• Journal of dental hygiene science
• /
• v.13 no.2
• /
• pp.135-141
• /
• 2013

One factor for successful prognosis of finished dental prosthesis is good marginal fit. The purpose of this study in vitro investigation was to compare the marginal fit of all-ceramic crown before and after porcelain veneering, to evaluate the influence of high temperature of the porcelain firing on the fit. For this experiment, model of abutment tooth of maxillary right central incisor was prepared. Ten working models were produced. Ten zirconia cores were made by dental computer aided design/computer aided manufacturing system. The marginal fit of specimens were examined using silicone replica technique. Silicone replicas were sectioned four times and were measured through a digital microscope (${\times}160$). Marginal fit is a distance connected between edge end part of specimen and abutment margin. Each specimens was measured twice, the first measurement was done prior to veneering porcelain firing, while the second measurement was done after the porcelain firing to evaluate this process. Statistical analyses were performed with paired t-test. $Mean{\pm}SD$ marginal fit was $60.8{\pm}14.2{\mu}m$ for zirconia core and $86.1{\pm}13.3{\mu}m$ for all-ceramic crown. They were statistically significant differences (p<0.001). But all specimens showed a marginal fit where the gap widths ranged within the clinical recommendation ($120{\mu}m$), all-ceramic crown production using the zirconia core was adequate.

• Journal of dental hygiene science
• /
• v.14 no.3
• /
• pp.405-410
• /
• 2014

The purpose of this study in vitro investigation was to compare the marginal and internal fit of Ni-Cr alloy metal ceramic crown before and after porcelain veneering. Furthermore, this study evaluated whether the influence of the porcelain firing on the precision of fit of dental prostheses. The maxillary right incisor was selected as an abutment for experiments. Ten working models were prepared. Ni-Cr alloy cores appropriate for each abutment were prepared by lost wax technique. The marginal area and four internal areas of the crowns were measured at two stages: before veneering process and after upper porcelain firing. Silicone replica techniques were used. The data were statistically analyzed with the paired t-test (${\alpha}=0.05$). $Mean{\pm}SD$ marginal and internal gap were $67.1{\pm}23.3{\mu}m$ for the nickle chrome alloy core group and $74.4{\pm}21.9{\mu}m$ for the metal ceramic crown group. There were statistically significant differences in all investigated areas (p<0.05). Within the limitations of this study, none of the Ni-Cr alloy metal crown values measured after porcelain firing process exceeded $120{\mu}m$, which is the clinically acceptable threshold.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.3
• /
• pp.152-158
• /
• 2017

PURPOSE. The purpose of this study was to evaluate the influence of different coping thicknesses and veneer ceramic cooling rates on the failure load of zirconia-ceramic crowns. MATERIALS AND METHODS. Zirconia copings of two different thicknesses (0.5 mm or 1.5 mm; n=20 each) were fabricated from scanning 40 identical abutment models using a dental computer-aided design and computer-aided manufacturing system. Zirconia-ceramic crowns were completed by veneering feldspathic ceramics under different cooling rates (conventional or slow, n=20 each), resulting in 4 different groups (CONV05, SLOW05, CONV15, SLOW15; n=10 per group). Each crown was cemented on the abutment. 300,000 cycles of a 50-N load and thermocycling were applied on the crown, and then, a monotonic load was applied on each crown until failure. The mean failure loads were evaluated with two-way analysis of variance (P=.05). RESULTS. No cohesive or adhesive failure was observed after fatigue loading with thermocycling. Among the 4 groups, SLOW15 group (slow cooling and 1.5 mm chipping thickness) resulted in a significantly greater mean failure load than the other groups (P<.001). Coping fractures were only observed in SLOW15 group. CONCLUSION. The failure load of zirconia-ceramic crowns was significantly influenced by cooling rate as well as coping thickness. Under conventional cooling conditions, the mean failure load was not influenced by the coping thickness; however, under slow cooling conditions, the mean failure load was significantly influenced by the coping thickness.

