• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.109-114
• /
• 2002

The adhesion of electroless plated Ni layer on Al/Si substrates has been investigated. The zincating treatment was conducted with a conventional method and a modified method. In a modified method, ultrasonic agitation was applied during zincating. Adhesion strength was evaluated by a pull-off test. The ultrasonic agitation during zincating increased the nucleation density of Zn particles and refined Zn particle size. the adhesion strength of electroless Ni layer deposited on the modified zincated surface was higher than that on the conventionally zincated surface. the improvement of adhesion was attributed to the fine and dense Zn particles.

• Resources Recycling
• /
• v.10 no.2
• /
• pp.27-33
• /
• 2001

Reusing of electroless Ni-Cu-P waste solution was investigated in the plating time, plating rate, solution composion and deposit. Plating time of nickel-catalytic surface took longer than that of zincated-catalytic surface. Initial solution with 50f) waste solution additive at batch type was possible to reusing of waste solution. Plating time of initial solution at continuous type took longer 10 times over than that of batch type. Plating time of 50% waste solution additive at continuous type took longer 3.7 times over than that of batch type. Component change of nickel-copper for electroless deposition was greatly affected by depolited inferiority and larger decreased plating rate.

• Resources Recycling
• /
• v.12 no.1
• /
• pp.18-24
• /
• 2003

Reusing of electroless Ni-Cu-B waste solution was investigated in the plating time, plating rate, solution composition and deposit. Plating time of nickel-catalytic surface took longer than that of zincated-catalytic surface. Initial solution with 40% waste solution additive at batch type was possible to reusing of waste solution. Plating time of initial solution at continuous type took longer 6 times over than that of batch type. Plating time of 40% waste solution additive at continuous type took longer 2 times over than that of batch type. Component change of nickel-copper for electroless deposition was greatly affected by deposited inferiority and larger decreased plating rate.

• Resources Recycling
• /
• v.14 no.4 s.66
• /
• pp.34-40
• /
• 2005

Reusing of electroless Co-Cu-P waste solution was investigated in the respect of plating time, plating rate, solution composition and deposit. Plating time of cobalt-catalytic surface took longer than that of zincated-catalytic surface. It was possible to reuse the waste solution by mixing $50\%$ fresh solution at batch type. Plating time of initial solution at continuous type took longer 7.5 times over than that of batch type. Plating time of $50\%$ waste solution additive at continuous type took longer 2.5 times over than that of batch type. Component change of cobalt-topper for electroless deposition was greatly affected by deposit inferiority and rapid decrease in plating rate.

• Korean Journal of Materials Research
• /
• v.32 no.9
• /
• pp.361-368
• /
• 2022

The overall process, from the pre-treatment of aluminum substrates to the eco-friendly neutral electroless Ni-P plating process, was observed, compared, and analysed. To remove the surface oxide layer on the aluminum substrate and aid Ni-P plating, a zincation process was carried out. After the second zincation treatment, it was confirmed that a mostly uniform Zn layer was formed and the surface oxide of aluminum was also removed. The Ni-P electroless plating films were formed on the secondary zincated aluminum substrate using electroless plating solutions of pH 4.5 and neutral pH 7.0, respectively, while changing the plating bath temperature. When a neutral pH7.0 electroless solution was used, the Ni-P plating layer was uniformly formed even at the plating bath temperature of 50 ℃, and the plating speed was remarkably increased as the bath temperature was increased. On the other hand, when a pH 4.5 Ni-P electroless solution was used, a Ni-P plating film was not formed at a plating bath temperature of 50 ℃, and the plating speed was very slow compared to pH 7.0, although plating speed increased with increasing bath temperature. In the P contents, the P concentration of the neutral pH 7.0 Ni-P electroless plating layer was reduced by ~ 42.3 % compared to pH 4.5. Structurally, all of the Ni-P electroless plating layers formed in the pH 4.5 solution and the neutral (pH 7.0) solution had an amorphous crystal structure, as a Ni-P compound, regardless of the plating bath temperature.