• The Journal of Advanced Prosthodontics
• /
• v.5 no.2
• /
• pp.92-97
• /
• 2013

PURPOSE. All-ceramic crowns are subject to fracture during function. To minimize this common clinical complication, zirconium oxide has been used as the framework for all-ceramic crowns. The aim of this study was to compare the fracture strengths of two computer-aided design/computer-aided manufacturing (CAD/CAM) zirconia crown systems: Lava and Digident. MATERIALS AND METHODS. Twenty Lava CAD/CAM zirconia crowns and twenty Digident CAD/CAM zirconia crowns were fabricated. A metal die was also duplicated from the original prepared tooth for fracture testing. A universal testing machine was used to determine the fracture strength of the crowns. RESULTS. The mean fracture strengths were as follows: $54.9{\pm}15.6$ N for the Lava CAD/CAM zirconia crowns and $87.0{\pm}16.0$ N for the Digident CAD/CAM zirconia crowns. The difference between the mean fracture strengths of the Lava and Digident crowns was statistically significant (P<.001). Lava CAD/CAM zirconia crowns showed a complete fracture of both the veneering porcelain and the core whereas the Digident CAD/CAM zirconia crowns showed fracture only of the veneering porcelain. CONCLUSION. The fracture strengths of CAD/CAM zirconia crowns differ depending on the compatibility of the core material and the veneering porcelain.

• The Journal of Advanced Prosthodontics
• /
• v.14 no.5
• /
• pp.324-333
• /
• 2022

PURPOSE. The purpose of this study is to evaluate translucency and masking ability of translucent zirconia compared to conventional zirconia and lithium disilicate materials. MATERIALS AND METHODS. Three types of zirconia blocks with different yttria contents (3Y, 4Y, 5.5Y) and LS blocks (Rosetta SM) were used. Ten specimens for each group were fabricated with 10 mm diameter, with both 0.8 mm and 1.5 mm thicknesses (± 0.02 mm). All groups of zirconia specimens were sintered and polished according to the manufacturer's instructions. To calculate the translucency parameter (TP), CIELAB value was measured with a spectrophotometer on black and white backgrounds. To investigate the color masking abilities, background shades of A2, normal dentin, discolored dentin, and titanium were used. The color difference (ΔE) was calculated with the CIELAB values of A2 shade background as a reference compared with the values in the various backgrounds. One-way ANOVA and Bonferroni tests were conducted (P < .05). RESULTS. The TP values of zirconia specimens increased as the yttria content increased. All materials used in the study were able to adequately mask normal dentin shade (ΔE < 5.5), but were incapable of masking severely discolored dentin (ΔE > 5.5). On the titanium background, all materials of 1.5 mm thickness were able to mask the background shade, but with a thickness of 0.8 mm, only 3Y-TZP and 4Y-PSZ were able to mask titanium background. CONCLUSION. All zirconia materials and lithium disilicate specimens used in this study were unable to adequately mask the shade of severely discolored dentin. It is recommended to use 3Y-TZP or 4Y-PSZ with a sufficient thickness of 0.8 mm or more to mask titanium.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.36 no.2
• /
• pp.61-69
• /
• 2020

Purpose: Zirconia fixed partial dentures with mandibular 2^nd premolar and 2^nd molar as abutments are fabricated and then the effects of inter-abutment distance on fracture resistance of zirconia fixed partial dentures is studied. Materials and Methods: The materials used in this study are Cameleon S zirconia block and S2 zirconia block, which are divided into CS Group and S2 Group applying different inter-abutment distance for each material, and the sintered zirconia fixed partial denture was luted to the epoxy resin die using a temporary luting cement, and then the fracture resistance was measured by placing a 6 mm diameter hardened steel ball on the occlusal surfaces of the pontics and applying pressure at a cross head speed of 1.0 mm/min on a universal testing machine with a load cell of 5.0 kN. Results: The fracture resistance of zirconia fixed partial dentures is not significantly affected by inter-abutment distance The fracture resistance of zirconia fixed partial dentures in CS Group was significantly higher in 15 mm of inter-abutment distance than in 13 mm and 17 mm of inter-abutment distance (P < 0.05). The fracture resistance of zirconia fixed partial dentures in S2 Group was not significantly different between the three groups (P > 0.05). Conclusion: The fracture resistance of zirconia fixed partial dentures with mandibular 2^nd premolar and 2^nd molar as abutments does not significantly affected by the inter-abutment distance.

