• Journal of the Korea Furniture Society
• /
• v.17 no.2
• /
• pp.9-23
• /
• 2006

Control particleboards were significantly higher in thickness swelling than wood particle-polypropylene fiber composites and their thickness swelling increased with the increase of target density. In the composites, thickness swelling did not vary significantly with the increase of target density but increased with the increase of wood particle content. And the composites with fine wood particles were significantly lower in thickness swelling than those with coarse wood particles irrespective of target density and formulation. In the scanning electron microscopy, significantly higher thickness swelling in the composites with coarse wood particles was thought to be the result of more interfacial separations by higher swelling stresses.

• Journal of the Korea Furniture Society
• /
• v.25 no.3
• /
• pp.223-232
• /
• 2014

To make metalized wood composites of 10 different korean wood species, it was tested by Low temperature melting Bi-Sn alloy injection method at high temperature and high pressure condition. Metalized wood composite of each wood species had light ash color, but still maintained its own natural wood grain and wood figures. It was evaluated on coating properties. Furthermore, it also was check on effect of coating as like a changes of main color, wood grain and wood figures. The results of test were following as; a coating properties as like a cold resistance, heat resistance, acid resistance, alkali resistance, durability of abrasion, and cross-cut test was proper on the conditions of the KS standard. And, In aspect of color changes, the metalized wood composites of 10 different korean wood species had a light ash color, but still maintained its own natural wood grain and wood figures. Also, the more weight per gain of alloy is, the more grey background of metalized wood composite is.

• Journal of the Korean Society of Safety
• /
• v.27 no.1
• /
• pp.26-31
• /
• 2012

Wood-plastic composites represents a growing class of materials used by the residential construction industry and furniture industry. In this study, the effect of flame retardants on the flammability and mechanical properties of wood flour-high density polyethylene(HDPE) composites were studied. we were manufactured wood flour-HDPE composites by modular intermeshing co-rotating twin screw extruder with L/D ratio of 42. The flame retardant properties were used limiting oxygen index(LOI) and mechanical properties were measured by universal testing machine(UTM). The Morphological analysis of composites were analyzed by Scanning electron microscope(SEM). It was found that Ammonium polyphosphate can effectively reduce the flammability of the wood flour-HDPE composites. Marginal reduction in the mechanical properties of the composites was found with addition of flame retardants. SEM images showed that the coupling agent improved wood flour-HDPE interfacial bonding.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.2
• /
• pp.155-163
• /
• 2009

This study examined the thermal stability of PLA-WF bio-composites. Wood flour (WF)-filled PLA bio-composites were reinforced with the flame retardants, Melamine pyrophosphate (MPP), resorcinol bis (diphenyl phosphate) (RDP) and zinc borate (ZB). The flame retardant was compounded with PLA and natural biodegradable filler. The thermal properties of the biodegradable polymer and bio-composites reinforced with the flame retardant were measured and analyzed by DSC, DMA and TGA. The results showed that the flame retardant-reinforced biodegradable bio-composite exhibited improved thermal properties.

• Elastomers and Composites
• /
• v.46 no.3
• /
• pp.223-230
• /
• 2011

Considering of utilizing renewable resources and recycled plastics, green composites consisted of recycled polyethylene (PE) as matrix and eco-friendly natural fibers as reinforcement were processed and characterized in the present study. First, the wood flour/recycled polyethylene pellets with different wood flour contents were prepared by twin-screw extrusion processing. Using the pellets, wood flour/recycled polyethylene green composites were fabricated and the effects of wood flour loading on their flexural, tensile, impact properties, heat deflection temperature and fracture behavior were investigated. It was concluded that the flexural strength, flexural modulus, tensile modulus and heat deflection temperature of wood flour/recycled polyethylene green composites were increased with wood flour, whereas the tensile strength and impact strength were decreased. The fracture behavior observed by means of scanning electron microscopy supported qualitatively the tendency of the impact strength with wood flour loading, compared with the ductile fracture pattern of recycled polyethylene.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.2
• /
• pp.33-44
• /
• 1997

