Effect of Application of ZirLiner® and Blasting Treatments on Shear Bond Strength of Zirconia-Veneered Porcelain Interface  

Shin, Young-Ho (Department of Prosthodontics, College of Dentistry, Wonkwang University)
Lee, Yu-Na (Department of Biomaterials Science, College of Dentistry, Dankook University)
Lee, Hae-Hyoung (Department of Biomaterials Science, College of Dentistry, Dankook University)
Dong, Jin-Keun (Department of Prosthodontics, College of Dentistry, Wonkwang University)
Oh, Sang-Chun (Department of Prosthodontics, College of Dentistry, Wonkwang University)
Publication Information
Journal of Dental Rehabilitation and Applied Science / v.24, no.1, 2008 , pp. 113-127 More about this Journal
Abstract
The purpose of this study was to evaluate effect of application of $ZirLiner^{(R)}$ and blasting treatments on shear bond strength of zirconia-veneered porcelain interface. 60 uncolored zirconia plates and 30 colored zirconia plates were fabricated and divided into nine groups of 10 according to blasting treatment such as as-ground, glass blasting and alumina blasting and zirliner application. Veneering porcelains were built up over the center of the treated zirconia ceramic surface using jig and fired according to the manufacturers' instructions. Each specimen was completely embedded in acrylic resin. The specimens were placed in a mounting jig and subjected to shear force by a universal testing machine. Load was applied at a crosshead speed of 0.5㎜/min until failure. Average shear strengths were analyzed with two-way analysis of variance and one-way analysis of variance and the Duncan's post-hoc test. The fracture surfaces of the failed specimens were examined by SEM. The obtained results were as follows: 1. Depending on surface treatment by blasting, the degree of roughness is revealed in the order of Glass-blasted, As-ground, and Alumnia-blasted. The roughness average of uncolored and colored zirconia ceramic were not significantly different from blasting treatments. 2. In uncolored zirconia ceramic, the shear bond strength were not significantly different from blasting treatments. However, the shear bond strength were significantly different from Zirliner application. 3. Used ZirLiner, mean shear bond strength of colored zirconia was lower than uncolored zirconia. Especially, mean shear bond strength of colored zirconia was quite low with alumina-blasting treatment. 4. SEM analysis showed that veneered porcelain failed in zirconia ceramic interface and there was no cohesive failure.
Keywords
shear bond strength; $ZirLiner^{(R)}$ and blasting treatments; zirconia-veneered porcelain interface;
Citations & Related Records
Times Cited By KSCI : 3  (Citation Analysis)
연도 인용수 순위
1 Kelly J, Campbell S, Bowen H. Fracture-surface analysis of dental ceramics. J Prosthet Dent 1989;62:536-541   DOI   ScienceOn
2 Yamamoto M. Metal-Ceramics. Quintessence. Pub. Co. Tokyo, 1985
3 Guggeberger R. Rocatec system-Adhesion by tribochemical coating. Dtsch Zahnarztl Z 1989;44: 874-876
4 Grey NJA, Wilson MA. In vitro comparison of conventional crowns and a new all-ceramic system. J Dent 1992;21:47-51   DOI   ScienceOn
5 Probster L. Compressive strength of two modern all-ceramic crowns. Int J Prosthodont 1992;5:409- 414
6 Shimizu K, Oka M, Kumar P, Kotoura Y, Yamamuro T, Makinouchi K, et al. Timedependent changes in the mechanical properties of zirconia ceramic. J Biomed Mater Res 1993;27:729-734   DOI   ScienceOn
