• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 제35회 춘계학술대회
• /
• pp.96-102
• /
• 2002

This paper was studied on the wear-corrosion behavior of ductile cast iron in the acidic environment. In the dry atmosphere and variety of pH solution, wear-corrosion characteristics and friction coefficient of GCD 60 with various sliding speed and distance were investigated. And electrochemical polarization test of GCD 60 was examined in the environment of various pH value. The main results are as following : In the dry atmosphere, boundary friction appears below nearly 5 $kg_{f}$ of contact load, and it is considered that solid friction occurs over nearly 5 $kg_{f}$ of contact load. As pH value becomes low, wear-corrosion loss in the aqueous solution increases. As the corrosion environment is acidified, corrosion potential of GCD 60 becomes noble, polarization resistance becomes low, and corrosion current density increases.

• International Journal of Railway
• /
• 제3권1호
• /
• pp.19-27
• /
• 2010

In the present study, the electrical sliding wear and corrosion resistance of pure copper (Cu) and six age-hardened copper alloys (CuCr, CuZr, CuCrZr, CuNiSiCr, CuBe and CuBeNi) were investigated by a pin-on-disc tribometer and electrochemical measurement. Various copper-based alloys in the form of cylindrical pin were forced to slide against a counterface stainless steel disc in air under unlubricated condition at a sliding velocity of 31 km/h under normal load up to 20 N with and without electric current. The worn surface of and wear debris from the specimens were studied by scanning electron microscopy. Both mechanical wear and electrical arc erosion were the wear mechanisms for the alloys worn at 50 A. Owing to its good electrical conductivity, high wear and corrosion resistance, CuCrZr is a promising candidate as the overhead catenary material for electric traction systems.

• 한국가스학회지
• /
• 제4권1호
• /
• pp.26-32
• /
• 2000

본 연구에서는 힌지재인 SM20C, YBsC3 및 STC4H재에 대하여 공기 및 여러 가지 부식환경중에서 이종금속간의 찰과마멸부식실험을 실시하여, 이종금속간의 찰과마멸부식특성에 미치는 환경조건의 영향을 연구하였으며, 주요 결론은 다음과 같다. 1) 이동측 금속인 SM20C의 찰과마멸부식에 미치는 지하수의 영향은 STC4H에서 더 민감하고 YBsC3에서는 둔화된다. 2) STC4H의 찰과마멸부식에 미치는 지하수의 영향은 작지만, $0.5\%\;H_2SO_4$ 및 $0.5\%HNO_3$ 용액중에서 더 크게 된다. 3) 이동측 SM20C의 찰과마멸부식은 $3.5\%\;NaCl$, $0.5\%\;H_2SO_4$ 및 $0.5\%\;HNO_3$ 용액중에서보다 지하수중에서 가장 작게 나타났다. 4) 시간이 경과함에 따라 찰과마멸부식에 미치는 영향은 $0.5\%\;HNO_3$ 용액중에서는 증가하지 $0.5\%\;H_2SO_4$ 용액중에서는 둔화된다.

• Tribology and Lubricants
• /
• 제29권6호
• /
• pp.360-365
• /
• 2013

In this study, sliding wear tests were conducted to investigate the effects of tempered hardness on the sliding wear behavior of bearing steel. At a sliding speed of 0.3 m/s, the wear resistance of bearing steel with a tempered hardness of HRC 54 was superior to that with HRC 62. It was found that bearing steel with HRC 54 showed a strong tendency for the occurrence of oxidation wear at that speed, compared to that with HRC 62. This would be due to the troostitic structure of bearing steel with HRC 54, which is highly susceptible to corrosion. In this context, it is considered that sliding wear behavior could be affected by the corrosion resistance of the material.

• 소성∙가공
• /
• 제12권4호
• /
• pp.394-400
• /
• 2003

TiN coated films exhibit excellent mechanical properties such as high wear, erosion and corrosion resistances and a high thermal stability. Therefore, they are widely applied to a coating material in tools, ornaments, parts and semiconductors. However, the fracture of TiN coated films frequently occurs. The distribution of preferred orientations, i.e., texture, of TiN coated films strongly influences the fracture behavior of these films. In the present study. various TiN coating layers having different textures were prepared by the reactive ion physical vapor deposition and the texture dependence of friction coefficient, erosion and corrosion in these coating layers was investigated. The sample depicting the (115) texture parallel to the coating layer normal displayed a flatter surface than that observed from the sample having the (111) texture. The friction coefficient of TiN thin films was hardly dependent on the texture of coated samples. The samples having (115) texture displayed higher wear, erosion and corrosion resistances than the samples having (111) texture.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2003년도 춘계학술대회논문집
• /
• pp.99-104
• /
• 2003

