• Advances in concrete construction
• /
• v.15 no.6
• /
• pp.419-430
• /
• 2023

In this study, the effect of two types of aggregates (fly ash aggregate and shale aggregate) on the density, strength, and durability of preplaced lightweight aggregate concrete (PLWAC) was studied. The results showed that the 7 - 28 days strength of concrete prepared with fly ash aggregates (high water absorption rate) significantly increased, which could attribute to the long-term water release of fly ash aggregates by the refined pore structure. In contrast, the strength increase of concrete prepared with shale aggregates (low water absorption rate) is not apparent. Although PLWAC prepared with fly ash aggregates has a lower density and higher strength (56.8 MPa @ 1600 kg/m³), the chloride diffusion coefficient is relatively high, which could attribute to the diffusion paths established by connected porous aggregates and the negative over-curing effect. Compared to the control group, the partial replacement of fly ash aggregates (30%) with asphalt emulsion (20% solid content) coated aggregates can reduce the chloride diffusion coefficient of concrete by 53.6% while increasing the peak load obtained in a three-point bending test by 107.3%, fracture energy by 30.3% and characteristic length by 103.5%. The improvement in concrete performance could be attributed to the reduction in the water absorption rate of aggregates and increased energy absorption by polymer during crack propagation.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.2
• /
• pp.63-68
• /
• 2008

Traditionally and generally used calcined clay was carburized, and its characteristics were studied. Carburization treatment was performed by the thermally decomposed carbon and the deposit carbon which occur in a so called 'Boudouard reaction $(2CO{\rightarrow}CO_2+C)'$ at fuel combustion process in a closed-type furnace. The color of the carburized calcine clay changed from yellow to black, and the carbon component revealed as crystalline graphite by the X-ray diffraction test. The weight of the carburized calcine clay decreased to about 4 wt.% by the 1st heating to $1400^{\circ}C$ in air but it does not decreased by the 2nd heating of the same conditions. By the carburization treatment, the water absorption changed from 13 wt.% to 6 wt.%, and the contact angle for water drop changed, too, from 0 to $87^{\circ}$ which was tested by the photograph of one minute after a water drop contact. It means the carburized calcine clay does not absorb water drop so it has a hydrophobic characteristic.

• Composites Research
• /
• v.34 no.3
• /
• pp.174-179
• /
• 2021

Currently, fluid transfer steel pipes take a lot of time and expense to maintain all facilities due to new construction and painting or corrosion and aging. Therefore, this study was conducted for designing a CFRP pipe structure with high corrosion resistance and chemical resistance as a substitute for steel pipes. The helical/hoop pattern was cross-laminated to improve durability, and HNT was added to suppress the moisture absorption phenomenon of the epoxy. The HNT/CFRP pipe was manufactured by a filament winding process, and performed a mechanical property test, and a moisture absorption test in distilled water at 70℃. As a result, the highest bending strength was obtained when the hoop pattern was laminated with a thickness equivalent to 0.6% of the pipe. The 0.5 wt% HNT specimen had the highest moisture absorption resistance. Also, the delamination phenomenon at the interlayer interface was delayed, resulting in the lowest strength reduction rate.

• Journal of the Korean Institute of Gas
• /
• v.9 no.4 s.29
• /
• pp.11-16
• /
• 2005

In this paper, the hydrogen osmosis test and the mechanical tensile test were carried out to examine hydrogen cracking behavior of STS444 with welding conditions. In $0.5MH_2SO_4+0.001M \;As_2O_3$ solution, the hydrogen embrittlement characteristics of weld zone of STS444 added to load of $1,400 kg/cm^2$ together with hydrogen osmosis by current of $30mA/cm^2$ for 60 min. was considered. As a result of study on the hydrogen embrittlement and mechanical characteristics of STS444외와 with welding conditions the tensile stress and elongation of STS444 get lower by the absorption of oil or water before welding. Also, the reduction rate of tensile stress and elongation of STS444 is larger because of hydrogen embrittlement by the absorption of oil or water. STS444 by the absorption of water before welding is more sensitive to hydrogen embrittlement than oil.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.50 no.spc1
• /
• pp.132-135
• /
• 2005

The water absorption ratio was not affected by the planting dates. Hannamkong showed higher water absorption ratio than any sprout -soybean varieties. Soybean seeds produced from later planting showed higher germination percentage than those planted May 25. Pungsannamulkong, Eunhakong, Doremikong, and Someongkong showed over $90\%$ germination after two days, while Tawonkong and Hannamkong were lower, The germination ratio test of the soybean seeds at $25^{\circ}C$ is usually for 7 days. But, germination ratio test of seeds used for sprout-soybean is suitable for 3 days at $25^{\circ}C$.

