The watertight property of concrete was examined, that is affected by the sort of self waterproofing admixture and the change of the addition ratio of admixture. Various self waterproofing admixtures were made by changing the mixing ratio of silica fume, zinc stearate and silica sand. The result showed as follows. As the adding ratio of self waterproofing admixture increases, the fluidity is increased and the setting time is delayed. While compressive strength of concrete with self waterproofing admixture A which is currently using is increased until the adding ratio of self waterproofing admixture reached 18kg/㎥ and decreased over 24 kg/㎥, that with self waterproofing admixture B, C and D which are developed are higher than that of A. Absorption is decreased as the adding ratio of self waterproofing admixture and the increasing of age in concrete. Especially, when self waterproofing admixture has a lot of zinc stearate, absorption is decreased manifestly. The property of permeability is similar to that of absorption; permeability is decreased as the adding ratio of self waterproofing admixture and the increasing of age in concrete. Consequently, when the ratio of silica fume, zinc stearate and silica sand in self waterproofing admixture is 1 : 2 : 1 and addition ratio of self waterproofing admixture is 6kg/㎥, the high quality concrete is obtained comparing to the concrete with existent self waterproofing admixture.
SF, ZS 및 SS의 혼합비율을 변화시켜 제조한 구체방수재를 대상으로, 방수재의 종류 및 첨가량에 따른 굳지 않은 콘크리트 및 경화콘크리트의 수밀특성을 분석한 결과는 다음과 같다. 구체방수재의 첨가량이 증가할수록 유동성은 증가하였으며, 응결시간은 지연되었다. 경화상태 압축강도는 기존 제품인 A의 경우, 방수재 첨가량 183kg/㎥까지는 증가하나, 그 이후 24kg/㎥에서는 감소하는 것으로 나타났으며, 시제작품인 B, C, D의 경우는 기존 구체방수재인 A에 비해 높은 강도특성이 있는 것으로 나타났다. 또한, 흡수량은 구체방수재 혼입량이 증가하고, 재령이 경과할수록 적어지는 것으로 나타났는데 특히, ZS의 첨가량이 많은 방수재 일수록 크게 낮아지는 것으로 나타났다. 투수량은 흡수량과 유사한 경향으로, 방수재 첨가량이 증가하고, 재령이 경과할수록 감소하는 등의 특성을 나타내고 있었다. 이상을 종합하여 볼 때 시제작품으로 가정한 SF : ZS : SS의 혼합비가 1 : 2 : 1이고, 혼입량이 63kg/㎥인 조건이면 기존 구체방수재보다 우수한 품질의 수밀콘크리트를 제조할 수 있는 것으로 판단되었다.