TiN coated films show a good mechanical properties, high thermal properties and wear, erosion and corrosion resistance and are widely used as a coating materials in tools, ornaments, parts and semiconductors. In spite of these good properties, the fracture of TiN coated films occur during use. The fracture of TiN thin films is related to their microstructure. Especially, the life of TiN coated layer is related to the texture of the TiN films. One researcher suggested that the corrosion and erosion resistance of the TiN thin films is related to a uniform and dense structure of films. In this study, we studied the relationships between textures and friction coefficient, erosion and corrosion in TiN coated films. The flatness of (115) texture surface of TiN thin films is flatter than that of (111) texture surface. The friction coefficient of (115) texture surface of TiN thin films is similar with that of (111) texture surface. The wear resistance of (115) texture surface of TiN thin films is better than that of (111) texture surface. The erosion and corrosion resistance of (115) texture surface of TiN thin films is better than that of (111) torture surface. As well as texture, the wear, erosion and corrosion of TiN thin films has to consider defects such as pinholes, cracks, surface roughness and open columnar structure. The life of TiN coated products is influenced by the properties of wear, erosion, and corrosion resistance of TiN thin films and is related to texture of TiN coated films, density of pinholes and cracks, density of structure, and surface flatness.

• Corrosion Science and Technology
• /
• 제13권1호
• /
• pp.15-19
• /
• 2014

Recently, anti-fouling paints which does not include the poison components such as tin(Sn), copper(Cu) have been increasingly developed in order to inhibit the environmental contamination of the sea water. Moreover, the wear ratios of these anti-fouling paints are very important problem to prolong their life time in economical point of view. In this study, five types of anti-fouling paints as self polishing type were investigated on the relationship between their polarization characteristics and wear ratios. It was verified that there was apparently a good relationship between the wear ratio and polarization characteristics, for example, the wear ratio increased with increasing the impedance ratio, and increased or decreased with the corrosion potential shifting in the negative or positive direction respectively. In addition, the wear ratio decreased with decreasing the corrosion current density. Consequently, it is suggested that we can qualitatively expect the wear ratio by only measuring the polarization characteristics. Therefore, before the examination of the wear ratio was actually carried out in the field, the evaluation of polarization property in the laboratory may give a available reference data for their developments.

• Tribology and Lubricants
• /
• 제35권3호
• /
• pp.176-182
• /
• 2019

The primary objective of this study is to treat a monocrystalline silicon (Si) wafer having a thickness of $279{\mu}m$ by employing the ultrasonic nanocrystal surface modification (UNSM) technology for improving the efficiency and service life of nano-electromechanical systems (NEMSs) and micro-electromechanical systems (MEMSs) by enhancing of wear and corrosion resistances. The wear and corrosion resistances of the Si wafer were systematically investigated before and after UNSM treatment, wherein abrasive, oxidative and spalling wear mechanisms were applied to the as-received and subsequently UNSM-treated Si wafer. Compared to the asreceived state, the wear and corrosion resistances of the UNSM-treated Si wafer are found to be enhanced by about 23% and 14%, respectively. The enhancement in wear and corrosion resistances after UNSM treatment may be attributed to grain size refinement (confirmed by Raman spectroscopy) and modified surface integrity. Furthermore, it is observed that the Raman intensity reduced significantly after UNSM treatment, whereas neither the Raman shift nor new phases were found on the surface of the UNSM-treated Si wafer. In addition, the friction coefficient values of the as-received and UNSM-treated Si wafers are found to be about 0.54 and 0.39, respectively. Hence, UNSM technology can be effectively incorporated as an alternative mechanical surface treatment for NEMSs and MEMSs comprising Si wafers.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 proceedings of the second asia international conference on tribology
• /
• pp.245-246
• /
• 2002

The objective of this study is to evaluate corrosive wear resistance of metals used for bearings and gears in seawater. Sliding wear test of ferrous and copper materials against $Al_2O_3$ were carried out in artificial seawater using an electrochemical potentiostat. As the results, the wear rate and the coefficient of friction of the copper materials are lower than those of the ferrous materials. The corrosive wear of stainless steel is remarkably affected by normal load and sliding speed in view of tribological characteristics including adhesion and corrosion products.

• 열처리공학회지
• /
• 제16권6호
• /
• pp.335-340
• /
• 2003

To improve properties of wear resistance and anti-corrosion of the trivalent chromium platings, oxinitrocarbunsing and steam oxidation were conducted. Armophous trivalent Cr platings could be transformed to chromium carbides of high hardness, that showed low friction and wear rate. Even though micro-cracks were within as platings, superior anti-corrosion property was obtained by these treatments due to healing of cracks at the interface between the trivalent chromium platings and substrate.