7 Christel P, Meunier A, Heller M, Torre JP, Peille CN. Mechanical properties and short-term in-vivo evaluation of yttrium-oxide partially stabiliwed zirconia. J Biomed Mater Res 1989;23:45-61   DOI   ScienceOn
8 Kosmac T, Oblak C, Jevnikar P, Funduk N, Marion L. The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic. Dent Mater 1999;15:426-433   DOI   ScienceOn
9 오상천, 이해형, 신미란, 이일권. 전부도재수복물을 위한 유색 및 무색 지르코니아 세라믹의 굴곡강도. 대한치과턱관절기능교합학회지 2007;23: 119-130
10 Sundh A, Molin M, Sjogren G. Fracture resistance of yttrium oxide partially-stabilized zirconia all-ceramic bridges after veneering and mechanical fatigue testing. Dent Mater 2005;21:476-482   DOI   ScienceOn
11 Albakry M, Guazzato M, Swain MV. Fracture toughness and hardness evaluation of three pressable all-ceramic dental materials. J Dent 2003;31:181-188   DOI   ScienceOn
12 Dündar M, Ozcan M, Gokce B, Comlekoglu E, Leite F, Valandro LF. Comparison of two bond strength testing methodolgies for bilayered all-ceramics. Dent Mater 2007;23:630-636   DOI   ScienceOn
13 Friedlander LD, Munoz CA, Goodacre CJ, Doyle MG, Moore BK. The effect of tooth preparation design on the breaking strength of Dicor crowns. Int J Prosthodont 1990;3:159-168
14 Tinschert J, Natt G, Mautsch W, Spiekermann H, Anusavice KJ. Marginal fit of alumina and zirconia-based fixed partial dentures produced by a CAD/CAM system. Oper Dent 2001;26:367-374
15 Tinschert J, Zwez D, Marx R, Anusavice KJ. Structural reliability of alumina-, feldspar-, leucite-, mica- and zirconia-based ceramics. J Dent 2000;28:529-535   DOI   ScienceOn
16 Chen HY, Hickel R, Setcos JC, Kunzelmann KH. Effects of surface finish and fatigue testing on the fracture strength of CAD-CAM and pressed-ceramic crowns. J Prosthet Dent 1999;82(4):468-475   DOI   ScienceOn
17 Luthardt RG, Holzhuter M, Sandkuhl O, Herold V, Schnapp JD, Kuhlisch E, et al. Reliability and properties of ground Y-TZP zirconia ceramics. J Dent Res 2002;81:487-491   DOI   ScienceOn
18 오상천, 이해형, 신미란, 박광수. 전부도재수복물을 위한 수종의 코어 세라믹의 반투명도 및 색 안정성. 대한치과턱관절기능교합학회지 2007;23: 157-170
19 Kelly JR, Nishimura I, Cambell SD. Ceramics in dentistry: historical roots and current perspectives. J Prosthet Dent 1996;75:18-32   DOI   ScienceOn
20 Albakry M, Guazzato M, Swain MV. Fracture toughness and hardness evaluation of three pressable all-ceramic dental materials. J Dent 2003;31:181-188   DOI   ScienceOn
21 Guazzato M, Proos K, Quach L, Swain MV. Strength, reliability and mode of fracture of bilayered porcelain/zirconia (Y-TZP) dental ceramics. Biomaterials 2004;25:5045-5052   DOI   ScienceOn
22 Aboushelib MN, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations. Part II: Zirconia veneering ceramics. Dent Mater 2006;22: 857-863   DOI   ScienceOn
23 Sundh A, Sjogren G. A comparison of fracture strength of yttrium-oxide-partially-stabilized zirconia ceramic crowns with varying core thickness, shapes and veneer ceramics. J Oral Rehabil 2004;31: 682-688   DOI   ScienceOn
24 Scherrer SS, Robert Kelly J, Quinn GD, Xu K. Fracture toughness (KIc) of a dental porcelain determined by fractographic analysis. Dent Mater 1999;15:342-348   DOI   ScienceOn
25 Komine F, Tomic M, Gerds T, Strub JR. Influence of different adhesive resin cements on the fracture strength of aluminum oxide ceramic posterior crowns. J Prosthet Dent 2004;92:359-364   DOI   ScienceOn