• Applied Chemistry for Engineering
• /
• v.24 no.6
• /
• pp.593-598
• /
• 2013

In this study, we have evaluated the water absorption phenomenon of photoresist dry film, which is commonly used to build circuits on PCB (Printed Circuit Board) by photolithography, by using ATR-FTIR (Attenuated Total Reflectance-Fourier Transform Infrared). We have firstly observed significant change in fracture mode of dry film with respect to temperature and humidity, which we assumed the material transition from ductile to brittle. Secondly, we have established the process of absorption test for determining the diffusion coefficients of water into the dry film both with gravimeter and ATR-FTIR. We have successfully calculated the diffusion coefficients for each environmental conditions from the results which we achieved by gravimeter and ATR-FTIR. Compared to the gravimeter which is a conventional method for absorption test, the ATR-FTIR method in this study has been found to be very easy to use and have the same accuracy as gravimeter. Moreover, we are expecting to use the ATR-FTIR as an appropriate method to study the absorption phenomena related to any kinds of solvent and polymer system.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.2
• /
• pp.137-144
• /
• 1997

The effcct of specific g~avity cont~olled In the .range fiom O.4 to 0.7 by particle size and added amount of A1 powder in the presence or absence of water repellent agent on the physical properties of ALC was examined to evaluate frost resistance and durability. The compressive sttcngth and the tensile strength are increased and independency with water repellent agent when the specific gravity is increased in the range from 0.4 to 0.7. According as the added amount of water repellent agent was increased. frost resistance was improved and absorption ratio was decreased. ALC produced from fine Al powder has a low volume reduction by scaling and a sound apperance after freezing/thawing test and top surface freezing test.

• Korean Chemical Engineering Research
• /
• v.49 no.1
• /
• pp.120-127
• /
• 2011

For the development of the environment-friendly insulating composite materials, natural cellulose (wood chip and sawdust) was used as a core material and activated Hwangtoh was used as a binder. Various specimens were prepared with the water/binder ratio and natural cellulose/binder ratio. The physical properties of these specimens were then investigated through compressive and flexural strength test, absorption test, hot water resistance test, thermal conductivity, measurement of pore distribution and observation of micro-structures using scanning electron microscope (SEM). Results showed that the absorption ratio increased with the increase of natural cellulose/binder ratio but decreased remarkably with the increase of polymer/binder ratio. The compressive and flexural strength development varied appreciably with the increase of water/binder ratio and natural cellulose/binder ratio. On the other hand, thermal conductivity decreased with the increase of natural cellulose/binder ratio and polymer/binder ratio. Through SEM, it was found that activated Hwangtoh that reacted with water formed a hydrate crystal leading to the compact structure and the total pore volume of the specimen using activated Hwangtoh was smaller than that of the non-activated Hwangtoh.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.34 no.12
• /
• pp.2062-2072
• /
• 2010

This research evaluates the change of the water absorbency and drying speed of a quick-drying knit fabric by repeated laundering and laundering conditions and investigates the influence of laundering conditions on the functional properties of the knit fabric. Four factors of laundering conditions were studied: detergent, water hardness, water temperature, and frequency of rotation. Knit fabrics were washed for 25 laundering cycles in a drum-type washing machine with nine different laundering conditions derived from an orthogonal array. The properties of knit fabrics were measured with a drop absorption test, a strip test, and a drying time test. Relaxation shrinkage pointed to a change in the structural characteristics of the knit fabric. Wetting time was faster and wickability was greater in the knit fabrics that underwent 5 laundering cycles; in addition, there were no obvious changes in wetting time and wickability. The detergent was the most important factor in wetting time (40.4%) and wickability (60% or above). Water hardness, water temperature and RPM had less of an effect on wetting time and wickability. There were no significant differences between the levels of laundering conditions (except for detergent) on wetting time and wickability. Drying times with neutral and alkali were slower by repeated laundering; however, there was no obvious change in drying time. Hardness, water temperature and RPM had less of an impact on drying time.

• Journal of Conservation Science
• /
• v.25 no.1
• /
• pp.77-86
• /
• 2009

The physical properties of the epoxy resins were studied with an addition of filler content and the application of artificial weathering test. When talc as a filler was added to the epoxy resin (L-30), the water resistance seemed to be increased because of the results of the reducing of water absorption rate and the increasing of contact angle. Although the adhesive strength of epoxy resins was not affected by the increasing amount of talc, its compressive strength was reduced. The physical properties of the epoxy resins had different trends according to the site environments. The artificial weathering test with the change of temperature and humidity showed that the changes of water absorption rate and colour differences of the epoxy resins containing talc were lower than the pure epoxy resin itself. However, the contact angle was higher. The artificial weathering test with ultraviolet irradiations showed the opposite result; the damage of epoxy resins was increased with the increasing of talc content. These mean the site environment of the stone monuments should be considered to determine the content of talc added to increase the durability of epoxy resin.