$V_2$$O_5$와 $CaCo_3$를 첨가한 Mn-Zn Ferrites의 자기적 특성에 관한 연구

Power transformers are increasingly becoming more significant in the advancement of electronic equipment. A high-performance, low-cost core material is necessary in order th come up with power transformers in the smallest and lightest scale possible and with low power requirements. In this study, we added V$_2$O$_{5}$ and CaCo$_3$to Mn-Zn ferrite to produce a high-performance low-cost core material. The compositions used were MnO : ZnO : Fe$_2$O$_3$= 37 : 11 : 52 mol%. The materials were sintered at 125$0^{\circ}C$ for three hours. Initial permeability was measured at 0.1MHz. At 200mT, power loss was measured by changing the temperature at 25KHz, 50KHz, 100KHz. When we added 0.lwt% and 0.1%wt% of V$_2$O$_{5}$와 CaCo$_3$, respectively we obtained 405 405KW/㎥ at 200mT, 100KHz, 6$0^{\circ}C$. We tan reduce eddy current loss as a primary loss of high frequency by adding a small amount of V$_2$O$_{5}$와 CaCo$_3$. This reduces power loss in the power transformersormers