• The Journal of Advanced Prosthodontics
• /
• v.3 no.2
• /
• pp.57-62
• /
• 2011

MATERIALS AND METHODS. Ceramics have a long history in fixed prosthodontics for achieving optimal esthetics and various materials have been used to improve ceramic core strength. However, there is a lack of information on how color is affected by fabrication procedure. The purpose of this study was to evaluate the effects of various dentin ceramic thicknesses and repeated firings on the color of zirconium oxide all-ceramic system (LavaTM) fabricated using CAD/CAM technology. MATERIALS AND METHODS. Thirty disc-shaped cores, 12 mm in diameter with a 1 mm thickness were fabricated from zirconium oxide based all ceramic systems ($Lava^{TM}$, 3M ESPE, St Paul, MN, USA) and divided into three groups (n = 10) according to veneering with dentin ceramic thicknesses: as 0.5, 1, or 1.5 mm. Repeated firings (3, 5, 7, or 9) were performed, and the color of the specimens was compared with the color after the initial firing. Color differences among ceramic specimens were measured using a spectrophotometer (VITA Easyshade, VITA Zahnfabrik, Bad $S{\ddot{a}}ckingen$, Germany) and data were expressed in CIELAB system coordinates. A repeated measures ANOVA and Bonferroni post hoc test were used to analyze the data (n = 10, ${\alpha}=.05$). RESULTS. $L^{\ast}a^{\ast}b^{\ast}$ values of the ceramic systems were affected by the number of firings (3, 5, 7, or 9 firings) (P<.001) and ceramic thickness (0.5, 1, or 1.5 mm) (P<.001). Significant interactions were present in $L^{\ast}a^{\ast}b^{\ast}$ values between the number of firings and ceramic thickness (P<.001). An increase in number of firings resulted in significant increase in $L^{\ast}$ values for both 0.5 mm and 1.5 mm thicknesses (P<.01, P=.013); however it decreased for 1 mm thickness (P<.01). The $a^{\ast}$ values increased for 1 mm and 1.5 mm thicknesses (P<.01), while it decreased for 0.5 mm specimens. The $b^{\ast}$ values increased significantly for all thicknesses (P<.01, P=.022). As the dentin ceramic thickness increased, significant reductions in $L^{\ast}$ values (P<.01) were recorded. There were significant increases in both $a^{\ast}$ and $b^{\ast}$ values (P<.01) as the dentin ceramic thickness increased. CONCLUSION. The number of firings and dentin ceramic thickness have a definite effect on the final color of all ceramic system tested. The mean ${\Delta}E$ value increased as the dentin ceramic thicknesses increased for zirconium-oxide based all ceramic specimens tested. However, the mean ${\Delta}E$ values were less than 3.7${\Delta}E$ units which is rated as a match in the oral environment.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.1
• /
• pp.89-98
• /
• 2003

Titanium requires special ceramic system for veneering. Low fusing dental ceramics with coefficients of thermal expansion matching that of titanium have been developed. The purpose of this study was determine the bond strengths between cast and noncast pure titanium and two commercial titanium porcelains, and to compare the results with a conventional nickel-chromium alloy-ceramic system. The bond strengths were determined using a 3-point flexure test. Three-point flexure specimens $25{\times}3{\times}0.5mm$ were prepared After removal of ${\alpha}-case$ layer, they were veneered with $8{\times}3{\times}1mm$ of ceramics at the center of the bar. Specimens were tested in a universal testing machine. Within the limits of this study, the following conclusions were drawn: 1. The bond strengths between pure titanium and two commercial porcelains exceeded th lower limit of the bonding strength value in ISO 9693(25MPa). 2. There was no significant difference between cast and noncast titanium-porcelain bonds. 3. There was no significant difference between two commercial titanium porcelains. 4. The bond strengths of the titanium-porcelain systems ranged from 73% to 79% of that of the Ni-Cr-conventional porcelain system.

