• Journal of Korean Society of Steel Construction
• /
• v.16 no.4 s.71
• /
• pp.415-423
• /
• 2004

To investigate the long-term corrosion resistance of an uncoated weathering steel, an important outdoor constructional steel material, skyward surfaces of the weathering steel and a control steel initially exposed to rural and industrial atmospheres for 9 years were electrochemically tested in neutral artificial rain in terms of electrochemical potentials, impedances, and anodic potentiodynamic polarization curves. Their results were then discussed. A quite passive and stable rust layer to the artificial rain was well formed on the skyward surface of the weathering steel exposed to the industrial and rural atmospheres, and its corrosion rate in the artificial rain was measured to be about a low $3{{\mu}m}/y$. Continuous immersion of all the weathered surfaces in the artificial rain revealed the gradual degradation of the weathered corrosion layers on the steel, resulting in a cathodically controlled corrosion of the substrate steel by the electrochemical measurements. Alloy components of the weathering steel were found to retard the degradation of the weathered corrosion layers on the steel in the artificial rain. For better corrosion evaluation of the weathering steel, more electrochemical measurements of surfaces that have been exposed for more than 9 years to more closely simulated atmospheric waters are needed. These measurements are almost non-destructive and can provide online and in situ information on the corrosion rate, the development of corrosion and the conditions of rust layers on any interested surface and at any exposure time of the steel, so they can be effectively applicable to the corrosion evaluation of steel structures such as bridges, towers, and architectures by forming an electrochemical cell on an interested structural surface and by using a portable electrochemical instrument.

• 보존과학연구
• /
• s.30
• /
• pp.79-91
• /
• 2009

Stone cultural heritages are mostly situated in field, so they are damaged from mechanical, chemical and biological weathering, and their degree of strength is also weaken. Therefore, the scientific conservation of the stone cultural heritages are necessary in order to the long-term maintenance and safety conservation. In this study, we attempt to estimate on the field application of consolidants which are Wacker OH 100, Remmers KSE 300 and 1T1G according to the quality of the rocks. Based on the ultrasonic velocity, conditions of weathering damage before treatment are mainly ranked completely weathering condition (CW) or partly highly weathering condition (HW). After the first treatment, weathering damage conditions are changed by the high weathering condition (HW). These results shows that the internal pores of stone are filled with consolidant materials, so average ultrasonic velocities increases after treatment. And Remmers KSE 300 which is consolidant material is highest rate of increase of average ultrasonic velocities.

• The Journal of Engineering Geology
• /
• v.34 no.1
• /
• pp.25-38
• /
• 2024

Laboratory tests of accelerated artificial weathering compared the effects of seawater and acidified distilled water on rock weathering. The experiments simulated chemical and physical weathering of five different types of volcanic rock by applying 45 freeze-thaw cycles using seawater and acidified distilled water (pH 3), both at 70℃. The physical properties and uniaxial compressive strength (UCS) of the rocks were measured after 15 and 45 cycles of artificial weathering. Most of degradation of physical properties appeared within the first 15 cycles, and acidified distilled water had a greater effect than seawater. Analysis of variance (ANOVA) statistically evaluated the differences in UCS of the different rock types during the tests. The rate of UCS reduction after 45 cycles was similar across the samples, being independent of the rock type and the trend of changes in physical properties. In contrast to the changes in the physical properties, the UCS was more affected by seawater than by acidified distilled water.

• 한국지구물리탐사학회:학술대회논문집
• /
• 2003.11a
• /
• pp.540-543
• /
• 2003

There are many stone monuments which are weathered by natural or artificial factors in Korea. The partly weathering in stone could accelerate the rate of weathering, so it is demanded to keep them from the further weathering. Consolidation is evaluated as one of the efficient treatments which have a good effectiveness in stone monuments. But following the former researches, the effectiveness of consolidation could be different, related to the kinds of stone or consolidants. Therefore, in this study, the change of properties was monitored in the long term for the exact evaluation of the stability of the consolidated stone. It is estimated that the pore structure of consolidated stone was filled by consolidant, according to the measurements of ultrasonic velocity, and the digital image analysis of the sample was shown that the color property of stone surface has varied during the curing.

• Economic and Environmental Geology
• /
• v.23 no.2
• /
• pp.201-213
• /
• 1990

Mineralogy, chemistry, physical property, and fossil abundance have been studied for the samples collected from three weathering profiles, two from the Duho Formation and one from the Hagjeon Formation in the Tertiary sediments in the Pohang area. The mineralogy of the samples from the Duho Formation shows somewhat different from that of the Hagjeon Formation. Kaolinite is more abundant and shows higher crystallinity in samples from the Duho Formation than those in the Hagjeon Formation, but clay mineral assemblage in each weathering profile remain fairly constant with depth. This difference in mineral distribution seems to be inherited from original source materials. It indicates that little or not severe leaching has been taking place in these three weathering profiles. Weathering indicies indicate different degrees of susceptibility to chemical weathering in these two formations. The Duho Formation has a higher degree of susceptibility to weathering than that of the Hagjeon Formation which is mainly due to differences in clay mineral assemblages in both formations. A noticeble colour difference between oxidized and unoxidized zones in each profile can be easily recognized which is definetely due to different decomposition rate organic carbon by various oxidation state from surface to bottom of the profile. Weathering process have also intensively influenced microfossil preservation about up to 7-10 m in depth in the Duho Formation. Consequently, characteristics observed at weathering surface should be used as a subsidiary tool in setting geologic boundary or establishing formation. Great care must be taken to choose sampling site for microfossil study.