This study was executed to examine the effects of polypropylene fiber length and process variables of the composites made from wood fiber and nonwood fiber mixed formulations. As a nonwood fiber the polypropylene with 3 denier thickness of tow condition was selected and cut into each length of 0.5, 1.0, 1.5, 2.0 and 2.5cm to mix with wood fiber. And also western hemlock wood fiber for medium density fiberboard was prepared. First, to decide an adequate polypropylene mixing fiber length, the composites of 1.0g/$cm^3$ density were made from 10% polypropylene fiber by each of five lengths and 90% western hemlock fiber mixed formulations. Thereafter as the experiments of process variable, the composites applied with adequate polypropylene fiber length(1.5cm) were made from 4 density levels (0.6, 0.8, 1.0, 1.2g/$cm^3$). 3 mixed formulations of wood fiber to polypropylene fiber(95 : 5, 90 : 10, 85 : 15), and 3 mat moisture contents(5, 10, 20%). According to the results and discussions it was concluded as follows ; The physical and mechanical properties were shown improved tendency. as polypropylene fiber length was increased in the range from 0.5 to 1.5cm, but shown decreasing tendency from 2.0 to 2.5 cm. Accordingly, it was shown that polypropylene fiber length is limited to 1.5cm or less length in mixing wood fiber and polypropylene fiber by turbulent air mixing process. As the densities of wood fiber-polypropylene fiber composites were increased, the physical and mechanical properties were clearly improved. Also they were shown significantly increasement statistically between densities respectively. In the mixed formulations, physical and mechanical properties were shown only slightly improvement, as they changed from 95 : 5 to 85 : 15 in wood fiber to polypropylene fiber. Despite of increasement of mat moisture content, mechanical properties were not improved significantly but physical properties were improved somewhat in wood fiber-polypropylene fiber composites.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.5
• /
• pp.88-97
• /
• 2006

Wood flour (WF)-recycled polypropylene (RPP) composites composed of 50% WF of Eucalyptus deglupta Blume species, 50% RPP, various contents of maleic anhydride (MAH) modifier (0; 1; 2; 5; 5; 7.5; and lo%), and 15% dicumyl peroxide (DCP) initiator (based on MAH weight) were subjected to weather for 1 year and subterranean termite (Coptotermes cuwignathus HOLMGREN) and dry wood termite (Cryptotermes cynocephalus LIGHT) for 3 and 4 weeks, respectively. WF-RPP composites with 2.5% MA modifier had tensile strength, breaking elongation and Young's modulus about 2.2, 2.3, and 1.2 times, respectively higher compared to MAH-free composites. The WF-RPP composites with or without MAH modifier had 5.5 times higher resistance to weather compared to RPP film alone. The color of the WF-RPP composites with or without MAH modifier became lighter after exposures to the weather. The WF-RPP composites with or without MAH modifier are resistant to subterranean termite Coptotermes curvignathus HOLMGREN and dry wood termite Cryptotermecs cynocephalus LIGHT under the experimental condition adopted.

• Journal of the Korea Furniture Society
• /
• v.27 no.4
• /
• pp.392-398
• /
• 2016

Wood-plastic composites (WPCs) composed of mainly wood flour and thermoplastics have attracted considerable attentions due to advantages of cost effectiveness, high durability, and microbial resistance. However, relatively poor fire resistance of WPCs from low thermal stability of wood and plastics prevents further uses. This study investigated the effect of expandable graphite (EG) and aluminium hydroxide (AH)/magnesium hydroxide (MH) on the properties of WPCs. The combined incorporation of both EG and metal hydroxide (i.e., AH or MH) into formulations leads to higher flexural modulus of filled composites compared to neat PP and WPC. In thermal properties, EG played an important role in improving thermal stability of filled composites by suppressing thermal decompositions of wood and PP. Moreover, EG showed better water absorption features. From this research, it can be said that EG and metal hydroxides have potentials as effective reinforcement, flame retardant, and moisture barrier.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.91-94
• /
• 2005

Polypropylene as a matrix has been used for wood polymer composites(WPC). In preparing WPC, the coupling agent, Polypropylene grafted Maleic Anhydride(PP-G-MA) was used in order to obtain a good interfacial bonding force between matrix and fillers and dispersion of wood powders. In this study, the effects of wood powder contents and water absorption on the mechanical properties were experimentally investigated. The tensile strength and flexural strength of composites reached its peak value when the wood powder content was around 60 wt%. However, the peak value of the impact was observed about 30 wt% of wood powder content. The tensile strength and flexural strength increase with increasing the wood power contents. But the impact strength decrease with increasing the wood powder contents. The slight change was observed with the water absorption in the WPC. The optimal condition of the compositions such as Anti-oxidant and UV stabilizers for the outdoor application was suggested in this research.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.3
• /
• pp.71-78
• /
• 2004

The purpose of this study was to investigate the water absorption and thickness swelling of biocomposites at room temperature. These properties of bio-composites mainly depend on the ability of the agro-flour to absorb water through hydrogen bonding between water and the hydroxyl groups of the holocellulose and lignin in the cell wall. As the content of agro-flour increased, the water absorption and thickness swelling of the bio-composites increased. The effects of agro-flour content and rice husk flour (RHF) particle size on the water absorption and thickness swelling of the bio-composites were evaluated. In general, wood-based materials showed significantly higher water absorption and thickness swelling than the bio-composites. This might be attributed to the ability of the polybutylene succinate (PBS) hydrophobic polymer to prohibit the water absorption and thickness swelling of the bio-composites, Therefore, the use of agro-flour filled PBS bio-composites, which exhibit improved dimensional stability in comparison with wood-based materials, is recommended.