• The Journal of Advanced Prosthodontics
• /
• v.4 no.2
• /
• pp.76-83
• /
• 2012

PURPOSE. Zirconia has been used in clinical dentistry for approximately a decade, and there have been several reports regarding the clinical performance and survival rates of zirconia-based restorations. The aim of this article was to review the literatures published from 2000 to 2010 regarding the clinical performance and the causes of failure of zirconia fixed partial dentures (FPDs). MATERIALS AND METHODS. An electronic search of English peer-reviewed dental literatures was performed through PubMed to obtain all the clinical studies focused on the performance of the zirconia FPDs. The electronic search was supplemented by manual searching through the references of the selected articles for possible inclusion of some articles. Randomized controlled clinical trials, longitudinal prospective and retrospective cohort studies were the focuses of this review. Articles that did not focus on the restoration of teeth using zirconia-based restorations were excluded from this review. RESULTS. There have been three studies for the study of zirconia single crowns. The clinical outcome was satisfactory (acceptable) according to the CDA evaluation. There have been 14 studies for the study of zirconia FPDs. The survival rates of zirconia anterior and posterior FPDs ranged between 73.9% - 100% after 2 - 5 years. The causes of failure were veneer fracture, ceramic core fracture, abutment tooth fracture, secondary caries, and restoration dislodgment. CONCLUSION. The overall performance of zirconia FPDs was satisfactory according to either USPHS criteria or CDA evaluations. Fracture resistance of core and veneering ceramics, bonding between core and veneering materials, and marginal discrepancy of zirconia-based restorations were discussed as the causes of failure. Because of its repeated occurrence in many studies, future researches are essentially required to clarify this problem and to reduce the fracture incident.

• The Journal of Korean Academy of Prosthodontics
• /
• v.51 no.1
• /
• pp.47-51
• /
• 2013

With the introduction of dental implants, restoration of missing teeth with conventional fixed or removable partial dentures is being replaced with implants. Especially, with young patients, not only longevity but also esthetic factors need to be considered. Implant restorations provide long-term success functionally but, esthetic complications such as, marginal exposure due to gingival recession, loss of the papilla and dark color of metal abutments may occur. Recently, zirconia restorations with CAD/CAM technology provide functional, biocompatible and esthetic restorations possible. All-ceramic restorations using the pressed ceramic technique show better fracture toughness values than those of the conventional porcelain veneering technique. Pressed ceramic technique creates the veneer design in wax and the lost wax technique is used to create the restoration. The final contour of the restoration may be controlled during wax-up. A 22-year old female patient was restored with dental implants and zirconia restorations using the pressed ceramic technique presenting short-term but optimistic prognosis.

• Journal of Technologic Dentistry
• /
• v.31 no.1
• /
• pp.23-36
• /
• 2009

The goal of esthetic restoration is to achieve morphologic, optical, and biologic acceptance. Creation of a natural looking ceramic restoration, which blends harmoniously with surrounding dentition, is not always achieved. A successful color match is an important aspect of any esthetic dental restoration. Since natural enamel has inherent translucency, it is important that ceramic restorations reproduce the translucency and color of the natural teeth. However, the final color match of porcelain crowns to adjacent natural dentition remains some problem. Difficulties related to color matching arise from the structural differences that exist between metal ceramic crowns and natural teeth, the limited range of available ceramic shades, inadequate shade guides, different types of metal alloys, repeated firing, the condensation technique, and varying compositions of ceramic materials. Many factors contribute to the esthetic success of dental restoration: optical properties such as color and its elements of hue, value, and chroma; translucency and opacity; light transmission and scattering; and metamerism and fluorescence. The purpose of this study was to determine the color changes of metal-ceramic system with different veneering porcelain powder after repeated firing. The objectives of this in vitro study were to measure the lightness($L^*$), chromaticity($a^*$), chromaticity($b^*$), chroma($C^*$), hue(h), reflectance(%), color difference(${\Delta}E$). The following conclusions were obtained: 1. An increase in the number of firings resulted in decrease in lightness($L^*$) but increase in chromacticity($a^*$) with all porcelain. After the second sintering resulted in decrease in chromacticity($b^*$) with opaque-dentin porcelain and dentin porcelain but in increase with enamel porcelain and translucency porcelain. And after the second sintering resulted in decrease in chroma($C^*$) with opaque-dentin porcelain and dentin porcelain, but on the whole side in decrease with enamel porcelain and translucency porcelain. 2. After the second firing, a increase in the number of firings resulted in decrease reflectance(%) in all wavelength. 3. There were noticeable color differences(${\Delta}E$) between first sintering and multiple firings(dentin porcelain: 5.29~8.15, opaque-dentin porcelain: 4.83~8.2, enamel porcelain: 8.93~13.15, translucency porcelain: 9.37~12.91), but the color difference(${\Delta}E$) after second sintering were down to 4.87 in all porcelain. 4. Given the NBS Criteria, a 'trace' was not found this study but a 'slight' was found 2-3, 3-5 in dentin porcelain, 2-3 in opaque-dentin porcelain, 3-5, 5-10 in enamel porcelain and translucency porcelain, a 'noticeable' was 2-5, 3-10, 5-10 in dentin porcelain and opaque-dentin porcelain, 2-3, 2-5, 3-10 in enamel porcelain 2-3, 3-10 in translucency porcelain, an 'appreciable' was 1-2, 1-3, 2-10 in dentin porcelain 1-2, 1-3, 2-10, 3-10 in opaque-dentin porcelain, 2-10 in enamel porcelain, 2-5, 2-10 in translucency porcelain, a 'much' was 1-5, 1-10 in dentin porcelain and opaque-dentin porcelain, 1-2, 1-3, 1-5 in enamel porcelain 1-2, 1-3, 1-5, 1-10 in translucency porcelain, a 'very much' was 1-10 in enamel porcelain.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.2
• /
• pp.146-150
• /
• 2015