• Journal of the Korean Geographical Society
• /
• v.45 no.3
• /
• pp.342-359
• /
• 2010

The Bangudae Petroglyphs locate at Bangudong, Daegok-ri, Eonyang-eup, Ulju-gun, Ulsan and was designated as the No. 285 national treasure since 1995. After the construction of Sayeon-dam in 1965, there were many controversies of the rock weathering problems by the periodic immersion for approximately a few months. The isopleths of water content on the rock are drawn and the result shows relationships between the isopleths and distribution of joints or exfoliations. The distributions of water content rates in the Petroglyphs show the downward increasing pattern. This may suggest that the rates of water content are further influenced by the duration of immersion. Also, the upper part of the Petroglyphs with dense joints shows high rates of water content. If the water content rates in rocks increase, the water absorption rates increase too, because of the increasement of coefficient of permeability and porosity. The weathering damages of the Petroglyphs in which the pores are saturated by the periodic immersion are in the critical conditions.

• Journal of Conservation Science
• /
• v.25 no.1
• /
• pp.77-86
• /
• 2009

The physical properties of the epoxy resins were studied with an addition of filler content and the application of artificial weathering test. When talc as a filler was added to the epoxy resin (L-30), the water resistance seemed to be increased because of the results of the reducing of water absorption rate and the increasing of contact angle. Although the adhesive strength of epoxy resins was not affected by the increasing amount of talc, its compressive strength was reduced. The physical properties of the epoxy resins had different trends according to the site environments. The artificial weathering test with the change of temperature and humidity showed that the changes of water absorption rate and colour differences of the epoxy resins containing talc were lower than the pure epoxy resin itself. However, the contact angle was higher. The artificial weathering test with ultraviolet irradiations showed the opposite result; the damage of epoxy resins was increased with the increasing of talc content. These mean the site environment of the stone monuments should be considered to determine the content of talc added to increase the durability of epoxy resin.

• The Journal of Engineering Geology
• /
• v.25 no.4
• /
• pp.499-510
• /
• 2015

Artificial accelerated weathering test evaluated rocks from near the circuit road of Ulleungdo island, approximately 120 km from east of the Korean Peninsula. The tests subjected rock specimens to conditions based on the climate of the island. The specimens (such as basaltic breccia, trachyte, volcanic breccia) were preliminarily classified using a TAS diagram (XRF data) and based on the constituent minerals (XRD data); they were further classified by weathering degree according to their absorption ratios. During the artificial accelerated weathering, the absorption ratio of most of the specimens increased, but the point-load strength did not decrease in most cases, except for the volcanic breccia. The greater initial absorption ratio of trachyte rock specimen in comparison with the other specimens led to a greater increase of its absorption ratio during the artificial accelerated weathering test. The volcanic breccia specimens showed the greatest increase of absorption ratio and the biggest reduction ratio of the point- load strength during the tests. These results could aid prediction of the weathering rate of rocks in Ulleungdo island subjected to weathering processes; trachyte which appears to accelerate with time, and volcanic breccia whose mechanical strength can largely decrease in a relative short period of time. Proper measures therefore appear necessary for the prevention of natural disaster such as rock fall and landslide around the circuit road.

• The Journal of Engineering Geology
• /
• v.20 no.4
• /
• pp.461-465
• /
• 2010

Weathering and permeability in rocks play a very important role in underground disposal of radioactive waste and their long-term management as well as stability security of rock structures. Weathering and permeability of rocks are largely controlled by the characters of inner structures of rocks. In other words, weathering rate can be accelerated depending on the quantity of pore and microcrack in rocks. Quantitative evaluation of inner structures of rocks can serve as a tool that can assess the degree of weathering of rocks. Therefore it can be said that the understanding of three dimensional distribution of the inner structure of rocks is important for long-term management of rock structures. This study was performed to analyze three dimensional distribution of pore in rocks using Micro Focus X-ray CT on fresh granite and weathered granite from Korea. Results of the analysis clearly show distribution of pore and porosity of the inner rock.

• Journal of the Korean GEO-environmental Society
• /
• v.23 no.3
• /
• pp.15-22
• /
• 2022

This study aims to observe the swelling representative rocks in Korea and to suggest improvements in the use of test methods and prior analysis in relation to the weathering of rocks. The swelling test and analysis were performed on the drilling cores obtained for the ground investigation at the domestic highway construction site. For the method of determining the absorption expansion index of rocks, the method proposed in "Standard Methods for Sample Collection and Specimen Preparation" of ISRM and Korean Rock Engineers Standard Rock Test Method was used. The specimen for the measurement of the expansion displacement was cylindrical with a height of 10 cm and a diameter of 5 cm. The existing swelling analysis method evaluates the sensitivity to weathering by using the maximum expansion displacement, but since the classification by bedrock grade is unclear, it is reasonable to use the rate of change of the expansion displacement according to the immersion time. It is necessary to conduct an experiment to distinguish between weathering and fault deterioration. In addition, long-term weathering prediction technology for each cancer type is needed through the expansion displacement analysis of the chemical weathering stage.