Abstract
Polycarbonates (PCs) with six different end capping agents were synthesized from melt polymerization. Chemical structure of the synthesized PC was determined by FT-IR spectroscopy. The average molecular weight and distribution, glass transition and thermal degradation temperatures were determined by GPC, DSC and TGA. Average molecular weight changed with the chemical structure of end capping agent, and 4-tert-butylphenol was estimated as the optimum end capping agent. The average molecular weights of PCs decreased with the concentration of the agent, the number average molecular weight was observed as 20,000 - 30,000 when 0.05-0.15 mol% of 4-tert-butylphenol added in PCs. The melt viscosities and glass transition temperature of the PCs decreased with molecular weight. The change for adding method of the agent affected on both the molecular weight distribution and decrease in power law index.
말단캡핑제(end capping agent) 6종류에 대해 폴리카보네이트를 용융중합법으로 제조하였다. 합성된 폴리카보네이트의 화학구조는 FT-IR 스펙트럼을 이용하여 확인하였다. 평균분자량 및 분자량분포도, 유리전이 온도 및 열분해 온도는 GPC, DSC와 TGA를 이용하여 측정하였다. 말단캡핑제의 화학구조에 따라 평균분자량이 증가 또는 감소를 나타내었으며, 말단캡핑제로 4-tert-butylphenol (TBP)이 사용되었을 때 최적의 분자량 조절 결과를 나타내었다. 말단캡핑제의 함량이 증가할수록 평균분자량은 감소하였고, 4-tert-butylphenol이 0.05 - 0.1 mol%가 첨가될 때 폴리카보네이트의 대형 사출물 가공에 적합한 20,000 - 30,000 정도의 수평균분자량을 나타내었다. 폴리카보네이트의 용융점도와 유리전이온도는 분자량이 감소할수록 감소하였다. 말단캡핑제의 투입방법 변경은 PC의 분자량분포도에 영향을 주었고, power law index의 감소를 보여주었다.