• Journal of Mechanical Science and Technology
• /
• v.15 no.11
• /
• pp.1524-1532
• /
• 2001

The effects of recirculated exhaust gas on the wear of cylinder liner and piston were experimentally investigated by a two-cylinder, four cycle, indirect injection diesel engine operating at 75% lo ad and 1600 rpm. For the purpose of comparison between the wear rates of the two cylinders with and without EGR, the recirculated exhaust gas was sucked into one of two cylinders after the soot in exhaust emissions was removed by an intentionally designed cylinder-type scrubber equipped with 6 water injectors(A water injector has 144 nozzles of 1.0 mm diameter), while only the fresh air was inhaled into the other cylinder. These experiments were carried out with the fuel injection timing fixed at 15.3$^{\circ}$ BTDC. It was found that the mean wear rate of cylinder liner with EGR was greater in the measurement positions of the second half than those of the first half, that the mean wear rate without EGR was almost uniform regardless of measurement positions, and that the wear rate of piston skirt with EGR increased a little bit, but the piston head diameter increased, rather than decreased, owing to soot adhesion and erosion wear, and especially larger with EGR.

• Transactions of Materials Processing
• /
• v.24 no.3
• /
• pp.205-211
• /
• 2015

The current investigation was performed to study sliding-wear-rate deviation (wear-rate data scatter) in carbon steels with various microstructures. Pure iron, 0.2 wt. % C steel, 0.45 wt. % C steel, and bearing steel (AISI52100) were used for the investigation. These steels possess different microstructures. Microstructures of the pure iron, two carbon steel and the bearing steel were full ferrite, ferrite + pearlite and full pearlite, respectively. Depending on the carbon content, the carbon steel had different pearlite-volume fractions. Dry sliding wear tests of the steel were conducted using a ball-on-disk wear tester at a sliding speed of 0.1 m/s using a bearing ball (AISI52100) as a counterpart. Applied load and sliding distance were 100 N and 300 m, respectively. More than three (up to twelve) tests were conducted for each steel under the same conditions, and the mean deviations in the wear rate of the steel (microstructure) were compared. The wear-rate deviation in the steel with ferrite + pearlite microstructure was higher than that with ferrite microstructure, and the deviation decreased with the increase of pearlite volume fraction. The pure iron and the bearing steel specimens showed much less deviation. The high deviation observed from the ferrite + pearlite steel was attributed to irregular subsurface-crack nucleation and growth at the interface between the two micro constituents (ferrite and pearlite) during the wear test.

• Tribology and Lubricants
• /
• v.20 no.2
• /
• pp.91-96
• /
• 2004

Wear behavior of self-mated stainless steels in NaCl solution has been investigated. The experiment was done in the corrosive liquid of which NaCl concentration of $0\~3\%$ and temperature of $15\~90^{\circ}C$. Two kinds of wear type were observed: one is 'severe wear' type which shows gradually increasing wear volume with increasing sliding distances, the other is 'mild wear' type which shows change of wear rate from high value to low at transition distance. The specific wear rate in severe wear type was not sensitive to the liquid temperature and concentration of NaCl but stable at value of $1\times10^{-3}\;mm^3$ approximately.

• Journal of Power System Engineering
• /
• v.10 no.2
• /
• pp.111-116
• /
• 2006

Tribologcal property of the ceramics used in severe condition was investigated and both $Al_2O_3$ ball and Al/SiC composite made by thermal spray process[TSP] were used as a specimen in this study. Four kinds of material couple in ball and disk specimens were tested in the dry condition by using ball-on-disk type tribo-tester. Friction coefficient, surface roughness, wear rate, and photograph of the worn surface were investigated. Generally, High SiC contents[$40{\sim}50%$] specimens showed very low friction coefficient below 0.05 and little wear rate in dry condition. And also, low SiC contents[0%] specimens showed a moderate wear rate and high coefficient of friction at the same condition.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.1
• /
• pp.82-88
• /
• 2009

A disadvantage in the design of gerotor pump is a lack of parts that can be adjusted to compensate for wear in the rotor set, and as a consequence, it causes a sharp reduction of efficiency. In this paper, an attempt has been made to reduce the wear rate between the rotors of a gerotor pump. To do this, floating genetic algorithm (FGA) is used as an optimization technique for minimizing the wear rate proportional factor (WRPF). The result shows that the wear rate can be reduced considerably, e.g. approximately 8% in this paper, throughout the optimization using FGA.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.05a
• /
• pp.304-309
• /
• 2002