26 Pallis K, Griggs JA, Woody RD, Guillen GE, Miller AW. Fracture resistance of three all-ceramic restorative systems for posterior applications. J Prosthet Dent 2004;91:561-569   DOI   ScienceOn
27 Thompson JY, Anusavice KJ, Naman A, Morris HF. Fracture surface characterization of clinically failed all-ceramic crowns. J Dent Res 1994;73:1824-1832   DOI
28 Wirz J, Hoffman A. Electroforming in restorative dentistry: new dimensions in bilologically based protheses. Quintessence Pub. Co. 1999
29 Scherrer SS, Robert Kelly J, Quinn GD, Xu K. Fracture toughness (KIc) of a dental porcelain determined by fractographic analysis. Dent Mater 1999;15:342-348   DOI   ScienceOn
30 Rosenblum MA, Schulman A. A review of all- ceramic restorations. J Am Dent Assoc 1997;128: 297-307   DOI
31 Traini T. Electroforming technology for ceramometal restoration. QDT 1995:21-29
32 Wagner WC, Chu TM. Biaxial flexural strength and indentation fracture toughness of there new dental core ceramics. J Prosthet Dent 1996;76:140-144   DOI   ScienceOn
33 Al-Dohan HM, Yaman P, Dennison JB, Razzoog ME, Lang BR. Shear strength of core-veneer interface in bi-layered ceramics. J Prosthet Dent. 2004;91: 349-355   DOI   ScienceOn
34 Kim CH, Jeon YC, Jeong CM, Lim JS. Effect of surface treatments of zirconia ceramic on the bond strength of resin cements. J Korean Acad Prosthodont 2004;42(4):386-396
35 Thompson G. Influence of relative layer height and testing method on the failure mode and origin in a bilayered dental ceramic composite. Dent Mater 2000;16:235-243   DOI   ScienceOn
36 Zhang Y, Lawn BR, Rekow ED, Thompson VP. Effect of sandblasting on the long-term performance of dental ceramics. J Biomed Mater Res Pt B Appl Biomater 2004;71B:381-386   DOI
37 De Jager N, Pallav P, Feilzer AJ. The influence of design parameters on the FEA-determined stress distribution in CAD-CAM produced all-ceramic dental crowns. Dent Mater 2005;21:242-251   DOI   ScienceOn
38 Josephson BA, Schulman A, Dunn ZA, Hurwitz W. A compressive strength study of complete ceramic crowns. Part II. J Prosthet Dent 1991;65:388-391   DOI   ScienceOn
39 Huang H, Zhang FQ, Sun J, Gao L. Effect of three kinds of rare earth oxides on chromaticity and mechanical properties of zirconia ceramic. Zhonghua Kou Qiang Yi Xue Za Zhi. 2006;41:327-330
40 류경희, 이선형. Dicor와 수종 전장도재간의 전단결합강도. 대한치과보철학회지. 1993;31:165-179
41 Fleming GJP, El-Lakwah SFA, Harris JJ, Marquis PM. The influence of interfacial surface roughness on bilayered ceramic specimen perfomance. Dent Mater 2004;20:142-149   DOI   ScienceOn
42 Southan DE, Jorgensen KD. Faulty in porcelain jacket crowns. Aust Dent J 1973;18:152-156   DOI   ScienceOn
43 Kwon HB, Yim SH. A qualitative analysis of bonding between electroformed surface and veneering ceramics. J Korean Acad Prosthodont 2000;38: 328-335   과학기술학회마을
44 Isgro G, Pallav P, van der Zel JM, Feilzer AJ. The influence of the veneering porcelain and different surface treatments on the biaxial flexural strength of a heat-pressed ceramic. J Prosthet Dent 2003;90:465-473   DOI   ScienceOn
45 Willamnn G, Fruh HJ, Pfaff HG. Wear characteristics of sliding pairs of zirconia(Y-TZP) for hip endoprostheses. Biomaterials 1996;17:2157-162   DOI   ScienceOn
46 Aboushelib M, De Jager N, Pallav P, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations. Dent Mater 2005;21:984-991   DOI   ScienceOn
47 Kelly N, Asgar K, O'Brien JJ. Tensile strength determination of the interface between porcelain fused to gold. J Biomed Mat Res 1969;3:403   DOI