A boron doping process using a boron tri-bromide ($BBr_3$) as a boron source was applied to form a $p^+$ emitter layer on an n-type mono-crystalline CZ substrate. Nitrogen ($N_2$) gas as an additive of the diffusion process was varied in order to study the variations in sheet resistance and the uniformity of doped layer. The flow rate of $N_2$ gas flow was changed in the range 3 slm~10 slm. The sheet resistance uniformity however was found to be variable with the variation of the $N_2$ flow rate. The optimal flow rate for $N_2$ gas was found to be 4 slm, resulting in a sheet resistance value of $50{\Omega}/sq$ and having a uniformity of less than 10%. The process temperature was also varied in order to study its influence on the sheet resistance and minority carrier lifetimes. A higher lifetime value of $1727.72{\mu}s$ was achieved for the emitter having $51.74{\Omega}/sq$ sheet resistances. The thickness of the boron rich layer (BRL) was found to increase with the increase in the process temperature and a decrease in the sheet resistance was observed with the increase in the process temperature. Furthermore, a passivated emitter solar cell (PESC) type solar cell structure comprised of a boron doped emitter and phosphorus doped back surface field (BSF) having Ni/Cu contacts yielding 15.32% efficiency is fabricated.

We report hybrid solar cells fabricated with polymer/fullerene bulk heterojunction layers that contain inorganic nanocrystals synthesized by in-situ reaction in the presence of polymer chains. The inorganic (cadmium sulfide) nanocrystal ($CdS_{NC}$) was generated by the reaction of cadmium acetate and sulfur by varying the reaction time up to 30 min. The synthesized $CdS_{NC}$ showed a rectangular flake shape, while the size of $CdS_{NC}$ reached ca. 150 nm when the reaction time was 10 min. The performance of hybrid solar cells with $CdS_{NC}$ synthesized for 10 min was better than that of a control device, whereas poor performances were measured for other hybrid solar cells with $CdS_{NC}$ synthesized for more than 10 min.

Colloidal quantum dot (CQD) solar cells have attracted great attention due to their cost-effectiveness and solution-processability, as well as their size-dependent optical and electrical properties. The power conversion efficiency of CQD solar cells has rapidly increased up to ~8.6%, which corresponds to the 3 - 4 fold improvement during the last 3 - 4 years. Up to now, there have been many pioneering results in CQD solar cells. Here, we review the recent progress of CQD solar cells including CQD synthesis strategy and device structure engineering.

Under concentrated illuminations, the solar cells show higher efficiencies mainly due to an increase of the open circuit voltage. In this study, InGaP/InGaAs/Ge triple-junction solar cells have been grown by a low pressure metalorganic chemical vapor deposition. Photovoltaic characteristics of the fabricated solar cells are investigated with a class A solar simulator under concentrated illuminations from 1 to 100 suns. Ideally, the open circuit voltage should increase with the current level when maintained at the same temperature. However, the fabricated solar cells show degraded open circuit voltages under high concentrations around 100 suns. This means that the heat sink design is not optimized to keep the cell temperature at $25^{\circ}C$. To demonstrate the thermal degradation, changes of the device performance are investigated with different bonding conditions and heat sink materials.

We have investigated the seed layer formation of front side contact using the inkjet printing process. Conductive silver ink was printed on textured Si wafers with 80 nm thick $SiN_x$ anti reflection coating (ARC) layers and thickened by light induced plating (LIP). The inkjet printable sliver inks were specifically formulated for inkjet printing on these substrates. Also, a novel method to prepare nano-sized glass frits by the sol-gel process with particle sizes around 5 nm is presented. Furthermore, dispersion stability of the formulated ink was measured using a Turbiscan. By implementing these glass frits, it was found that a continuous and uniform seed layer with a line width of $40{\mu}m$ could be formed by a inkjet printing process. We also investigated the contact resistance between the front contact and emitter using the transfer length model (TLM). On an emitter with the sheet resistance of $60{\Omega}/sq$, a specific contact resistance (${\rho}_c$) below $10m{\Omega}{\cdot}cm^2$ could be achieved at a peak firing temperature around $700^{\circ}C$. In addition, the correlation between the contact resistance and interface microstructures were studied using scanning electron microscopy (SEM). We found that the added glass particles act as a very effective fire through agent, and Ag crystallites are formed along the interface glass layer.

$Cu_2ZnSn(S_xSe_{1-x})_4$ (CZTSSe) absorber thin films were prepared on Mo coated soda lime glass substrates by sulfo-selenization of sputtered stacked Zn-Sn-Cu precursor thin films. The Zn-Sn-Cu precursor thin films were sulfo-selenized inside a graphite box containing S and Se powder using rapid thermal processing furnace at $540^{\circ}C$ in Ar atmosphere with pre-treatment at $300^{\circ}C$. The effect of different S/Se ratio on the structural, compositional, morphological and electrical properties of the CZTSSe thin films were studied using XRD (X-ray diffraction), XRF (X-ray fluorescence analysis), FE-SEM (field-emission scanning electron microscopy), respectively. The XRD, FE-SEM, XRF results indicated that the properties of sulfo-selenized CZTSSe thin films were strongly related to the S/Se composition ratio. In particular, the CZTS thin film solar cells with S/(S+Se)=0.25 shows best conversion efficiency of 4.6% ($V_{oc}$ : 348 mV, $J_{sc}$ : $26.71mA/cm^2$, FF : 50%, and active area : $0.31cm^2$). Further detailed analysis and discussion for effect of S/Se composition ratio on the properties CZTSSe thin films will be discussed.

For the dissemination of new and renewable energy, Korean government introduced a renewable portfolio standard (RPS) scheme in 2012 after terminating feed-in tariff (FIT) scheme that was introduced in 2004. With the RPS scheme, 64.7% of its own goal (95.7% in PV and 63.3% in non-PV) was achieved in 2012 and 67.2% of that (94.9% in PV, 65% in non-PV) was achieved in 2013. The deployment of PV systems met the goal very well and that of non-PV did not. Recently, Korean government revised the target year of supplying 10% electricity from new and renewable energy from 2022 to 2024 and released a couple of measures on PV area. Recent studies showed that the bankability of a project plays a key role for PV dissemination. Therefore, the dissemination should be assessed from the point of bankability under the RPS scheme and a little adjustment is necessary to achieve the goal. Especially, installing a small size PV (<100 kwp) system needs a minimum REC price or a FIT scheme. In non-PV area, permission process is a common bottleneck and the related regulation should be eased. In addition, to achieve the long term goal, an implementing scenario has to be prepared. Currently, the portion of the waste-gas energy originated from fossil fuel is too large among the new and renewable energy sources and the portion should be lowered or eliminated in the 10% of electricity supply goal. Seoul Metropolitan Government (SMG) has its own FIT scheme for PV dissemination from 2014 SMG and revised the PV tariff from 50 to 100 won/kwh in effective of 2015. It is worth to spread the other provinces.

In this paper, We have simulated the output variation of the PV arrays installation with position & angle change. The existing 3 solar array system are $43^{\circ}$ southeast and each of the mounting angle is $17^{\circ}$. The PV output power is 240 kW. The composite studied systems in this paper arrays altered 2 PV array among 3 PV array system- the output 144kW. We simulated this system using Solar Pro ver.4.1. The simulation conditions are southwest $43^{\circ}/array$, mount angle $27^{\circ}/array$. Because the southeast have shadow effect-higher mountain The purpose of southwest $43^{\circ}$ is reduce the shadow effect. The simulation results of the suggestion design algorithm compared to 1,590 kWh/year output is increased with the southeast.