• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.1
• /
• pp.40-44
• /
• 2022

Wet etching of α-Ga₂O₃ epitaxy film was performed using a 35 % hydrochloric (HCl) acid solution. As the temperature of the 35 % HCl solution increased, the α-Ga₂O₃ etch rate increased, and the etch rate of 119.6 nm/min was obtained at 75℃, the highest temperature examined in this work. The activation energy for etch reaction was determined to be 0.776 eV, and this suggests that the wet etching of α-Ga₂O₃ in the 35 % HCl solution was dominated by the reaction-limited mechanism. AFM analysis showed that the surface roughness of the etched surface increased as the temperature of the etchant solution increased.

• Korean Journal of Crystallography
• /
• v.8 no.1
• /
• pp.33-37
• /
• 1997

The optical properties of (1210) GaN epitaxy films grown on the (1012) $\alpha-A1_2O_3$ substrates have been studied. The hetero-epitaxy films were grown by the halide vapor phase epitaxy (HVPE) method using $Ga/HC1/NH_3/He$ system at $990^{\circ}C$. XRD, RHEED and SEM are used for the identification of the hetero-epitaxy films structure and surface morphology. The confirmed (1210) GaN epitaxy films were characterized by PL and Raman. By the Raman scattering, the active phonon modes of single-phase GaN films are varied with the arrangement of both polarization and propagation directions of laser beam with reference to the axis in single-phase crystal films. The Y(Z, Y & Z) X geometry allows scattering pat-terns of $A_1(TO)=533\;cm^{-1},\;E_1(TO)=559\;cm^{-1}\;and\;E_2=568 cm^{-1}$ modes, whereas in the Z(Y, Y & Z) X geometry the only $E_2$ mode are observed.

• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.4
• /
• pp.113-118
• /
• 2019

In this study, we investigated the growth of single-crystallinity α-Ga₂O₃ thin films on c-plane sapphire substrates using halide vapor pressure epitaxy. We also found the optimal growth conditions to suppress the phase transition of α-Ga₂O₃. Our results confirmed that the growth temperature and partial pressure of the reactive gas greatly influenced the crystallinity. The optimal growth temperature range was about 460~510℃, and the α-Ga₂O₃ thin films with the highest crystallinity were obtained at a III/VI ratio of 4. The thickness and surface morphology of the thin films was observed by scanning electron microscopy. The film thickness was 6.938 ㎛, and the full width at half maximum of the ω-2θ scan rocking curve was as small as 178 arcsec. The optical band gap energy obtained was 5.21 eV, and the films were almost completely transparent in the near-ultraviolet and visible regions. The etch pit density was found to be as low as about 6.0 × 10⁴ cm^-2.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.6
• /
• pp.425-433
• /
• 2000

The stochiometric mix of evaporating materials for the $CuGaTe_2$single crystal thin films was prepared from horizontal furnance. Using extrapolation method of X-ray diffraction patterns for the $CuGaTe_2$polycrystal, it was found tetragonal structure whose lattice constant $a_0 and c_0$ were 6.025 $\AA$ and 11.931 $\AA$, respectively. To obtain the single crystal thin films, $CuGaTe_2$mixed crystal was deposited on throughly etched semi-insulator GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $670^{\circ}C$ and $410^{\circ}C$ respectively, and the thickness of the single crystal thin films is 2.1$\mu\textrm{m}$. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). Hall effect on this sample was measured by the method of van der Pauw and studied on carrier density and mobility dependence on temperature. The carrier density and mobility of $CuGaTe_2$single crystal thin films deduced from Hall data are $8.72{\times}10{23}$개 $\textrm m^3$, $3.42{\times}10^{-2}$ $\textrm m^2$/V.s at 293K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $CuGaTe_2$single crystal thin film, we have found that the values of spin orbit coupling $\Delta$s.o and the crystal field splitting $\Delta$cr were 0.0791 eV and 0.2463 eV at 10 K, respectively. From the PL spectra at 10 K, the peaks corresponding to free bound excitons and D-A pair and a broad emission band due to SA is identified. The binding energy of the free excitons are determined to be 0.0470 eV and the dissipation energy of the donor-bound exciton and acceptor-bound exciton to be 0.0490 eV, 0.0558 eV, respectively.