Abstract
This study was done to evaluate whether vital bleaching agents could influence on the translucency of the bovine enamel. The anterior bovine teeth that were extracted one day before and without any gross discoloration were obtained and then were preserved in physiologic saline. 6 mm cylindrical tooth specimens were fabricated with diamond puncher perpendicularly on labial surface of bovine tooth. After embedded in transparent acrylic resin with labial surface being exposed, they were cut to a thickness of 1.2 mm with low speed diamond saw (Isomat, Buehler Co., Lake Bluff, IL, USA). They were smoothly ground to 1 mm thickness of enamel with sandpaper. 24 specimens were randomly divided into 3 groups and control group respectively. Opalescence (10% carbamide peroxide, Ultradent, South Jordan, USA), Rembrandt (10% carbamide peroxide, DenMat, USA) and Opalescence F (15% carbamide peroxide with fluoride, Ultradent, USA) were applied on labial sides of the bovine enamel for 7 days (bleaching agents were reapplied every 24 hours) and the opposite surface was contacted to cotton that soaked in distilled water. The control group was soaked in distilled water. Three stimulus value X, Y and Z were evaluated with colorimeter (Color ' Color Differencerneter, Model TC-6FX, Tokyo Denshoku Co., Japan) on the labial surface of all specimen three times on white and black background plate before the bleaching agents were applied and on 3rd, 5th and 7th day after applied. The degree of translucency was normally assessed by measuring the inverse property, opacity (contrast ratio). 10% Opalescence, 15% Opalescence-F, and control group showed no significant variation in the translucency of bovine enamel, However Rembrandt decreased the translucency of it (p < 0.01).
본 연구에서는 현재 임상에서 home bleaching을 위해 사용되고 있는 표백 재료들이 치아 법랑질의 투명도에 어떠한 변화를 일으키는지 고찰해 보고자 시행하였다. 실험 대상으로는 하루 전 발거한 우치 (bovine tooth)를 사용하였다. 치아의 순면에 수직되게 다이아몬드 드릴을 이용해 수주 하에서 직경 6 mm의 원통형 치아 시편을 만들어 순면이 노출된 상태로 투명한 아크릭 레진에 포매한 후, low speed diamond saw (Isomat, Buehler Co., USA)를 사용하여 1.2 mm 두께로 절단하였다. 절단된 시편은 순면을 먼저 편평하게 연마하고,절단된 면을 연마하여 두께 1 mm의 시편을 완성하였다. 완성된 시편(우치 25개)을 무작위로 추출하여 3개의 그룹으로 나누고 나머지는 대조군으로 하였다. Opalescence$^{(R)} (10% carbamide peroxide, Ultradent, Milford, USA), Rembrandt$^{(R)} (10% carbamide peroxide, DenMat, USA) 및 Opalescence$^{(R)} F(15% carbamide peroxide with fluoride, Ultradent)를 시편의 순면에 1주일 동안 적용 (표백제는 24시간마다 교체)하였고, 설측면은 증류수를 적신 거즈에 접촉된 상태로 보관하였다 표백제를 적용하기 전과 적용 3, 5, 7일째에 시편의 삼자극치 X, Y, Z 값을 색채색차계 (Color & Color Differencemeter, Model TC-6FX, Tokyo Denshoku Co., Japan)로 백색 배경판과 흑색 배경판 상에서 측정하였다 백색 배경판과 흑색 배경판 상에서 측정된 Y값의 평균값을 이용해 contrast ratio를 계산하였다 얻어진 값을 One Way Repeated Measured ANOVA를 이용하여 통계 처리한 결과 10% Opalescence$^{(R)}처치군, 15% Opalescence$^{(R)}-F처치군 및 대조군에서는 통계적으로 유의할만한 증감을 보이지 않았고, Rembrandt$^{(R)}처치군에서는 Contrast ratio가 증가하였다 (p < 0.01).