• Journal of the Korean Vacuum Society
• /
• v.9 no.4
• /
• pp.373-378
• /
• 2000

There was a great difference in the formation kinetics of $TiO_2$ and $Bi_2O_3$ on silicon, but the growth of bismuth titanate (BIT) thin film was mainly limited by the formation of $TiO_2$. As a result, the BIT film was easy to be lack of bismuth. The pulse injection metalorganic chemical vapor deposition (MOCVD) process was introduced in order to overcome this problem by recovering the insufficient bismuth content in the film. By this pulse injection method, bismuth content was increased and also the uniform in-depth composition of the film was attained with a abrupt $Bi_4Ti_3O_{12}/Si$ interface. In addition, the crystallinity of $Bi_4Ti_3O_{12}$ thin film prepared by pulse injection process was greatly improved and the leakage current density was lowered by 1/2~1/3 of magnitude. Clockwise hysteresis of C-V was observed and the ferroelectric switching was confirmed for $Bi_4Ti_3O_{12}$ film deposited by pulse injection method.

• Journal of the Korean Ceramic Society
• /
• v.35 no.11
• /
• pp.1130-1140
• /
• 1998

Thin films of $Bi_4Ti_3O_{12}\;nBaTiO_3(n=1&2)$ were prepared using sols erived Ba-Bi-Ti complex alkoxides. The sols were spin-cast onto $Pt/Ti/SiO_2/Si$ substrates and followed by pyrolysis for 1 hr at $620^{\circ}C,\;700^{\circ}C\;and\;750^{\circ}C$ In the thin films a pyrochlore phase seemed to be formed at a lower temperature and then tran-formed to the layered perovskite phase as the heating temperature increased. In the thin films pyrolyzed at formed to the layered perovskte phase as the heating temperature increased. In the films pyrolyzed at $750^{\circ}C$ the amount of $Bi_4Ti_3O_{12}{\cdot}BaTiO_3$ reached to 94% while $Bi_4Ti_3O_{12}{\cdot}BaTiO_3$ was 77% in composition. This result shows that the formation of the layered pervoskite phase becomes difficult as the amount of complexing $BaTiO_3$ increases. The microstructures and the electrical properties of the thin films were gen-erally improved with the incease of the heating temperature. However the presence of the pyrochlore phase could not be removed effectively. Our study showed that the electrical properties of $Bi_4Ti_3O_{12}{\cdot}BaTiO_3$ were pronouncedly improved with complexing with BaTiO3 when compared to those of $Bi_4Ti_3O_{12}$ while the presence of the pyrochlore phase was detrimental to the those of $Bi_4Ti_3O_{12}{\cdot}2BaTiO_3$.

• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.897-907
• /
• 1997

Thin films of Bi4-xSmxTi3O12(0$\leq$x$\leq$2) were prepared on Pt/Ti/SiO2/Si(100) at $700^{\circ}C$ using spin-coating with sols derived from Bi-Sm-Ti complex alkoxides. From X-ray diffraction analysis, it was observed that Sm-substituted phases resembled ferroelectric Bi4Ti3O12 in structure. Variations of their lattice parameters depending on the amount of Sm-substitution showed that an anomalous structural distortion might exist at x=1. The grain sizes of the thin films decreased from 0.115 ${\mu}{\textrm}{m}$ to 0.078${\mu}{\textrm}{m}$ with increasing the amount of Sm-substitution. The dielectric constants and the remanent polarizations of the thin films decreased with increasing the amount of the Sm-substitution, which were related to decrease of the stereo-active Bi3+ ion contributing to polarization. However, these values were exceptionally high at x=1, compared to those of the other substituted phases. Such an anomaly suggests that the phase of x=1 has 1:1 chemical ordering between Sm and Bi in structure. The thin films of all compositions except x=2 showed ferroelectricity. The thin film of x=2 was paraelectric, whose grains were too fine to exhibit ferroelectricity.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.6
• /
• pp.272-278
• /
• 2003

$Bi_4Ti_3O_{12}$ (BIT) and $(Bi_{3.25}La_{0.75})(Ti_{2.97}V_{0.03})O_{12}$ (BLTV) thin films were deposited on ITO/glass substrates by metal organic chemical vapor deposition (MOCVD) using ultrasonic spraying. After deposition of the films in oxygen atmosphere for 30 min, the films were heated by rapid thermal annealing (RTA) method, especially direct insertion, at various temperatures. The films were investigated on phase formation temperature, microstructure and electrical properties. From x-ray diffraction (XRD) patterns, the perovskite phase formation temperature of BLTV thin film was about $600^{\circ}C$ which was lower than that of BIT, $650^{\circ}C$. The leakage current of the BLTV thin film was measured to be $1.52\times 10^{-9}$A/$cm^2$ at an applied voltage of 1 V. The remanent polarization (Pr) and coercive field (Ec) values of the BLTV film deposited at $650^{\circ}C$ were $5.6\muC/cm^2$ and 96.5 kV/cm, respectively.