• Journal of dental hygiene science
• /
• v.14 no.2
• /
• pp.140-149
• /
• 2014

The purpose of this study was to investigate the influence of etching surface treatment and aging treatment of zirconia on the shear bond strength between zirconia core and veneered ceramic. Four groups of zirconia-ceramic specimens were prepared; 1) NEZ group (no etching zirconia), 2) EZ group (etching zirconia), 3) ANEZ group (aging and no etching zirconia), 4) AEZ group (aging and etching zirconia). The shear bond strength between zirconia and porcelain was measured using Instron Universal Testing Machine. Surface texture with crystalline structure of zirconia surface was examined by the field emission scanning electron microscopy (FE-SEM) with ingredient analysis. The fractured surfaces of specimens were examined to determine the failure pattern by a digital microscope. The mean${\pm}$standard deviation of shear bond strengths were $23.47{\pm}3.47$ Mpa in NEZ, $28.30{\pm}4.34$ Mpa in EZ, $21.85{\pm}4.65$ Mpa in ANEZ, $24.65{\pm}3.65$ Mpa in AEZ group, respectively, and were significantly different (p<0.05). The average shear bond strength was largest in EZ group, followed by AEZ, NEZ, and ANEZ groups. Most specimens in NEZ group showed adhesive failure and most specimens in EZ, AEZ, and ANEZ group showed mixed failure. Surface of etching treatment group (EZ and AEZ) showed complex micro-structure and irregular surface texture which may facilitate mechanical interlocking, while untreated zirconia surface presented simpler micro-structure. In conclusion, an etching treatment improved bonding strength between zirconia and porcelain by forming mechanical interlocking.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.4
• /
• pp.349-360
• /
• 2009

Purpose: As the esthetic demands of dental implant patients are increased, the demands of zirconia as implant abutment material are also increased. It has non-metalic color, good biocompatibility, high strength and high toughness. Even thought the advatage of zirconia abutment, there are a few studies about mechanical properties of zirconia abutment. This study evaluated the mecanical strength with compressive bending strength and endurance limit of implant-zirconia abutment assembly. Materials and Methods: Static and cyclic loading of implant-Zirconia abutment assembly were simulated under worst case condition according to ISO. Test groups were implants of external butt joint with straight regular diameter and angled regular diameter zirconia abutment, implant of external butt joint with narrow straight diameter zirconia abutment and implant of internal conical joint with straight narrow diameter zirconia abutment. All test group were evaluated the mecanical strength with compressive bending strength and endurance limit. After fatique testing, fracture surface were examined by SEM. Results: The compressive bending strengths exceed 927N. Regular diameter zirconia abutment were stronger than narrow diameter zirconia abutment(P<.05). The endurance limits ranged from 503N to 868N. Conclusion: Within the limitation of this study, zirconia implant abutment exceeded the estabilished values for maximum incisal biting forces reported in the literature.

• Korean Chemical Engineering Research
• /
• v.57 no.1
• /
• pp.133-141
• /
• 2019

High specific surface area zirconia with acid-basic property was synthesized by precipitation using reflux method or hydrothermal synthesis method using ammonium hydroxide solution as precipitant in the range of pH of Zr solution from 2 to 10. The prepared zirconia was characterized by the nitrogen adsorption, X-ray diffraction (XRD), isopropanol temperature programmed desorption (IPA-TPD), scanning electron microscopy and X-ray photoelectron spectroscopy, and the catalytic activity in the IPA decomposition reaction was correlated with the acid-basic properties. When using reflux method, high pH of Zr solution was required to obtain high fraction of tetragonal zirconia, and pure tetragonal zirconia was possible at pH 9 or higher. High pH was required to obtain high specific surface area zirconia, and the hydrous zirconia synthesized at pH 10 had high specific surface area zirconia of $260m^2g^{-1}$ even after calcination at $600^{\circ}C$. However, hydrothermal synthesis with high pressure under the same conditions resulted in very low specific surface area below $40m^2g^{-1}$ and monoclinic phase zirconia was synthesized. High pH of the solution was required to obtain high specific surface area tetragonal phase zirconia. In hydrothermal synthesis requiring high pressure, monoclinic zirconia was produced irrespective of the pH of the solution, and the specific surface area was relatively low. Zirconia with high specific surface area and tetragonal phase was predominantly acidic compared to basicity and only propylene, which was observed as selective dehydration reaction in IPA decomposition reaction, was produced.

