Abstract
We prepared 100 nm-thick CoNi composite silicide on a 70 nm-thick polysilicon substrate. Composite silicide laye.s were formed by rapid thermal annealing(RTA) at the temperatures of $700^{\circ}C,\;900^{\circ}C,\;1000^{\circ}C$ for 40 seconds. A Focused ion beam (FIB) was used to make nano-patterns with the operation range of 30 kV and $1{\sim}100$ pA. We investigated the change of thickness, line width, and the slope angle of the silicide patterns by FIB. More easily made with the FIB process than with the conventional polycide process. We successfully fabricated sub-100nm etched patterns with FIB condition of 30kv-30pA. Our result implies that we may integrate nano patterns with our newly proposed CoNi composite silicides.
기판전면에 패턴 없이 15 nm Co/15 nm Ni/70 nm polysilicon/200 nm $SiO_2$/Si(100) 구조로 적층된 구조로부터 급속열처리기 (rapid thermal annealer : RTA)를 이용하여 40초간 700, 900, $1000^{\circ}C$의 실리사이드화 온도를 변화시키면서 CoNi 복합실리사이드를 형성하였다. 완성된 두께 100 nm 정도의 CoNi 복합실리사이드층으로 배선층을 만든다고 상정하여, 이중 집속이온빔(dual beam focused ion beam : FIB)을 써서 30 kV에서 표면전류를 $1{\sim}100$ pA 범위에서 조절하면서 나노급 선폭제작의 가능성을 확인하였다. 각 온도별 복합실리사이드에 동일한 이온빔 조건으로 $100{\mu}m$ 길이의 패턴을 만들고, 이온빔으로 양 끝단에 트렌치를 만들어 FE-SEM으로 각 조건에서의 선폭, 두께, 최종 에칭형상을 확인하였다. 기존 형상변형이 많아서 나노급 선폭 구현이 불리한 폴리사이드 공정에 비해서, 최초로 새로운 저저항 복합실리사이드에 대해서 100 nm 이하의 나노급 피치를 가진 선폭 제작이 $30kV{\sim}30pA$ 범위에서 가능하였다.