/cycle, respectively. At given growth conditions, the microstructures of $TiO_2$, $Al_2O_3$ and $TiO_2-Al_2O_3$ nanolaminated films were amorphous. The potentiodynamic polarization test revealed that the $TiO_2-Al_2O_3$ nanolaminated film coated SS316L had a best corrosion resistance, although all ALDcoated SS316L exhibited a clear improvement of the corrosion resistance compared with a bare SS316L.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.1
• /
• pp.3-9
• /
• 2000

Arc-melted alloys of TiAl-(o.25, 0.5, 1.0at%) Si were isothermally oxidized at 800, 900 and $1000^{\circ}C$ in air for 60hr. It was found that the oxidation resistance of the prepared TiAl-Si alloys was much better than that of pure TiAl, being progressively increasing with an increase in the Si content. This was attributed to the formation of $SiO_2$in addition to ($TiO_2$+$Al_2$$O_3$) oxides which formed in TiAl alloys with and without silicon additions. However, the silica formation within the oxide layer unfortunately accelerated the oxide scale spallations. During oxidation, all the elements in the base alloy diffused outward, whereas oxygen from the atmosphere diffused inward. The oxides were primarily composed of an outer thick $TiO_2$layer, an intermediate diffuse $Al_2$$O_3$layer and an inner $TiO_2$layer. A small amount of $SiO_2$was present all over the oxide scale and some voids were found around the intermediate layer.

• Journal of the Korean Ceramic Society
• /
• v.30 no.1
• /
• pp.1-6
• /
• 1993

Dielectric and piezoelectric porperties of pseudoternary xPb(Al2/3W1/3)O3-(1-x)Pb(Zr0.52Ti0.48)O3 (x=1~10mol%) ceramic system have been investigated as a function of the amount of PAW[Pb(Al2/3W1/3)O3] and sintered from 110$0^{\circ}C$ to 120$0^{\circ}C$ for 1hr. As the amount of PAW increases, the c/a of tetragonal structure decreases. The grain size was reduced with increasing the amount of PAW addition. However, the density, dielectric constant and electromechanical coupling factor(kp) exhibited a maximum value at the amount of 5mol% PAW addition.

• Journal of Welding and Joining
• /
• v.10 no.4
• /
• pp.213-221
• /
• 1992

Al$_{2}$O$_{3}$ ceramic coating layer by gas flame spraying was very porous, therefore it could not have wear and corrosion resistance at all. To get a dense and strong coating layer, a method to infiltrate an alloy into the pores of $Al_{2}$O$_{3}$ ceramic coating was investigated. Cu-Ti alloys, which had good wettability and reactivity with $Al_{2}$O$_{3}$ ceramic, were examined for infiltration. Infiltration of the alloys was performed in vacuum at 1100.deg.C. The melt of Cu-50 at % Ti alloy was well penetrated through the porous $Al_{2}$O$_{3}$ coating and tightly sealed the pores, unbounded area and microcracks in the coating. The alloy melt in the pores reacted with $Al_{2}$O$_{3}$ ceramic to produce a suboxide phase, Cu$_{2}$Ti$_{4}$O. This composite layer which was composed of $Al_{2}$O$_{3}$ and Cu$_{2}$Ti$_{4}$O phase had good microstructure and wear and corrosion resistance. Additionally, microstructures at interfaces between coating layers were greatly improved owing to the effect of vacuum heat treating.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05c
• /
• pp.67-70
• /
• 2002

The composites were fabricated 61vol% ${\beta}$-SiC and 39vol.% $TiB_2$ powders with the liquid forming additives of 8, 12, 16wt% $Al_2O_3+Y_2O_3$ by pressureless annealing at $1650^{\circ}C$ for 4 hours to form YAG. The result of phase analysis of composites by XRD revealed ${\alpha}$-SiC(6H), $TiB_2$, and YAG($Al_5Y_3O_{12}$) crystal phase. The relative density and the Young's modulus showed the highest value of 82.29% and 54.60 Gpa for composites added with 16wt% $Al_2O_3+Y_2O_3$ additives at room temperature.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1289-1290
• /
• 2007