• Korean Journal of Materials Research
• /
• v.14 no.10
• /
• pp.701-706
• /
• 2004

Bismuth layered structure ferroelectric thin films, La-substituted $Bi_{4}Ti_{3}O_{12}$ ($Bi_{1-x}La_{x}Ti_{3}O_{12}$, x=0.75, BLT) were prepared on the $Pt(111)/Ti/SiO_2/Si(100)$ substrates by a sol-gel spin coating process. The thin films were annealed in various conditions, i.e., oxygen, nitrogen and vacuum atmospheres for various annealing time. We investigated the annealing condition effects on the grain orientation and ferroelectric properties. The measured XRD patterns revealed that the BLT thin films showed only $Bi_{4}Ti_{3}O_{12}$-type phase with random orientation. $La^{3+}$ ion substitution for $Bi^{3+}$ ion in perovskite layers of $Bi_{4}Ti_{3}O_{12}$ decreased the degree of c-axis orientation and increased the remanent polarization ($2P_{r}$). The remanent polarization ($2P_{r}$) and the coercive field ($2E_{c}$) of the BLT thin film annealed at $650^{\circ}C$ for 5 min in oxygen atmosphere were $87{\mu}C/cm^2$ and 182 kV/cm, respectively, at an applied electric field of 240 kV/cm. For all of the BLT thin films annealed in various conditions, the fatigue resistance was shown. The improvement of ferroelectric properties with La substitution in $Bi_{4}Ti_{3}O_{12}$ could be attributed to the changes in space charge densities and grain orientation in the thin film.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.67 no.4
• /
• pp.543-548
• /
• 2018

Ferroelectric $Bi_4Ti_3O_{12}$ films were deposited on $SrTiO_3(100)$ and Si(100) substrate by using conductive $SrRuO_3$ films as underlayer, and their ferroelectric and electrical properties were investigated depending on crystal structure and orientation. C-axis oriented $Bi_4Ti_3O_{12}$ films were grown on well lattice-matched pseudo-cubic $SrRuO_3$ films deposited on $SrTiO_3(100)$ substrate, while random-oriented polycrystalline $Bi_4Ti_3O_{12}$ films were grown on $SrRuO_3$ films deposited on Si(100) substrate. The random-oriented polycrystalline film showed a good ferroelectric hysteresis property with remanent polarization ($P_r$) of $9.4{\mu}C/cm^2$ and coercive field ($E_c$) of 84.9 kV/cm, while the c-axis oriented film showed $P_r=0.64{\mu}C/cm^2$ and $E_c=47kV/cm$ in polarizaion vs electric field curve. The c-axis oriented $Bi_4Ti_3O_{12}$ film showed a dielectric constant of about 150 and lower thickness dependence in dielectric constant compared to the random-oriented film. Furthermore, the c-axis oriented $Bi_4Ti_3O_{12}$ film showed leakage current lower than that of the polycrystalline film. The difference of ferroelectric properties in two films was explained from the viewpoint of depolarization effect due to orientation of spontaneous polarization and layered crystal structure of bismuth-base ferroelectric oxide.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.1002-1005
• /
• 1998

Bismuth titanate thin films were prepared on {{{{ { SrTiO}_{3 } }}(100) and Si(100) substrates by dipping-pyrolysis pro-cess using metal naphthenates as starting materials. crystallinity and in-phase alignment of the films were analyzed by X-ray diffraction $\theta$-2$\theta$ scans and $\beta$ scans (pole-figures) respectively. Highly c-axis-oriented {{{{ { { {Bi }_{4 }Ti }_{3 }O }_{12 } }} thin films with smooth surfaces were obtained after heat treatment at 75$0^{\circ}C$ on {{{{ { SrTiO}_{3 } }}(100) sub-strate while the films grown of Si(100) exhibited polycrstalline characteristics. C-axis oriented film show-ed an epitaxial relationship with the {{{{ { SrTiO}_{3 } }} substrate.

• Journal of Electrical Engineering and Technology
• /
• v.2 no.1
• /
• pp.98-101
• /
• 2007

Yttrium(Y)-substituted bismuth titanate $(Bi_{4-x},Y_x)Ti_3O_{12}$ [x=0, 0.25, 0.5, 0.75, 1](BYT) thin films were deposited using an RF sputtering method on the $Pt/TiO_2/SiO_2/Si$ substrates. The structural properties and electrical properties of yttrium-substituted $(Bi_4-xYx)Ti_3O_{12}$ thin films were analyzed. The remanent polarization of $(Bi_4-xYx)Ti_3O_{12}$ films increased with increasing Y-content. The $(Bi_{3.25}Y_{0.75})Ti_3O_{12}$ films fabricated using a top Au electrode showed saturated polarization-electric field(P-E) switching curves with a remanent polarization(Pr) of $8{\mu}C/cm^2$ and coercive field (Ec) of 53 kV/cm at an applied voltage of 7 V. The $(Bi_{3.25}Y_{0.75})Ti_3O_{12}$ films exhibited fatigue-free behavior up to $4.5{\times}10^{11}$ read/write switching cycles at a frequency of 1MHz.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.4
• /
• pp.290-296
• /
• 2009

$Bi_{4}Ti_{3}O_{12}$ (BiT) thin films were grown on the Pt/Ti/$SiO_2$/si substrate using a metal organic decomposition (MOD) method. Effects of oxygen annealing on the structural properties and dielectric properties of the BiT thin films were investigated. The BiT films were well developed when rapid thermal annealed at $>500^{\circ}C$ in oxygen ambient. For the film annealed at $700^{\circ}C$, no crystalline phase was observed under oxygen free annealing atmosphere while its crystallinity was significantly enhanced as the oxygen pressure increased. The BiT film also exhibited a smooth surface with defect free grains. A high dielectric constant and a low dielectric loss were achieved satisfactory in the frequency range from 75 kHz to 1 MHz. Especially, the BiT film, annealed at $700^{\circ}C$ and 10 torr oxygen pressure, showed good dielectric properties: dielectric constant of 51 and dielectric loss of 0.2 % at 100 kHz. Its leakage current was also considerably improved, being as $0.62\;nA/cm^2$ at 1 V. Therefore, it is considered that the oxygen annealing has effects on an enhancement of crystallinity and dielectric properties of the BiT films.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.197.1-197
• /
• 2000