• The Journal of the Korean dental association
• /
• v.49 no.5
• /
• pp.260-264
• /
• 2011

Zirconia ($ZrO_2$) is a crystalline dioxide of zirconium. Dental zirconia blocks for CAD/CAM are usually fabricated with powders of tetragonal zirconia polycrystals (TZP) stabilized with 3mol% yttria. Because of its mechanical properties similar to those of metals and color similar to tooth, it is evaluated to attain the two purposes at a time, strength and aesthetic in prosthetic dentistry. The ability of transformation of Y-TZP from tetragonal to monoclinic helps to prevent crack propagation and contributes the increase of strength and fracture toughness. Two different types of blocks, soft and hard, are used to prepare the zirconia frameworks. The fuzzy-sintered block is difficult in machining, so pre-sintered soft 3Y-TZP block is usually used to mill by computer aided machining.

• The Journal of Advanced Prosthodontics
• /
• v.4 no.2
• /
• pp.93-96
• /
• 2012

PURPOSE. The objective of this study was to compare the light transmittance of zirconia in different thicknesses using various light curing units. MATERIALS AND METHODS. A total of 21 disc-shaped zirconia specimens (5 mm in diameter) in different thicknesses (0.3, 0.5 and 0.8 mm) were prepared. The light transmittance of the specimens under three different light-curing units (quartz tungsten halogen, light-emitting diodes and plasma arc) was compared by using a hand-held radiometer. Statistical significance was determined using two-way ANOVA (${\alpha}$=.05). RESULTS. ANOVA revealed that thickness of zirconia and light curing unit had significant effects on light transmittance ($P$ <.001). CONCLUSION. Greater thickness of zirconia results in lower light transmittance. Light-emitting diodes light-curing units might be considered as effective as Plasma arc light-curing units or more effective than Quartz-tungsten-halogen light-curing units for polymerization of the resin-based materials.

• Journal of Technologic Dentistry
• /
• v.31 no.2
• /
• pp.9-14
• /
• 2009

In this study, to improve the flexure strength of Zirconia, on the Zirconia pellet surface measure the flexure strength to melt or permeate the Alumina (Vita Zahnfabrik, Bad Sachkingen, Germany) of private used In-Cream and observe by Scanning election microscope. In the control group(3Y-TZP group), the average of flexure strength was 1623.7MPa, and in the experimental group(Glass-infiltrated 3Y-TZP group) was 1800.2MPa. As a result of observing the interface between glass and zirconia with a scanning election microscope, it was showed that the glass dissolves to permeate into the surface of zirconia, so filled the zirconia with particles.

• Tribology and Lubricants
• /
• v.16 no.2
• /
• pp.84-90
• /
• 2000

High Temperature wear behavior of plasma sprayed zirconia coatings containing up to 10 mol% of Fe$_2$O$_3$ were investigated. The wear test results showed that the addition of Fe$_2$O$_3$ particles to zirconia improved the wear resistance and lowered the coefficient of friction. Optimum concentration of Fe$_2$O$_3$ was about 5 mol%. Similar degradation behavior was observed at about 40$0^{\circ}C$ for both zirconia and Fe$_2$O$_3$ added zirconia coatings. The results indicated that stabilization of tetragonal phase and changes in mechanical properties such as hardness and toughness were responsible for tribological behavior of plasma sprayed zirconia contain Fe$_2$O$_3$.