The composites were fabricated 61Vo.% ${\beta}$-SiC and 39Vol.% $TiB_2$ powders with the liquid forming additives of 12wt% $Al_{2}O_{3}+Y_{2}O_{3}$ as a sintering aid by pressure or pressureless annealing at $1650^{\circ}C$ for 4 hours. The present study investigated the influence of annealed sintering on the microstructure and mechanical of SiC-$TiB_2$ electroconductmive ceramic composites. Reactions between SiC and transition metal $TiB_2$ were not observed in the microstructure and the phase analysis of the SiC-$TiB_2$ electroconductive ceramic composites. Phase analysis of SiC-$TiB_2$ composites by XRD revealed mostly of ${\alpha}$-SiC(6H), $TiB_2$, and In Situ YAG($Al_{5}Y_{3}O_{12}$). The relative density, the flexural strength, the Young's modulus showed the highest value of 86.69[%], 136.43[MPa], 52.82[GPa] for pressure annealed SiC-$TiB_2$ ceramic composites.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.6
• /
• pp.288-294
• /
• 2006

Alloys of TiAl-Mn-(0, 5, 10)wt.% $Y_2O_3$ were prepared by a powder metallurgical route, and their oxidation behavior was studied at 800, 900 and $1000^{\circ}C$ in 1 atm of air. The scale formed on the alloys consisted of $TiO_2$ and $Al_2O_3$ oxides. During oxidation, Mn tended to diffuse outward, whereas oxygen diffused inward. The dispersoids of $T_2O_3$, which segregated at the matrix grain boundaries, acted as a diffusion channel for cations and oxygen ions, nucleation sites for oxides, and vacancy annihilation sites. $T_2O_3$ increased the scale thickness, but improved the scale adherence.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.9
• /
• pp.807-811
• /
• 2003

We investigated the electrical characterisitics of T $a_2$ $O_{5}$ (tantalum pentoxide) film and Ti-O/T $a_2$ $O_{5}$ film deposited on $Al_2$ $O_3$based substrate. Ta (tantalum) electrode and $Al_2$ $O_3$ substrate was used for the purpose of simplifying the manufacturing process in IPD's (integrated passive devices). Dielectric materials (T $a_2$ $O_{5}$ and Ti-O/T $a_2$ $O_{5}$ films) deposited on Ta/Ti/A $l_2$ $O_3$ were annealed at 700 $^{\circ}C$ for 60 sec. in vacuum. The XRD results showed that as-deposited T $a_2$ $O_{5}$ film possessed amorphous structure, which was transformed to crystallines by rapid thermal heat treatment. We compared the lnJ- $E^{{\frac}{1}{2}}$, C-V, C-F of both as-deposited and annealed dielectric thin films deposited on Ta bottom electrode. From this results, we concluded that the leakage current could be reduced by introducing Ti-O buffer layer and conduction mechanisms of T $a_2$ $O_{5}$ and Ti-O/T $a_2$ $O_{5}$ could be interpreted appropriately by Schottky emission effect.

• Journal of the Korean Ceramic Society
• /
• v.38 no.7
• /
• pp.621-627
• /
• 2001

알루미나 졸에 평균 25nm의 TiO$_2$(Degussa P25) 광 촉매 분말을 분산하여 광촉매 코팅제를 제조하였다. 점도 약 24 cps를 가지 4.4 wt%의 알루미나 졸로부터 약 300nm 두께의 코팅막이 제조되었으며, 졸 점도의 증가에 비례하여 코팅막의 두께도 증가하였다. TiO$_2$광 촉매의 코팅용 바인더로 이용한 알루미나 졸의 결정형은 25~30$0^{\circ}C$에서 pseudo boehmite (AlOOH)이었으며, 50$0^{\circ}C$ 이상에서는 ${\gamma}$-Al$_2$O$_3$으로 전환되었다. AlOOH/TiO$_2$코팅막은 oleic acid와 humic acid에 대한 기상 및 수상 조건에서의 광 촉매 실험에서 우수한 유기물의 광분해 효능을 나타내었다. 아울러 EGI(Electro-Galvanized Iron)에 코팅된 AlOOH/TiO$_2$코팅막은 내식성 및 내지문성의 효과도 부수적으로 나타내었다.

• Journal of Powder Materials
• /
• v.2 no.3
• /
• pp.231-237
• /
• 1995

The powder mixtures of Al, Ti and Cr were mechanically alloyed to obtain nanocrystalline powders of $Ti_{25}Cr_8Al_{67}$ composition. Both FCC phase and undissolved metal chromium formed by MA. During the annealing of the MA powders, the phase transition from FCC to ordered $Ll_2$ started at ~$300^{\circ}C$ and was completed below $600^{\circ}C$. As a result of the high-temperature compressive test for the MA powder compacts, the stress-strain curves showed serrated yielding behavior at 400 and $600^{\circ}C$, and softening phenomenon below the strain rate of $5{\times}10^{-3}s^{-1}$ at $800^{\circ}C$. The compressive yield strength as a function of test temperatures showed the nature of the positive-temperature dependence which has the peak temperature around $600^{\circ}C$.