PURPOSE. This in vitro study aimed to compare the failure load and failure characteristics of two different zirconia framework designs of premolar crowns when subjected to static loading. MATERIALS AND METHODS. Two types of zirconia frameworks, conventional 0.5 mm even thickness framework design (EV) and 0.8 mm cutback of full contour crown anatomy design (CB), were made for 10 samples each. The veneer porcelain was added on under polycarbonate shell crown made by vacuum of full contour crown to obtain the same total thickness of the experiment crowns. The crowns were cemented onto the Cobalt-Chromium die. The dies were tilted 45 degrees from the vertical plane to obtain the shear force to the cusp when loading. All crowns were loaded at the lingual incline of the buccal cusp until fracture using a universal testing machine with cross-head speed 0.5 mm/min. The load to fracture values (N) was recorded and statistically analyzed by independent sample t-test. RESULTS. The mean and standard deviations of the failure load were $1,170.1{\pm}90.9$ N for EV design and $1,450.4{\pm}175.7$ N for CB design. A significant difference in the compressive failure load was found (P<.05). For the failure characteristic, the EV design was found only cohesive failures within veneering porcelain, while the CB design found more failures through the zirconia framework (8 from 10 samples). CONCLUSION. There was a significant difference in the failure load between two designs, and the design of the framework influences failure characteristic of zirconia crown.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.24 no.1
• /
• pp.113-127
• /
• 2008

The purpose of this study was to evaluate effect of application of $ZirLiner^{(R)}$ and blasting treatments on shear bond strength of zirconia-veneered porcelain interface. 60 uncolored zirconia plates and 30 colored zirconia plates were fabricated and divided into nine groups of 10 according to blasting treatment such as as-ground, glass blasting and alumina blasting and zirliner application. Veneering porcelains were built up over the center of the treated zirconia ceramic surface using jig and fired according to the manufacturers' instructions. Each specimen was completely embedded in acrylic resin. The specimens were placed in a mounting jig and subjected to shear force by a universal testing machine. Load was applied at a crosshead speed of 0.5㎜/min until failure. Average shear strengths were analyzed with two-way analysis of variance and one-way analysis of variance and the Duncan's post-hoc test. The fracture surfaces of the failed specimens were examined by SEM. The obtained results were as follows: 1. Depending on surface treatment by blasting, the degree of roughness is revealed in the order of Glass-blasted, As-ground, and Alumnia-blasted. The roughness average of uncolored and colored zirconia ceramic were not significantly different from blasting treatments. 2. In uncolored zirconia ceramic, the shear bond strength were not significantly different from blasting treatments. However, the shear bond strength were significantly different from Zirliner application. 3. Used ZirLiner, mean shear bond strength of colored zirconia was lower than uncolored zirconia. Especially, mean shear bond strength of colored zirconia was quite low with alumina-blasting treatment. 4. SEM analysis showed that veneered porcelain failed in zirconia ceramic interface and there was no cohesive failure.