Fretting wear test in room temperature water was performed to evaluate the wear coefficient of Inconel 600,690 (Pressurized Water Reactor, PWR) and Alloy 800 (CANadian DeuteriumUranium, CANDU) steam generator (SG) tubes against ferritic and martensitic stainless steels. The main focus is to compare the wear behaviors between Alloy 800 and Inconel alloys. Test conditions are $10{\sim}30N$ of normal load, $200{\sim}450{\mu}m$ of sliding amplitude and 30Hz of frequency. The result indicated that the wear rate of Alloy 800 was higher than those of Inconel 690 at various test condition such as normal loads, sliding amplitudes etc. From the results of SEM observation, there was little evidence of plastic deformation layer that were dominantly formed on the worn surfaces of Inconel 690. Also, wear particles in Alloy 800 were released from contacting asperities deformed by severe plastic flow during fretting wear. Main cause of wear rate between Alloy 800 and Inconel 690 may be due to the difference of hardness between martensitic and ferritic stainless steel. The wear rate and wear mechanism of two tubes in room temperature water are discussed.

• Journal of Powder Materials
• /
• v.13 no.4 s.57
• /
• pp.250-255
• /
• 2006

Wear behaviors of gas atomized and extruded Al-Si alloys were investigated using the dry sliding wear apparatus. The wear tests were conducted on Al-Si alloy discs against cast iron pins and vice versa at constant load of 10N with different sliding speed of 0.1, 0.3, 0.5m/s. In the case of Al-Si alloy discs slid against the cast iron pins, the wear rate slightly increased with increasing the sliding speed due to the abrasive wear occurred between Al-Si alloy discs and cast iron pins. Conversely, in the case of cast iron discs against Al-Si alloy pins, the wear rate decreased with increasing the sliding speed up to 0.3m/s. However, the wear rate increased with increasing the sliding speed from 0.3m/s to 0.5m/s. It could be due to adhesive wear behavior and abrasive wear behavior_between cast iron discs and Al-Si alloy pins.

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.3
• /
• pp.159-167
• /
• 1998

In this study, friction-wear test was carried out on the carburized layer depth of a mechanical structure steel SNCM carburized with RX and LPG for 7hrs at $930^{\circ}C$ and also the wear properties of wear loss, wear rate, coefficient of friction, friction force and friction temperature were investigated. The wear properties for carburized layer of SNCM were tested on dry condition at the room temperature by the thrust load of 49~245N range at sliding speed of 0.2m/sec and the sliding speed of 0.2~1.0m/sec range at thrust load of 98N. Wear loss on the depth of carburizing layer was increased with increasing of thrust load and sliding speed, and with decreasing of hardness. The condition of worn surfaces were showed mild wear at less than the thrust load of 98N and sliding speed of 0.6m/sec but were showed severe wear at more than 98N and 0.6m/sec. The friction load and temperature were increased with increasing of thrust load but with increasing sliding speed was appeared minimum at 0.6m/sec. With increasing thrust load the wear rate was increased and the coefficient of friction was decreased, but with increasing sliding speed the wear rate and the coefficient of friction were decreased in 0.2~0.6m/sec and increased in 0.6~1.0m/sec, therefore 0.6m/sec in this testing is a transition velocity.

• Advances in materials Research
• /
• v.5 no.3
• /
• pp.193-203
• /
• 2016

Compared to metal-to-metal tribology, polymer tribology presents further complexity as it is more prone to be influenced by operating conditions. Over the past two decades, progress in the field of wear of polymers has led to the establishment of more refined wear mechanisms. The current paper establishes the link between different load parameters and the wear rate of polymers, based on experimental investigations. A pin-on-plate reciprocating tribometer was used to examine the wear behaviour of polyamide sliding against a steel counterface, under constant and fluctuating loads, in dry conditions. In addition, the influence of controlled imperfections in the polymer surface upon its wear rate were examined, under cyclic and steady loading, in order to better understand surface fatigue wear of polymers. The imposed imperfections consisted of vertical artificial deep crack (slit) perpendicular or parallel to the direction of sliding. The study concludes with the followings findings; in general, wear of polymers shows a significant tendency to the type of applied load. Under cyclic loads, polymers show an increase in wear rate compared to those tested under static loads. Such increase was found to increase with the increase in cyclic load frequency. It is also demonstrated that surface cracks results in higher wear rates, particularly under cyclic loads.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.50 no.2
• /
• pp.162-168
• /
• 2014

The friction and wear characteristics of the rubber matrix composites filled with nano sized silica particles were investigated at ambient temperature by pin-on-disc friction test. The volume fraction of silica particles was 19%. The cumulative wear volume and wear rate of these materials on counterpart roughness were determined experimentally. The major failure mechanisms were lapping layers, deformation of matrix, ploughing, debonding of particles, fracture of particles and microcracking by scanning electric microscopy photograph of the tested surface. The cumulative wear volume showed a tendency to increase with increase of sliding distance. The wear rate of these composites tested indicated low value as increasing the sliding distance.